Filtry
wszystkich: 887
wybranych: 178
-
Katalog
- Publikacje 573 wyników po odfiltrowaniu
- Czasopisma 6 wyników po odfiltrowaniu
- Osoby 12 wyników po odfiltrowaniu
- Wynalazki 1 wyników po odfiltrowaniu
- Projekty 1 wyników po odfiltrowaniu
- Zespoły Badawcze 1 wyników po odfiltrowaniu
- Kursy Online 58 wyników po odfiltrowaniu
- Wydarzenia 5 wyników po odfiltrowaniu
- Dane Badawcze 230 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: quartz sands
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Woman 24 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with elbows resting on the armrests of the chair - Woman 24 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with elbows resting on the table top - Man 53 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with elbows in the air - Man 30 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with elbows in the air - Woman 24 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Woman 30 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with single fingers - elbows resting on the armrests of the chair - Woman 30 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with elbows resting on the armrests of the chair - Man 30 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with elbows in the air - Woman 30 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
Scanning Electrone Microscope images of biochar produced from straw and wood chips
Dane BadawczeThis dataset contains scanning electron microscope images of two types of biochars derived from waste plant biomass: straw and wood chips. Imaging was performed using a scanning electron microscope, FEI Quanta FEG250. with a SE-ETD detector (secondary electron – Everhart-Thornley detector), using 20 kV accelerating voltage.
-
SEM micrographs of VO2 and V6O13 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V6O13 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under a reducing atmosphere (94% Ar, 6% H2) at 600 and 700C for 10h.
-
SEM micrographs of NH4VO3 crystals - molar concetration factor after annealing
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 nano_crystals obtained by the LPE-IonEx method with different morphology after annealing at 400C under argon atmosphere (with a heating rate of 10 C/min).
-
SEM micrographs of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the electron microscopy (SEM) micrographs of ammonium vanadate nanobelts obtained by the hydrothermal method with different conditions. The results show that the morphology of samples dependent on reaction conditions.
-
SEM micrographs of morphology evolution of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-800C. The...
-
SYNAT Music Genre Parameters PCA 19
Dane BadawczeThe dataset contains feature vector after Principal Component Analysis (PCA) performing, so there are 11 music genres and 19-element vector derived from music excerpts. Originally, a feature vector containing 173 elements was conceived in earlier research studies carried out by the team of authors [1-6]. A collection of 52532 music excerpts described...
-
SYNAT_PCA_48
Dane BadawczeThere is a series of datasets containing feature vectors derived from music tracks. The dataset contains 51582 music tracks (22 music genres) and feature vector after Principal Component Analysis (PCA) performing, so there are 48-element vectors derived from music excerpts. Originally, a feature vector containing 173 elements was conceived in earlier...
-
SYNAT_PCA_11
Dane BadawczeThe dataset contains 51582 music tracks (22 music genres) and feature vector after Principal Component Analysis (PCA) performing, so there are 11-element vectors derived from music excerpts. Originally, a feature vector containing 173 elements was conceived in earlier research studies carried out by the team of authors [1-6]. A collection of more than...
-
SEM micrographs of NH4VO3 crystals - molar concetration factor
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 nano_crystals obtained by the LPE-IonEx method. The SEM images clearly show that the morphology of the end product can be nicely tuned by changing the molar concentration of ammonium salt in the solvent.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C dependent on film thickness
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (2-3 AsP layers) were deposited on a silicon substrate and were annealing at 1000°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Man 29 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Second Man 29 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Woman 27 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
PULSE and ECG measurement from the hand with first elbow rests on the armrest, second elbow in the air - Woman 28 age
Dane BadawczeThe data set presents the measurements of the pulse and the ECG signal from the hand made with the use of a proprietary measuring system based on the AD8232 chip, a set of green diode and a phototransistor made on the STM32 microcontroller. Thanks to such a constructed device, it is possible to measure the ECG signal in a non-standard way - from the...
-
SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrodes sintered at 1050 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with La0.6Sr0.4Co0.2Fe0.8O3-δ oxygen electrode sintered at 1050 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using...
-
SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C before and after test
Dane BadawczeThis dataset contains cross section SEM images of Solid Oxide Fuel Cell interface with Sr0.95Ti0.30Fe0.70O3-d oxygen electrode sintered at 800 °C before and after test. The cell was tested using Open Flanges™ test Set-up at 700 °C. During the test, the cell was aged for approximately 120 hours at a load of 0.5 A/cm^2. Images were obtained using a FEI...
-
SEM micrographs of morphology evolution of V2O3 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that the morphology dependent on the annealing temperature.
-
XRD patterns of the V2O5 coatings after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 coatings on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 500C, 600C, and 700C for 10 under a reducing atmosphere (94% Ar, 6% H2).
-
SEM micrographs of the V2O5 coatings after thermal treatment under reducing atmosphere
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 coatings on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 600C and 700C for 10 under a reducing atmosphere (94% Ar, 6% H2).
-
SEM micrographs of V2O5 thin film morphology dependent on substrate types
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin film morphology dependent on substrate types. The as-prepared thin films were deposited on alumina, zirconium, zirconium oxide and metallic vanadium substrate, then was annealing under an oxidizing atmosphere at 600C for 10h. The results show that the morphology of...
-
SEM micrographs of morphology evolution of V2O5 thin films on silicon substrate
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range 250-600C. The results show that the morphology of the films dependent on the annealing temperature.
-
Scanning Electron Microscopy images of nanocubes suspension 1 month after synthesis
Dane BadawczeThis dataset contains the SEM images of the gold nanocubes suspension in citrate buffer. The goal of the study was to evaluate the size of the synthesized nanocubes, their stability one month after the synthesis process, and to verify the optimal conditions regarding nanocubes concentration for the SEM analysis. Solutions with two different AuNC concentrations...
-
SEM micrographs of NH4VO3 crystals
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 crystals obtained by the LPE-IonEx method. The SEM images clearly show that the morphology of the end product can be nicely tuned by changing the type of ammonium salt and the solvent. It can be concluded that the used solvent affected crystal shapes and their size was...
-
Tellurite based glass doped by Eu3+ ions - XPS measurements
Dane BadawczeEu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
The topography of carbon black-polylactide composite 3D printed electrodes after femtosecond laser ablation
Dane BadawczeThis dataset contains a series of scanning electron microscopy images revealing the topography of 3D printed carbon black-polylactide composite electrodes after laser ablation with a femtosecond laser. Different laser powers were investigated, namely: 10%, 25%, 50%, 75% and 100%. The CB-PLA electrodes were 3D printed using an Ender printer. Femtosecond laser NKT Photonics, Origami XP parameters: power at 100%...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Morphology and structure of V2O5 nanorods deposited on the silicon substrate after reduction
Dane BadawczeThe DataSet contains the XRD patterns and SEM micrographs of V2O5 nanorods on the silicon substrate after thermal treatment under a reducing atmosphere. Thin films were annealed at 500C for 40 under a reducing atmosphere (94% Ar, 6% H2).
-
SEM micrographs of V2O5 thin films deposited on isotropic etching silicon substrates (111)
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin films deposited on isotropic etching silicon substrates (111). The silicon wafers were etched in a mixture of nitric acid, hydrofluoric acid, and acetic acid in the ratio of 40:1:15. The soaking time for the substrates was from 30 to 90 seconds. The thin films were...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Distribution of population by tenure status, 2015 (% of population)
Dane BadawczeFactor affecting the attractiveness of property market in terms of investment, especially of housing, is the ratio of the number of dwellings owned by the population .In 2015, more than a quarter (26.9%) of the EU population lived in their own housing with credit or mortgages, while over 42% occupied their own residential units without credit or mortgages....
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Dane BadawczeThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
The set of 22 sessions of 14-channel eeg signals recorded during watching pictures
Dane BadawczeThe data were collected in order to perform research on the possibility of controlling the content displayed on the monitor screen using human emotional states extracted from EEG signals. The dataset contains recordings of 14-channel EEG signals collected from 10 persons within 22 sessions, during which 45 different random photos taken from the ImageNet...
-
UAV spectrometer reflectance and leaf area index for vegetation near Gdynia, Poland
Dane BadawczeReflectance data from the UAV flights with UV-VIS spectrometer along with leaf area index measurements for vegetaion near Gdynia, Poland.
-
The luminescence study of Sr2TiO4:Sm3+ coumpounds.
Dane BadawczeA luminescent material based on the strontium orthotitanate (Sr2TiO4) matrix doped with 1% of a mole of samarium was obtained using the typical solid-state synthesis method under a neutral atmosphere of nitrogen. The sample was investigated using powder X-ray diffraction (XRD) and several luminescence techniques to study the phase composition, luminescence...