Linear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Nonlinear impedance of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured with impedance spectroscopy method at low temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 glass-ceramic heat-treated at 913 K was measured by impedance spectroscopy method.
-
Direct conversion of secondary phosphine oxides and H-phosphinates with [di(acyloxy)iodo]benzenes to phosphinic and phosphonic amides
PublicationW publikacji przedstawiono metodę pozwalająca na bezpośrednie otrzymywanie amidów kwasu fosfinowego i fosfonowego w reakcji drugorzędowych tlenków fosfin lub H-fosfinianów z [di(acyloksy)iodo]benzenami w obecności amin pierwszo lub drugorzędowych. Wykorzytując silne acylujące właściwości układu [di(acyloksy)iodo]benzen/R2P(O)H.
-
Impedance spectroscopy as a diagnostic tool of degradation of Solid Oxide Fuel Cells = Spektroskopia impedancyjna jako narzędzie diagnostyczne degradacji tlenkowych ogniw paliwowych
PublicationTlenkowe ogniwa paliwowe SOFC sa obecnie bliskie komercjalizacji. Wiedza na temat mechanizmów degradacji ogniw paliwowych jest niezbędna do dalszej poprawy ich działania. Spektroskopia impedancyjna jest skutecznym narzędziem diagnostycznym. Pozwala ona na wskazanie który element ogniwa SOFC ulega pogorszeniu oraz pozwala poznać dokładniej naturę procesu degradacji. W tej pracy degradacja ogniwa SOFC została zbadana przy użyciu...
-
Ultraviolet to near-infrared down-conversion in Bi3+–Yb3+ co-doped YAM phosphor
Publication -
Direct synthesis of fine boron carbide powders using expanded graphite
Publication -
Thermal stability of expanded perlite modified by mullite
Publication -
Correlations of structural, thermal and electrical properties of sodium doped complex borophosphosilicate glass
Publication -
Influence of Ni ion site occupancy on laser induced third harmonic generation (THG) studies in Li2SO4–MgO–P2O5 amorphous system
Publication -
Methodical engineering of defects in MnXZn1-X O(x = 0.03, and 0.05) nanostructures by electron beam for nonlinear optical applications: A new insight
Publication -
Ultrafast high-temperature sintering (UHS) of cerium oxide-based compound
PublicationUltrafast high-temperature sintering (UHS) is an innovative sintering technique that can densify ceramics in a few seconds, dramatically reducing the carbon footprint and firing costs. In this work, the feasibility of applying UHS in Gd-doped ceria (GDC) and GDC-Er-stabilized bismuth oxide (ESB) composite powders was investigated. At high UHS currents (22-24 A), a fully dense GDC sample with a large grain size was obtained. Nonetheless,...
-
Correlations of structural, thermal and electrical properties of sodium doped complex borophosphosilicate glass
PublicationBorophosphosilicate glasses with varying sodium ion concentrations were investigated for their, structural, thermal, and electrical properties. All the obtained glasses were transparent except the glass with the highest sodium content, which exhibited translucency due to inhomogeneities. Increasing sodium content led to reduced boron and silicon content while maintaining a constant B/Si ratio, indicating progressive depolymerization...
-
Processing and thermal characterization of polymer derived SiCN(O) and SiOC reticulated foams
Publication -
Cold sintering of colloidal silica particles using different alkali solutions
Publication -
Characterization of magnesium doped lanthanum orthoniobate synthesized by molten salt route
PublicationMolten salt synthesis method has been used to prepare the single phase magnesium doped lanthanum orthoniobate. The phase composition has been checked by X-ray diffraction method and the microstructure studies have been performed by scanning electron microscopy. The high temperature properties of the material have been investigated by thermogravimetry and electrochemical impedance spectroscopy. A dependence between sample total...
-
Fe3O4/graphene oxide/Fe4[Fe(CN)6]3 nanocomposite for high performance electromagnetic interference shielding
Publication -
Dielectric and electrical properties of synthesized PBGO/Fe3O4 nanocomposite
Publication -
High temperature monoclinic-to-tetragonal phase transition in magnesium doped lanthanum ortho-niobate
PublicationMagnesium doped lanthanum ortho-niobate (La0.98Mg0.02NbO4) was prepared by the molten salt synthesis method. X-ray diffraction and dilatometry methods were used to study high temperature behavior of the ceramic material. Special attention was paid to the phase transition between the monoclinic and tetragonal phases. The values of spontaneous strain on the basis of unit cell parameter, obtained by Rietveld refinement, have been...
-
Influence of Antimony Substitution on Spontaneous Strain and Thermodynamic Stability of Lanthanum Orthoniobate
PublicationThe analysis of the antimony substitution influence on temperature dependence of unit cell distortion has been done. The values of spontaneous strain and Landau order parameter for three different antimony contents varied had been calculated. The phase transition occurring for antimony substituted lanthanum orthoniobate was found to be second order. The high temperature solution calorimetry method has been used to investigate...
-
Electrophoretic deposition (EPD) of nanohydroxyapatite - nanosilver coatings on Ti13Zr13Nb alloy
PublicationTitanium and its alloys are the biomaterials most frequently used in medical engineering, especially as parts of orthopedic and dental implants. The surfaces of titanium and its alloys are usually modified to improve their biocompatibility and bioactivity, for example, in connection with the deposition of hydroxyapatite coatings. The objective of the present research was to elaborate the technology of electrophoretic deposition...
-
Praseodymium substituted lanthanum orthoniobate: Electrical and structural properties
PublicationThe results of ionic transport and structural measurements for the lanthanum orthoniobate doped by praseodymium are presented and discussed. The influence of calcium co-doping on these properties has also been analyzed. The results suggest the predominant protonic conductivity for the investigated system in the whole range of investigated temperatures. The influence of calcium co-doping on phase purity is analyzed.
-
Effects of solution composition and electrophoretic deposition voltage on various properties of nanohydroxyapatite coatings on the Ti13Zr13Nb alloy
PublicationThe purpose of the research was to establish the influence of the solution composition and the electrophoretic deposition voltage on the coating homogeneity and thickness, nanohardness, adhesion, corrosion resistance and wettability. The Ti13Zr13Nb alloy was coated by the electrophoretic technique with hydroxyapatite in a solution containing 0.1, 0.2 or 0.5 g nanoHAp in 100 mL of suspension and at voltage 15, 30 or 50 V. The scanning...
-
Heat capacities and thermodynamic properties of antimony substituted lanthanum orthoniobates
PublicationThe results of heat capacity measurements for the lanthanum orthoniobate substituted with 10, 20 and 30 mol% of antimony (LaNb0.9Sb0.1O4, LaNb0.8Sb0.2O4 and LaNb0.7Sb0.3O4) are presented and discussed. Temperature dependence of low temperature heat capacity was analyzed within the Debye and Einstein models. The Debye temperature decreased, whereas the Einstein temperature increased with antimony content. The decrease of the Debye...
-
Protective properties of Al2O3 + TiO2 coating produced by the electrostatic spray deposition method
PublicationMechanical resistance of Al2O3 + TiO2 nanocomposite ceramic coating deposited by electrostatic spray deposition method onto X10CrAlSi18 steel to thermal and slurry tests was investigated. The coating was produced from colloidal suspension of TiO2 nanoparticles dispersed in 3 wt% solution of Al2(NO3)3, as Al2O3 precursor, in ethanol. TiO2 nanoparticles of two sizes, 15 nm and 32 nm, were used in the experiments. After deposition,...
-
Effect of plasma sprayed and laser re-melted Al2O3 coatings on hardness and wear properties of stainless steel
PublicationCommercially available austenic stainless steel substrate was coated with commercially available, raw Al2O3 powder applied by means of plasma spraying method and then re-melted with CO2 laser beam of various parameters. Tribological and mechanical properties of the 120 J/mm and 160 J/mm laser re-melted coatings were compared with the tribological and mechanical properties of the “as-sprayed” coating. The influence of the laser...
-
In-situ Cu-doped MnCo-spinel coatings for solid oxide cell interconnects processed by electrophoretic deposition
PublicationThe Cu doping of the Mn–Co spinel is obtained “in-situ” by electrophoretic co-deposition of CuO and Mn1.5Co1.5O4 powders and subsequent two-step reactive sintering. Cu-doped Mn1.5Co1.5O4 coatings on Crofer22APU processed by electrophoretic co-deposition method are tested in terms of long term oxidation resistance and area specific resistance tests up to 3600 h. The introduction of Cu in the spinel lead to higher level of densification...
-
Effects of La0.8Sr0.2MnO3 and Ag electrodes on bismuth-oxide-based low-temperature solid electrolyte oxygen generators
PublicationIn this study, La0.8Sr0.2MnO3 (LSM) was used as the ceramic electrode in a (Bi1.50Y0.50)0.98Zr0.04O3+δ (BYO)-based solid electrolyte oxygen generator (SEOG) and its performance was compared with that of a previously studied high-fire Ag electrode. Among La0.6Sr0.4Co0.2Fe0.8O3, LaNi0.6Fe0.4O3, Cu1.4Mn1.6O4, and LSM materials, only LSM materials did not trigger any chemical reaction or interdiffusion with BYO at temperatures up to...
-
Influence of hydrogen on a nanocrystalline high-entropy oxide with application potential in hydrogen technologies
PublicationThe influence of hydrogen on a (Co0⋅2Cu0⋅2Mg0⋅2Ni0⋅2Zn0.2)O HEO with a rock salt structure was studied. Two forms of this HEO (nanopowder and sinter) were prepared via mechanochemical synthesis (MS) and additional heat treatment, respectively. The chemical stability of the synthesized samples in a pure hydrogen atmosphere was investigated using Sievert’s technique. High-pressure hydrogenation at 250 ◦C had no noticeable effect...
-
Effects of electrophoretic deposition times and nanotubular oxide surfaces on properties of the nanohydroxyapatite/nanocopper coating on the Ti13Zr13Nb alloy
PublicationLoad-bearing implants are developed with a particular emphasis placed on an application of ceramic hydroxyapatite coatings in order, to enhance the bioactivity of titanium implants and to shorten the healing time. Therefore, thin, fully crystalline coatings that are, highly adhesive, hydrophilic and demonstrating antibacterial properties are ly looked for. The aim of this research was to develop and characterize the properties...
-
New trifunctional acrylic water-based paint with self-cleaning, biocidal and magnetic properties
PublicationIn the present study, we report the synthesis and application of ZnFe2O4/SiO2-TiO2 nanocomposites with nonstoichiometric content of Fe to Zn used for the first time for the preparation of new generation trifunctional paints with self-cleaning, biocidal and magnetic properties. Currently, there are no compositions on the market for obtaining protective coatings in the form of paint, which simultaneously exhibit biocidal, magnetic...
-
Silicon oxycarbide-tin nanocomposite derived from a UV crosslinked single source preceramic precursor as high-performance anode materials for Li-ion batteries
PublicationIn this work, we report an innovative and facile UV light-assisted synthesis of a nanocomposite based on silicon oxycarbide (SiOC) and tin nanoparticles. SiOC ceramic matrix, containing a conductive free carbon phase, participates in lithium-ion storage, and buffers the volume changes of Li-alloying/de-alloying material. The reported synthesis procedure through a polymer-derived ceramic route involves the preparation of a single-source...
-
Mobility measurements in oxide semiconductors
PublicationPraca zawiera wyniki badań właściwości elektrycznych, optycznych i strukturalnych cienkich warstw ito i sno2. badania wykazały, że cienkie warstwy tlenków metali wykazują rezystywność charakterystyczną dla półprzewodników. poziom transmisji światła w zakresie widzialnym pozwala zaliczyć badane warstwy do materiałów przezroczystych. badane cienkie warstwy wykonano metodą rozpylania magnetronowego.
-
VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K05
Open Research DataVIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K08
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K07
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K03
Open Research DataVIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...
-
VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K04
Open Research DataVIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...
-
VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). No lubrication (DRY). Specim. set K01
Open Research DataVIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DRY. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180...
-
WŁAŚCIWOŚCI ELEKTRYCZNE SZKIEŁ TLENKOWYCH ZAWIERAJĄCYCH Fe2O3
PublicationZbadano właściwości elektryczne szkieł krzemianowo – ołowiowo - żelazowych. Szkła tlenkowe zawierające jony żelaza mogą potencjalnie wykazywać przewodnictwo polaronowe. Celem niniejszej pracy było bliższe określenie zachodzącego w nich mechanizmu przewodnictwa. Wytworzono szkła o składzie dobranym na podstawie ich zakresu szklenia: (50 – 0.5x)[SiO2, PbO] - xFe2O3 gdzie x wynosił odpowiednio 2, 5, 10, 15, 20 i 25 (w % mol). Otrzymane...
-
WPŁYW METODY SYNTEZY NA WŁAŚCIWOŚCI STRUKTURALNE I KATALITYCZNE ZWIĄZKU Ce0.9Pr0.1O2-δ PODCZAS WYSOKOTEMPERATUROWEJ PRACY W BIOGAZIE
PublicationTlenkowe ogniwa paliwowe zasilane biogazem degradują się pod wpływem węgla osadzającego się na anodzie. Aby wyeliminować ten efekt, szuka się warstw katalitycznych, które nałożone na anodę powstrzymują osadzanie się węgla i zmniejszają straty wydajności ogniwa. Związkiem użytym w tym celu jest Ce0,9Pr0,1O2-δ wytworzony dwiema metodami: Pechiniego i metodą strącania z odwróconej emulsji. Aby zbadać wpływ metody syntezy na właściwości...
-
Increasing the conductivity of V2O5-TeO2 glass by crystallization: structure and charge transfer studies
PublicationIn the present paper, V 2 O 5 -TeO 2 glass was prepared by the melt-quenching technique. Crystallization of glass with a vanadium content higher than 35%mol results in an increase in electrical conductivity by a few orders of magnitude and a decrease in activation energy from ~0.40 to ~0.12 eV. In this work, a critical review of existing charge transfer models was presented on the example of V 2 O 5 -TeO 2 glass and glass–ceramics....
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.