Hydrogen embrittlement of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints under cathodic protection
PublikacjaThe effect of cathodic polarization conditions on hydrogen degradation of X2CrNiMoCuN25-6-3 super duplex stainless steel welded joints, obtained using flux cored arc and submerged arc welding methods, was evaluated. Slow strain rate tensile tests of base material and welded specimens, ferrite content measurements, scanning electron microscopy observations, and statistical analysis were performed. It was found that hydrogenation...
-
ENVIRONMENTAL DEGRADATION OF DISSIMILAR AUSTENITIC 316L AND DUPLEX 2205 STAINLESS STEELS WELDED JOINTS
PublikacjaThe paper describes structure and properties of dissimilar stainless steels welded joints between duplex 2205 and austenitic 316L steels. Investigations were focused on environmentally assisted cracking of welded joints. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement was determined in slow strain rate tests (SSRT) with the strain rate of 2.2 × 10–6 s–1. Chloride-inducted SCC was determined in the...
-
Sulfate‐reducing bacteria‐assisted hydrogen‐induced stress cracking of 2205 duplex stainless steels
PublikacjaThe paper presents the results of a laboratory investigation of the microbiologically assisted hydrogen‐induced stress cracking (HISC) of 2,205 duplex stainless steel (DSS). The testing of susceptibility toward HISC was performed with two different methods. Precharged in sulfate‐reducing bacteria (SRB), inoculated medium samples were subjected to slow strain‐rate testing in artificial seawater. In situ constant load tests were...
-
Hydrogen Damage in Superaustenitic 904L Stainless Steels
Publikacjaresults on the influence of hydrogen on corrosion resistance and of hydrogen embrittlement of 904L superaustenitic stainless steel were investigated. The cracking behavior was studied by performing a slow strain rate test in synthetic seawater under varying cathodic polarization conditions. The results showed that the steel’s plasticity varied with the applied cathodic current density. Significant reductions in ductility were found,...
-
Hydrogen Embrittlement and Oxide Layer E ect in the Cathodically Charged Zircaloy-2
PublikacjaThe present paper is aimed at determining the less investigated effects of hydrogen uptake on the microstructure and the mechanical behavior of the oxidized Zircaloy-2 alloy. The specimens were oxidized and charged with hydrogen. The different oxidation temperatures and cathodic current densities were applied. The scanning electron microscopy, X-ray electron diffraction spectroscopy, hydrogen absorption assessment, tensile, and...
-
Mechanical properties of PVDF-coated fabric under tensile tests
PublikacjaThis article describes the laboratory tests necessary to identify the mechanical properties of the polyvinylidene fluoride (PVDF)-coated fabrics named Precontraint 1202S and Precontraint 1302S. First, a short survey of the literature concerning the description of coated woven fabrics is presented. Second, the material parameters for PVDF-coated fabrics are specified on the basis of biaxial tensile tests. A comparison of the 1:1...
-
Potential and strain rate impact on the electrochemical properties of 304L stainless steel under tensile stresses.
PublikacjaPraca skupia się na badaniach aspektu elektrochemicznego i mechanicznego pękania warstwy pasywnej obecnej na stali 304L. Przedstawione zostały wyniki chwilowych zmian impedancji oraz zmiany parametrów elektrochemicznych warstwy pasywnej podczas testów rozciągania przy różnych poziomach polaryzacji anodowej oraz szybkości rozciągania. Na ich podstawie można stwierdzić, że zarówno czynnik elektrochemiczny, jak i mechaniczny wpływają...
-
Tensile validation tests with failure criteria comparison for various GFRP laminates
PublikacjaThe paper studies the mechanical properties of glass fibre reinforced polymers (GFRP) with various types and orientation of reinforcement. Analyzed specimens manufactured in the infusion process are made of polymer vinyl ester resin reinforced with glass fibres. Several samples were examined containing different plies and various fibres orientation [0, 90] or [+45, –45]. To assess the mechanical parameters of laminates, a series...
-
Mechanical properties of Precontraint 1202 S2 based on uniaxial tensile and creep tests
PublikacjaThe purpose of the paper is the estimation of the polyvinyl chloride – polyester-coated fabric (Precontraint 1202 S2) mechanical properties under uniaxial tensile tests as well as short- and long-time creep tests. The uniaxial tests are the basis of non-linear elastic description while the creep tests are used for the evaluation of the stiffness parameters in time and for the identification of the standard viscoelastic model. The...
-
Pile Model Tests Using Strain Gauge Technology
PublikacjaOrdinary pile bearing capacity tests are usually carried out to determine the relationship between load and displacement of pile head. The measurement system required in such tests consists of force transducer and three or four displacement gauges. The whole system is installed at the pile head above the ground level. This approach, however, does not give us complete information about the pile-soil interaction. We can only determine...
-
Non-linear strain rate analysis of earthquake-induced pounding between steel buildings
PublikacjaPast and recent earthquakes have shown that ground motions may cause severe structural damage to civil engineering structures. Earthquake-induced pounding between adjacent buildings has been identified as one of the reasons which intensifies damages. The aim of this paper is to show the results of the detailed nonlinear FEM analysis of earthquake-induced pounding between two steel buildings. The elastic – perfectly plastic material...
-
Polyester sail technical woven fabric behaviour under uniaxial and biaxial tensile tests
PublikacjaThe paper is focused on the identification of mechanical properties of a sail technical woven fabric (yacht sailcloth polyester) style 480 AP with MTO (Medium Tempered Optimized) finish. The non-linear elastic behaviour of the fabric applied for sails is investigated under uniaxial and biaxial tensile tests. Comparison of non-linear elastic parameters with others polyester coated fabrics is made. This paper is intended to be an...
-
Erroneous GNSS Strain Rate Patterns and their Application to Investigate the Tectonic Credibility of GNSS Velocities
PublikacjaThe paper concerns investigation of the credibility of tectonic interpretation of GNSS strain rates. The analysis was focused on stable regions, where the crustal deformations are small and the reliability of GNSS velocities is questionable. We are showing how the unreliable motion of stations affects calculated strains around them. We expressed distribution of local principal strains by a sinusoidal function and used them to investigate...
-
On some problems in determining tensile parameters of concrete model from size effect tests
PublikacjaThe paper presents results of numerical simulations of size effect phenomenon in concrete specimens. The behaviour of in-plane geometrically similar notched and unnotched beams under three-point bending is investigated. In total 18 beams are analysed. Concrete beams of four different sizes and five different notch to depth ratios are simulated. Two methods are applied to describe cracks. First, an elasto-plastic constitutive law...
-
An optimized controlled rate slow cooling protocol for bovine ovarian tissue cryopreservation by means of X-ray computed tomography
Publikacja -
The effect of strain rate on the passive layer cracking of 304L stainless steel in chloride solutions based on the differential analysis of electrochemical parameters obtained by means of DEIS
PublikacjaOkreślono wpływ szybkości rozciągania w zakresie 10-5s-1 ÷ 16∙10-5s-1 na niestacjonarny proces elektrochemiczny pękania warstwy pasywnej. Badania przeprowadzono na stali wysokostopowej 304L w temperaturze pokojowej w środowisku chlorków za pomocą dynamicznej elektrochemicznej spektroskopii impedancyjnej (DEIS). W rezultacie uzyskano zestaw chwilowych widm impedancyjnych odzwierciedlających dynamikę badanego układu korozyjnego....
-
Influence of High Temperature Oxidation on Hydrogen Absorption and Degradation of Zircaloy-2 and Zr 700 Alloys
PublikacjaThe present research was aimed at determining the effects of the oxide layers on hydrogen absorption, microstructure and mechanical properties of the Zircaloy- 2 and Zr 702 alloys. The oxidation was made at 350 °C, 700 °C and 900 °C for 10 to 30 min in laboratory air, followed by hydrogen cathodic charging for 72 h and annealing at 400 °C for 4 h. The slow strain rate tests were carried out on oxidized, charged and annealed specimens. The...
-
Jacek Tomków dr hab. inż.
OsobyWykształcenie:1. 2018 r.Doktor inżynier - Politechnika Gdańska, Wydział Mechaniczny, Inżynieria Materiałowa,rozprawa doktorska: Wpływ warunków spawania pod wodą na skłonność do tworzenia pęknięć zimnych w stalach o podwyższonej wytrzymałości 2. 2012 r.Magister inżynier - Politechnika Gdańska, Wydział Mechaniczny, Mechanika i Budowa Maszyn, specjalność: Technologia Maszyn i Komputerowe Wspomaganie Produkcji,praca magisterska: Badania...
-
Hydrogen induced degradation of structural steel exposed to the technical liquid hydrocarbons
PublikacjaSusceptibility of the differently heat treated 26H2MF steel to stress corrosion cracking has been evaluated in the constant strain rate tension tests done at the strain rate 10-6s-1 and in the constant load tests done at the 0,98 of fracture load. The boiler fuel and the aged mineral oil at 135C and 80C respectively, have been used as the aggressive environments.
-
Application of the Bodner-Partom constitutive equations for modelling of the technical fabric Valmex used for the hanging roof of the Forest Opera in Sopot
PublikacjaThe study of an inelastic properties of the technical fabric Valmex used for 20 years as the roof structure of the Forest Opera in Sopot (Poland) is presented. The uniaxial tensile laboratory tests with constant strain rate have been conducted and analysed. Parameters of the Bodner-Partom constitutive model have been identified and verified by numerical simulations. Two approaches of the parameters identification have been proposed:...
-
Hydrogen degradation of pre-oxidized zirconium alloys
PublikacjaThe presence of the oxide layers on Zr alloys may retard or enhance the hydrogen entry and material degradation, depending on the layer features. This research has been aimed to determine the effects of pre-oxidation of the Zircaloy-2 alloy at a different temperature on hydrogen degradation. The specimens were oxidised in laboratory air at 350°C, 700°C, and 900°C. After, some samples were tensed at 10-5 strain rate and simultaneously...
-
Properties of surface layers of duplex stainless steel after burnishing processes
PublikacjaStress corrosion cracking resistance of cold worked layers of 25 Cr duplex stainless steel grade UR52N+ has been investigated. The surface layers were performed through burnishing treatment. The residual stresses at surface layers were determined using grazing angle incidence X-ray diffraction method (g-sin2 Ψ). Corrosion tests were performed with the use of Slow Strain Rate Test technique in boiling 35% MgCl2 solution. It has...
-
Environmental degradation of Ti alloys in artificial saliva and a role of fluorides
PublikacjaThe titanium and its alloys are potentially prone to hydrogen embrittlement, including those proposed for dental implants. The research has been aimed to assess a susceptibility to environment-enhanced degradation of the Ti-13Zr-13Nb alloy in artificial saliva with or without hydrofluoric acid, subject or not to cathodic polarisation. The results have shown that even if artificial saliva is safe environment, both cathodic polarization...
-
Environmental degradation of titanium alloy in artificial saliva
PublikacjaThe titanium and its alloys are potentially prone to hydrogen embrittlement, including those proposed for dental implants. The research has been aimed to assess a susceptibility to environment-enhanced degradation of the Ti-13Zr-13Nb alloy in artificial saliva with or without hydrofluoric acid, subject or not to cathodic polarisation. The results have shown that even if artificial saliva is safe environment, both cathodic polarization...
-
The elasto-plastic numerical study of crack initiation in notched PMMA specimens under uniaxial loading conditions – Tension and torsion
PublikacjaThis paper presents the results of FEM numerical calculations aimed at describing the plastic strain and stress fields under critical loading conditions: tensile force or torsional moment. The calculations were carried out with reference to the results of experimental tensile and torsional tests of flat PMMA specimens weakened with V-notches of different root radii: 0.5, 2 and 10 mm. The procedure for conducting nonlinear numerical...
-
Stress–strain model of lower corroded steel plates of normal strength for fitness-for-purpose analyses
PublikacjaThis study investigates the mechanical properties of specimens made of normal strength steel subjected to lower marine immersed corrosion degradation levels (below 25 %). The specimens were corroded in laboratory conditions, and only natural factors were controlled to raise the corrosion rate (reaching the level of 1 mm/year). Three different thicknesses of plates made of normal strength of shipbuilding steel are investigated (between...
-
The fracture behaviour of notched PMMA specimens under simple loading conditions – Tension and torsion experimental tests
PublikacjaThis paper presents the results of experimental testing of flat PMMA specimens during uniaxial loading conditions. Two separate tests were conducted: tensile and torsion. The specimens were weakened with V-type edge notches with different root radii: 0.5; 2 and 10 mm. The specimens were made in two thickness variants: 5 and 15 mm. Monotonic tensile and torsion tests were carried out while keeping the averaged strain rate constant,...
-
CHARACTERIZATION STUDY ON MECHANICAL PROPERTIES OF POLYESTER COATED FABRIC
PublikacjaThe scope of the paper is to determine the mechanical properties of the Precontraint 1302 polyester coated fabric under uniaxial and biaxial tensile tests. The results are compared for Precontraint 1302 fabric and other types of coated fabrics. The author applied an orthotropic model and a dense net model to reflect the polyester coated fabric performance under uniaxial and biaxial tensile tests. Material parameters are specified...
-
Fatigue life improvement using low transformation temperature weld material with measurement of residual stress
PublikacjaWelding processes often produce high levels of tensile residual stress. Low transformation temperature (LTT) welding wires utilise phase transformation strains to overcome the thermal contraction of a cooling weld. In this paper, the residual stress within each weld was quantified using the milling/strain gauge method, being the strain change measured as the weldment was milled away. The fatigue tests were conducted under uniaxial...
-
Determination of Mechanical Properties of P91 Steel by Means of Magnetic Barkhausen Emission
PublikacjaIn this work, an attempt at determination of mechanical properties by means of a method based on magnetic Barkhausen emission measurements was proposed. The specimens made of P91 steel were subjected to creep or plastic flow which were interrupted after a range of selected time periods in order to achieve specimens with an increasing level of strain. Subsequently, measurements of magnetic Barkhausen emission were carried out, and...
-
Microstructure and Mechanical Properties of Carboxylated Nitrile Butadiene Rubber/Epoxy/XNBR-grafted Halloysite Nanotubes Nanocomposites
PublikacjaThe effect of various amounts of carboxylated nitrile butadiene rubber (XNBR) functionalized halloysite nanotubes (XHNTs) on the cure characteristics, mechanical and swelling behavior of XNBR/epoxy compounds was experimentally and theoretically investigated. The morphology of the prepared XNBR/epoxy/XHNTs nanocomposites was imaged using scanning electron microscopy (SEM). The effects of various XNBR-grafted nanotubes on the damping...
-
Hydrogen production from ethanol In nitrogen microwave plasma At atmospheric pressure
PublikacjaHydrogen seems to be one of the most promising alternative energy sources. It is a renewable fuel as it could be produced from e.g. waste or bio-ethanol. Furthermore hydrogen is compatible with fuel cells and is environmentally clean. In contrast to conventional methods of hydrogen production such as water electrolysis or coal gasification we propose a method based on atmospheric pressure microwave plasma. In this paper we present...
-
Wpływ kierunku rozchodzenia się fali detonacyjnej oraz współczynnika asymetrii na rozkład prędkości odkształceń w kotlinie walcowniczej podczas asymetrycznego walcowania pasma Al-Cu. The influences of the direction of explosion wave and asymetrical coefficient at the distribution of strain rate in the roll cap of bimetallic plate Al-Cu of rolling process.
PublikacjaPrzedstawiono symulacje komputerowe walcowania blach Al-Cu łączonych wybuchowo. Symulacje przeprowadzono dla procesu walcowania w walcarce o średnicy walców D=150 mm z indywidualnym napędem walców roboczych. W ramach badań numerycznych określony został wpływ kierunku rozchodzenia się fali detonacyjnej na rozkład prędkości odkształcenia w kotlinie walcowniczej asymetrycznie walcowanej blachy bimetalowej Al-Cu.
-
Application of galvanodynamic impedance spectroscopy for studying passive film cracking under mechanical strain
PublikacjaThe paper reports the results of simultaneous mechanical and electrochemical investigations on austenitic (18/8) stainless steel in a 2 % solution of sulphuric acid. The measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Electrochemical analysis of mechanical passive layer cracking and repassivation conditions during a tensile test was carried out. Application of this methodology allowed...
-
Influence of thermal effects on mechanical properties of PVDF-coated fabric
PublikacjaThis paper describes the method of laboratory tests necessary for identification of temperature influence on mechanical properties of polyvinylidene fluoride-coated polyester fabric often used for tensile structures. Two nonlinear model descriptions are investigated. The first one is based on the piece-wise linear relations between stress and strain and the second one on the Murnaghan model of solid behavior. This paper is proposed...
-
Application of atmospheric pressure microwave plasma source for hydrogen production from ethanol
PublikacjaIn contrast to conventional technologies of hydrogen production like water electrolysis or coal gasification we propose a method based on the atmospheric pressure microwave plasma. In this paper we present results of the experimental investigations of the hydrogen production from ethanol in the atmospheric pressure plasma generated in waveguidesupplied cylindrical type nozzleless microwave (915 MHz and 2.45 GHz) plasma source (MPS)....
-
Method of sacrificial anode dual transistor-driving in stray current field
PublikacjaIn order to control a magnesium anode in a stray current interference field, a dual transistor driving system has been proposed. It consisted of a combination of PNP and NPN transistors. Dual transistor driven system and direct anode to cathode connection were electrochemically tested in 3% NaCl solution. The dual transistor driven system increased the anode efficiency and reduced hydrogen evolution and the risk of embrittlement....
-
Method of sacrificial anode transistor-driving in cathodic protection system
PublikacjaA magnesium anode driving system has been proposed. A PNP driving transistor has been used. Electrochemical testing in 3%NaCl, results and comparison of the driving system and classic direct anode to cathode connection are presented. The driving system reduced the protection current and stabilized the working conditions of the anode. Higher anode efficiency was achieved. Overprotection and hydrogen embrittlement threats were prevented...
-
Effect of wet Hydrogen Sulfide on Carbon Steels Degradation in Refinery Based on Case Study
PublikacjaMaterial degradation caused by wet hydrogen sulfide (Wet H2S) is one of the major issues in refineries. Carbon steel is the main construction material used in refineries and is subjected not only to thickness loss but the hydrogen is the major concern. H2S leads to high atomic hydrogen penetration in steel which causes degradation in the form of blistering and/or cracking (HIC/SOHIC) and stress cracking in the area of welds and...
-
Właściwości mechaniczne tworzywa PET - przegląd literatury
PublikacjaThe article describes the influance of the microstructure and environment conditions on the mechanical properties of PET material. From the microskopic point of view, mechanical and thermal properties of PET material have the biggest influance on orientation and crystallization processes of material. From the macroskopic point of view mechanical properties can be described by parameters derived from strees-strain mechanical answers...
-
Mechanical properties for preliminary design of structures made from PVC coated fabric
PublikacjaIn this paper, laboratory tests necessary for the identification of non-linear elastic immediate properties of the PVC coated polyester fabric (like AF 9032) are described. The material parameters are specified on the basis of the uniaxial tensile tests in the warp and weft directions as well as on the base of the biaxial tensile tests. For the identification process techniques based on the least squares method are used. The authors...
-
Experimental study on polymer mass used to repair damaged structures
PublikacjaA new method of repairing damaged structures by injecting the cracks with specially designed polymer mass (flexible two-component grout based on polyurethane resin) has been recently proposed. The technique is mainly dedicated to damaged masonries, especially historical structures where minimum intervention is permitted. The cracks are filled with the special injection, forming the flexible joints bonding the disrupted structural...
-
Plasticity of Bead-On-Plate Welds Made with the Use of Stored Flux-Cored Wires for Offshore Applications
PublikacjaExtreme atmospheric conditions in the marine and offshore industry are harmful to engineering materials, especially to welded joints, and may cause degradation of their properties. This article presents the results of research on the plasticity of bead-on-plate welds made using two types of seamless, copper plated flux-cored wires. Before welding, spools with wire were stored for 1 month in two distinct locations with different...
-
Properties of Barium Cerate Thin Films Formed Using E-Beam Deposition
PublikacjaThis article focuses on the properties of the BaCeO3 thin films formed by electron-beam vapor deposition and investigates the formation of barium cerates on supports with different thermal expansion coefficients (Stainless Steel, Invar, Glass Sealing, and Inconel substrates) and the influence of the technological parameters on the properties of the formed thin films with an emphasis on the stability of the films. Morphology and...
-
Effect of underwater local cavity welding method conditions on diffusible hydrogen content in deposited metal
PublikacjaOne of the methods with great potential for applications in underwater repairs is local cavity welding. In local cavity method, cooling conditions and diffusible hydrogen amount in weld metal are nearly the same as those existed during welding in the air. This paper presents the results of literature survey and preliminary tests of the effect of local cavity welding conditions on diffusible hydrogen amount in a deposited metal....
-
Tensile curve of E grade steel for shipbuilding
Dane BadawczeIn the shipbuilding industry, the risk of brittle fractures developing in constructions is limited by employing certified materials of specific impact strength, determined using the Charpy method (for a given design temperature) and by exercising control over the welding processes (technology qualification, supervision of production, tests of non-destructive...
-
Effect of water salinity on properties of multipass underwater wet manual metal arc welded joints
PublikacjaThe weldability of steel under the water is limited due to the influence of the environment. Water causes limited visibility, presence of the residual stresses, increasing the cooling rate, and increasing the diffusible hydrogen content in deposited metal, leading to the formation of brittle microstructures in heat-affected zone (HAZ). The paper presents the results of mechanical properties testing of S420G2+M steel welded joints...
-
Prediction of the Mechanical Properties of P91 Steel by Means of Magneto-acoustic Emission and Acoustic Birefringence
PublikacjaThe paper describes an application of nondestructive volumetric magnetic and ultrasonic techniques for evaluation of the selected mechanical parameter variations of P91 steel having direct influence on its suitability for further use in critical components used in power plants. Two different types of deformation processes were carried out. First, a series of the P91 steel specimens was subjected to creep and second, one to plastic...
-
Adhesive Monitoring with Instrumented Wedge Test
PublikacjaThe wedge test (sometimes called the Boeing wedge test) is amongst the most readily exploitable techniques for assessment of the rate-dependent fracture energy of adhesive materials when used to bond relatively rigid substrates. With its siblings: the double cantilever beam (DCB), and the tapered double cantilever beam (TDCB), a force is applied, essentially in cleavage, to provoke substrate separation perpendicularly to the bondline...
-
PA32 aluminum alloy - tensile properties
Dane BadawczeIn addition to steel, aluminium alloys are the main building material used in the shipbuilding industry. Due to its undoubted advantages, such as low density (nearly three times lower than in the case of steel for shipbuilding) and high corrosion resistance, it is often used for hulls of yachts and small vessels as well as superstructures. For safety...