TEM imaging of Ag-Au nanoalloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of metal thin layers (Au/Ag or Ag/Au) followed by annealing under 550 Celsius degree in an argon atmosphere. The basic single layer thickness was usually ca. 3 nm. For investigations two samples wih 50% Au and 50% Ag were selected and samples 1/3 Ag - 2/3 Au and 2/3 Ag - 1/3...
-
Interaction of PDA monomers with Au
Dane BadawczeThis dataset contains supplementary information in the form of Electrostatic difference potential (EDP) map, density of states (DOS) spectra, and adsorption geometries of polydopamine PDA monomers on the Au surface. PDA was modelled either as the oxidised (indolequinone, IQ) and reduced (dihydroxyindole, DHI) chemistries.
-
Depth profile of the chemical composition of the Au-Ag multilayers
Dane BadawczeSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Temperature of formation of Au nanostructures
Dane BadawczeNanostructures were obtained via annealing of thin Au films. In order to determine possible nanoislands formation mechanisms, dependence on initial film thickness was examined. For the surface morphology studies, nanograin structure and chemical composition analysis, SEM, HR TEM and EDS measurements were performed, respectively. Morphology studies shown...
-
Interactions of PDA tetramers with the Au surfaces
Dane BadawczeThis dataset contains electrostatic difference potential (EDP) maps, density of states (DOS) spectra, and adsorption geometries of cyclic tetramers on the Au surface. The real polydopamine was modelled either as the cyclic tetramers in the oxidised (indolequinone, IQ) and reduced (dihydroxyindole, DHI) chemistries with all units being the same - either...
-
Chemical analysis of the Au-Ag nanoaloys
Dane BadawczeThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Au nanostructures coated with a ultrathin film of Al2O3 - measurements and FDTD simulations
Dane BadawczeGold plasmonic platforms have been coated with an ultra-thin films of aluminium oxide. Optical measurements, showing the influence of the thickness of Al2O3 on plasmon resonance position. The observed red-shift of the resonance location with the increase of the thickness of the Al2O3 film, can be explained by the change in the dielectric function of...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
SEM micrographs of the topography of Cu-Sn-TiO2 nanocomposite coatings
Dane BadawczeThe dataset contains the scanning electron microscopy (SEM) micrographs of nanocomposite Cu-Sn-TiO2 coatings electrodeposited from oxalic acid bath containing Cu and Sn salts as well as TiO2 nanoparticles under various treatments: mechanical stirring, ultrasonic or none. The details of the electrodeposition process are presented in the readme file attached...
-
The XRD pattern of CeO2/10wt.%Cu prepared with BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
Electrical and noise responses of Graphene-Silicon Schottky diodes decorated with Au nanoparticles for light-enhanced sensing of organic gases
Dane BadawczeGraphene-Silicon Schottky junctions decorated with Au nanoparticles were used for light-enhanced detection of organic tetrahydrofuran and chloroform. Au nanoparticles exhibited localized surface plasmon resonance (LSPR) in the range of yellow light; thus yellow LED (wavelength of 592 nm) was utilized to induce the plasmonic effect, that increased the...
-
The TPO oxidation profile of CeO2/10wt.%Cu with BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
Physicochemical and photocatalytic data of Cu-TiO2/Ti3C2 composites
Dane BadawczeIn this dataset, we include the data regarding the physicochemical properties (XRD, DR/UV-vis, photoluminescence, electrochemistry) and photocatalytic activity of TiO2/Ti3C2 and Cu-TiO2/Ti3C2 composites in the reaction of carbamazepine degradation. Herein we present the results for pure TiO2/Ti3C2 and composites modified with copper particles (0.25%,...
-
The electrochemical response to Au electrode modification steps towards viral electrochemical immunosensor preparation
Dane BadawczeThe dataset contains the electrochemical measurements (CV/EIS) carried out for the consecutive steps of the Au electrode functionalization, in separate subfolders, as described. The cyclic voltammetry (CV) was conducted using a Palmsens 4 potentiostat/galvanostat system (Methrom, Autolab, Netherlands) in the standard three-electrode configuration, with...
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Cu
Dane BadawczeThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Cu oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
The XRD pattern of CeO2/10wt.%Cu prepared without BCD
Dane BadawczeThe dataset includes the XRD pattern of CeO2/10wt.%Cu. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The TPO oxidation profile of CeO2/10wt.%Cu without BCD - prereduced
Dane BadawczeThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Cu with BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
The XPS studies revealing the surface chemistry of Cu-Sn-TiO2 nanocomposite coatings
Dane BadawczeThe dataset contains the X-Ray Photoelectron Spectroscopy (XPS) data of nanocomposite Cu-Sn-TiO2 coatings electrodeposited from oxalic acid bath containing Cu and Sn salts as well as TiO2 nanoparticles under various treatments: mechanical stirring, ultrasonic or none. The details of the electrodeposition process are presented in the descriptor file...
-
The TPR reduction profile of CeO2/10wt.%Cu without BCD - 2 cycles
Dane BadawczeThe dataset includes the TPR reduction profiles of CeO2/10wt.%Cu. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
Powder x-ray diffraction pattern of polycrystalline Cu(IO3)2*xH2O
Dane BadawczeHydrated copper(II) iodate sample was prepared in water solution by reacting copper(II) sulfate and potassium iodate, following the method described by Peterson (J. Chem. Educ. 1957, 34, 12, 612). The sample was subsequently dried at various temperatures in order to produce an anhydrous Cu(IO3)2:
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CLO/Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Ce0.8La0.2O2+10wt.%Cu nanocatalyst. The specatra were collected every 1 minute.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CeO2/Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using CeO2+10wt.%Cu nanocatalyst. The specatra were collected every 1 minute.
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/1%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/1%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of CeO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of CeO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using Al2O3/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using AlOOH/1%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using CeO2/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using CeO2/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
FTIR spectra of gas mixtures from the process of biogas dry reforming using Al2O3/5%Cu catalyst
Dane BadawczeThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Al2O3 (TMDAR)/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Dane BadawczeThe ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 900 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
Au nanoparticles identifiction with the use of AFM Volta potential mapping
Dane BadawczeThe specific physical, chemical and electrochemical electrical properties of gold nanoparticles have led to their extensive use as high-performance chemical and biochemical sensors. The described properties relate to surface plasmon resonance, fluorescence quenching or enhancement, high electrical conductivity and light scattering. The described nanoparticles...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials synthesized via the solid state reaction method
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
SEM images of tge gold nanostructures on silicon
Dane BadawczeAu nanostructures were prepared on Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%)....
-
Formation of gold anostructures detected by SEM microscope
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air...
-
SEM images of dewetted gold films
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Optical properties of MnO-B2O3 based glass
Dane BadawczeMnO-B2O3 based glass with Au nanoparticles samples were annealing for a various time (in a range of 24-96 hours) at various temperatures (from 340 up to 350 deg.). Presence of silver nanoparticles was detected by UV-VIS measurements. On the basis of change optical bandgap, Ag NPs was detected.
-
Morphology of the sol-gel derived LTO:Cu films
Dane BadawczeMorphology of the lithium titanate doped by Cu thin films were investigated by SEM microscope. Films were deposited by spin-coater from sol-gel derived sol. SEM images showed a high porous structure, tipaciall for sol-gel based films. For measurements samples with a various content of Cu were selected.
-
XPS measurement of the Fe-Ti based materials
Dane BadawczeThe mono‐ and bimetal‐modified (Pd, Cu) titanium(IV) oxide and iron oxide (III) photocatalysts were prepared by chemical reduction method and characterized using XPS method. The composition of elements incorporated in the surface layer of mono- and bimetallic photocatalysts was determined by XPS analysis, as well as the valence state of elements. Measurements...
-
Depth profile of the gold-silver bimetallic structures
Dane BadawczeSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
X-ray diffraction (XRD) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
Structural investigations of the LTO:Cu thin films
Dane BadawczeLithium titanate (Li1+xTi2-xO4) doped with Cu2+ ions was synthesized by sol-gel processing method. The structure was characterized by X-ray Diffraction (XRD). All samples revealed presence of LTO spinel phase. X-ray pattern of undoped LTO was free of any impurities and other crystal phases. Similarly, samples with low amount of copper dopant (x = 0.05...
-
The reductivity of the transition metals - calculations
Dane BadawczeThe dataset includes the reduction enthalpy and Gibbs energy simulated for Co, Cu, Fe, La, Mo, Ni, Sr, Ti, and W from oxide form into metallic form in hydrogen. Simulations were performed using HSC Chemistry software.
-
XRD (X-ray Diffraction) patterns of PMH, PMD and simulated MIL-53(Al)
Dane BadawczeThese data contain XRD (X-ray Diffraction) patterns of PMH, PMD and simulated MIL-53(Al). The results were recorded by a Philipsdiffractometer using Cu Ka radiation. Sample abbreviations (PMH, PMD, MIL-53(Al)) are in agreement with the markings used in the linked publication.