Wyniki wyszukiwania dla: ceramika tlenkowa

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...

• WPŁYW METODY SYNTEZY NA WŁAŚCIWOŚCI STRUKTURALNE I KATALITYCZNE ZWIĄZKU Ce0.9Pr0.1O2-δ PODCZAS WYSOKOTEMPERATUROWEJ PRACY W BIOGAZIE

  Publikacja

  • Z. Pilecka
  • B. Wnęk
  • M. Chlipała
  • B. Bochentyn

  - Rok 2019

  Tlenkowe ogniwa paliwowe zasilane biogazem degradują się pod wpływem węgla osadzającego się na anodzie. Aby wyeliminować ten efekt, szuka się warstw katalitycznych, które nałożone na anodę powstrzymują osadzanie się węgla i zmniejszają straty wydajności ogniwa. Związkiem użytym w tym celu jest Ce0,9Pr0,1O2-δ wytworzony dwiema metodami: Pechiniego i metodą strącania z odwróconej emulsji. Aby zbadać wpływ metody syntezy na właściwości...

• WŁAŚCIWOŚCI ELEKTRYCZNE SZKIEŁ TLENKOWYCH ZAWIERAJĄCYCH Fe2O3

  Publikacja

  • N. A. Wójcik

  - Rok 2012

  Zbadano właściwości elektryczne szkieł krzemianowo – ołowiowo - żelazowych. Szkła tlenkowe zawierające jony żelaza mogą potencjalnie wykazywać przewodnictwo polaronowe. Celem niniejszej pracy było bliższe określenie zachodzącego w nich mechanizmu przewodnictwa. Wytworzono szkła o składzie dobranym na podstawie ich zakresu szklenia: (50 – 0.5x)[SiO2, PbO] - xFe2O3 gdzie x wynosił odpowiednio 2, 5, 10, 15, 20 i 25 (w % mol). Otrzymane...

• Nanokrystaliczne warstwy ceramiczne otrzymywane metodą pirolizy aerozolowej w tlenkowych ogniwach paliwowych

  Publikacja

  • B. Kamecki

  - Rok 2023

  Niniejsza rozprawa doktorska dotyczy badań materiałów wytwarzanych w postaci cienkich, nanokrystalicznych warstw ceramicznych metodą pirolizy aerozolowej dla zastosowań w tlenkowych ogniwach paliwowych (SOFC). Badane są trzy możliwe obszary zastosowań wytwarzanych warstw tj. osadzanie powłok ochronnych na stalowych interkonektorach dostarczających gazy do elektrody tlenowej, wytwarzanie bariery ochronnej zapobiegającej dyfuzji...

  Pełny tekst do pobrania w portalu

• Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method

  Dane Badawcze

  open access

  • N. Wójcik
  • J. Ryl
  • R. Barczyński

  The nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method. 

• Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region

  Dane Badawcze

  open access

  • N. Wójcik
  • J. Ryl
  • R. Barczyński

  The nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method. 

• Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region

  Dane Badawcze

  open access

  • N. Wójcik
  • J. Ryl
  • R. Barczyński

  The nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method. 

• Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region

  Dane Badawcze

  open access

  • N. Wójcik
  • J. Ryl
  • R. Barczyński

  The nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method. 

• Increasing the conductivity of V2O5-TeO2 glass by crystallization: structure and charge transfer studies

  Publikacja

  • P. Okoczuk
  • N. A. Wójcik
  • L. Murawski
  • L. Wicikowski
  • M. S. Łapiński
  • P. Winiarz
  • B. Kościelska

  - JOURNAL OF MATERIALS SCIENCE - Rok 2023

  In the present paper, V 2 O 5 -TeO 2 glass was prepared by the melt-quenching technique. Crystallization of glass with a vanadium content higher than 35%mol results in an increase in electrical conductivity by a few orders of magnitude and a decrease in activation energy from ~0.40 to ~0.12 eV. In this work, a critical review of existing charge transfer models was presented on the example of V 2 O 5 -TeO 2 glass and glass–ceramics....

  Pełny tekst do pobrania w portalu

• Wpływ posuwu nagniatania na chropowatość powierzchni przedmiotów ze stali w stanie utwardzonym

  Publikacja

  • P. Waszczur
  • S. Dzionk
  • B. Ścibiorski
  • W. Przybylski

  - Mechanik - Rok 2016

  Przedstawiono wyniki badań eksperymentalnych procesu nagniatania stali twardej (62 HRC) narzędziem ceramicznym (kulką) z dociskiem hydrostatycznym. Analizowano wpływ posuwu nagniatania oraz parametrów poprzedzającej obróbki toczeniem na twardo na stan powierzchni opisanej wybranymi parametrami chropowatości.

  Pełny tekst do pobrania w portalu

• Barium boron aluminum silicate glass system for solid state optical gas sensors

  Publikacja

  • M. Silva
  • J. Karczewski
  • P. Jasiński
  • A. Chrzan
  • P. Kalinowski
  • D. Grudzień
  • G. Jasiński

  - Rok 2016

  Recent increasing demand for new eco-friendly materials and for low cost fabrication process for use in optical sensors field, raise concern about alternative materials for this application. We have designed two glass-ceramics compositions from the quaternary ROAl2O3- SiO2-B2O3(R=Ba) alkali-earth aluminum silicate system, labeled B72 and B69, with high refractive index (>1.6), large values of Abbe number (94.0 and 53.0, respectively),...

  Pełny tekst do pobrania w serwisie zewnętrznym

• Selected perowskite type LSFO thin films for the infrared detectors

  Publikacja

  • A. Łoziński
  • P. Wierzba

  - Rok 2007

  Przedstawiono technologię wytwarzania cienkich warstw ceramicznych tlenków lantanowo-strontowo-żelazowych (LSFO). Zaprezentowano konstrukcję bolometrycznych detektorów podczerwieni wykonanych z opracowanych warstw. Przedstawiono charakterystyki prądowo-napięciowe wybranych detektorów, wyniki pomiaru ich szumów i termicznej stałej czasowej. Przedstawione detektory były w stanie wykryć obiekt o temperaturze 38 stopni Celcjusza znajdujący...

• Multivariate Statistical Approach for Nephrines in Womenwith Obesity

  Publikacja

  • R. Robeva
  • M. Nedyalkova
  • G. Kirilov
  • A. Elenkova
  • S. Zacharieva
  • B. Kudłak
  • N. Jatkowska
  • V. Simeonov

  - MOLECULES - Rok 2021

  Catecholamines are physiological regulators of carbohydrate and lipid metabolism during stress, but their chronic influence on metabolic changes in obese patients is still not clarified. The present study aimed to establish the associations between the catecholamine metabolites and metabolic syndrome (MS) components in obese women as well as to reveal the possible hidden subgroups of patients through hierarchical cluster analysis...

  Pełny tekst do pobrania w portalu

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30,...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15,...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15,...

• VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  VIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15,...

• Study of Phase and Chemical Composition of Bi1-xNdxFeO3 Powders Derived by Pressureless Sintering

  Publikacja

  • J. Dzik
  • A. Lisińska-Czekaj
  • A. Zarycka
  • D. Czekaj

  - ARCHIVES OF METALLURGY AND MATERIALS - Rok 2013

  In the present paper studies on Bi1xNdxFeO3 for x =0.1-0.4 are reported. The mixed oxide method followed with pressureless sintering was employed for ceramics fabrication. Thermal behavior of stoichiometric mixtures of simple oxide powders, viz. Bi2O3, Nd2O3 and Fe2O3 was studied by simultaneous thermal analysis. It was found that with an increase in neodymium content the weight loss increased from 0.75% to 3.16% for x =0.1 and...

  Pełny tekst do pobrania w portalu

• Bioactive core material for porous load-bearing implants

  Publikacja

  • S. Sobieszczyk
  • M. Melaniuk
  • A. Zieliński

  - Advances in Materials Science - Rok 2012

  So far state of knowledge on biodegradable materials is reviewed. Among a variety of investigated materials, those composed of polymers and ceramics may be considered as only candidates for a core material in porous titanium alloy. The collagen and chitosan among natural polymers, polyhydroxy acids among synthetic polymers, and hydroxyapatite and tricalcium phosphate among ceramics are proposed for further research. Three essential...

  Pełny tekst do pobrania w portalu

• Setups for measurement of thermal time constant of bolometers and resistive layers

  Publikacja

  • P. Wierzba

  - Proceedings of SPIE - Rok 2006

  Przedstawiono dwa układy do pomiaru termicznej stałej czasowejbolometrów i warstw rezystywnych, umożliwiające pomiar wartości tego parametru w zakresie od pojedynczych milisekund do kilku sekund. Przedstawiono wyniki pomiarów termicznej stałej czasowej wybranych warstw rezystywnych wykonanych w technologii LTCC z niestechiometrycznych tlenków lantanowo-strontowo-żelazowych oraz bolometru cienkowarstwowego wykonanego w tej samej...

  Pełny tekst do pobrania w serwisie zewnętrznym

• Wykorzystanie fourierowskiej spektroskopii w podczerwieni do badania stężenia gazów wylotowych z tlenkowego ogniwa paliwowego zasilanego biogazem

  Publikacja

  • O. Białk
  • M. Chlipała
  • B. Bochentyn

  - Rok 2018

  W dzisiejszych czasach bardzo ważne jest pozyskiwanie energii ze źródeł odnawialnych i bezpiecznych dla środowiska. Jedną z obiecujących technologii są tlenkowe ogniwa paliwowe (ang. Solid Oxide Fuel Cell, SOFC). Stanowią one bezpieczną i ekologiczną alternatywę dla energii uzyskanej z paliw kopalnych. SOFC charakteryzuje się sprawnością energetyczną na poziomie 45-60 %, podczas gdy sprawność klasycznych elektrowni cieplnych nie...

  Pełny tekst do pobrania w portalu

• Materiały stosowane do wytwarzania implantów kości

  Publikacja

  • H. Janik
  • M. Mallach

  - Przemysł Chemiczny - Rok 2015

  Materiały stosowane do wytwarzania implantów kostnych muszą być biokompatybilne, nietoksyczne, bioaktywne oraz wykazywać odpowiednie właściwości mechaniczne, takie jak wytrzymałość na ściskanie, na zginanie oraz sztywność i twardość. Gama stosowanych materiałów jest bardzo szeroka, obejmuje metale, polimery, ceramikę oraz ich kompozyty. Każdy z tych materiałów ma swoje mocne i słabe strony. Praca stanowi przegląd materiałów stosowanych...

  Pełny tekst do pobrania w serwisie zewnętrznym

• Al203 sealing elements lapping

  Publikacja

  • J. Molenda
  • A. Barylski

  - Journal of KONES - Rok 2012

  Przedstawiono wyniki badań własnych wydajnosci docierania ceramiki Al203. Badano elementy uszczelniające na docierarce jednotarczowej o standardowym układzie kinematycznym. Określono wpływ wielkości mikroziaren węglika boru o numerze F400/17, F800/6.5 i F1200/3 oraz wartości nominalnego nacisku jednostkowego na ubytek materiału w czasie 15 i 20 min. Scharakteryzowano mechanizm usuwania naddatku przy docieraniu elementów ceramicznych....

  Pełny tekst do pobrania w portalu

• Mixed ionic-electronic conductivity and structural properties of strontium-borate glass containing nanocrystallites of Bi2 VO5.5

  Publikacja

  • N. A. Wójcik
  • M. Prześniak-Welenc
  • P. Kupracz
  • J. Karczewski
  • M. Gazda
  • R. J. Barczyński

  - PHYSICA STATUS SOLIDI B-BASIC SOLID STATE PHYSICS - Rok 2017

  Samples of strontium borate glass containing bismuth vanadate nanocrystallites were prepared. Nanocomposites containing up to 45mol% of the Bi2VO5.5 phase exhibit electrical properties closer to the strontium-borate glass than to the ferroelectric Bi2VO5.5 ceramic. The glass matrix still may contain some part of bismuth and vanadium ions even after crystallization process and there is too little of crystalline phase to observe...

  Pełny tekst do pobrania w portalu

• BET adsorption-desorption isotherm of nano-MgO

  Dane Badawcze

  open access

  • P. Błaszczak
  • B. Bochentyn

  The dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric MgO (CA-assisted method of synthesis)

• BET adsorption-desorption isotherm of nano-ZrO2

  Dane Badawcze

  open access

  • P. Błaszczak
  • B. Bochentyn

  The dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric ZrO2 (CA-assisted method of synthesis)

• BET adsorption-desorption isotherm of nano-SrTiO3

  Dane Badawcze

  open access

  • P. Błaszczak
  • B. Bochentyn

  The dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric SrTiO3 (CA-assisted method of synthesis)

• Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - full run

  Dane Badawcze

  open access

  • J. Łubiński
  • K. Druet

  - seria: Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%).

  Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #24 - #25.

  Dane Badawcze

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - seria: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #24 (upper, rotating), #25 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.

  Dane Badawcze

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - seria: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #30 - #31.

  Dane Badawcze

  open access

  • J. Łubiński
  • T. Łubiński dr inż.
  • K. Druet

  - seria: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #30 (upper, rotating), #31 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #20 - #21.

  Dane Badawcze

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - seria: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #20 (upper, rotating), #21 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #22 - #23.

  Dane Badawcze

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - seria: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #22 (upper, rotating), #23 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.

  Dane Badawcze

  open access

  • J. Łubiński
  • T. Łubiński dr inż.
  • K. Druet

  - seria: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #26 - #27.

  Dane Badawcze

  open access

  • J. Łubiński
  • T. Łubiński
  • K. Druet

  - seria: Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics. Paraffin oil lubrication.

  Specimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #26 (upper, rotating), #27 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...

• Tellurite based glass doped by Eu3+ ions - XPS measurements

  Dane Badawcze

  open access

  • M. Łapiński

  Eu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after...

• BET adsorption-desorption isotherm of CeO2 pure

  Dane Badawcze

  open access

  • P. Błaszczak
  • B. Bochentyn

  The dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric pure CeO2 (CA-assisted method of synthesis)

• PolyCat-SOFC Ogniwa tlenkowe zasilane plastikami nie podlegającymi recyklingowi

  Projekty

  Kierownik projektu: prof. dr hab. inż. Piotr Jasiński   Program finansujący: Polsko-Tajwański Program Badawczy

  Projekt realizowany w Katedra Inżynierii Materiałów Funkcjonalnych WETI zgodnie z porozumieniem POLTAJ10/2022/50/PolyCatSOFC/2023 z dnia 2023-09-05

• KKK_P02_Pol Nowe kwantowe i quasi-niskowymiarowe materiały tlenkowe

  Projekty

  Kierownik projektu: dr inż. Kamil Kolincio   Program finansujący: Programy NAWA

  Projekt realizowany w Katedra Fizyki Ciała Stałego zgodnie z porozumieniem BPN/BFR/2021/1/00042/U/00001

• Modelowanie spalania w pojedynczym płomieniu przy wysokotemperaturowym podgrzewie utleniacza

  Publikacja

  • M. Jewartowski

  - Rok 2009

  Rozprawa dotyczy badań eksperymentalnych procesów spalania paliw gazowych, ze szczególnym uwzględnieniem paliwa niskokalorycznego pochodzącego z gazyfikacji biomasy, w utleniaczu o wysokiej temperaturze i stosunkowo niskiej zawartości tlenu. Zaprojektowano i zbudowano stanowisko badawcze, umożliwiające uzyskanie środowiska utleniającego o kontrolowanej temperaturze i zawartości tlenu na bazie spalin wytwarzanych podczas konwencjonalnego...

• Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 813 K measured with impedance spectroscopy method at high temperature region

  Dane Badawcze

  open access

  • N. Wójcik
  • J. Ryl
  • R. Barczyński

  Nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 813 K was measured by impedance spectroscopy method. 

• Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region

  Dane Badawcze

  open access

  • N. Wójcik
  • J. Ryl
  • R. Barczyński

  The linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K was measured by impedance spectroscopy method. 

• Nonlinear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat-treated at 613 K measured with impedance spectroscopy method at high temperature region

  Dane Badawcze

  open access

  • N. Wójcik
  • J. Ryl
  • R. Barczyński

  Nonlinear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass-ceramic heat treated at 613 K was measured by impedance spectroscopy method.