prof. dr hab. inż. Bogusław Kusz
Zatrudnienie
Publikacje
Filtry
wszystkich: 90
Katalog Publikacji
-
YSZ Thin film deposited on porous substrate by spray pyrolysis
PublikacjaIn this work the results of deposition of YSZ layer on a porous substrate using an ultrasonic Spray Pyrolysis are presented.
-
Microstructural and electrical properties of Y0.07Sr0.93-xTiO3 perovskite ceramics
PublikacjaIn order to find a relationship between electrical and microstructural properties, yttrium-doped strontium titanate (7 mol%) with various values of strontium nonstoichiometry was investigated and shown in this work. It has been observed that yttrium doping can affect the electrical properties of SrTiO3 to a great extent. Moreover, the microstructural and electrical properties can be influenced by strontium nonstoichiometry. The...
-
Structural and electrical properties of Sr(Ti,Fe)O3-δ materials for SOFC cathodes
PublikacjaW niniejszym artykule, dwa związki SrTiO3 domieszkowanego Fe przebadano pod względem przydatności na katody w tlenkowych ogniwach paliwowych. SrTi0.65Fe0.35O3 i SrTi0.5Fe0.5O3 zostały przebadane pod względem reaktywności chemicznej z elektrolitem YSZ. Stwierdzono, że przewodnictwo elektryczne tych związków jest stosunkowo niskie: 0,4 S/cm i 2 S/cm odpowiednio dla STF35 i STF50.
-
The comparison of SrTi0.98Nb0.02O3-δ-CeO2 and SrTi0.98Nb0.02O3-δ-YSZ composites for use in SOFC anodes
PublikacjaWytworzono i przebadano właściwości strukturalne i elektryczne kompozytów SrTi0.98Nb0.02O3-δ-CeO2 i SrTi0.98Nb0.02O3-δ-YSZ. Przeprowadzono testy materiałów zastosowanych jako anody w tlenkowych ogniwach paliwowych.
-
Materiały katalityczne dla tlenkowych ogniw paliwowych zasilanych biogazem
PublikacjaTlenkowe ogniwa paliwowe (SOFC) są jednymi z najbardziej obiecujących przyrządów do konwersji energii ze względu na wysoką wydajność, niską emisję zanieczyszczeń i możliwość zastosowania szerokiej gamy paliw. Jednak zastosowanie biogazu jako paliwa w obecnie wytwarzanych ogniwach paliwowych, w których anoda jest zbudowana z niklu i tlenku itru stabilizowanego tlenkiem cyrkonu, powoduje osadzanie się węgla oraz degradację ogniwa....
-
Microstructure and electrical properties of SrTi0.98Nb0.02O3-δ-based composites applied as porous layers for SOFCs
PublikacjaPrzebadano właściwości elektryczne oraz strukturalne kompozytów Sr(Ti,Nb)O3-YSZ i Sr(Ti,Nb)O3-CeO2 naniesionych w postaci warstw porowatych na podłoża YSZ
-
Perovskites in Solid Oxide Fuel Cells
PublikacjaPrzeglądowa publikacja dotycząca wykorzystania ceramicznych materiałów perowskitowych w tlenkowych ogniwach paliwowych.
-
Microstructural and electrical properties of Y0.07Sr0.93-xTiO3-δ perovskite ceramics
PublikacjaIn order to find a relationship between electrical and microstructural properties, yttrium-doped strontiumtitanate (7 mol%) with various values of strontium nonstoichiometry was investigated and shown in this work.It has been observed that yttrium doping can affect the electrical properties of SrTiO3 to a great extent.Moreover, the microstructural and electrical properties can be influenced by strontium nonstoichiometry.The defect...
-
Influence of pore formers on electrical properties of CaTi0.9Fe0.1O3-δ perovskite-type ceramics
PublikacjaPorous CaTi0.9Fe0.1O3-δ (CTF) perovskites were synthesized by the standard solid state method at different sintering temperatures with carbon black (CB), corn starch (CS) and potato starch (PS) as pore-forming agents. The ceramic samples of porosity between 9% and 42% with 5 - 40 μm pore sizes, were obtained by a 6 h sintering at either 1130º C or 1200º C of precursor powder prepared at 1470º C. X-ray diffraction analysis proved...
-
Electronic conduction in (Bi,Pb)-Sr-Ca-Cu-O glass-ceramics
PublikacjaAmorficzny materiał (Bi,Pb)4Sr3Ca3Cu4Ox wygrzewany w odpowiednich warunkach staje się nieuporządkowanym metalem i nadprzewodnikiem. Przedstawiono model mechanizmu przewodnictwa elektrycznego tych materiałów. Przeprowadzono dyskusję istniejących teorii do opisu badanych materiałów.
-
Electrical conductivity of disordered (Bi,Pb)-Sr-Ca-Cu-O materials
PublikacjaAmorficzny materiał (Bi,Pb)4Sr3Ca3Cu4Ox wygrzewany w odpowiednich warunkach staje się nieuporządkowanym metalem i nadprzewodnikiem. Ma duży opór i zazwyczaj ujemny współczynnik temperaturowej zależności oporu. W pracy dyskutowane są właściwości w stanie normalnym oraz przejście do stanu nadprzewodzącego.
-
Conductivity and superconductivity of (Bi,Pb)-Sr-Ca-Cu-O
PublikacjaAmorficzny materiał (Bi,Pb)4Sr3Ca3Cu4Ox w zależności od warunków wygrzewania może być albo granulastym materiałem albo silnie nieuporządkowanym metalem. Przejście do stanu nadprzewodzącego zachodzi w materiałach, w których Josephsonowskie sprzężenie między granulami jest silniejsze niż oddziaływania Coulombowskie.
-
Conductivity and superconductivity of (Bi,Pb)4Sr3Ca3Cu4Ox glass-ceramics
PublikacjaAmorficzny materiał (Bi,Pb)4Sr3Ca3Cu4Ox w zależności od warunków wygrzewania może być albo granulastym materiałem albo silnie nieuporządkowanym metalem. W pracy przedstawiony jest wpływ mikrostruktury na właściwości elektryczne w stanie normalnym oraz przejście do stanu nadprzewodzącego.
-
Electroconductivity and mechanical properties of carbon black Printex L6 filled polyurethanes
PublikacjaOpisano uzyskanie i badania kompozycji poliuretanowo-sadzowych na bazie sadzy przewodzącej Printex L6. Zaprezentowano wyniki badań nad wpływem udziału napełniacza przewodzącego na przewodnictwo elektryczne stałoprądowe i właściwości mechaniczne uzyskanych materiałów.
-
Chemical interaction between perovskite La0.6Sr0.4FeO3 and Super-Ionic Zr0.84Y0.16Ox
PublikacjaW pracy przedstawiono wyniki badań interakcji chemicznej pomiędzy materiałem perowskitowym LSF a materiałem superjonowym YSZ. Materiał superjonowy został wytworzony w niskiej temperaturze z użyciem prekusora polimerowego i zawiesiny proszku ceramicznego.W badaniach korzystano z spektroskopii rentgenowskiej.
-
Electronic conduction in (Bi,Pb)-Sr-Ca-Cu-O granular superconductors
PublikacjaMetale i nadprzewodniki granulaste są bardzo ciekawymi materiałami dzięki jednoczesnej obecności oddziaływań kulombowskich, tunelowania elektronów i par Coopera oraz różnych zjawisk związanych z nieuporządkowaniem. W pracy przedstawiono właściwości elektryczne granulastego nadprzewodnika (Bi,Pb)-Sr-Ca-Cu-O otrzymanego wskutek krystalizacji w fazie stałej. Badane materiały mogą być traktowane jako układ granul umieszczonych w matrycy...
-
Electrical properties of Y0.08Sr0.92Ti0.92Nb0.08O3_−delta after reduction in different reducing conditions
PublikacjaPraca przedstawia badania właściwości elektrycznych perowskitów Y0.08Sr0.92Ti0.92Nb0.08O3−ı redukowanych w różnych warunkach termicznych. Obserwowano wysoką przewodność elektryczną próbek redukowanych w atmosferze amoniaku. Przewodność Y0.08Sr0.92Ti0.92Nb0.08O3−ı redukowanego w amoniaku w 1500 ◦C była rzędu 600 S/cm w 200 ◦C. Przewodność elektryczna próbek redukowanych w amoniaku w 1500 ◦C była stabilna zarówno w atmosferze wodoru...
-
Structure and electric conductivity of reduced lead-germanate, bismuth-germanate and bismuth-silicate glasses modified with potassium
PublikacjaZbadano szkła germanianowo-ołowiowe i krzemianowo+bizmutowe. Warstwy metalicznych granul wytwarzano w nich poprzez redukcję powierzchni w atmosferze wodoru. Praca dotyczy wpływu potasu na właściwości szkła. Przeprowadzono badania metodami mikroskopii sił atomowych, DSC oraz pomiary przewodności elektrycznej. Stwierdzono, że obecność potasu poprawia mechaniczne i technologiczne właściwości szkła.
-
(Bi,Pb)-Sr-Ca-Cu-O glass-ceramics - superconductor and granular metal
PublikacjaW materiale o składzie (Bi,Pb)-Sr-Ca-Cu-O wskutek stosowania różnych warunków wytwarzania można otrzymać materiały o różnorodnych właściwościach. W efekcie wygrzewania materiał amorficzny częściowo krystalizuje. To powoduje wzrost rozmiaru i zawartości przewodzących i nadprzewodzących granul oraz zmniejszenie szerokości izolujących barier pomiędzy granulami. Zależność temperaturowa oporu słabo skrystalizowanego materiału jest funkcją...
-
Effect of structure modification with potassium on grains layer creation process and phase transitions
PublikacjaZbadano szkła germanianowo-ołowiowe i krzemianowo bizutowe. Wartwy metalicznych granul wytwarzano w nich poprzez redukcję powierzchni w atmosferze wodoru. Praca dotyczy wpływu potasu na tworzenie się warstwy granul oraz na procesy topnienia i krzepnięcia granul w trakcie obróbki termicznej.
-
Conductivity and superconductivity in granular materials
PublikacjaMetale i nadprzewodniki granulaste są bardzo ciekawymi materiałami dzięki jednoczesnej obecności oddziaływań kulombowskich, tunelowania elektronów i par Coopera oraz różnych zjawisk związanych z nieuporządkowaniem. W pracy przedstawiono i porównano niektóre właściwości granulastych nisko- i wysokotemperaturowych nadprzewodników. Granulasty nadprzewodnik wysokotemperaturowy otrzymano metodą krystalizacji w fazie stałej szkła (Bi,Pb)-Sr-Ca-Cu-O....
-
Structure and electrical properties of nitrided NbN-TiN sol-gel derived films
PublikacjaW pracy przedstawiono rezultaty badań struktury oraz właściwości elektrycznych warstw NbN-TiN (o różnym stosunku molowym NbN/TiN)otrzymanych w wyniku termicznego azotowania warstw tlenkowych otrzymanych metodą zol-żel. Badania struktury przeprowadzono metodami AFM, XRD oraz XPS. Wynika z nich, iż głównymi fazami w wartstwach są NbN i TiN o rozmiarach ziaren około 100 nm. Jednakże zaobserwowano również istnienie niewielkiej ilości...
-
Electrical and structural properties of Nb-doped SrTiO3 ceramics
PublikacjaPrzebadano wpływ zawartości niobu na strukturę i własności elektryczne tytanianu strontu. Zbadany został wpływ warunków redukcji i porowatości na właściwości materiału. Za optymalne uznano domieszkowanie niobem w wysokości 2% molowych.
-
The structure and melting of lead nanocrystalline layer in reduced lead-germanate glass
PublikacjaNanokrystaliczna warstwa granul Pb na powierzchni szkieł ołowiowo-germanianowych została wytworzona poprzez wygrzewanie w wysokich temperaturach, w atmosferze wodoru. Właściwości tej warstwy silnie zależą od temperatury i czasu redukcji. Artykuł prezentuje rentgenowskie i mikroskopowe badania struktury warstwy oraz wpływ topnienia i krzepnięcia granul Pb na jej przewodnictwo.
-
Superconducting lead granular layer prepared by reducting in hydrogen lead of germanate glass
PublikacjaCienka warstwa granul Pb została wytworzona poprzez wygrzewanie w wodorze, w wysokiej temperaturze. Struktura i nadprzewodzące właściwości warstwy ołowiu zależą od temperatury i czasu redukcji. Artykuł analizuje wpływ warunków redukcji na wytworzoną warstwę granul Pb.
-
Solid Oxide Fuel Cells with Ni infiltrated perovskite anode
PublikacjaNiobium-doped strontium titanate was used as the anode for a solid oxide fuel cell. Electrolyte-supported cells were prepared with pure perovskite and composite perovskite–yttria–stabilized-zirconia (YSZ) anodes. Fuel cell tests demonstrated significant improvement in power density after infiltration with a small amount of Ni. The obtained values of power densities are comparable with conventional Ni/YSZ cermet anode. In addition,...
-
Electrical properties of Y0.08Sr0.92Ti0.92Nb0.08O3-δ after reduction in different reducing conditions
PublikacjaElectrical properties of perovskite Y0.08Sr0.92Ti0.92Nb0.08O3−ı after reduction in different conditions were studied. Relatively high electrical conductivity in samples reduced in ammonia was observed. The conductivity of Y0.08Sr0.92Ti0.92Nb0.08O3−ı reduced in ammonia at 1500 ◦C was of about 600 S/cm at 200 ◦C. Conductivity after reduction in ammonia at 1500 ◦C was stable both in hydrogen and oxygen atmosphere up to 600 ◦C. Reduction...
-
Interactions between components of SrTi0.98 Nb0.02O3-δ-YSZ and SrTi0.98 Nb0.02O3-δ -CeO2 composites
PublikacjaComposites consisting of SrTiO3-based perovskite and either yttria-stabilized zirconia or ceria were investigated. The mechanical compatibility and possible inter-diffusion between phases were characterized by scanning electron microscopy, X-ray diffraction, and energy-dispersive X-ray spectroscopy. A gradual disappearance of Ce-containing phases with an increase in the temperature of reduction in hydrogen was noticed. Moreover,...
-
Electrical and structural properties of Nb-doped SrTiO3
PublikacjaNiobium-doped strontium titanate synthesized via conventional solid-state reaction has been studied. Influence of niobium content on the lattice parameters and electrical conductivity has been reported. Various reduction conditions have been investigated. For samples reduced in hydrogen at 1400°C, a transition from thermally activated to metallic behavior has been observed. Maximum electrical conductivity (ca. 55 Scm−1 at 650°C)...
-
Microstructural and electrical properties of Y0:07Sr0:93−xTiO3− perovskite ceramics
PublikacjaIn order to find a relationship between electrical and microstructural properties, yttrium-doped strontium titanate (7 mol%) with various values of strontium nonstoichiometry was investigated and shown in this work. It has been observed that yttrium doping can affect the electrical properties of SrTiO3 to a great extent. Moreover, the microstructural and electrical properties can be influenced by strontium nonstoichiometry. The...
-
Investigation methods of ionic conductivity measurements in polycrystalline MIEC (mixed ionic-electronic conductor) based on perovskite ceramics
PublikacjaPaper about the measurements of ionic conductivity in LSM and strontium titanate ceramics.
-
Structure and electric properties of double magnesium zirconium orthophosphate
PublikacjaPublikacja przedstawia wyniki pomiarów elektrycznych i strukturalnych ortofosforanu magnezowo-cyrkonowego.
-
Nano - and microcrystals of doped niobates
PublikacjaPublikacja przedstawia wyniki analizy pomiarów wysokotemperaturowej rentgenografii strukturalnej niobanu lantanu domieszkowanego magnezem.
-
Optimization of microstructure and properties of acceptor-doped barium cerate
PublikacjaThe presented research concerns acceptor doped barium cerate and the attempts of improvement of its production method that would allow obtaining the solid electrolyte characterized by the particular properties. The authors suggest combining two production methods, molten salt synthesis and self-combustion, in order to achieve the compound material that has some of the advantages of both of the initial methods. An impact of nickel...
-
Characterization of CaTi0.9Fe0.1O3/La0.98Mg0.02NbO4 composite
PublikacjaA composite of CaTi0.9Fe0.1O3 and electrolyte material, i.e. magnesium doped La0.98Mg0.02NbO4 was prepared and studied. The phase content and the sample microstructure was examined by an X-ray diffraction method and scanning electron microscopy. EDS measurements were done both for composite samples and the diffusion couple. The electrical properties were studied by four terminal DC method. The Ahigh-temperature interaction between...
-
Correlation between structural and electrical properties in highly porous (Y,Sr)(Ti,Nb)O3-delta SOFC anodes
PublikacjaIn order to find a relationship between structural and electrical properties, niobium and yttrium doped SrTiO3 ceramics were prepared via solid-state reaction. The samples were sintered in hydrogen and air conditions. The samples were also fabricated with a pore-former to obtain highly porous specimens. The electrical properties of Nb-doped SrTiO3 samples and yttrium and niobium co-doped SrTiO3 were compared. The comparable electrical...
-
Metodyka wykonywania pomiarów oraz ocena niepewności i błędów pomiaru
Publikacjaelem każdego ćwiczenia w laboratorium studenckim jest zmierzenie pewnych wielkości, a następnie ob- liczenie na podstawie tych wyników pomiarów wartości wielkości badanej. Rezulta- tem końcowym badań jest nie tylko otrzymany wynik liczbowy. Nie mniej ważne jest dokonanie oceny dokład- ności pomiaru oraz opraco- wanie wniosków końcowych. Warto zadać sobie pytanie: czy to, co zostało zmierzone, ma sens i co z tego wynika?...
-
Planowanie eksperymentu
PublikacjaW pracy przedstawiono schemat postępowania przy planowaniu eksperymentu naukowego
-
Wiedza ogólna o eksperymencie naukowym
PublikacjaW pracy przedstawiono podstawowe pojęcia z zakresu metodologii badań w nauce i w technice
-
Ionic conductivity in bismuth silicate glasses.
PublikacjaZbadano właściwości elektryczne szkieł krzemianowo- bizmutowych zawierających 55 mol% tlenku bizmutu. Uzyskane wyniki potwierdzają jonowy charakter przewodnictwa, za które odpowiedzialne są jony tlenu.
-
Electrical conductivity of reduced lead-germanate glasses
PublikacjaPewna grupa szkieł tlenkowych poddana procesowi redukcji w atmosferze gorącego wodoru wykazuje gwałtowne zmiany swoich właściwości elektrycznych i optycznych. Szkła ołowiowo-germanianowe, którym poświęcona jest niniejsza praca należą do takich szkieł i charakteryzują się szczególnymi redukcyjnie indukowanymi właściwościami. Wystarczająco długie wygrzewanie prowadzi bowiem do wzrostu przewodnictwa elektrycznego nawet o 12 rzędów...
-
Positron Annihilation Studies of Silicon Oxides and Oxygen Precipitates in Silicon
PublikacjaTechniki pozytonowe dają możliwości badania defektów i zmian strukturalnych nie obserwowanych innymi metodami. W tej pracy zastosowano 3 różne techniki pozytonowe do badania zmian strukturalnych i tworzenia wydzieleń SiOx w krzemie.
-
Ionic conductivity of bismuth silicate and bismuth germanate glasses.
PublikacjaPrzedstawiono wyniki badań przewodnictwa d.c i a.c. szkieł BixGe1-xO2-0.5x (gdzie x=0.13, 0.23, 0.33, 0.47) i BixSi1-xO2-0.5x (gdzie x=0.47, 0.57, 0.67). Wyniki sugerują, że przewodnictwo elektryczne jest zdeterminowane ruchem jonów tlenu. Znaczący wzrost przewodnictwa elektrycznego przy x> 0.33 został wytłumaczony na podstawie faz perkolacyjnego modelu ruchu jonów w podsieci BiO5-6.
-
Structural studies and melting of bismuth nanocrystals in reduced bismuthgermanate and bismuth silicate glasses.
PublikacjaOtrzymano nanostruktury krystalicznego bizmutu w matrycy XO2 (X=Si,Ge) oraz warstwę nanostruktur krystalicznego bizmutu na powierzchni redukowanych w atmosferze wodoru szkieł Bi0.33Ge0.67O1.84 i Bi0.57Si0.43O1.72. Kompozyt Bi-szkło badano metodą DSC, XRD oraz AFM. Zaobserwowano zmniejszenie temperatury topnienia nanokrystalicznego bizmutu znajdującego się w matrycy szkła z 544 K do 387 K oraz do 502 K w przypadku powierzchniowej...
-
Structural studies of bismuth nanocrystals embedded in SiO2 or GeO2 matrices.
PublikacjaW wyniku wygrzewania w atmosferze wodoru szkieł bizmutowych i germanowych otrzymano warstwę nanogranul bizmutu w otoczeniu amorficznej matrycy oraz powierzchniową warstwę bizmutowych granul. Grubość i struktura tak otrzymanych warstw silnie zależy od czasu i temperatury redukcji.
-
Structure changes in (Bi-Pb)-Sr-Ca-Cu-O glass ceramics during the first minutes of crystallization.
Publikacja(Bi0.8Pb0.2)4Sr3Ca3Cu4Ox szkło otrzymano standardową metodą chłodzenia stopionych substratów. Częściowo skrystalizowane próbki otrzymano poprzez wygrzewanie szkła w temperaturze między 700stC i 870stC. Obecność faz krystalicznych badano metodą dyfrakcji rentgenowskiej w temperaturze pokojowej oraz w temperaturze krystalizacji. Stwierdzono obecność faz nadprzewodzących (Bi0.8Pb0.2)2Sr2CuOx, (Bi0.8Pb0.2)2Sr2CaCu2Ox i (Bi0.8Pb0.2)2Sr2Ca2Cu3Ox...
-
Electrical conductivity and superconductivity in (Bi-Pb)-Sr-Ca-Cu-O glassceramics during the first minutes of crystallisation.
Publikacja(Bi0.8Pb0.2)4Sr3Ca3Cu4Ox częściowo skrystalizowane próbki otrzymano poprzez wygrzewanie szkła w temperaturze między 700st.C i 870st.C przez krótki czas.Pomiary temperaturowej zależności oporności przeprowadzono metodą 4-punktową w temperaturze od 3K do 300K. Przeprowadzono również pomiary przewodności w czasie trwania wygrzewania. Stwierdzono, że w czasie wygrzewania następuje stopniowa zmiana mechanizmu przewodnictwa. Niektóre...
-
Bismuth germanate and bismuth silicate glasses in cryogenic detectors.
PublikacjaStwierdzono, że przewodnictwo elektryczne redukowanych szkieł silnie zależy od temperatury, czasu reakcji i koncentracji Bi. Zależność przewodnictwa elektrycznego od temperatury jest dobrze opisana przez funkcję ĺ~exp[-(T0/T)n,gdzie n=1/4. Współczynnik emisji wtórnej elektronów jest praktycznie niezależny od stopnia redukcji ale znacznie rośnie po domieszkowaniu szkieł alkalicznymi jonami. Badania dowiodły, że modyfikowane...
-
Structural and electrical transport studies of reduced in hydrogen surfaceof bismuth germanate glass
PublikacjaOtrzymano nanostruktury krystalicznego bizmutu w matrycy szkła germanowegooraz warstwę nanostruktur krystalicznego bizmutu na powierzchni redukowanegow atmosferze wodoru szkła Bi0.33Ge0.67O1.83. Zaproponowano prosty model bu-dowy zredukowanych szkieł bizmutowo-germanowych potwierdzony wynikami badańAFM i XRD. Zbadano wpływ czasu i temperatury redukcji oraz topnienia bizmu-tu na własności elektryczne badanych szkieł. Przeanalizowano...
-
Structure and morphology of hydrogen reduced surface of bismuth germanateand bismuth silicate glasses.
PublikacjaOtrzymano nanostruktury krystalicznego bizmutu w matrycy XO2(X=Si,Ge) oraz warstwę nanostruktur krystalicznego bizmutu na powierzchni redukowanych w atmosferze wodoru szkieł Bi0.33Ge0.67O1. i Bi0.57Si0.43O1.72. Zaproponowano prosty model budowy zredukowanych szkieł bizmutowo-germanowych potwierdzony wynikami badań AFM i XRD. Obserwowane zmiany przewodnictwa elektrycznego redukowanych szkieł wyjaśniono na podstawie modelu.