The study on application of biopolyols obtained by cellulose biomass liquefaction performed with crude glycerol for the synthesis of rigid polyurethane foams
PublikacjaIn this work rigid polyurethane foams (PUR) were obtained by replacement of 0–70 wt% of petrochemical polyol with bio-polyol obtained via cellulose liquefaction in presence of crude glycerol. The foams with different content of a bio-polyol were prepared by single step method for NCO/OH ratio equals 1.5. The prepared materials were analyzed in terms of their morphology, chemical structure, thermal stability and basic physical and...
-
Synthesis and thermal studies of flexible polyurethane nanocomposite foams obtained using nanoclay modified with flame retardant compound
PublikacjaThis work presents thermal studies of nanocomposites based on the flexible polyurethane (PU) matrix and filled using montmorillonite organically modified with organophosphorus flame retardant compound. Flexible PU nanocomposite foams were prepared in the reaction carried out between reactive alcoholic hydroxyl and isocyanate groups with the ratio of NCO to OH groups equal to 1.05. The amount of an organoclay ranging from 3 to 9...
-
A Comprehensive Review of Reactive Flame Retardants for Polyurethane Materials: Current Development and Future Opportunities in an Environmentally Friendly Direction
PublikacjaPolyurethanes are among the most significant types of polymers in development; thesematerials are used to produce construction products intended for work in various conditions. Nowa-days, it is important to develop methods for fire load reduction by using new kinds of additivesor monomers containing elements responsible for materials’ fire resistance. Currently, additiveantipyrines or reactive flame retardants can be used during...
-
Single-phase product obtained via crude glycerine depolymerisation of polyurethane elastomer: structure characterisation and rheological behaviour
PublikacjaPolyurethane recycling is a topic of growing interest due to the increasing amount of polyurethanewaste. The main purpose of polyurethane feedstock recycling is to recover the starting polyol, a valuable material. In thiswork, amethod of polyurethane thermo-chemical recycling, glycerolysisbymeansof crude glycerine, is proposed. Themaineffort is focusedonthe employment of crude glycerine without purification from biodiesel production...
-
Study of the Effect of Filling Thermoplastic Medical Polyurethane with PVA, PLA or Diatomite on the Relaxation Times Distributions of 1H NMR
PublikacjaIn this work, to characterize the mobility of diferent sections of the macromole‑ cules of polyurethane (PUR), polyvinyl alcohol (PVA), and polylactic acid (PLA), as well as the density of crosslinks of the polymer chains when using fllers, we used the distributions of spin–lattice and spin–spin relaxation times for the protons. It is shown that the rigidity of the thermoplastic polymers depends on the sizes of the granules of...
-
Polyurethane glycolysate from industrial waste recycling to develop low dielectric constant, thermally stable materials suitable for the electronics
PublikacjaWe are utilizing a new method to improve the dielectric properties of a conventional polymer using a recycled polymer product. The polyurethane foams are recycled by glycolysis process and the derived material was applied to improve the dielectric properties of the brittle DGEBA epoxy resin. Two main parameters that determine the applicability of the material as a dielectric (the dielectric constant and dielectric loss), were studied...
-
Effect of Variation of Hard Segment Content and Graphene-Based Nanofiller Concentration on Morphological, Thermal, and Mechanical Properties of Polyurethane Nanocomposites
PublikacjaThis study describes the development of a new class of high-performance polyurethane elastomer nanocomposites containing reduced graphene oxide (RGO) or graphene nanoplatelets (GNP). Two types of polyurethane elastomers with different contents of hard segments (HS) were used as a polymer matrix. The developed nanocomposites were characterized by thermal analysis (DSC, TG), dynamic mechanical testing (DMA), hardness testing, mechanical...
-
Segmented bio-based polyurethane composites containing powdered cellulose obtained from novel bio-based diisocyanate mixtures
PublikacjaA considerable number of research works focus on the positive influence of cellulose on the properties of polymer-based composites and their wide range of application possibilities. The present work is focused on the synthesis of novel bio-based polyurethane (bio-PU) composites filled with powdered cellulose (microcellulose, MC) in an amount of 5 wt.%. Bio-PU composites were synthesized via a non-solvent prepolymer method. First,...
-
Sustainable Strategy for Algae Biomass Waste Management via Development of Novel Bio-Based Thermoplastic Polyurethane Elastomers Composites
PublikacjaThis work concerns the waste management method of algae biomass wastes (ABW). For this purpose, we prepared bio-based thermoplastic polyurethane elastomer (bio-TPU) composites. Algae biomass wastes are derived from algal oil extraction of Chlorella vulgaris and from biomass of Enteromorpha and Zostera marina. ABWs were used in the bio-TPUs composites as a filler in the quantity of 1, 5, 10, and 15 wt.%. The bio-based composites...
-
Thermo-Chemical Decomposition Study of Polyurethane Elastomer Through Glycerolysis Route with Using Crude and Refined Glycerine as a Transesterification Agent
PublikacjaDue to the increasing amount of polyurethane waste, chemical recycling of these materials is a topic of growing interest for many researchers. The primary pur- pose of polyurethane feedstock recycling is to recover the starting polyol. In this study glycerolysis using glycerine from two sources and two purity grades is proposed as a method of chemical recycling. The main effort of this paper focuses on the employment of commercial...
-
Structural, thermal and physico-mechanical properties of polyurethane/brewers’ spent grain composite foams modified with ground tire rubber
PublikacjaIn this work, brewers’ spent grain (BSG) and ground tire rubber (GTR) waste fillers were applied as low-cost reinforcement phase in rigid polyurethane foam (PUR). PUR/BSG/GTR composites were prepared by a single step method, using polyglycerol as partial substitute of commercially available petrochemical polyols. Foaming parameters, chemical structure, dynamic mechanical properties, thermal stability, physico-mechanical properties...
-
Glass transition temperatures of polyurethane-urea elastomers based on N, N′-ethylenethiourea and N, N′-ethyleneurea as chain extenders
Publikacja -
Microstructure–Property Relationship of Polyurethane Foams Modified with Baltic Sea Biomass: Microcomputed Tomography vs. Scanning Electron Microscopy
Publikacja -
Ciprofloxacin-modified degradable hybrid polyurethane-polylactide porous scaffolds developed for potential use as an antibacterial scaffold for regeneration of skin
PublikacjaThe aim of the performed study was to fabricate an antibacterial and degradable scaffold that may be used in the field of skin regeneration. To reach the degradation criterion for the biocompatible polyurethane (PUR), obtained by using amorphous α,ω-dihydroxy(ethylene-butylene adipate) macrodiol (PEBA), was used and processed with so-called “fast-degradable” polymer polylactide (PLA) (5 or 10 wt %). To meet the antibacterial requirement...
-
Bio-Based Polyurethane Composites and Hybrid Composites Containing a New Type of Bio-Polyol and Addition of Natural and Synthetic Fibers
PublikacjaThis article describes how new bio-based polyol during the liquefaction process can be obtained. Selected polyol was tested in the production of polyurethane resins. Moreover, this research describes the process of manufacturing polyurethane materials and the impact of two different types of fibers—synthetic and natural (glass and sisal fibers)—on the properties of composites. The best properties were achieved at a reaction temperature...
-
The influence of different flame retardants on thermal stability, mechanical and physical properties of rigid polyurethane foams blown with n-pentane
PublikacjaW artykule opisano wpływ klasycznych uniepalniaczy na właściwości sztywnych pianek poliuretanowych. Opisano 7 układów piankowych oraz wyniki charakterystyki fizyczno-mechanicznej oraz stabilności termicznej.
-
Transport Mechanism of Paracetamol (Acetaminophen) in Polyurethane Nanocomposite Hydrogel Patches—Cloisite® 30B Influence on the Drug Release and Swelling Processes
PublikacjaThis article describes the swelling and release mechanisms of paracetamol in polyurethane nanocomposite hydrogels containing Cloisite® 30B (organically modified montmorillonite). The transport mechanism, swelling and release processes of the active substance in nanocomposite matrix were studied using gravimetric and UV-Vis spectroscopic methods. Swelling and release processes depend on the amount of clay nanoparticles in these...
-
Fire-Retardant Flexible Foamed Polyurethane (PU)-Based Composites: Armed and Charmed Ground Tire Rubber (GTR) Particles
PublikacjaInadequate fire resistance of polymers raises questions about their advanced applications. Flexible polyurethane (PU) foams have myriad applications but inherently suffer from very high flammability. Because of the dependency of the ultimate properties (mechanical and damping performance) of PU foams on their cellular structure, reinforcement of PU with additives brings about further concerns. Though they are highly flammable and...
-
Microstructure–Property Relationship of Polyurethane Foams Modified with Baltic Sea Biomass: Microcomputed Tomography vs. Scanning Electron Microscopy
PublikacjaIn this paper, novel rigid polyurethane foams modified with Baltic Sea biomass were compared with traditional petro-based polyurethane foam as reference sample. A special attention was focused on complex studies of microstructure, which was visualized and measured in 3D with high-resolution microcomputed tomography (microCT) and, as commonly applied for this purpose, scanning electron microscopy (SEM). The impact of pore volume,...
-
Bio‑derived polyurethanes obtained by non‑isocyanate route using polyol‑based bis(cyclic carbonate)s—studies on thermal decomposition behavior
PublikacjaNon-isocyanate polyurethanes (NIPUs) constitute one of the most prospective groups of eco-friendly materials based on their phosgene-free synthesis pathway. Moreover, one of the steps of their obtaining includes the use of carbon dioxide (CO 2 ), which allows for the promotion of the development of carbon dioxide capture and storage technologies. In this work, non- isocyanate polyurethanes were obtained via three-step synthesis...
-
The influence of amorphous macrodiol, diisocyanate type and l-ascorbic acid modifier on chemical structure, morphology and degradation behavior of polyurethanes for tissue scaffolds fabrication
PublikacjaStudies described in this work were related to the bulk synthesis and characterization of polyurethanes (PURs) obtained with the use of cyclic 4,4′-methylene bis(cyclohexyl isocyanate) (HMDI) or linear 1,6-hexamethylene diisocyanate (HDI), amorphous α,ω-dihydroxy(ethylene-butylene adipate) macrodiol (PEBA), 1,4-butandiol (BDO) chain extender and dibutyltin dilaurate (DBTDL) catalyst. Obtained PURs were modified with l-ascorbic...
-
The Impact of Ground Tire Rubber Oxidation with H2O2 and KMnO4 on the Structure and Performance of Flexible Polyurethane/Ground Tire Rubber Composite Foams
PublikacjaThe use of waste tires is a very critical issue, considering their environmental and economic implications. One of the simplest and the least harmful methods is conversion of tires into ground tire rubber (GTR), which can be introduced into different polymer matrices as a filler. However, these applications often require proper modifications to provide compatibility with the polymer matrix. In this study, we examined the impact...
-
Characterization of Highly Filled Glass Fiber/Carbon Fiber Polyurethane Composites with the Addition of Bio-Polyol Obtained through Biomass Liquefaction
PublikacjaThis work aims to investigate the process of obtaining highly filled glass and carbon fiber composites. Composites were manufactured using previously obtained cellulose derived polyol, polymeric methylene diphenyl diisocyanate (pMDI). As a catalyst, dibutyltin dilaurate 95% and Dabco® 33-LV were used. It was found that the addition of carbon and glass fibers into the polymer matrix causes an increase in the mechanical properties...
-
Conductive Thermoplastic Polyurethane Nanocomposite Foams Derived from a Cellulose/MWCNTs Aerogel Framework: Simultaneous Enhancement of Piezoresistance, Strength, and Endurance
PublikacjaHigh conductivity and excellent mechanical properties of composite polymers favors their application as piezoresistive strain sensors. Nonetheless, it is difficult to develop composite polymers with desirable piezoresistance, mechanicaland durable properties. Herein, we developed conductive cellulose/MWCNTs aerogel using the freeze-drying technique. Besides, we explored the application of the highly-sensitive piezoresistive polymer...
-
Porosity and swelling properties of novel polyurethane–ascorbic acid scaffolds prepared by different procedures for potential use in bone tissue engineering
PublikacjaIn this work, a novel polyurethane (PU) system based on poly(ethylene-butylene) adipate diol, 1,6-hexamethylene diisocyanate, 1,4-butanediol, and ascorbic acid was used to prepare scaffolds with potential applications in bone tissue engineering. Two fabrication methods to obtain porous materials were chosen: phase separation (PS)/salt particle leaching (PL) and solvent casting (SC)/salt PL. The calculated porosity demonstrated...
-
Ciprofloxacin – Modified Degradable Hybrid Polyurethane-Polylactide Porous Scaffolds Developed for Potential Use as an Antibacterial Scaffold for Regeneration of Skin
Publikacja -
Rheological characteristics of oligomeric semiproducts gained via chemical degradation of polyurethane foam using crude glycerin in the presence of different catalysts
PublikacjaPolyurethane (PU) recycling is a topic of growing interest due to the increasing amount of polyurethane waste. The main purpose of polyurethane chemical recycling is to recover the starting polyol. In this study, a method of polyurethane thermochemical recycling, glycerolysis by means of crude glycerin, is proposed. This work presents a comparative study of commercial catalysts used in order to accelerate the decomposition process,...
-
Progress in non-isocyanate polyurethanes synthesized from cyclic carbonate intermediates and di- or polyamines in the context of structure–properties relationship and from an environmental point of view
PublikacjaCommercially, polyurethanes are produced by the reaction of diisocyanates, polyols (polyester or polyether) and low molecular weight chain extender. Toxicity, moisture sensitivity and phosgene-based synthesis of diisocyanates resulted in investigations focused on obtaining the non-isocyanate polyurethanes (NIPUs). This work presents the review of synthesis and structure–properties relationship of non-isocyanate polyurethanes obtained...
-
Composite Polyurethane-Polylactide (PUR/PLA) Flexible Filaments for 3D Fused Filament Fabrication (FFF) of Antibacterial Wound Dressings for Skin Regeneration
Publikacjahis paper addresses the potential application of flexible thermoplastic polyurethane (TPU) and poly(lactic acid) (PLA) compositions as a material for the production of antibacterial wound dressings using the Fused Filament Fabrication (FFF) 3D printing method. On the market, there are medical-grade polyurethane filaments available, but few of them have properties required for the fabrication of wound dressings, such as flexibility...
-
Comprehensive Enhancement of Prepolymer-Based Flexible Polyurethane Foams’ Performance by Introduction of Cost-Effective Waste-Based Ground Tire Rubber Particles
PublikacjaMaterial innovations in polyurethane (PU) foams should ideally combine performance enhancement, environmental impact limitation, and cost reduction. These goals can be achieved by applying recycled or waste-based materials without broader industrial applications, implicating their low price. Herein, from 5 to 20 parts by weight of ground tire rubber (GTR) particles originated from the recycling of postconsumer car tires were incorporated...
-
Towards sustainable catalyst-free biomass-based polyurethane-wood composites (PU-WC): From valorization and liquefaction to future generation of biocomposites
PublikacjaA substantial aspect of materials engineering lies in the responsible process of designing polymer-based materials. Due to environmental pollution, excessive consumption of natural resources, and increasing environmental awareness of society, there is a massive need for polyurethane (PU) materials with reduced environmental impact. To date, research on catalyst-free polyurethane-wood composites (PU-WC) has demonstrated a huge potential...
-
The impact of filler thermomechanical modifications on static and dynamic mechanical performance of flexible foamed polyurethane/ground tire rubber/zinc borate composites
PublikacjaThe rapid development of the automotive industry is very beneficial to many aspects of human life, but it is also a very significant environmental burden. The most straightforward impact is related to the generation of exhaust, but the management of post-consumer car parts is also a major challenge. Among them, waste tires are very burdensome due to their enormous numbers. Therefore, it is essential to develop novel, environmentally...
-
Highly sensitive large strain cellulose/multiwalled carbon nanotubes (MWCNTs)/thermoplastic polyurethane (TPU) nanocomposite foams: From design to performance evaluation
PublikacjaAerogel-based polymer composite foams are promising for large strain piezoresistive sensors, but their aerogel skeleton is partially destroyed during the foaming process, limiting their sensitivity. Herein, the thermoplastic polyurethane was synthesized on the aerogel skeleton to obtain cellulose/multiwalled carbon nanotubes (MWCNTs)/thermoplastic polyurethane (TPU) nanocomposite materials foamed with the aid of supercritical carbon...
-
Micro-Raman spectroscopy in the studies of multiphase separated polyurethanes. [online] W: [Proc.] UTECH Europe 2003 . The International Polyurethane Industry Conference and Exhibition. 25/26/27 March 2003, The Hague, Netherlands. London: Crain Communications Ltd. Dostępny w World Wide Web: http://UTECH-2003.com + wydruk.**2003 [s. 123-130 bibliogr. 41 poz.]Mikro-Ramanowska spektroskopia w badaniach poliuretanów wykazujących separację wielofazową.
PublikacjaPrzedmiotem badań były trzy próbki poliuretanowe o zawartości 30% segmentówsztywnych otrzymanych z politlenku propylenu, diizocyjanianu difenylometanui butanodiolu. Próbki te wykazują morfologię wielofazową, w której można wy-różnić globule i sferolity rozproszone w matrycy polimerowej.Za pomocą spek-troskopii mikro-Ramana przeprowadzono mikroanalizę chemiczną wszystkich ele-mentów morfologicznych. Stwierdzono odmienny skład...
-
Poliuretany do zastosowań w medycynie na bazie poli(ε-aprolaktonodiolu) oraz poliglikolu etylenowego. Poly(ε-caprolactonediol) and polyethylene glycol-based polyurethanes for medical applications
PublikacjaOmówiono sposoby otrzymywania poliuretanów do zastosowań medycznych. W wyniku modyfikacji znanej metody prepolimerowej syntezy otrzymano dwie serii nowych poliuretanów różniących się składem chemicznym, dlaktórych przygotowano pełne charakterystyki właściwości. Wykazano, że wprowadzenie poliglikolu etylenowego do struktury poliestouretanówotrzymanych na bazie polikaprolaktonu znacząco poprawia powinowactwo materiałów do wody, zwiększa...
-
Structure versus hydrolytic and thermal stability of bio-based thermoplastic polyurethane elastomers composed of hard and soft building blocks with high content of green carbon
PublikacjaNowadays, sustainability plays a key role in the design and synthesis of new materials. One of the methods for the preparation of green materials is incorporation into their structure the monomers with a high content of green carbon. Therefore, the aim of this work was to investigate the influence of the type and molecular mass of two bio-based polyester polyols and bio-glycol on the properties of aliphatic partially bio-based...
-
Eco-friendly Route for Thermoplastic Polyurethane Elastomers with Bio-based Hard Segments Composed of Bio-glycol and Mixtures of Aromatic–Aliphatic and Aliphatic–Aliphatic Diisocyanate
PublikacjaApplication of bio-based diisocyanates with low volatility instead petrochemical diisocyanates has positive impact on environment by reduction of hazardous effects on living organisms and lead to bio-based polyurethanes (bio-PUs) with good usage properties. This work was focused on the synthesis and chosen properties examination of partially bio-based thermoplastic polyurethane elastomers (bio-PUs) obtained using diisocyanate mixtures,...
-
Bio polyetherurethane composites with high content of natural ingredients: hydroxylated soybean oil based polyol, bio glycol and microcrystalline cellulose
PublikacjaIn our study, we focused on obtaining bio-polyurethane composites using bio-components such as bio glycol, modified natural oil-based polyol, and microcrystalline cellulose (MCC). The pre-polymer method was used to prepare the bio polyurethane matrix. Prepolymer was synthesized using 4,4’-diphenylmethane diisocyanate (MDI) and a polyol mixture containing 50 wt.% of commercial polyether and 50 wt.% of hydroxylated soybean oil (H3)....
-
Influence of Surface-Modified Montmorillonite Clays on the Properties of Elastomeric Thin Layer Nanocomposites
PublikacjaIn recent years, polyurethane nanocomposites have attracted more attention due to the massive demand for materials with increasingly exceptional mechanical, optical, electrical, and thermal properties. As nanofillers have a high surface area, the interaction between the nanofiller and the polymer matrix is an essential issue for these materials. The main aim of this study is to validate the impact of the montmorillonite nanofiller...
-
Timber Frame Houses with Different Insulation Materials - Seismic Analysis
PublikacjaThe aim of this article is to present results of a dynamic numerical analysis focused on the response of two timber frame building structures exposed to seismic excitations. The first structure was insulated with mineral wool, while the second one with polyurethane foam. Specifications and technology involved in the models' construction are based on the previously conducted experimental study, upon which numerical structural models...
-
One More Step Towards a Circular Economy for Thermal Insulation Materials—Development of Composites Highly Filled with Waste Polyurethane (PU) Foam for Potential Use in the Building Industry
PublikacjaThe rapid development of the building sector has created increased demand for novel materials and technologies, while on the other hand resulting in the generation of a severe amount of waste materials. Among these are polyurethane (PU) foams, which are commonly applied as thermal insulation materials. Their management is a serious industrial problem, due to, for example, their complex chemical composition. Although some chemical...
-
Michał Strankowski dr hab. inż.
OsobyJest zatrudniony w Katedrze Technologii Polimerów na Wydziale Chemicznym od 2006 roku. W tym samym roku uzyskał stopień doktora nauk technicznych w zakresie technologii chemicznej. Stopień doktora habilitowanego w dziedzinie nauk ścisłych i przyrodniczych uzyskał w 2019 roku. W okresie 2013-2015 pełnił funkcję kierownika projektu „PUR-GRAF” pt. „Nanokompozyty poliuretanowe zawierające zredukowany tlenek grafenu”. Za opracowane...
-
Challenges and recent advances in bio-based isocyanate production.
PublikacjaPolyurethanes (PUs) are key players in the plastics industry. According to the Global Polyurethane Market (2019–2023), their value in the global market reached $95.13 billion in 2019 and is expected to grow at a compound annual growth rate of 12%. This is in line with the increase in the number of research papers and patents on the synthesis and application of petroleum-based PUs (P-PUs) and biomass or green PUs (G-PUs) (from 67 657...
-
Józef Tadeusz Haponiuk prof. dr hab. inż.
Osoby -
Polymers doped by Ca or P. Chemical composition investigations
Dane BadawczeThe calcium and phosphorus doped polyurethane polymers (PU) were analyzed by XPS method. A series of samples with various content of Ca and P dopand - from 0% up to 21%) were selected for measutements. The chemical composition and valence state of elements were measurements using OmicronNatechnology UHV system wih Argus hemispherical photoelectron...
-
Influence of bio-polyols with different molecular weight on properites of PUR-PIR foams
Dane BadawczeThis work attempts to validate the possibility of replacing petrochemical polyols with previously synthesized bio-polyols and their impact on the structure and properties of rigid polyurethane-polyisocyanurate (PUR-PIR). The influence of bio-polyols addition on foam properties was investigated by mechanical testing, Fourier transform infrared spectroscopy...
-
Biopolyols obtained via crude glycerol-based liquefaction of cellulose: their structural, rheological and thermal characterization
PublikacjaIn this work lignocellulose biomass liquefaction was used to produce biopolyols suitable for the manufacturing of rigid polyurethane foams. In order to better evaluate the mechanism of the process, pure cellulose was applied as a raw material. The effect of time and temperature on the effectiveness of liquefaction and the parameters of resulting biopolyols were characterized. The prepared materials were analyzed in terms of their...
-
Bio‐polyols synthesized by liquefaction of cellulose: Influence of liquefaction solvent molecular weight
PublikacjaCurrently, the plastics industry including polyurethanes is based on the use of petrochemicals. For this reason, scientists are looking for new types of renewable resources for the substitution of petrochemical substances. This work aims to evaluate the effect of polyethylene glycols (PEG) with different molecular mass impact on properties of bio-based polyols synthesized via biomass liquefaction of cellulose. To date, research...
-
Termooksydacyjna i fotooksydacyjna degradacja pianek poliuretanowych
PublikacjaPrzeprowadzono ocenę efektywności działania wybranych środków przeciwstarzeniowych w sztywnych piankach poliuretanowych, otrzymywanych na drodze syntezy jednoetapowej. Ocenę tę oparto na pomia-rach zmian barwy oraz wytrzymałości mechanicznej zsyntezowanych materiałów. Na podstawie analizy uzyskanych wyników stwierdzono, iż dodatek 3% mieszaniny I rzędowego antyutleniacza fenolowego oraz benzotriazolowego absorbera UV znacząco zmniejsza...
-
Novel bio-based thermoplastic poly(ether-urethane)s. Correlations between the structure, processing and properties
PublikacjaThe main purpose of this work was to analyze the effect of the number of unreacted isocyanate groups and the [NCO]/[OH] molar ratio during the chain extension of a prepolymer during the polymerization process on the structure, processing and selected properties of thermoplastic poly(ether-urethane)s. Three series of novel thermoplastic polyurethanes were obtained via a prepolymer route. Three prepolymers were synthesized from diisocyanate...