Filtry
wszystkich: 3016
wybranych: 479
-
Katalog
- Publikacje 2283 wyników po odfiltrowaniu
- Czasopisma 45 wyników po odfiltrowaniu
- Osoby 56 wyników po odfiltrowaniu
- Wynalazki 2 wyników po odfiltrowaniu
- Projekty 5 wyników po odfiltrowaniu
- Zespoły Badawcze 1 wyników po odfiltrowaniu
- Aparatura Badawcza 1 wyników po odfiltrowaniu
- Kursy Online 102 wyników po odfiltrowaniu
- Wydarzenia 2 wyników po odfiltrowaniu
- Dane Badawcze 519 wyników po odfiltrowaniu
Filtry wybranego katalogu
Wyniki wyszukiwania dla: BERYLLIUM-TELLURIUM-IRON GLASSES
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Dane BadawczeElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
Linear and nonlinear impedance of iron containing silicate glasses
Dane BadawczeThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
The structure of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
Topography and microstructure of phosphate-iron glasses containing niobium and titanium
Dane BadawczeThe topography and microstructure of phosphate-iron glasses containing niobium and titanium were investigated by the means of X-ray diffraction (XRD), scanning electron microscopy (SEM). Glass samples of the composition of 35P2O5-30Fe2O3-(35-x)Nb2O5-xTiO2 where x= 0; 7.5 and 15 (in %mol) were prepared by the conventional melt quenching technique. Appropriate...
-
The morphology of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
The structure of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
The morphology of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
The morphology of lead-borate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional meltquenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate...
-
The structure of lead-borate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and...
-
Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Dane BadawczeLinear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO2, 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O, Li2O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered...
-
Magnetic properties of of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeMagnetic properties of iron-doped glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15 and 20 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Dane BadawczeElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Electrical properties of nanostructures in lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeElectrical properties of iron oxide nanostructures observed in silicate glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15, 20 and 25 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where...
-
Topography of iron-phosphate glasses doped with niobium and titanium tested by confocal microscope
Dane BadawczeThe topography of phosphate-iron glasses containing niobium and titanium were investigated with the use of confocal miscroscope. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5, 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 and 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents...
-
XPS measurements of the Fe-Bi based glass
Dane BadawczeFe-Si-O and Fe-Si-Pb-O glass was measured by XPS method. The influence of Pb dopand on the glass structure, including the valence of iron, was investigated. The influence of the annealing temperature on the behavior of iron in glass was also investigated. Studies have confirmed the mixed valence of iron in glasses and a high proportion of metallic Fe.
-
Tellurite based glass doped by Eu3+ ions - XPS measurements
Dane BadawczeEu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after...
-
Optical properties of tellurium dioxide thin films
Dane BadawczeTeO2 and TeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by optical spectroscopy. Metallic Te target and Te-Eu mosaic target with diameter of 50.8 mm were sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate...
-
Structural analysis of the tellurium dioxide thin films
Dane BadawczeTeO2 thin films were deposited by magnetron sputtering method. After deposition, amorphous samples were annealed at various temperatures. Influence of annealing temperature on a presence of crystalline phase was investigated.
-
XRD analysis of the tellurium dioxide thin films
Dane BadawczeTellurium dioxide thin films were deposited by magnetron sputtering method. The XRD analysis of the films annealed at 200, 500, 650 and 700 celsius degree showed appearing of crystalline phase in a higher temeratures.
-
Detection of the Ag nanoparticles in Te-Bi-Ba-Oa glass
Dane BadawczeThe influence of the manufacturing parameters of tellurium-bismuth-barium glasses on the presence of silver nanoparticles was investigated. Glasses were annealed at 330, 335, 340, 345 and 350 degrees Celsius for 24 and 48 hours. Presence of the Ag nanoparticles was measured by XPS method. The growth of nanoparticles was observed along with the extension...
-
Structure and optical measurements of Eu doped tellurium oxide thin films
Dane BadawczeThin films were deposited by magnetron sputtering method and simultaneously heated at 200 oC. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the films was examined by X-ray diffraction method. ...
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Dane BadawczeThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
XPS measurements of the iron elements covered by chromium
Dane BadawczeAnticorrosive coatings are an important issue in modern materials engineering. One of the most commonly used, for that coating materials, is chrome. Three metal elements were measured, named as Turcja, WB Tech and Nomet. Names were given according to producer of elements. XPS measurements of the Cr 2p region give an ansver concering on surface chemical...
-
The topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by SEM.
-
Chemical properties of bismuth telluride – carbon composites.
Dane BadawczeCarbon nanotubes and amorphous carbon have been introduced into bismuth telluride matrix (in 0.15 and 0.30 wt % ratio) in order to investigate influence of carbon on composite’s thermoelectric properties. Composites with well-dispersed additives have been obtained by sonication and ball-milling. Chemical composition of materials was confirmed by XPS...
-
The topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with SEM method
Dane BadawczeThe topography of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by SEM.
-
Thermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. was measured by DSC.
-
GDP growth in Iran
Dane BadawczeThe economy of the Islamic Republic of Iran is one of the fastest growing in the Middle East. Iran should not only be associated with crude oil industry but also other areas of the economy. The sanctions that hindered oil exports from Iran meant that the authorities had to take measures to increase exports of other products. There was an increase in...
-
The structure of strontium–borate glasses and glass-ceramics containing nanocrystallites of Bi2VO5.5. measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing Bi2VO5.5 nanocrystallites was measured by XRD.
-
Thermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with DSC method
Dane BadawczeThermal properties of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by DSC.
-
Microstructure of barium-vanadate glasses
Dane BadawczeThe structure of barium-vanadate glasses was measured by SEM and XRD techniques. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar....
-
Topography of barium-vanadate glasses
Dane BadawczeThe topography of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was performed...
-
The structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides measured with X-ray diffraction method
Dane BadawczeThe structure of strontium–borate glasses and glass-ceramics containing bismuth and vanadium oxides was measured by XRD.
-
The AFM topographic measurements of the surface heterogeneity of iron hexacyanoferrate on a steel surface
Dane BadawczeMeasurements in semi-contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
The morphology of vanadate glasses containing BaTiO3
Dane BadawczeThe morphology of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573 K) brass...
-
Dielectric properties of barium-vanadate glasses
Dane BadawczeThe linear impedance of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was...
-
The structure of vanadate glasses containing BaTiO3.
Dane BadawczeThe structure of vanadate glasses doped with BaTiO3 was measured by SEM technique. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
Inflation rate (In percentage) in Iran
Dane BadawczeCurrently, a major concern of the Iranian economy is high inflation. Increasing prices of basic goods, and their increase in wages do not follow. At the same time the unemployment rate has raised. The following data set present the inflation rate between 2010-2020 (forecast).
-
Nonlinear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe nonlinear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear impedance of vanadate glasses containing BaTiO3
Dane BadawczeThe linear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Compressive strength and density of cement pastes containing iron oxide (Fe3O4) nanoparticles (nanomagnetite)
Dane Badawcze*.ODS - open-data source spreadsheet - Dataset presenting:
-
Images of topography and mechanical properties (phase imaging) of cast iron samples from water installations
Dane BadawczeMeasurements in contact and semi-contact mode. NTEGRA Prima (NT-MDT) device. CSG 10.
-
Top 10 Iran Import Goods in 2011
Dane BadawczeThe following dataset shows the volume of trade of the European Union countries with Iran. One can observe a significant drop in both imports and exports (the year 2012 meant tightening of sanctions, which clearly limited the import of Iranian products to the EU). After lifting the sanctions it is expected to substantially increase the level of trade...
-
Top 10 Iran Export Goods in 2011
Dane BadawczeIn the structure of Iranian exports the dominant position are different types of fuel (including chemical industry products). The structure of imports is much more fragmented. Positions worth of consideration are machinery and equipment, steel, vehicles parts, cereals and food.
-
Top 10 Iran Export Partners in 2011
Dane BadawczeLifting of Iranian sanctions could lead to a rapid improvement in the economic situation of Iran. This will not only remove the barriers of international transactions, but also enable the investments of foreign entities on the territory of Iran, increasing the competitiveness of operators, including in the key mining sector.
-
Top 10 Iran Import Partners in 2011
Dane BadawczeThe leader in the supply of goods and services to Iran are the United Arab Emirates. As many as 32% of the total value of imports to Iran comes from this country. This was followed by China, South Korea and Germany. These four largest countries supplied goods to Iran of nearly 72% of the total value of imports.
-
Influence of controlled crystallization and SrF2 content on the structure and properties of Eu3+ doped phosphate glasses
Dane BadawczeThe attached data contains the results of measurements of phosphate glasses and glass-ceramics doped with Eu. On their basis, the new material was characterized and the influence of the SrF2 addition on the glass structure was determined. In addition, the influence of the SrF2 content and controlled crystallization on the luminescent properties of Eu3+...
-
The morphology of vanadate glasses containing BaTiO3 measured with the use of AFM
Dane BadawczeThe morphology of vanadate glasses doped with BaTiO3 was measured with the use of AFM method. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured...
-
Linear impedance of 35P2O5-30Fe2O3-20Nb2O5-15TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and...