API 5L X65 steel - tensile properties in room temperature +20°C, across rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - tensile properties in room temperature +20°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - tensile properties in room temperature -10°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - tensile properties in room temperature -10°C, across rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
X-ray diffractometry results of the Sr1.05Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.05Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr0.90Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.90Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr1.00Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr1.00Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the Sr0.95Ti0.30Fe0.70O3-d material before and after H2-TPR measurement
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.95Ti0.30Fe0.70O3-d material. The phase composition of the investigated powders was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder and powder after H2-TPR (temperature programmed...
-
X-ray diffractometry results of the SrTi0.50Fe0.50O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.50Fe0.50O3-d (STF50) powder after ball milling. The phase composition of the investigated STF50 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.35Fe0.65O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.35Fe0.65O3-d (STF35) powder after ball milling. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
X-ray diffractometry results of the SrTi0.30Fe0.70O3-d powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the SrTi0.30Fe0.70O3-d (STF70) powder after ball milling. The phase composition of the investigated STF70 powder was analyzed by XRD at room temperature. The X-ray diffractometry (XRD) technique was used to determine the phase composition of the fabricated powder. Measurements...
-
Results of SEM examination of nanohydroxyapatite coatings doped nanoCu particles on Ti13Zr13Nb alloy
Open Research DataThe database contains the images of the microstructure of the coatings observed with the SEM scanning electron microscope. The nanohydroxyapatite (nanoHAp) with the addition of copper nanoparticle (nanoCu) coatings deposited on the Ti13Zr13Nb alloy by an electrophoresis process were tested. Two different fractions of nanoCu (with average particles size...
-
Results of SEM examination of chitosan/Eudragit E 100 coatings electrophoretically deposited on the Ti grade 2 substrate
Open Research DataThe database contains the images of the microstructure of the coatings observed with the SEM scanning electron microscope. The chitosan/Eudragit E 100 coatings deposited on the Ti grade 2 substrate by an electrophoresis process were tested. Different process parameters like Eudragit E 100 concentration (0.25 g and 0.5 g in 100 mL of 1% (v/v) acetic...
-
TG-hydroxyl groups in TiO2-P25
Open Research DataTG analyses were performed for powdered TiO2 - commercial P25 sample, which was heat-treated from room temperature to 500 C in the nitrogen atmosphere. Mass loss at lower temperature such as 120 C was related to the physisorbed water, and that one occurring at 500 C to the chemisorbed hydroxyl groups.
-
Low temperature electrical conductivity of the SrFeO3-d pellet
Open Research DataThis dataset contains results of low temperature electrical conductivity measurements of dense SrFeO3-d (SFO) pellet. DC electrical conductivity measurements of SFO were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas flow rate of 40...
-
Low temperature electrical conductivity of the SrTi0.65Fe0.35O3-d pellet
Open Research DataThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.65Fe0.35O3-d (STF35) pellet. DC electrical conductivity measurements of STF35 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.30Fe0.70O3-d pellet
Open Research DataThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.30Fe0.70O3-d (STF70) pellet. DC electrical conductivity measurements of STF70 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.50Fe0.50O3-d pellet
Open Research DataThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.50Fe0.50O3-d (STF50) pellet. DC electrical conductivity measurements of STF50 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
Low temperature electrical conductivity of the SrTi0.10Fe0.90O3-d pellet
Open Research DataThis dataset contains results of low temperature electrical conductivity measurements of dense SrTi0.10Fe0.90O3-d (STF90) pellet. DC electrical conductivity measurements of STF90 were performed by the Van der Pauw method between 400 °C and room temperature with 20 °C step. Studies were performed at Synthetic Air flow under humidified (~4 vol%) gas...
-
X-ray diffractometry results of the Sr0.86Ti0.65Fe0.35O3 powder
Open Research DataThis dataset contains results of X-ray diffractometry mesurement (XRD) of the Sr0.86Ti0.65Fe0.35O3-d (STF35) powder. The phase composition of the investigated STF35 powder was analyzed by XRD at room temperature. It confirms the formation of the cubic perovskite oxide phase. Calculated average lattice constant is a 3.90882(1) Å, with Goodness of Fit...
-
XRD patterns of nickel-modified V2CTx
Open Research DataThe set includes data for XRD pattern preparation of nickel-modified V2CTx samples.
-
Nitrogen sorption isotherm for V2CTx
Open Research DataData of points for nitrogen sorption isotherm for sample V2CTx (only sorption branch). The V2CTx was prepared via selective etching of aluminium from MAX matrice V2AlC using 50% HF for 96 h at room temperature.
-
Measurements of the chemical composition of LTO:Cu powders
Open Research DataLithium titanate doped by copper was measured by X-ray photoemission spectroscopy (XPS). For sol-gel synthesis lithium acetate dehydrate and titanium (IV) butoxide 97% and copper (II) nitrate from Alfa Aesar were used as a reagents. Cu precursor was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate...
-
FTIR spectra of VO2 and V2O3 nanostructures
Open Research DataThe DataSet contains the FTIR spectra of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
Sol-gel derived lithium titanate powders measured by XPS method
Open Research DataFor sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate and copper nitrate were dissolved...
-
Thermographic images during testing measuring instrument boards
Open Research DataThe dataset presents thermografic images acquired during testing the prototype of measuring instrument for resistiometric corrosion monitoring. The testing was performed in the room temperature. VIGOcam v50 thermal imaging camera (VIGO System S.A., Ozarow Mazowiecki, Poland) was used for taking the pictures. These pictures were used as preliminary tests...
-
The topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with confocal microscope
Open Research DataThe topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with confocal microscope.
-
The topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with AFM
Open Research DataThe topography of as-quenched and heat treated 50(2Bi2O3-V2O5)-50SrB4O7 and 50Bi2VO5.5-50SrB4O7 glasses measured with AFM.
-
The structure of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with X-ray diffraction method
Open Research DataThe structure of strontium–borate glasses and glass-ceramics containing Bi2VO5.5 nanocrystallites was measured by XRD.
-
XPS study of the lithium titanate doped by copper
Open Research DataLithium titanate doped by copper was measured by X-ray photoemission spectroscopy. For sol-gel synthesis lithium acetate dehydrate from Alfa Aesar GmbH &Co and titanium (IV) butoxide 97% from Aldrich were used as reagents. Copper (II) nitrate from Alfa Aesar was used as a source of Cu dopant. It was added in the proper weight to get an x index equal...
-
Electrical and noise responses of carbon nanotube networks enhanced by UV light for nitrogen dioxide sensing
Open Research DataNetworks consisting of randomly oriented carbon nanotubes (CNN) were investigated toward nitrogen dioxide detection by means of electrical and low-frequency noise measurements. UV-activation of CNN layers improved gas sensitivity and reduced the limit of detection, especially by employing 275 nm-LED. This data set includes DC resistance measurements...
-
The luminescence study ofNaK2Li[Li3SiO4]4:Eu coumpounds.
Open Research DataNarrowband green phosphors with high quantum efficiency are required for backlighting white light-emitting diode (WLED) devices. Materials from the A[Li3SiO4]4:Eu2+ family have recently been proposed as having superior properties to industry-standard β-SiAlON green phosphors. Here, we show that a cheap, easily synthesized host NaK2Li[Li3SiO4]4 (NKLLSO)...
-
The XRD diffraction patterns of Ce(Pr,Sm)O2-s samples
Open Research DataThe dataset includes XRD diffraction patterns of Ce(Pr,Sm)O2-s samples of various stoichiometries of Pr and Sm dopants. Samples were produced using aqueous soft chemistry methods (microemulsion method).
-
XRD data of V2AlC, Mo3AlC2, Mo3CTx and V2AlCTx
Open Research DataRaw data for XRD diffractograms of MAX phases: V2AlC and Mo3AlC2 and corresponding MXenes after selective etching of Al.
-
Chemical composition of La-Sr-Ce-Ni-Ti ceramics material measured by XPS method
Open Research DataLa-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS)...
-
SEM images of Ni-Mo2CTx/Mo3AlC2 before and after catalytic dry reforming of methane
Open Research DataThe dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
-
The structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with X-ray diffraction method
Open Research DataThe structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by XRD.
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials synthesized via the solid state reaction method
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
XRD and electrochemical results for MoO3 films deposited using pulsed laser deposition system
Open Research DataThe attached data contains XRD and electrochemical results for MoO3 films deposited on fluorine-doped tin oxide glasses. Films were deposited using a pulsed laser deposition system at different conditions. Part of the samples was deposited at room temperature and then annealed at 575°C for given times (samples labeled PLD_RT_575C_xmin, where x stands...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 900 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XAS spectra of O-K edges, Fe-L edges in pristine, La-, and Nb-doped SFM in 3 states: as-prepared, reduced and reoxidized
Open Research DataThis dataset contains the normalized and exported to *.txt spectra for x-ray absorption spectroscopy. The samples analyzed were strontium ferrite molybdate based, doped with lanthanum and niobium. The powders were measured in as-prepared state (denoted in filename as AP), reduced (red) and reoxidized (reox). The filenames are written accordingly: Edge_(optional:...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
XRD diffraction patterns for strontium ferrite molybdate-based compounds: as-prepared, reduced and reoxidized
Open Research DataThe dataset contains the XRD diffractograms collected at room temperature for SFM, LSFM and SFMNb in 3 different oxidation states, namely: as-prepared, reduced and reoxidized.
-
The structure of strontium–borate glass-ceramics containing crystalites of Bi2VO5.5. measured with X-ray diffraction and SEM methods
Open Research DataThe structure of strontium–borate glass-ceramics containing Bi2VO5.5 crystallites was measured by XRD and SEM.
-
The SEM micrographs of the cavitation erosion-corrosion process of selected copper alloys degradation
Open Research DataThe dataset contains Scanning Electron Micrographs of CuZn40Mn3Fe brass compared with Superston and Novoston bronze after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The micrographs compare the topography of samples subjected cavitation erosion in 3% NaCl at room temperature, leading to the surface...
-
The hydrogen evolution reaction (HER) performance of some FTO/MoS2/SnO2 electrodes
Open Research DataTo demonstrate the electrochemical performance of the FTO/MoS2/SnO2 for HER (hydrogen evolution reaction), the LSV (linear sweep voltammetry) was performed. The polarization curves of the obtained composite were measured in 1 M H2SO4 at room temperature with a scan rate 10 mV/s. For comparison, the LSV for the FTO, pure MoS2 and Pt plate electrode were...
-
FTIR spectra of V2O5 nanostructures
Open Research DataThe DataSet contains FTIR spectra of vanadium pentaoxide nanostructures obtained by the sol-gel with different annealing temperatures under synthetic air.
-
Temperture-programmed reduction (H2-TPR) of Ni-Mo2CTx_Mo2Ga2C and Ni-Mo2CTx_Mo3AlC2 catalysts
Open Research DataThe dataset includes the data for the preparation of plots illustrating the reduction peaks versus the temperature of the catalyst sample.
-
Linear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass heat-treated for 3 hours at 693 K, measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of partially crystallized 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.