Search results for: strontium doped titanates
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Open Research DataThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Influence of sintering temperature of porous SrTi0.65Fe0.35O3-d oxygen electrode on electrochemical impedance spectroscopy spectra measured at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C; 900 °C and 1000 °C). Measure temperature was 800 °C (syntetic air, 40 ml min-1). Results converted to electrode surfaces area and dived by two electrodes.
-
SEM image and line EDS of SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C
Open Research DataThis dataset contains image of the SrTi0.50Fe0.50O3-d porous electrode sintered at 800 °C with line EDS analysis results. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 20 kV in a high vacuum mode. The chemical compositions of the investigated powder...
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperaturs (800 °C, 900 °C and 1000 °C). EIS spectra were measured at 700 °C with synthetic air flow (21% O2, 40 ml min-1). Results converted to electrode surfaces area and dived by two...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 800 °C and 15% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 100% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 100% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Selection of the lambda parameter for DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure
Open Research DataThis dataset contains results of selection of the lambda parameter for Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. Used lambdas: 5 x 10^(-3), 1 x 10^(-3), 5 x 10^(-4) and 1 x 10^(-4)....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 20% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 5% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 5% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 600 °C and 15% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 600 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results converted...
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 15% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using three R-CPE fiting elements
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated three R-CPE elements from equivalent circuit,...
-
Results of EIS measuremnts and DRT analysis of SrTi0.30Fe0.70O3-d oxygen electrode at 800 °C and 1% oxygen partial pressure by using two R-CPE fiting elements
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 1% of oxygen partial pressure. EIS and DRT spectra of simmulated two R-CPE elements from equivalent circuit,...
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Area specific resistance (at 800 °C - 500 °C) of the SrTi0.30Fe0.70O3 porous oxygen electrodes at different oxygen partial pressures
Open Research DataIn this dataset are presented results of the polarization resistance of SrTi0.30Fe0.70O3 porous oxygen electrodes sintered at 800 °C. The measurement temperature range was between 800 °C and 500 °C. Applied different oxygen partial pressure flow was: 1%, 20% and 100% pO2. Results converted to electrode surfaces area and dived by two electrodes. All...
-
Exemplary SEM images of polished cross sections of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C
Open Research DataThis dataset contains images of polished cross section of symmetrical cell with SrTi0.50Fe0.50O3-d electrodes and CGO-20 substrate sintered at 800 °C. Images were obtained using a PhenomXL (Thermo Fisher Scientific, the Netherlands) scanning electron microscope (SEM) with an accelerating voltage of 12 kV in a high vacuum mode.
-
Sol-gel derived TeO2:RE powders
Open Research DataTellurium dioxide powders doped by Europium or Dysprosium were prepared by sol-gel method. Samples were annealed in ix of Ar and O2 atomosphere at 600 degrees. Presence of rare earth dopants and Te4+ phase was confirmed by X-Ray Photoemission Spectroscopy method (XPS). For XPS measurements samples with 1 atomic % and 5 atomic % of dopand were selected.
-
Optimization of boron-doping process of titania nanotubes via electrochemical method toward enhanced photoactivity
PublicationIn this work, we were focused on the development of the electrochemical approach resulting in a stable boron doping of titania nanotubes. The doping procedure concerns anodic polarization of as-anodized titania in a H3BO3 solution acting as n boron precursor. The series of attempts were taken in order to elaborate the most beneficial doping conditions. The parameters of electrochemical doping allowing to obtain boron-doped titania...
-
RARE-EARTH ELEMENTS DOPING OF BARIUM CERATE AND ZIRCONATE SOLID SOLUTION
PublicationThe properties of doped barium cerate barium zirconate solid solution are presented in presented work. It was found that doping of solid solution of barium cerate and zirconate by rare-earth elements have an influence on microstructure and electrical properties of the samples.
-
STUDY OF CuO AND V2O5 EFFECT ON IR SPECTRA OF POLYCRYSTALLINE BISMUTH NIOBATE
PublicationBismuth niobate (BiNbO4) ceramics were fabricated by mixed oxide method and sintered by presureless sintering method. BiNbO4 ceramics doped with V2O5 additive in amount 0.125 wt%, 0.250 wt% and 1 wt% of was sintered at T = 910°C whereas BiNbO4 ceramics doped with 2 wt% of CuO additive was sintered at T = 890°C and T = 910°C. It was found that V2O5 additive improved morphology of the ceramic samples. However, the chemical composition...
-
Three electrode configuration measurements of electrolyte-diffusion barrier-cathode interface
PublicationMeasurements of a system consisting of cathode/doped ceria diffusion barrier/doped zirconia electrolyte were made using two- and three-electrode configuration. Results obtained on a three-electrode measurement configuration were compared with and reflect the results obtained in two-electrode configuration. Three-electrode measurements allowed separating the impact of the symmetrical interface in the investigated system. They also...
-
Diamond Structures for Tuning of the Finesse Coefficient of Photonic Devices
PublicationFinesse coefficient is one of the most important parameters describing the properties of a resonant cavity. In this research, a mathematical investigation of the application of diamond structures in a fiber-optic Fabry–Perot measurement head to assess their impact on the finesse coefficient is proposed. We present modeled transmission functions of cavities utilizing a nitrogen-doped diamond, a boron-doped diamond, nanocrystalline...
-
FTIR spectra of gas mixtures from the methanation chamber filled with 50-50wt.% NiO-GDC
Open Research DataThe dataset includes the FTIR spectra collection of the outlet gas mixtures (CO2, CO, CH4) from reactor chamber filled with 50/50 wt.% NiO-GDC (Gadolinia Doped Ceria 20mol.%Gd2O3) catalyst for perfoming methanation reaction. The inlet gas mixture was composed of 3:1 by vol. H2:CO. Spectra were collected using PerkinElmer FTIR every 1 min.
-
Curing epoxy with electrochemically synthesized Zn Fe3-O4 magnetic nanoparticles
PublicationCathodic electrodeposition (CED) was applied in synthesis of undoped and zinc (Zn) doped Fe3O4 nanoparticles. Changes in the lattice structure of nanoparticles were monitored using X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM) supported by dispersive X-ray spectrometry (EDS), and vibrating sample magnetometry (VSM). Detailed analyses explored the formation of ZnxFe3–xO4 nanoparticles with x ≈ 0.1,...
-
A novel approach for processing CaAlSiON glass-ceramics by spark plasma sintering: Mechanical and electrical properties
PublicationLithium containing glassy materials can be used as solid electrolytes or electrode materials for lithium-ion batteries due to their high energy density. Conventional melt-quenched Ca11Al14Si16O49N10 glass powder containing 24 e/o N, doped with Li-ions (1, 3, and 6 wt. %) and sintered by spark plasma sintering technique (SPS) was studied. The benefits of using SPS to produce glass-ceramics are rapid heating rates compared to conventional...
-
Non-metaldoped TiO2 nanotube arrays for high efficiency photocatalytic decomposition of organic species in water
PublicationTitanium dioxide is a well-known photoactive semiconductor with a variety of possible applications. The procedure of pollutant degradation is mainly performed using TiO2 powder suspension. It can also be exploited an immobilized catalyst on a solid support. Morphology and chemical doping have a great influence on TiO2 activity under illumination. Here we compare photoactivity of titania nanotube arrays doped with non-metal atoms:...
-
Thermal stability analysis of poly(lactic acid)-carbon black-nanodiamond composite
Open Research DataThis dataset contains thermal stability tests carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include: thermogravimetric analysis (TGA)...
-
Electrochemical degradation of textile dyes in a flow reactor: effect of operating conditions and dyes chemical structure
PublicationIn this study, electrochemical oxidation of five azo dyestuffs (Yellow D-5GN, Red D-B8, Ruby F-2B, Blue D-5RN, Black DN), that are widely used in the textile industry, was investigated in a flow reactor. BDD electrode with a high boron doping level (C/B = 10 000) was prepared and used. Two configurations of reactor were considered, i.e., one with the undivided cell, and the other with the cell divided by anodic and cathodic compartments....
-
The Influence of the Co-Dopant Dexamethasone Phosphate on the Electrodeposition Process and Drug-Release Properties of Polypyrrole-Salicylate on Iron
PublicationIn this work, the influence of incorporation of two anti-inflammatory drugs dexamethasone phosphate and sodium salicylate on the electrodeposition process of polypyrrole (PPy) film on iron has been studied. The incorporation of the agents into PPy has been carried out in a one-step electropolymerization process on oxidizable iron. The role of each drug agent during the deposition process has been discussed. The morphological and...
-
Electron impact iozization of CCl4 and SF6 embedded in superfluid helium droplets
PublicationElectron impact ionization of helium nano-droplets containing several 104 He atoms and doped with CCl4 or SF6 molecules is studied with high-mass resolution. The mass spectra show significant clustering of CCl4 molecules, less so for SF6 under our experimental conditions. Positive ion efficiency curves as a function of electron energy indicate complete immersion of the molecules inside the helium droplets in both cases. For CCl4...
-
High-conducting Bi4V2-xFexO11-δ ceramics containing Fe2O3 nanocrystals: Structure and properties
PublicationThe topography, structure, thermal, magnetic, and electrical properties of Bi4V2-xFexO11-δ ceramics substituted with x = 0.5 and 0.7 Fe were studied. The microscope analysis showed the presence of iron-rich nanocrystals formed on the Bi-Fe-V-O grains. The X-ray diffraction studies confirmed that grains are built mostly of tetragonal Bi4V1.5Fe0.5O10.5 phase. Thermal properties analysis showed an order-disorder type γ ↔ γʹ phase...
-
Praseodymium substituted lanthanum orthoniobate: Electrical and structural properties
PublicationThe results of ionic transport and structural measurements for the lanthanum orthoniobate doped by praseodymium are presented and discussed. The influence of calcium co-doping on these properties has also been analyzed. The results suggest the predominant protonic conductivity for the investigated system in the whole range of investigated temperatures. The influence of calcium co-doping on phase purity is analyzed.
-
Materiały dla jednowarstwowych ogniw paliwowych
PublicationA composite material, which may be further applied as a single layer fuel cell, was synthesizes using solid state synthesis method. Composite consisted of two components. The first was a nanoeramic proton conductor - calcium doped lanthanum niobate. The second one was a nanoceramic semiconductor oxide composed of lithium, nickel and zinc oxides respectively.
-
Luminescence of TeO2:Eu thin films
Open Research DataTellurium dioxide doped by europium thin films were deposited by magnetron sputtering method and simultaneously heated at 200 oC. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the films was...
-
Fabrication and Crystal Structure of Sol-Gel Deposited BST Thin Films with Compositional Gradient
PublicationIn the present research technology of compositionally graded barium strontium titanate Ba1-xSrxTiO3 thin films deposited on stainless steel substrates by sol-gel spin coating followed with thermal annealing at T = 650°C is reported. Results of thermal behavior of the sol-gel derived powders with compositions used for fabrication of graded structure (i.e. with Sr mole fraction x = 0.5, 0.4 and 0.3) are described. X-ray diffraction...
-
Optical and photoelectrochemical characterization of pulsed laser deposited Bi4V2O11, BICUVOX, and BIZNVOX
PublicationThin layers of three compounds from the BIMEVOX family (Bi4V2O11, Bi2V0.9Cu0.1O5.35, and Bi2V0.9Zn0.1O5.35) were prepared via pulsed laser deposition technique on quartz, silicon, and platinum foil and tested as photoanodes for water photooxidation. The film formation, as well as the crystallization upon heating, was characterized using X-ray diffraction and Raman spectroscopy. The optical properties were investigated using spectroscopic...
-
Tuning of the finesse coefficient of optoelectronic devices
PublicationOptoelectronic devices attracted considerable attention in many branches of science and technology, which can be attributed to their unique properties. Many of them use optical cavities which parameters can be adopted to specific requirements. This thesis investigates the introduction of diamond structures (nitrogen-doped diamond film, boron-doped diamond film, undoped diamond sheet) to optical cavities to tune their finesse coefficient....
-
The morphology of vanadate glasses containing BaTiO3 measured with the use of AFM
Open Research DataThe morphology of vanadate glasses doped with BaTiO3 was measured with the use of AFM method. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured...
-
XRD and electrochemical results for MoO3 films deposited using pulsed laser deposition system
Open Research DataThe attached data contains XRD and electrochemical results for MoO3 films deposited on fluorine-doped tin oxide glasses. Films were deposited using a pulsed laser deposition system at different conditions. Part of the samples was deposited at room temperature and then annealed at 575°C for given times (samples labeled PLD_RT_575C_xmin, where x stands...
-
Physicochemical studies (BET) of nanoparticles used for 3D printable conductive composites
Open Research DataThis dataset contains physico-chemical examination of fillers used to fabricate new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Geometric surface area of the nanoparticles was studied by Brunauer–Emmett–Teller (BET) adsorption/desorption isotherms. Investigated samples: CB Ensaco 250G, detonation...
-
Au-RE-TiO2 nanocomposites: Surface characteristics and photoactivity
PublicationThe photocatalysts based on TiO2 co-doped with rare earth metal (RE) and gold nanoparticles have been prepared using a sol-gel method and followed by gold reduction. Specific surface areas of the modified photocatalysts were calculated by the Brunauer-Emmett-Teller method (BET). Diffuse reflectance spectra of the obtained photocatalysts were recorded in a UV-Vis spectrophotometer (DRS UV-Vis). The influence of the type of rare...
-
Evolution of magnetic and transport properties in (Cr1−xMnx)2AlC MAX-phase synthesized by arc melting technique
PublicationHerein we initiate a comeback to the arc melting technique to produce MAX-phase solid solutions. Bulk samples of (Cr1−xMnx)2AlC MAX-phase with X = 0, 0.025, 0.05 and 0.1 were synthesized and studied by means of X-ray diffractometry, scanning electron microscopy in combination with energy-dispersive X-ray spectroscopy. Samples were established to be homogeneous with an incorporation of Cr7C3, AlCr2 and Al2O3 secondary phases which...
-
Design and Microwave-Assisted Synthesis of TiO2-Lanthanides Systems and Evaluation of Photocatalytic Activity under UV-LED Light Irradiation
PublicationThe TiO2-Eu and TiO2-La systems were successfully synthesized using the microwave method. Based on the results of X-ray diffraction analysis, it was found that regardless of the analyzed systems, two crystal structures were noted for the obtained samples: anatase and rutile. The analysis, such as XPS and EDS, proved that the doped lanthanum and europium nano-particles are present only on the TiO2 surface without disturbing the...
-
INFLUENCE OF CERAMIC COATING ON MECHANICAL PROPERTIES OF STAINLESS STEEL
PublicationCrystal structure and phase composition of stainless steel substrates (AISI 304 type) was studied and it was found that they adopted the cubic symmetry. The calculated elementary cell parameter for the mayor Fe-Ni phase (weight fraction 99%) was a = 3.593 Å, whereas the mean grain size was = 2932 Å. Morphology of the stainless steel substrate surface was studied with profilometry. Mechanical properties of the stainless steel...
-
Physicochemical studies (Raman, XRD) of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains physico-chemical examination of a new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include Raman spectroscopy and X-ray diffraction...
-
Rheology studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains rheology measurements carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was performed by melt mass-flow rates (MFR)....
-
Mechanical studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains mechanical tests carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was dynamic mechanical analysis (DMA). The measurements...