Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
The morphology of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at low temperature region
Dane BadawczeThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
The structure of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
The morphology of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
Effects of La0.8Sr0.2MnO3 and Ag electrodes on bismuth-oxide-based low-temperature solid electrolyte oxygen generators
PublikacjaIn this study, La0.8Sr0.2MnO3 (LSM) was used as the ceramic electrode in a (Bi1.50Y0.50)0.98Zr0.04O3+δ (BYO)-based solid electrolyte oxygen generator (SEOG) and its performance was compared with that of a previously studied high-fire Ag electrode. Among La0.6Sr0.4Co0.2Fe0.8O3, LaNi0.6Fe0.4O3, Cu1.4Mn1.6O4, and LSM materials, only LSM materials did not trigger any chemical reaction or interdiffusion with BYO at temperatures up to...
-
Influence of controlled crystallization and SrF2 content on the structure and properties of Eu3+ doped phosphate glasses
Dane BadawczeThe attached data contains the results of measurements of phosphate glasses and glass-ceramics doped with Eu. On their basis, the new material was characterized and the influence of the SrF2 addition on the glass structure was determined. In addition, the influence of the SrF2 content and controlled crystallization on the luminescent properties of Eu3+...
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear impedance of strontium–borate glass measured with impedance spectroscopy method at high temperature region
Dane BadawczeThe linear electrcial properties of strontium–borate glass was measured by impedance spectroscopy method.
-
Influence of free carbon on the Young's modulus and hardness of polymer‐derived silicon oxycarbide glasses
Publikacja -
Magnetic properties of of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeMagnetic properties of iron-doped glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15 and 20 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere...
-
Wpływ procesu redukcji na właściwości strukturalne i mechaniczne szkieł tlenkowych z grupy (Pb,Bi)-(Si,Ge)-O = Influence of reduction process on the structural and mechanical properties of (Pb,Bi)-(Si,Ge)-O oxide glasses
PublikacjaThe effect of the reduction process in H2 at 380 °C on the microstructure and elemental composition of a glass Bi0.4Pb0.2Si0.4Ox has been investigated. It has been shown that after reduction a clearly separated top layer with a thickness of approx. 50 µm was formed on the surface of the sample. This layer is depleted of oxygen and has higher electrical conductivity than the interior of the glass. It has also been found that some...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Dane BadawczeElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Mixed electronic-ionic conductivity in transition metal oxide glasses con-taining alkaline ions
PublikacjaOpisano właściwości elektryczne szkieł z tlenkami metali przejściowych zawierających jony metali alkalicznych. Szczególną uwagę zwrócono na typowe zmiany przewodnictwa występujące przy domieszkowaniu tego typu szkieł jonami metali alkalicznych. Porównano przewodnictwo elektryczne szkieł fosforanowo-żelazowych zawierających jony sodu z przewodnictwem szkieł bizmutowo-miedziowych.
-
Structure of partially reduced xPbO (1-x)SiO2 glasses: combined EXAFS and MD study
PublikacjaWykorzystując połączenie metody EXAFS (extended X-ray absorption finestructure) i symulacji MD (molecular dynamics) zbadano strukturęczęściowo zredukowanych szkieł ołowiowo-krzemianowych o różnejstechiometrii wyjściowej. W wyniku analizy uzyskano szczegółowyopis struktury lokalnej wokół atomów ołowiu i jej zmiany w funkcjiskładu szkła i poziomu redukcji. Określono również jaką tendencjędo aglomeracji w metaliczne klastry wykazują...
-
TEM, EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures.
Dane BadawczeData consists of raw TEM/EDS and optical microscope images of pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures. Additional TEM images and optical microscope images of silica shells were included.
-
Electrical properties of nanostructures in lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeElectrical properties of iron oxide nanostructures observed in silicate glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15, 20 and 25 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where...
-
Synthesizing of Sensitizing Glasses in Very Small Volumes and Strictly Controlled Atmospheres for Fiber and Integrated Optic Sensors
Publikacja -
Structural and luminescence investigation of GeO2-PbO-Bi2O3-SrF2 glasses doped with Eu3+, Tb3+ and Tm3+ ions
PublikacjaThe GeO2-PbO-Bi2O3-SrF2 (GePbBiSr) glass systems doped with Eu3 +, Tb3 +, Tm3 + and triply-doped with Eu3 +/Tb3 +/Tm3 + ions were successfully synthesized. Their structural and luminescent properties have been investigated with various techniques. Obtained results indicate that these glass systems are suitable materials for the RE3 + ions hosts. RE3 + ions can be excited by single UV light wavelength (355/378/395 nm) and simultaneously...
-
PHYSICS AND CHEMISTRY OF GLASSES
Czasopisma -
XRD, DTA and luminescence measurements of B2O3-Bi2O3-AlF3 glasses doped with Eu3+, Tb3+ and Tm3+ ions
Dane BadawczeThe DataSet contains the XRD,DTA and luminescence measurements for the B2O3-Bi2O3-AlF3 glass system. Samples were prepared by the conventional melt quenching technique. Starting materials were melted in porcelain crucibles at 950 oC for 20 min. XRD and DTA data were collected for 50B2O3-50Bi2O3,45B2O3-45Bi2O3+10AlF3 and 40B2O3-40Bi2O3+20AlF3 glasses....
-
Topography of iron-phosphate glasses doped with niobium and titanium tested by confocal microscope
Dane BadawczeThe topography of phosphate-iron glasses containing niobium and titanium were investigated with the use of confocal miscroscope. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5, 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 and 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents...
-
<title>Nonlinear glasses and metaglasses for photonics, a review: Part I. Nonlinear electrical susceptibility and refractive index</title>
Publikacja -
High Pressure Luminescence of Cr-Related Centers in (3CaO-Ga 2 O 3 -3GeO 2 ) Glasses
Publikacja -
Sol–gel glasses with enhanced luminescence of laser dye Rhodamine B due to plasmonic coupling by copper nanoparticles
Publikacja -
Thermal properties of ceramic Bi2VO5.5 and strontium–borate glass-ceramics containing crystalites of Bi2VO5.5. measured with DSC
Dane BadawczeThermal properties of ceramic Bi2VO5.5 and strontium–borate glass-ceramics containing Bi2VO5.5 crystallites was measured by DSC.
-
The X-ray crystallographic structures, spectral and magnetic properties of nickel(II), copper(II) and cobalt(II) complexes with tetra(3-iso-propylpyrazol-1-yl)borate
Publikacja -
Luminescent GeO2–Pb–Bi2O3 glasses co-doped with Tb3+1 and Eu3+: Excitation energy transfer and color chromaticity
Publikacja -
Lead-free bismuth-based perovskites coupled with g–C3N4: A machine learning based novel approach for visible light induced degradation of pollutants
PublikacjaThe use of metal halide perovskites in photocatalytic processes has been attempted because of their unique optical properties. In this work, for the first time, Pb-free Bi-based perovskites of the Cs3Bi2X9 type (X = Cl, Br, I, Cl/Br, Cl/I, Br/I) were synthesized and subjected to comprehensive morphological, structural, and surface analyses, and photocatalytic properties in the phenol degradation reaction were examined. Furthermore,...
-
The structure of strontium–borate glass-ceramics containing crystalites of Bi2VO5.5. measured with X-ray diffraction and SEM methods
Dane BadawczeThe structure of strontium–borate glass-ceramics containing Bi2VO5.5 crystallites was measured by XRD and SEM.
-
<title>Non-linear glasses and metaglasses for photonics, a review: Part II. Kerr nonlinearity and metaglasses of positive and negative refraction</title>
Publikacja -
Physics and Chemistry of Glasses-European Journal of Glass Science and Technology Part B
Czasopisma -
White emitting phosphors based on glasses of the type 10AlF3–10TiO2–39PbO–30H3BO3–10SiO2–xEu2O3–(1−x)Tb2O3: An energy transfer study
Publikacja -
Photocatalytic hydrogen evolution from glycerol-water mixture under visible light over zinc indium sulfide (ZnIn2S4) nanosheets grown on bismuth oxychloride (BiOCl) microplates
PublikacjaZnIn2S4 (ZIS) is one of the widely studied photocatalyst for photocatalytic hydrogen evolution applications due to its prominent visible light response and strong reduction ability. However, its photocatalytic glycerol reforming performance for hydrogen evolution has never been reported. Herein, the visible light driven BiOCl@ZnIn2S4 (BiOCl@ZIS) composite was synthesized by growth of ZIS nanosheets on a template-like hydrothermally...
-
Marcin Wekwejt dr inż.
OsobyMarcin Wekwejt, absolwent studiów inżynierskich w inż. biomedycznej (2016; Politechnika Bydgoska im. J. i J. Śniadeckich & Collegium Medicum im. L. Rydygiera), studiów magisterskich w inż. mechaniczno-medycznej (2018; Politechnika Gdańska & Gdański Uniwersytet Medyczny) oraz studiów doktoranckich w dyscyplinie inż. materiałowej (2021, Politechnika Gdańska). Uzyskał z wyróżnieniem stopień naukowy doktora nauk inżynieryjno-technicznych...
-
X-ray diffraction (XRD) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
Structural and luminescence properties of B2O3-Bi2O3-AlF3 glass doped with Eu3+, Tb3+ and Tm3+ ions
PublikacjaThe B2O3-Bi2O3-AlF3 glass system doped with Eu3+, Tb3+, Tm3+ and triply doped with Eu3+/Tm3+/Tb3+ ions in different molar ratios were successfully synthesized. Glass transition and crystallization temperatures were examined by Differential Scanning Calorimetry (DSC) measurements. X-ray Diffraction (XRD) confirmed the amorphous character of the samples. Fourier Transform Infrared Spectroscopy (FTIR) revealed that the glass matrix...
-
X-ray diffraction (XRD) of silica-coated bismuth oxide/gadolinium oxide (Bi2O3+Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide Bi2O3+Gd2O3 structures
Dane BadawczeExcel (*.xlsx) and Csv (*.csv) files containing raw mechanical (compressive strength) data of cement pastes after 1, 2, 7 and 28 days of curing
-
X-ray diffraction (XRD) of silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain results from X-ray diffraction (XRD) measurements of pristine Bi2O3 and Gd2O3 structures using Aeris diffractometer (Malvern Panalytical, Malvern, UK) with Cu-Kα radiation (λ = 1.544 Å)
-
Particle size distribution (laser granulometry) of pristine bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeData contain raw results of particle size distribution (by volume) of Bi2O3 and Gd2O3 particles determined using a laser diffraction method (Malvern Mastersizer 2000, Worcestershire, UK).
-
Mechanical properties of cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw mechanical (compressive strength) data of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.
-
Thermgravimetric analysis (TGA) data of cement pastes containing pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeThermogravimetric (TGA) data of cement pastes after 2, 7 and 28 days. Samples designations: Control, BG, BG-A and BG-B are associated with the specimen names in the associated publication.
-
Transmission electron microscope (TEM) and optical microscope images of pristine and silica-coated bismuth oxide and gadolinium oxide particles
Dane BadawczeCollection of raw transmission electron microscope (TEM) micrographs and optical microscope images used in the associated manuscript. All data in accessible *.tif format. Zip package contains:
-
Isothermal calorimetry data for cement pastes containing pristine and silica-coated bismuth oxide (Bi2O3) and gadolinium oxide (Gd2O3) structures
Dane BadawczeExcel file containing raw calorimetric data determined up to 168 h (Tam Air 3 8-channel isothermal calorimeter) of cement pastes containing variable amount of Bi2O3, Gd2O3, Bi2O3-SiO2 and Gd2O3-SiO2 structures. Sample designation in the Excel file is in line with sample designation in the manuscript associated with dataset.
-
Thermal, electrical, and magnetic properties of Fe2O3–PbO–SiO2 glass prepared by traditional melt-quenching and twin roller fast-cooling methods
PublikacjaIn this study, Fe–Pb–Si oxide glasses containing between 12.5 and 17.5 mol% Fe2O3 were prepared using two different methods comprising traditional melt-quenching and twin roller fast-cooling techniques. The topography and structure of the materials obtained were characterized by X-ray powder diffraction and scanning electron microscopy. All of the materials were found to be amorphous. The topography of most of the glasses comprised...
-
Eye tracking within near-to-eye display
PublikacjaIn this paper we investigate the effectiveness of the gaze interaction within near-to-eye display. The practical aspect of the paper is about combining an eye tracker with smart glasses. Presented research is related with the eGlasses project, which is focused on the development of an open platform in the form of multisensory electronic glasses and related interaction methods. One of the implemented interaction methods is the one...
-
Superconductivity and appearance of negative magnetocaloric effect in Ba1–xKxBiO3 perovskites, doped by Y, La and Pr
PublikacjaRecently, substantial attention is given to the bismuth-based perovskites for variety of electronic applications. The perovskites are used for quantum dots displays (QLED), photovoltaic systems and superconducting (HTS) devices. In this paper comprehensive studies of Ba1–xKxBi1–yREyO3 bismuth perovskites (REBKBO, RE = Y , La or Pr) are reported. Apart from structural anomalous behavior at low temperatures, the electronic properties...
-
Influence of synthesis conditions on glass formation, structure and thermal properties in the Na 2 O-CaO-P 2 O 5 system doped with Si 3 N 4 and Mg
PublikacjaOxynitride phosphate glasses and glass-ceramics were prepared using new synthesis routes for phosphate glasses. Materials were melted from pre-prepared glass samples in the system Na-Ca-P-O with addition of Mg and/or Si3N4 powders under different preparation conditions. The melting process was conducted at 1000–1500 °C either under air or nitrogen atmosphere to obtain materials with different nitrogen content. Their topography...
-
Tunable emission and energy transfer of B2O3–Bi2O3–AlF3 glass system doped with Eu3+/Dy3+
PublikacjaThe structure and luminescent properties of the B2O3–Bi2O–AlF3 glass system doped with Eu3+/Dy3+ ions in different molar ratios were studied. A series of glasses were synthesized by the conventional melt quenching technique. Glass transition and crystallization temperatures were examined by Differential Thermal Analysis (DTA) measurements. The amorphous character of the prepared samples was confirmed by the X-ray diffraction (XRD)...