XRD for MoS2-Carbon Based Materials
Open Research DataThe presented data showcases the results of XRD analysis conducted on molybdenum sulfide modified with carbon. The MoS2-carbon base materials were prepared via a facile hydrothermal method. Structural characterization confirmed the successful incorporation of carbon into the MoS2 support. XRD was recorded using an X-ray diffractometer (Philips X”Pert...
-
AFM and SSRM investiagtion of carbon nanowalls properties
Open Research DataStructures with limited dimensionality are of great interest in modern nanotechnology. The properties of these objects are used, among others, for the construction of modern displays or as a base for quantum computers. Carbon nanowalls, which are the subject of the imaging results contained in this collection, are also considered interesting building...
-
Chemical properties of bismuth telluride – carbon composites.
Open Research DataCarbon nanotubes and amorphous carbon have been introduced into bismuth telluride matrix (in 0.15 and 0.30 wt % ratio) in order to investigate influence of carbon on composite’s thermoelectric properties. Composites with well-dispersed additives have been obtained by sonication and ball-milling. Chemical composition of materials was confirmed by XPS...
-
SEM micrographs of the V2O5 nanorods after thermal treatment under reducing atmosphere
Open Research DataThe DataSet contains the SEM micrographs of V2O5 nanorods after thermal treatment under a reducing atmosphere. Samples were annealed at 450C for 2, 20, and 40h under a reducing atmosphere (94% Ar, 6% H2).
-
Chemical composition of V2O5 nanorods
Open Research DataThe DataSet contains the chemical compositions of the V2O5 nanorods on a silicon substrate. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The As-prepared thin films were annealed at 600C under a synthetic air atmosphere.
-
Crystallization kinetics of V2O5 nanorods
Open Research DataThe DataSet contains the DSC curves of As-prepared xerogel powder with different heating rates. The information about sol synthesis is described in the Journal of Nanomaterials.
-
X-ray diffraction spectra of the NiCo2O4 modified by carbon
Open Research DataThis dataset comprises XRD results for NiCo2O4 modified with carbon, varying according to the amount of carbon. In this context, the XRD data provide insights into the crystalline structure and phase composition of the NiCo2O4 material as it is modified with varying quantities of carbon. This investigation is valuable for understanding how the presence...
-
Carbon dioxide (CO2) calibration set of FTIR spectra
Open Research DataThe calibration spectra for CO2 concentration calibration were supplied with this dataset
-
Carbon (II) oxide (CO) calibration set of FTIR spectra
Open Research DataThe calibration spectra for CO concentration calibration were supplied with this dataset
-
Carbon balance of SOFC fueled by biogas mixture at 750 C
Open Research DataThe dataset contains the calculated carbon balance for the SOFC fueled by synthetic biogas mixture (60:40 CH4:CO2). The outlet concentration of the gases from SOFC were measured using novel FTIR-based unit.
-
Raman spectra and electrochemical data of carbon nanowall with tailored defects
Open Research DataThis dataset comprises of Raman spectra aquired with different excitation laser sources and the electrochemical data of defect-induced carbon nanowall electrodes (CNW).
-
SEM micrographs of boron-doped nanocrystalline diamond-carbon nanospikes
Open Research DataThis dataset contains the Scanning Electron Microscopy (SEM) micrographs taken for rich boron-doped carbon crystalline nanospikes/nanograss structures, at different magnifications, encoded in the labels of the images. The micrographs were made using Hitachi S-3400N SEM microscope in secondary electron mode under 20 kV accelerating voltage. No additional...
-
SEM micrographs of V2O5 nanorods as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 nanorods as cathode materials before and after the galvanostatic charge/discharge curves.
-
Rheology studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains rheology measurements carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was performed by melt mass-flow rates (MFR)....
-
Electrochemical studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains electrochemical investigation on electrodes 3D printed using a new composite composed of poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The presented results contain:1. electrochemical characterisation...
-
Mechanical studies of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains mechanical tests carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques was dynamic mechanical analysis (DMA). The measurements...
-
Linear impedance of V2O5 nanorods obtained at 903K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 923K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 913K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Linear impedance of V2O5 nanorods obtained at 893K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Morphological and electrochemical characterization of ceramic carbon foam electrodes water treatment applications
Open Research DataThis dataset contains morphological and electrochemical characterization of ceramic carbon foam employed as an electrode (CFFE) for the oxidation of a target pollutant. The dataset includes:
-
Thermal stability analysis of poly(lactic acid)-carbon black-nanodiamond composite
Open Research DataThis dataset contains thermal stability tests carried out on new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include: thermogravimetric analysis (TGA)...
-
The impact of carbon black particle size on curing characteristics of GTR modified with bitumen
Open Research DataPresented data shows an impact of particle size of GTR and three different loadings of carbon black on curing characteristics of GTR modified with bitumen. Samples were prepared using a two-roll mill – all in the same manner. After 24 hours of stabilization at ambient conditions they were submitted to the curing analysis via Rheometer Monsanto 100S....
-
Scanning electron microscopy (SEM) images of the boron-doped carbon nanowalls surfaces
Open Research DataThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of boron-doped carbon nanowalls electrodes on silicon substrates. The surface is characterized by nano-walled structures. The obtained electrodes were doped with boron at the level of [B]/[C] = 5000ppm in the gas atmosphere during the synthesis.
-
Scanning electron microscopy (SEM) images of the boron-dopied carbon nanowalls surfaces
Open Research DataThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of boron-doped carbon nanowalls electrodes on silicon substrates. The surface is characterized by nano-walled structures. The obtained electrodes were doped with boron at the level of [B]/[C] = 1200ppm in the gas atmosphere during the synthesis.
-
Scanning electron microscopy (SEM) images of the boron-doped carbon nanowalls surfaces
Open Research DataThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of boron-doped carbon nanowalls electrodes on silicon substrates. The surface is characterized by nano-walled structures. The obtained electrodes were doped with boron at the level of [B]/[C] = 2000ppm in the gas atmosphere during the synthesis.
-
Electrochemical impedance spectra and CV curves of V2O5 nanorods
Open Research DataThe DataSet contains the EIS spectra for coin-cells and CV curves with the V2O5 nanorods obtained by the sol-gel method. Cyclic voltammetry and electrochemical impedance spectroscopy (EIS) were measured using the AUTOLAB 302N potentiostat-galvanostat under Nova software. The EIS measurements were recorded in the frequency range 100 kHz to 10 mHz for...
-
Non-linear impedance of V2O5 nanorods obtained at 923K
Open Research DataThe DataSet contains the non-linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Thermal stability of V2O5 nanorods under inert atmosphere
Open Research DataThe DataSet contains the TGA curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Thermal stability of V2O5 nanorods under oxidizing atmosphere
Open Research DataThe DataSet contains the TGA curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Topography studies of screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Open Research DataThis dataset contains topography examination of SPCE containing boron-doped diamond BDD foils done with scanning electron microscope. Different points mark different electrode spots: A) working electrode, B) reference electrode, C) counter electrode, D) pads.
-
Rheology studies of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains MFR/MVR (melt flow rate) rheology studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The study aims to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Physicochemical studies (Raman, XRD) of poly(lactic acid)-carbon black-nanodiamond composites
Open Research DataThis dataset contains physico-chemical examination of a new 3D printing-dedicated composites with poly-lactic acid (PLA), carbon black (CB) and nanodiamond fillers. Two types of nanodiamonds were studied: detonation nanodiamonds (DND) and boron-doped carbon nanowalls (BCNW). The investigated techniques include Raman spectroscopy and X-ray diffraction...
-
Electrochemical studies for screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Open Research DataThis dataset contains electrochemical examination of SPCE paste and SPCE containing boron-doped diamond BDD foils. The studies include kinetics analyses with cyclic voltammetry and electrochemical impedance spectroscopy with different redox probes: hexacyanoferrate(III) and Hexaammineruthenium(III) and potentiostatic open circuit potential at different...
-
Pore size distribution of PC-X (porous carbon materials obtained at various temperatures)
Open Research DataThese data contain pore size distribution of PC-700 (porous carbon materials obtained at 700°C), PC-800 (porous carbon materials obtained at 800°C) and PC-900 (porous carbon materials obtained at 900°C) analyzed by the nitrogen adsorption/desorption technique.
-
Topography studies of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains topography studies with scanning electron microscope of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material...
-
Electrochemical analyses of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains cyclic voltammetry studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
Thermal analyses of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains thermal analyses (TGA, DTG, DSC) studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different...
-
Compression test results of fused filamend fabricated polylactyde and polylactyde with carbon fiber filler
Open Research DataThe DataSet contains the results of the mechanical behaviour of cube specimens with dimensions 30 x 30 x 30 cm3. The specimens were additively manufactured with the fused filament fabrication (FFF) method. They used two different materials polylactide (PURE PLA) and polylactide with carbon fibre filler (PLA+CF). The specimens were segregated into three...
-
Tensile test results of fused filamend fabricated polylactyde and polylactyde with carbon fiber filler
Open Research DataThe Dataset contains the results of the mechanical behaviour of dog-bone shaped specimens. The specimens were additively manufactured with the fused filament fabrication (FFF) method. They used two different materials polylactide (PURE PLA) and polylactide with carbon fibre filler (PLA+CF). The specimens were segregated into three groups - unsterilized,...
-
Cyclic voltammetry curves of the V2O5 nanorods (Na-ion batteries)
Open Research DataThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanorods obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanorods (Li-ion batteries)
Open Research DataThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Changes in heat flow of V2O5 nanorods under inert atmosphere
Open Research DataThe DataSet contains the DSC curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Changes in heat flow of V2O5 nanorods under oxidizing atmosphere
Open Research DataThe DataSet contains the DSC curves of V2O5 nanorods obtained at 650°C. The information about nanorods synthesis is described in the Journal of Nanomaterials.
-
Raman spectroscopy analysis of poly(lactic acid)-carbon black composite treated by femtosecond laser
Open Research DataThe dataset contains the Raman spectroscopy measurements of commercially available carbon black-filled poly(lactic acid) 3D printed electrodes after femtosecond laser ablation. These results were utilized in the manuscript published in Electrochimica Acta: 10.1016/j.electacta.2022.140288
-
Electrical and noise responses of carbon nanotube networks enhanced by UV light for nitrogen dioxide sensing
Open Research DataNetworks consisting of randomly oriented carbon nanotubes (CNN) were investigated toward nitrogen dioxide detection by means of electrical and low-frequency noise measurements. UV-activation of CNN layers improved gas sensitivity and reduced the limit of detection, especially by employing 275 nm-LED. This data set includes DC resistance measurements...
-
Chemical and structural studies of screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Open Research DataThis dataset contains chemical analyses and structural studies by XPS and Raman spectroscopy, carried out for SPCE containing boron-doped diamond BDD foils done with scanning electron microscope. Different points for XPS analysis mark different electrode spots: A) working electrode, B) reference electrode, C) counter electrode, D) pads.
-
Physicochemical studies (Raman) of multiple times processed poly(lactic acid)-carbon black composites
Open Research DataThis dataset contains Raman spectroscopy studies of commercially available ProtoPasta 3D printable filament, composed of poly-lactic acid (PLA) and conductive carbon black (CB) filler. The aim of the study is to observe structural differences and applied properties changes under multiple reprocessing of the composite material at different temperatures...
-
The topography of carbon black-polylactide composite 3D printed electrodes after femtosecond laser ablation
Open Research DataThis dataset contains a series of scanning electron microscopy images revealing the topography of 3D printed carbon black-polylactide composite electrodes after laser ablation with a femtosecond laser. Different laser powers were investigated, namely: 10%, 25%, 50%, 75% and 100%. The CB-PLA electrodes were 3D printed using an Ender printer. Femtosecond laser NKT Photonics, Origami XP parameters: power at 100%...
-
The electrochemical response to glassy carbon electrode modification steps towards viral electrochemical immunosensor preparation
Open Research DataThe dataset contains the electrochemical measurements (CV/EIS) carried out for the consecutive steps of the glassy carbon GC electrode functionalization, in separate subfolders, as described. The cyclic voltammetry (CV) was conducted using a Palmsens 4 potentiostat/galvanostat system (Methrom, Autolab, Netherlands) in the standard three-electrode configuration,...