DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
Non-wage factors for choosing the first job
Dane BadawczeThe creation of an effective remuneration system depends on a number of factors. However, some components are relatively versatile and commonly used. Therefore, employees report fairly standard expectations, which are then verified by employers. Mutual expectations are also the subject of many analyzes and scientific studies.
-
Magdalena Szuflita-Żurawska
OsobyMagdalena Szuflita-Żurawska jest kierownikiem Sekcji Informacji Naukowo-Technicznej na Politechnice Gdańskiej oraz Liderem Centrum Kompetencji Otwartej Nauki przy Bibliotece Politechniki Gdańskiej. Jej główne zainteresowania badawcze koncentrują się w obszarze komunikacji naukowej oraz otwartych danych badawczych, a także motywacji i produktywności naukowej. Jest odpowiedzialna między innymi za prowadzenie szkoleń dla pracowników...
-
Konstrukcje i zastosowania współczesnych silników Stirlinga
PublikacjaW pracy omówione zostały przyczyny rosnącego zainteresowania komercyjnego wykorzystania silników Stirlinga. Scharakteryzowane zostały podstawowe typy silników Stirlinga ze względu na układ przestrzeni roboczej i cylindrów. W pracy przedstawione zostały przykłady współczesnych konstrukcji tych silników, dokonano również analizy aktualnych i planowanych zastosowań silników Stirlinga. Omówiono podstawowe zalety i wady wykorzystania...
-
Application of Semantic Knowledge Management System in Selected Areas of Polish Public Administration
PublikacjaThis paper describes an application of semantic technologies and knowledge management systems in chosen areas of Polish public administration. Short analyses of crisis management and EU policy coordination processes are presented. An architecture of a knowledge management system with interfaces using controlled natural language is proposed. A lot of examples are shown that prove a usefulness of semantic knowledge management and...
-
Creating a radiological database for automatic liver segmentation using artificial intelligence.
PublikacjaImaging in medicine is an irreplaceable stage in the diagnosis and treatment of cancer. The subsequent therapeutic effect depends on the quality of the imaging tests performed. In recent years we have been observing the evolution of 2D to 3D imaging for many medical fields, including oncological surgery. The aim of the study is to present a method of selection of radiological imaging tests for learning neural networks.
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
Nanostructures fabrication with use of electrical AFM litography
Dane BadawczeIn the last 10 years, one of the nanotechnological trends has been observed, consisting in the development of new variants of computer memory systems with high capacity and speed of access, using quantum dots. One of the techniques for creating nanodots and other nanostructures is based on the use of an atomic force microscope acting as a lithographic...
-
Microscopic examination of the texture of paper products
Dane BadawczeAtomic force microscopy (AFM) can be used to study the state of the paper fibers with the aim of providing qualitative and semi-quantitative information on degradation and aging. The work [1] reports the results of tests of various paper products subjected to deliberate aging processes under the influence of various factors. Chemical and biological...
-
Joanna Janczewska prof. dr hab.
OsobyJoanna Janczewska odbyła studia wyższe magisterskie na kierunku Matematyka w latach 1994–1999 z wynikiem bardzo dobrym i uzyskała w 1999 roku tytuł magistra. W 2002 roku na Uniwersytecie Gdańskim uzyskała stopień naukowy doktora nauk matematycznych w zakresie matematyki. Promotorem w przewodzie doktorskim był dr hab. Andrzej Borysowicz, prof. UG. W październiku 2004 roku podjęła pracę na stanowisku adiunkta w Katedrze Algebry...
-
Luminescence of TeO2:Eu thin films
Dane BadawczeTellurium dioxide doped by europium thin films were deposited by magnetron sputtering method and simultaneously heated at 200 oC. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the films was...
-
Wyznaczenie obciążeń na poszycie okrętu wywołanych uderzeniem fal i uderzeniem w lód i ich wpływ na bezpieczeństwo okrętu
PublikacjaThe main problem is the vessels rather accurate determination of the hydrodynamic loads so-called hydroelasticity outside . This can be done by theoretical analysis , computer simulation or by experiment. This gives the hydrodynamic pressure distribution on the walls of the ship's hull and also on the walls of marine vessels .The most dangerous are the impact of extreme storm waves , the impact of the wharf and the impact zone...
-
A comparative analysis of numerically simulated and experimentally measured static responses of a floating dock
PublikacjaTwo numerical methods, dynamic and static analyses, are proposed to calculate the static responses of a floating dock under different ballast water distributions. Model-scale experimental tests were conducted to compare with these numerical methods. The dynamic analysis includes a 6-degree-of-freedom (6-DOF) model, a hydrostatic force model and a hydrodynamic force model to simulate the dock's freely floating processes. The dock's...
-
Focused ion beam-based microfabrication of boron-doped diamond single-crystal tip cantilevers for electrical and mechanical scanning probe microscopy
PublikacjaIn this paper, the fabrication process and electromechanical properties of novel atomic force microscopy probes utilising single-crystal boron-doped diamond are presented. The developed probes integrate scanning tips made of chemical vapour deposition-grown, freestanding diamond foil. The fabrication procedure was performed using nanomanipulation techniques combined with scanning electron microscopy and focused ion beam technologies....
-
Non-Coaxially Rotating Motion in Casson Martial along with Temperature and Concentration Gradients via First-Order Chemical Reaction
PublikacjaThe effect of non-coaxial rotation on the transport of mass subjected to first-order chemical reaction is studied analytically. The effects of thermal radiation, buoyancy, constructive and destructive chemical reactions along with Casson fluid in rotating frame are discussed. Time evolution of primary and secondary velocities, energy and solute particles are analyzed. The behavior of flow under the variation of intensity of magnetic...
-
AUDITORY DISPLAY FROM THE MUSIC TECHNOLOGY PERSPECTIVE . Obecność wirtualnego środowiska dźwiękowego w technologiach muzycznych
PublikacjaThis paper presents some applications of Auditory Displays (AD) in the domain of music technology. First, the scope of music technology and auditory display areas are shortly outlined. Then, the research trends and system solutions within the fields of music technology, music information retrieval and music recommendation are discussed. Finally, an example of an auditory display that facilities music annotation process based on...
-
Compensation of magnetic disturbances caused by sensors in a differential magnetometric system
PublikacjaStudy of low magnetic fields necessitates the use of precision magnetometers working in a differential system. Minimization of this error is a substantial issue in the case of magnetometers working in a differential system on a mobile platform. The compensation method of heading error consists in taking measurements of changes in magnetic induction with the use of the tested magnetometer for various locations of the sensor in relation...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - full run
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - pre-run (10s)
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Follow the Light. Where to search for useful research information
PublikacjaArchitectural Lighting Design (ALD) has never been a standalone professional discipline. Rather, it has existed as the combination of art and the science of light. Today, third generation lighting professionals are already creatively intertwining these fields, and the acceleration in scientific, technological and societal studies has only increased the need for reliable multidisciplinary information. Therefore, a thorough re-examination...
-
Time-Domain Description of Point-Source Acoustic Wavefields as a Useful Approach in Ultrasonic Techniques
PublikacjaIn traditional acoustics, field problems are usually treated in the frequency domain, broadband fields being reduced to superposition of harmonic spectrum components. However, this approach is inherently acausal and it is known that in case of arbitrary signals, the distribution-based, time-domain description can be more effective. The present paper is an attempt to expand the time-domain linear systems formalism onto space problems...
-
Time-domain description of point-source acoustic wavefields as a useful approach in ultrasonic techniques
PublikacjaIn traditional acoustics, field problems are usually treated in the frequency domain, broadband fields being reduced to superposition of harmonic spectrum components. However, this approach is inherently acausal and it is known that in case of arbitrary signals, the distribution-based, time-domain description can be more effective. The present paper is an attempt to expand the time-domain linear systems formalism onto space problems...
-
An effective method for studying intermolecular interactions in binary liquids with hydrogen bonds: FTIR spectra and ab initio calculations in the N-methylformamide - methanol system
PublikacjaMolecular complexes in methanol (MeOH)−N-methylformamide (NMF) mixtures were studied based on their FTIR-ATR spectra, to which two methods of analysis were applied: factor analysis and a quantitative version of the difference-spectra method. The mean composition of a complex between NMF and MeOH molecules over the whole range of mixture compositions was determined. Absorbing species differentiated with regard to the interaction...
-
Scattering From a Cylindrical Object of Arbitrary Cross Section With the Use of Field Matching Method
PublikacjaA simple and intuitive solution to scattering problems in shielded and open structures is presented. The main idea of the analysis is based on the direct field matching technique involving the usage of projection of the fields at the boundary on a fixed set of orthogonal basis functions. Different convex shapes and various obstacle materials are considered to verify the validity of the method in open and closed structures. The...
-
Ontology as a Tool for the IT Management Standards Support
PublikacjaIn this paper the authors discuss the initial idea of using ontologies to model requirements of the standards that support IT management processes. The Open Group Architecture Framework (TOGAF) is set as an example. A need for transition from the generic model do the organization-specific one is indicated. The described example serves as a ground for considering the usefulness of such modeling approach in the wider spectrum of...
-
Application of electrochemical sensors and sensor matrixes for measurement of odorous chemical compounds
PublikacjaIn this paper describes the principle of operation of the electrochemical sensors and the sensor matrixes comprised of electrochemical sensors intended for measurement of odorous compounds. Critical comparison of these sensors’ advantages and disadvantages has been made. The fields of economy contributing to release of odours and the potential sources of their emission have been identified. Commercially available electrochemical...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
The morphology of vanadate glasses containing BaTiO3 measured with the use of AFM
Dane BadawczeThe morphology of vanadate glasses doped with BaTiO3 was measured with the use of AFM method. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Dane BadawczeOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...