Protection of bridges against stray current corrosion
PublikacjaA case study of Siennicki Bridge stray current corrosion hazard is presented. A corrosion risk was caused by incorrectly designed tram line traction which goes over the bridge. No dielectric insulation between running rails and bridge steel construction was used. A variety of protection methods against stray currents are described. Characteristics of the endangered bridge were described. Impressed current cathodic protection system...
-
Case Study of Stray Current Corrosion of Tall Ship Mast
PublikacjaNowadays, in the present technical civilization there are numerous complex technical systems that may generate various hazards. Large transport units like ships can be considered as the most dangerous systems. Therefore, it is important to eliminate all possible hazards, especially for ship crewmembers. Destruction of ship structural components caused by vast corrosion is one of these hazards. Usually, its activity leads to a decrease...
-
Some Aspects of Potential Measurements in a Stray Current Field
Publikacja -
Method of sacrificial anode dual transistor-driving in stray current field
PublikacjaIn order to control a magnesium anode in a stray current interference field, a dual transistor driving system has been proposed. It consisted of a combination of PNP and NPN transistors. Dual transistor driven system and direct anode to cathode connection were electrochemically tested in 3% NaCl solution. The dual transistor driven system increased the anode efficiency and reduced hydrogen evolution and the risk of embrittlement....
-
Detection of stray current field interference on metal constructions using STFT
PublikacjaZaprezentowano metodę detekcji pola prądów błądzących wykorzystującą krótkoczasową transformatę Fouriera STFT. Ten sposób analizy umożliwia wyznaczenie zmian spektralnej gęstości mocy sygnału (np. potencjału konstrukcji) w funkcji czasu. Przedstawiono rezultaty analizy zmian potencjału w polu prądów błądzących generowanych przez trakcję tramwajową. Spektrogramy są kompozycją prążków w łącznej dziedzinie czasu i częstotliwości....
-
A new time-frequency detection method of stray current field interferenceon metal structures.
PublikacjaA new detection method has been presented of stray current field interference on underground metal structures. The method employs short time Fourier transformation (STFT). This method of analysis allows determination of signal spectral power density changes (e.g., structure potential) in the function of time. In the paper results have been presented of total time–frequency analysis of a pipeline potential in a stray current field...
-
Electrolytic corrosion of water pipeline system in the remote distance from stray currents– case study
PublikacjaCase study of corrosion failure of urban water supply system caused by the harmful effects of stray currents was presented. The failure occurred at a site distant from the sources of these currents namely the tramway and railway traction systems. Diagnosis revealed the stray currents flow to pipeline over a remote distance of 800 ÷ 1,000 meters from the point of failure. At the point of failure stray currents flowed from the pipeline...
-
The determination and identification of stray current source influences on buried pipelines using time/frequency analysis
PublikacjaZaprezentowano metodę detekcji źródła interferencji prądów błądzących na rurociągach podziemnych w aglomeracjach miejskich z wykorzystaniem łącznej analizy czasowo-częstotliwościowej mierzonych sygnałów. Badania przeprowadzono na rurociągu podziemnym zlokalizowanym w sąsiedztwie dwóch trakcji elektrycznych: tramwajowej i kolejowej. Wyniki analiz zaprezentowano w formie spektrogramów, które ilustrują zmiany spektralnej gęstości...
-
Determination of Local Corrosion Current from Individual Harmonic Components
PublikacjaHarmonic analysis has been used in corrosion measurements for several decades. During this period the method has been refined and developed. Nevertheless, the technique has not been applied to properties determination in local scale yet. This paper is focused on local corrosion current measurements based on harmonic analysis. For this purpose, a non-linear nature of electrode processes is used and measured in local scale applying...
-
Investigation of the Process of Automatic Control of Current Polarity Reversal in the Conditions of Hybrid Technology of Electrochemical Processing of Corrosion-Resistant Steels
Publikacja -
Potential changes in an electric field and electrolytic corrosion.
PublikacjaSources have been described of corrosively hazardous electric fields and methods of determination of the corrosion hazard to metal structures caused by electrolytic corrosion. Results of potential and impedance investigations in the field of stray currents flowing out of a tram traction and in the presence of a defined electric field of low frequency have been presented. Uncertainties have been indicated relating to the generally...
-
Detection and time/frequency analysis of electric fields in the ground
PublikacjaThis paper sets out to detect and characterize electric fields in the ground (such as stray current fields) using a tandem time/frequency method of signal analysis. Results were obtained from investigations performed in the presence of a generated electric field with controlled variable characteristics, and in the presence of an electric field generated by a tramline. The analysis of measurement registers was performed using Short‐Time...
-
Wybrane metody diagnostyki łożysk silników indukcyjnych oparte o pomiar prądu
PublikacjaW artykule zawarto przegląd wybranych metod diagnostyki łożysk silnika indukcyjnego, bazujących na pomiarach prądu zasilającego. Jedno z nowych rozwiązań przetwarzania sygnałów zostało zaadaptowane przez autorów do stosowanego przez nich systemu diagnostycznego. Wyniki wstępnych badań symulacyjnych zweryfikowanych badaniami na rzeczywistym obiekcie wskazują, że rozwiązanie to ułatwia diagnozowanie. Autorzy zamierzają prowadzić...
-
ANALIZA STANU TECHNICZNEGO RUROCIĄGÓW: WODY PRZeMYSŁOWEJ I SOLANKI
PublikacjaPracę wykonano na zlecenie Przedsiębiorstwa Badawczo-Wdrożeniowego "HYDRO-POMP" Sp. z o.o. ul. Wróblewskiego 19, 93-578 Łódź. Wykonawcą zlecenia jest Politechnika Gdańska, Wydział Chemiczny, Katedra Elektrochemii, Korozji i Inżynierii Materiałowej, 80-233 Gdańsk, ul. G. Narutowicza 11/12. Celem pracy była analiza stanu technicznego i badania dwóch rurociągów: solanki oraz wody przemysłowej. Badania wykonywano w warunkach terenowych...
-
Adaptive estimation of the transformer stray capacitances for DC–DC converter modelling
PublikacjaNew low cost and accurate estimation method of transformer stray capacitances for wide band DC–DC converter modelling and design is proposed. The Wiener filter (WF) method is applied to estimate the transformer impedance – referred to the selected transformer winding configurations. Laboratory tests are used to adapt the filter, that is to find optimal impedance which minimises mean square error between measured, noise perturbed...
-
Influence of plastic deformation on stray magnetic field distribution of soft magnetic steel sample
PublikacjaThe effect of various combinations of conditions, i.e., presence of the Earth’s magnetic field during and after deformation on the distribution of stray magnetic field of S355 steel sample, which is locally deformed, was investigated. Some of the stages of the experiment were carried out in zero magnetic field. Compensation of the Earth’s magnetic field was obtained by the application of a pair of Helmholtz coils. These coils are...
-
Discussion of Derivability of Local Residual Stress Level from Magnetic Stray Field Measurement
PublikacjaThe NDT procedure dubbed ‘metal magnetic memory’ method and the related ISO 24497 standard has found wide industrial acceptance in some countries, mainly in Russia and China. The method has been claimed by some researchers (Roskosz and Bieniek in NDT&E Int 45:55–62, 2012; Wilson et al. in Sens Actuators A 135:381–387, 2007) as having potential for quantitative determination of local residual stress state in engineering structures,...
-
Evaluation of the impact of geometry and plastic deformation on the stray magnetic field around the bone shaped sample
PublikacjaInfluence of two factors: the variable cross-section and the localized plastic deformation, which affect the stray magnetic field profile of a ferromagnetic sample have been studied. Evaluation of an effect size is based on the analysis of the stray magnetic field component which is tangential to the longest dimension of a sample. However, in order to describe the nature of the stray magnetic field, the normal component (perpendicular...
-
Isolation of the relative decrease in magnetic permeability contribution to reluctance of an open magnetic circuit based on stray field measurements
PublikacjaThe goal of the study was to evaluate a relative decrease in magnetic permeability in open magnetic circuits based on stray magnetic field measurements. The boundary element method was used to simulate magnetic circuits with variable geometry and variable magnetic permeability. The simulated magnetic circuits were rectangular or bone-shaped flat samples. Reluctance was increased in the middle of the samples resulting in leakage...
-
Development Of Dynamic Method For Evaluation Of Corrosion Rate On The Example Of Organic Corrosion İnhibitor
PublikacjaMeasurements of the corrosion rate belong to the most important aspects of materials science. In order to reduce material loss corrosion inhibitors are used. However selection of proper inhibitor should be based on evaluation of its mechanism and effective concentrations. Mechanism of inhibition usually has dynamic character so physicochemical parameters are changing in time. Most of actually used methods...
-
Application of the corrosion tester in corrosion tests using the acoustic emission method.
PublikacjaThe article presents an innovative method of corrosion tests using the acoustic emission method and the corrosion tester. The problem of corrosion occurring in ballast tanks and tanks carrying petroleum products is discussed. The acoustic method is presented which, due to the use of a unique corrosion tester, is used to monitor the course of corrosion processes in steel. The principle of operation of the corrosion tester, its construction...
-
High temperature corrosion and corrosion protection of porous Ni22Cr alloys
PublikacjaIn this work corrosion kinetics of the porous IN625 alloy is studied in the temperature range of 700 °C – 800 °C in air and humidified hydrogen for up to 1000 hours. Moreover, an effective and simple method of reducing corrosion rates of porous alloys by the infiltration of the rare earths elements is shown. Modification by the yttrium containing precursor reduces the corrosion rate by a factor of 50 in air at 700 °C so that the...
-
Effect of native air-formed oxidation on the corrosion behavior of AA7075 aluminum alloys
PublikacjaThe microstructure of aluminum alloys plays a key role in their corrosion resistance. In particular, the presence of intermetallic precipitates differing in the potential from the alloy matrix induces local corrosion. The study presents the effect of native air-formed oxidation on the corrosion behavior of AA 7075 aluminum alloy. Various microscopic and spectroscopic techniques were used to examine the changes occurring in the...
-
Instantaneous impedance monitoring of AA 7075 aluminum alloy corrosion in borate buffer with admixed chloride ions
PublikacjaThe study presents a research capabilities of Dynamic Electrochemical Impedance Spectroscopy (DEIS) as a tool used for instantaneous on-line monitoring of corrosion processes on the example of AA 7075 aluminum alloy. A borate buffer with admixed chloride ions in a quantity ranging from 0.05 to 25 mM was used to represent different types of corrosion attack. The surface of samples specimens was evaluated before and after the tests...
-
Influence of pitting corrosion on fatigue and corrosion fatigue of ship structures. Part I: pitting corrosion of ship structures.
PublikacjaThe paper is a literature survey focused on pitting corrosion and its influence on fatigue of ship and offshore steels. Mechanisms of short- and long-term pitting corrosion in marine environment have been described including pit nucleation and growth phases. Some models of pit growth versus time of exposure have been presented. Some factors which influence the pit growth have been discussed briefly.
-
Corrosion degradation impact on mechanical properties of structural steel
PublikacjaRecently, extensive research was conducted regarding the impact of corrosion degradation on the mechanical properties of structural steel. Studies show that at the material level, the microstructure is somewhat unchanged due to corrosion degradation. However, the corrosion causes pits and structural surface irregularities that consequently impact the mean stress-strain response of typical coupon specimens subjected to tensile loading....
-
Aqueous Molybdate Provides Effective Corrosion Inhibition of WE43 Magnesium Alloy in Sodium Chloride Solutions
PublikacjaCorrosion and corrosion inhibition of WE43 magnesium alloy were investigated in NaCl solutions containing different amounts of sodium molybdate. Electrochemical, microscopic, and spectroscopic experiments were utilized to examine the mechanism of corrosion inhibition by molybdates. Electrochemical data showed that Na2MoO4 inhibitor provides reliable inhibition at concentrations at and above 100 mM. Raman and XPS spectroscopy demonstrated...
-
Wet H2S corrosion and degradation of pipeline in amine regeneration system
PublikacjaThe paper presents the results of NDT examinations, metallographic tests and risk assessment of degradation related to corrosion of amine regeneration unit in a desulphurisation system. Intensive corrosion resulting from acid gases environment upon water condensation causes perforation of the pipeline. Detailed analysis reveals cracking related to the mechanism of wet H2S. Hydrogen penetration, resulting from the wet H2S process,...
-
Determination of pitting corrosion stage of stainless steel by galvanodynamic impedance spectroscopy
PublikacjaThis paper investigates the methodology for differentiation of multistep process of pitting corrosion of AISI 304 stainless steel in the environment of iron (III) chloride. Measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Application of this methodology allowed monitoring of natural corrosion process without external current (IDC = 0A) nor potential perturbation of the system. Applied...
-
Corrosion hazards and inhibitor protection in the seawater injection system on the Baltic sea rig
PublikacjaOil extraction efficiency in LOTOS Petrobaltic Company is increased by means of injection of seawater into an oilfield aquifer, which is implemented on the Baltic Beta rig, operating on the Baltic Sea. Operational experience has shown a significant degree of corrosion aggressiveness in the injected water, which necessitates frequent repairs of the seawater injection installation. Evaluation of the corrosion phenomena is crucial...
-
Novel fast non-linear electrochemical impedance method for corrosion investigations
PublikacjaThe paper presents a novel approach to corrosion rate monitoring using non-linear electrochemical impedance spectroscopy. The authors propose a new variant of non-linear impedance measurement using amplitude-modulated multi-frequency ac perturbation signal. It allows shortening of measurement duration so it is possible to monitor corrosion rate of the systems experiencing rapid changes. In this way a limitation resulting from lack...
-
Multi-sensor monitoring of the corrosion rate and the assessment of the efficiency of a corrosion inhibitor in utility water installations
PublikacjaThis paper presents an implementation of the monitoring of the corrosion rate and the assessment of the efficiency of a corrosion inhibitor in a utility water installation using an automated corrosion monitoring system. Due to the fact that the corrosion inhibitor was added to water intended for human consumption, it was necessary to build a multi-sensor monitoring system. In order to implement corrosion monitoring using a linear...
-
Surface and Corrosion Properties of AA6063-T5 Aluminium Alloy in Molybdate-containing Sodium Chloride Solutions
PublikacjaCorrosion properties of aluminium alloy AA6063-T5 were investigated in molybdate-containing NaCl solutions. Electrochemical, microscopic, and spectroscopic experiments were utilized to examine the mechanism of corrosion inhibition by molybdates. SEM-EDX, magnetic force, and intermodulation electrostatic force microscopy data suggested that the inhibition initiation preferentially occurred over Fe-rich cathodic IMPs. Spectroscopic...
-
Aspects of intergranular corrosion of AISI 321 stainless steel in high-carbon-containing environments
PublikacjaPurpose – The purpose of this paper is to present a case study of unexpected sensitization to intergranular corrosion of highly resistant AISI 321 steel in petrochemical conditions, where it was subjected to the simultaneous influence of elevated temperature of 250°C and vapors from the asphalt production process. Design/methodology/approach – Corrosion coupons were exposed in an installation carrying asphalt vapors. To identify...
-
The Application of Dynamic Electrochemical Impedance Spectroscopy (DEIS) Technique in Corrosion and Corrosion Inhibition Studies
Publikacjaorrosion studies have attracted considerable interest in the areas of materials chemistry and industrial chemistry, as it affects the direct and indirect costs of industry, leading to huge economic setbacks due to the need for repair, maintenance, and even shutdowns due corrosion damage. This new volume is a comprehensive resource that presents new and up-to-date, theoretical, and experimental corrosion inhibition studies.
-
Corrosion degradation of spacers – examination of changes in bone cement coating.
PublikacjaSpacer is a special implant used at the time of infection after endoprosthetic surgery. It consists of a metal core and bone cement coating with an antibiotic. In the human body spacers are exposed to degradation processes. This paper looks at the effect of corrosion on spacers. Electrochemical corrosion tests were performer on titanium pins with bone cement coating in two solutions: Ringer’s solution and artificial...
-
DETERMINATION OF THE EFFECT OF ENVIRONMENTAL FACTORS ON THE CORROSION OF WATER DISTRIBUTION SYSTEM BASED ON ANALYSIS OF ON-LINE CORROSION MONITORING RESULTS
PublikacjaCorrosion of water distribution system is a significant issue causing problems with quality, safety and continuity of distribution. The changes of corrosion rates of the water distribution systems in Cracow made of carbon steel were investigated by analysis of online corrosion monitoring system results. Corrosion rates were determined using the linear polarization method. The impact of rain, temperatures, conductivity, dissolved...
-
The effect of pre-hydrogen charging on corrosion behaviour of superduplex stainless steel welded joints
PublikacjaThe paper presents results of research undertaken to determine the influence of hydrogen on passivity and corrosion resistance of 2507 super duplex stainless steel welded joints. Butt welded joints were made with low heat input using flux corded arc welding (FCAW) method. Coupons of 5.0 x 5.0 mm were cut from the welded joints containing weld metal (WM), heat affected zone (HAZ) and parent metal (PM). Hydrogen was introduced...
-
The effect of current delay angle on tripping of residual current devices
PublikacjaPower electronics converters applied in domestic or similar installations may utilize current delay (phase) angle control to change the level of transferred power. Due to application of such types of converters, earth fault current in the installation may be strongly distorted. The current distortion level depends on a value of current delay angle. This delay angle also influences the tripping threshold of residual current devices....
-
Detection of high frequency current components by residual current devices
PublikacjaThe negative impact of current harmonics on the main components of residual current devices is presented. A solution for the improvement of the operation of residual current devices is proposed.
-
Experimental ultimate strength assessment of stiffened plates subjected to marine immersed corrosion
PublikacjaThis study experimentally analyses the impact of marine immersed corrosion degradation on the compressive strength of the stiffened plates where the lower degradation levels were considered. The corrosion degradation test was accelerated by controlling the natural corrosion environmental factors, avoiding applying an electric current. Different groups of corrosion degradation levels and initial plate thicknesses were investigated....
-
Exploring Mechanism of Corrosion Inhibition of WE43 and AZ31 Alloys by Aqueous Molybdate in Hank’s Solution by Multisine Impedimetric Monitoring
PublikacjaThe concept of utilizing multisine dynamic electrochemical impedance spectroscopy to monitor effectiveness of a model molybdate inhibitor for AZ31 and WE43 Mg alloys is proposed. The corrosion kinetics and instantaneous values of inhibition efficiency (IE) of molybdate at concentrations up to 150 mM were examined. The inhibitor provides inhibition in Hank’s solution at concentrations starting from ca. 25 mM, with the IE of about...
-
Current divider-based nanosecond high current pulse measuring systems
PublikacjaThis paper presents the analysis of the new approach to the measurement methodology of significant values (in order of hundreds of kA) and huge steepness (in order of MA/μs) current pulses based on current dividers along with a comparison of the various types transducers suitability in measuring systems with such extreme parameters. Such dividers are used to extend the measurement ranges of current transducers with limited current...
-
Influence of pitting corrosion on fatigue and corrosion fatigue of ship and offshore structures. Part II: Load - pit crack interaction
PublikacjaIn the paper has been discussed influence of stresses on general corrosion rate and corrosion pit nucleation and growth rate, whose presence has been questioned by some authors but accepted by most of them. Influence of pit walls roughness on fatigue life of a plate suffering pit corrosion and presence of so called "non damaging" pits which never lead to initiation of fatigue crack, has been presented. Possibility of prediction...
-
Corrosion monitoring by harmonic analysis in aqueous environments
PublikacjaThis paper presents tests concerning the rate of corrosion in non-alloy steel (type S235JR) in an aqueous environment, with an additive of sodium chloride by means of polarization resistance measurements and harmonic analysis. The tests have been carried out for steel samples exposed to the testing environment for six weeks, in order to obtain a constant rate of corrosion in the function of time. The measurements have aimed at...
-
Influence of Surface Modification of Titanium and Its Alloys for Medical Implants on Their Corrosion Behavior
PublikacjaTitanium and its alloys are often used for long-term implants after their surface treatment. Such surface modification is usually performed to improve biological properties but seldom to increase corrosion resistance. This paper presents research results performed on such metallic materials modified by a variety of techniques: direct voltage anodic oxidation in the presence of fluorides, micro-arc oxidation (MAO), pulse laser treatment,...
-
Time-current tripping characteristics of RCDs for sinusoidal testing current
PublikacjaLow-voltage electrical installations are verified initially – before being put into operation, as well as periodically – during their utilization. According to the IEC standards, the scope of the verification includes measurements of both the tripping current and the disconnection time of residual current devices (RCDs). Experiences in RCDs testing show that disconnection times of two or more similar RCDs can be quite different....
-
Corrosion Monitoring in Petroleum Installations—Practical Analysis of the Methods
PublikacjaThis paper presents the most typical corrosion mechanisms occurring in the petroleum industry. The methods of corrosion monitoring are described for particular corrosion mechanisms. The field and scope of the application of given corrosion-monitoring methods are provided in detail. The main advantages and disadvantages of particular methods are highlighted. Measurement difficulties and obstacles are identified and widely discussed...
-
Corrosion mechanisms in columns for atmospheric distillation of crude oil
PublikacjaThe paper presents the most common corrosion processes occurring in the columns for atmospheric distillation of crude oil. It describes the mechanisms leading to formation of the chemical compounds, which contribute to corrosion phenomena. The main technological factors influencing corrosion processes have been indicated. The paper also presents the interactions between particular corrosion mechanisms resulting in acceleration...
-
Corrosion behavior of hydrogen charged super duplex stainless steel welded joints
PublikacjaThe electrochemical behavior of the weld metal, heat-affected zone (HAZ), and base material of super duplex stainless steel (SDSS) welded joints, made with the application of flux-cored arc welding (FCAW) and submerged arc welding (SAW), were investigated with the use of metallographic examinations (optical microscopy and scanning electron microscopy), potentiodynamic polarization measurements and total hydrogen content determination...