DLC coating in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h. The test was augmented...
-
DLC coating in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was augmented by vibration...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
DLC coating doped with W in ring-on-ring sliding with water lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: WATER. Tribometer: PT-3. Overall test time >15h. The test was...
-
Nanotechnologies in Development of Structural Materials and Biomaterials
PublikacjaThe nanometric materials and technologies resulted in nanostructures are reviewed. The examples of nanomaterials are shown. The typical nanotechnologies, including plastic deformation, mechanical attrition, controlled detonation, hot plasma jet synthesis, laser vaporisation, CVD and PVD, mechanical milling, annealing, ultrasonic irradiation, nanolithography, electrocrystallisation, electrospinning, sol-gel method, cryogenic laser-enhanced...
-
On Surface Kinetic Constitutive Relations
PublikacjaIn the framework of the strain gradient surface elasticity we discuss a consistent form of surface kinetic energy. This kinetic constitutive equation completes the statement of initial–boundary value problems. The proposed surface kinetic energy density is the most general function consistent with the constitutive relations in bulk. As the surface strain energy depends on the surface deformation gradient and its gradient, the kinetic...
-
Ryszard Katulski prof. dr hab. inż.
Osoby -
Two-step Conversion of Crude Glycerol Generated by Biodiesel Production into Biopolyols: Synthesis, Structural and Physical Chemical Characterization
PublikacjaIn this work biopolyols were synthesized via two-step process from crude glycerol and castor oil. For better evaluation of analyzed process, the impact of its time and temperature on the structure and properties of biopolyols was determined. Obtained results fully justified conducting of synthesis in two steps. Prepared materials were characterized by hydroxyl value and water content comparable to polyols industrially applied in...
-
Tuning of eg electron occupancy of MnCo2O4 spinel for oxygen evolution reaction by partial substitution of Co by Fe at octahedral sites
PublikacjaTo study the effect of partial Co substitution by Fe in the B site of MnCo2O4 spinel on its physicochemical and electrochemical properties, a series of MnCo2-xFexO4 powders (x=0.125; 0.250; 0.500; 0.750; 1.000) were synthesized by means of the sol-gel method. The produced powders were characterized by powder X ray diffraction (pXRD), scanning and transmission electron microscopy (SEM & TEM) coupled with energy dispersive spectroscopy...
-
ThreSpect a program for the determination of the Appearance Energies
Dane BadawczeDataset presents the “ThreSpect” computer program dedicated to simulating threshold energies of neutral and ionized products generated in the collisions of photons or charged particles with atoms and molecules.
-
Influence of bio-polyols with different molecular weight on properites of PUR-PIR foams
Dane BadawczeThis work attempts to validate the possibility of replacing petrochemical polyols with previously synthesized bio-polyols and their impact on the structure and properties of rigid polyurethane-polyisocyanurate (PUR-PIR). The influence of bio-polyols addition on foam properties was investigated by mechanical testing, Fourier transform infrared spectroscopy...
-
Sol-gel derived TeO2:RE powders
Dane BadawczeTellurium dioxide powders doped by Europium or Dysprosium were prepared by sol-gel method. Samples were annealed in ix of Ar and O2 atomosphere at 600 degrees. Presence of rare earth dopants and Te4+ phase was confirmed by X-Ray Photoemission Spectroscopy method (XPS). For XPS measurements samples with 1 atomic % and 5 atomic % of dopand were selected.
-
A comprehensive evaluation of mimosa extract as a corrosion inhibitor on AA6060 alloy in acid rain solution: part I. Electrochemical AC methods
PublikacjaThe inhibition effect of mimosa extract on the corrosion of AA6060 aluminum alloy in acid rain solution was investigated by electrochemical impedance spectroscopy and dynamic electrochemical impedance spectroscopy (DEIS). All the studied electrochemical parameters showed good corrosion inhibitive characteristics with respect to the aluminum alloy in the tested solution. Inhibitor efficiency increased with the concentration and...
-
Magdalena Szuflita-Żurawska
OsobyMagdalena Szuflita-Żurawska jest kierownikiem Sekcji Informacji Naukowo-Technicznej na Politechnice Gdańskiej oraz Liderem Centrum Kompetencji Otwartej Nauki przy Bibliotece Politechniki Gdańskiej. Jej główne zainteresowania badawcze koncentrują się w obszarze komunikacji naukowej oraz otwartych danych badawczych, a także motywacji i produktywności naukowej. Jest odpowiedzialna między innymi za prowadzenie szkoleń dla pracowników...
-
Measurements of the chemical composition of LTO:Cu powders
Dane BadawczeLithium titanate doped by copper was measured by X-ray photoemission spectroscopy (XPS). For sol-gel synthesis lithium acetate dehydrate and titanium (IV) butoxide 97% and copper (II) nitrate from Alfa Aesar were used as a reagents. Cu precursor was added in the proper weight to get an x index equal 0, 0.1 and 0.2. In the first step lithium acetate...
-
Microscopic examination of the texture of paper products
Dane BadawczeAtomic force microscopy (AFM) can be used to study the state of the paper fibers with the aim of providing qualitative and semi-quantitative information on degradation and aging. The work [1] reports the results of tests of various paper products subjected to deliberate aging processes under the influence of various factors. Chemical and biological...
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 20MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 20MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
DLC coating doped with W in ring-on-ring sliding with saline solution (0.9% wt.) lubrication 10MPa/0.1m/s
Dane BadawczeWear tests in sliding friction of 1% W (tungsten) doped DLC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, DLC-W over DLC-W. Mean contact stress: 10MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9% wt.). Tribometer: PT-3. Overall test time >15h....
-
Nanostructures fabrication with use of electrical AFM litography
Dane BadawczeIn the last 10 years, one of the nanotechnological trends has been observed, consisting in the development of new variants of computer memory systems with high capacity and speed of access, using quantum dots. One of the techniques for creating nanodots and other nanostructures is based on the use of an atomic force microscope acting as a lithographic...
-
XPS data of as-grown BDD, as-implanted Mn-BDD, and annealed Mn-BDD thin films
Dane BadawczeXPS survey spectra and detailed spectra O1, C1s and Mn2p of as-grown BDD, as-implanted Mn-BDD, and annealed Mn-BDD thin films. X-ray photoelectron spectroscopy (XPS) studies were conducted on an Escalab 250 Xi from Thermo Fisher Scientific with an Al Kα radiation. Results were published in the paper ( https://doi.org/10.1002/adfm.202308617)
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Distribution of Relaxation Times analysis results of impedance measured in function of temperature on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. Electrochemical impedance spectroscopy were measured at 800 °C; 750 °C and 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof. Ciucci’s group, was used...
-
Joanna Janczewska prof. dr hab.
OsobyJoanna Janczewska odbyła studia wyższe magisterskie na kierunku Matematyka w latach 1994–1999 z wynikiem bardzo dobrym i uzyskała w 1999 roku tytuł magistra. W 2002 roku na Uniwersytecie Gdańskim uzyskała stopień naukowy doktora nauk matematycznych w zakresie matematyki. Promotorem w przewodzie doktorskim był dr hab. Andrzej Borysowicz, prof. UG. W październiku 2004 roku podjęła pracę na stanowisku adiunkta w Katedrze Algebry...
-
In vivo performance of intraperitoneal onlay mesh after ventral hernia repair
PublikacjaBackground: Ventral hernia repair needs to be improved since recurrence, postoperative pain and other complications are still reported in many patients. The behavior of implants in vivo is not sufficiently understood to design a surgical mesh mechanically compatible with the human abdominal wall. Methods: This analysis was based on radiological pictures of patients who underwent laparoscopic ventral hernia repair. The pictures...
-
Nondestructive Testing of the Miter Gates Using Various Measurement Methods
PublikacjaWhen any problems related to civil engineering structures appear, identifying the issue through the usage of only one measuring method is difficult. Therefore, comprehensive tests are required to identify the main source. The strains and displacement measurements, as well as modal identification, are widely used in the nondestructive testing of structures. However, measurements are usually carried out at several points and confirm...
-
Bearing capacity of working platform using distinct layout optimization method
PublikacjaBearing capacity of the working platforms from sandy soil resting on NC and OC clays was analyzed using LimitState GEO program. Different failure modes are considered using distinct layout optimization (DLO) method, which forms the upper bound solution of limit state analysis. Different mechanisms of failure were observed as a function of the platform thickness, angle of internal friction of the platform material and undrained...
-
A novel in vivo approach to assess strains of the human abdominal wall under known intraabdominal pressure
PublikacjaThe study concerns mechanical behaviour of a living human abdominal wall. A better mechanical understanding of a human abdominal wall and recognition of its material properties is required to find mechanically compatible surgical meshes to significantly improve the treatment of ventral hernias. A non-invasive methodology, based on in vivo optical measurements is proposed to determine strains of abdominal wall corresponding to...
-
A comparative analysis of numerically simulated and experimentally measured static responses of a floating dock
PublikacjaTwo numerical methods, dynamic and static analyses, are proposed to calculate the static responses of a floating dock under different ballast water distributions. Model-scale experimental tests were conducted to compare with these numerical methods. The dynamic analysis includes a 6-degree-of-freedom (6-DOF) model, a hydrostatic force model and a hydrodynamic force model to simulate the dock's freely floating processes. The dock's...
-
Non-Coaxially Rotating Motion in Casson Martial along with Temperature and Concentration Gradients via First-Order Chemical Reaction
PublikacjaThe effect of non-coaxial rotation on the transport of mass subjected to first-order chemical reaction is studied analytically. The effects of thermal radiation, buoyancy, constructive and destructive chemical reactions along with Casson fluid in rotating frame are discussed. Time evolution of primary and secondary velocities, energy and solute particles are analyzed. The behavior of flow under the variation of intensity of magnetic...
-
Focused ion beam-based microfabrication of boron-doped diamond single-crystal tip cantilevers for electrical and mechanical scanning probe microscopy
PublikacjaIn this paper, the fabrication process and electromechanical properties of novel atomic force microscopy probes utilising single-crystal boron-doped diamond are presented. The developed probes integrate scanning tips made of chemical vapour deposition-grown, freestanding diamond foil. The fabrication procedure was performed using nanomanipulation techniques combined with scanning electron microscopy and focused ion beam technologies....
-
Reliability estimation of underground horizontal fuel tank limit states
PublikacjaFuel tanks are designed with regard to standard loads and operating conditions. The investigations of the paper show the impact of such factors as tank corrosion and other means on the variation of stress fields and deformation of the underground horizontal tank shell. The introduction of probabilistic methods allows for structural reliability assessment. While the computational time of the entire tank FEM model is high, the preliminary...
-
Diagnostics of zno varistors by means of nondestructive testing
PublikacjaStandard industrial testing of high-voltage varistors for surge arresters demands application of high voltages and intensive currents. Nondestructive methods for varistor quality and endurance evaluation have been proposed and described. They rely on the application of resonant ultrasound spectroscopy, electro-ultrasonic spectroscopy, noise measurement and nonlinearity testing at voltages lower than continuous operating range....
-
Spectroscopic Study of Plasma Polymerized a-C:H Films Deposited by a Dielectric Barrier Discharge
PublikacjaPlasma polymerized a-C:H thin films have been deposited on Si (100) and aluminum coated glass substrates by a dielectric barrier discharge (DBD) operated at medium pressure using C2Hm/Ar (m = 2, 4, 6) gas mixtures. The deposited films were characterized by Fourier transform infrared reflection absorption spectroscopy (FT-IRRAS), Raman spectroscopy, and ellipsometry. FT-IRRAS revealed the presence of sp3 and sp2 C–H stretching and...
-
Structural, electrical, and magnetic study of La-, Eu-, and Er- doped bismuth ferrite nanomaterials obtained by solution combustion synthesis
PublikacjaIn this work, the multiferroic bismuth ferrite materials Bi0.9RE0.1FeO3 doped by rare-earth (RE = La, Eu, and Er) elements were obtained by the solution combustion synthesis. Structure, electrical, and magnetic properties of prepared samples were investigated by X-ray photoelectron spectroscopy, Mössbauer spectroscopy, electrical hysteresis measurement, broadband dielectric spectroscopy, and SQUID magnetometry. All obtained nanomaterials...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - full run
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - pre-run (10s)
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Dane BadawczeFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate folders).Specimen...
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....
-
Distribution of Relaxation Times analysis results of impedance measured at 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures
Dane BadawczeThis dataset contains results of Distribution of Relaxation Times analysis (DRT) of impedance of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at different temperatures (800 °C, 900 °C and 1000 °C). Electrochemical impedance spectroscopy were measured at 700 °C (syntetic air). The DRTTools Matlab GUI, available from prof....