Search results for: KOROZJA, STAL NIERDZEWNA, SPAWANIE, CORROSION, STAINLESS STEEL, WELDING
-
API 5L X65 steel - tensile properties in room temperature -10°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - CMOD-force record in -10°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - tensile properties in room temperature +20°C, across rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - tensile properties in room temperature -10°C, across rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - CMOD-force record in -10°C, across rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - tensile properties in room temperature +20°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - fracture documentation of CMOD-force test in -10°C, along rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
API 5L X65 steel - fracture documentation of CMOD-force test in -10°C, across rolling direction
Open Research DataSteel designated as API 5L X65 is often used for oil and gas transportation pipelines. It is caused due to its high ductility, weldability and good corrosion resistance. API 5L X65 is a low alloy steel with carbon content less than 0.3% (depends on delivery condition). Once installed, a pipeline remains in place for many years. Throughout its life,...
-
Diffusible Hydrogen Control in Flux Cored Arc Welding Process
PublicationOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper an experimental...
-
Role of bead sequence in underwater welding
PublicationThis paper presents examinations of the role of the bead sequence in underwater welding. Two specimens of wet welded layers made by covered electrodes with the use of normalized S355G10+N steel were welded by a reasonable bead sequence. For each specimen, metallographic macro- and micro-scopic tests were done. Then, Vickers HV10 hardness measurements were conducted for each pad weld in the welded layer. The results show that welding...
-
Novel fast non-linear electrochemical impedance method for corrosion investigations
PublicationThe paper presents a novel approach to corrosion rate monitoring using non-linear electrochemical impedance spectroscopy. The authors propose a new variant of non-linear impedance measurement using amplitude-modulated multi-frequency ac perturbation signal. It allows shortening of measurement duration so it is possible to monitor corrosion rate of the systems experiencing rapid changes. In this way a limitation resulting from lack...
-
Preliminary investigations of effect of conditions of FCAW process on diffusible hydrogen content in deposited metal
PublicationOne of the types of hydrogen degradation of steel welded joints is cold cracking. The direct cause of the formation of cold cracks is simultaneous presence of hydrogen, residual stresses and brittle structure. The way of preventing the occurring of degradation is to eliminate at least one of these factors. Practice has shown that the best solution is to control the amount of hydrogen in deposited metal. In this paper the state...
-
Influence of nanoparticle concentration on convective heat transfer of water-Al2O3 nanofluids inside horizontal tubes
PublicationThis work presents preliminary results of the experimental investigation of the forced convection heat transfer of water-Al2O3 nanofluids inside stainless steel tube with 8 mm internal diameter and 2000 mm length. Nanoparticles were tested at the concentrations of 0.01%, 0.1%, 1% and 5% by weight and the Reynolds number range encompasses laminar as well as turbulent flows.
-
Protection of bridges against stray current corrosion
PublicationA case study of Siennicki Bridge stray current corrosion hazard is presented. A corrosion risk was caused by incorrectly designed tram line traction which goes over the bridge. No dielectric insulation between running rails and bridge steel construction was used. A variety of protection methods against stray currents are described. Characteristics of the endangered bridge were described. Impressed current cathodic protection system...
-
Degradation of protective coatings in steel chimneys of flue gas desulfurisation system
PublicationThis paper presents problems associated with corrosion of steel stacks and changes in philosophy of corrosion protection when implemented into flue gas desulphurization systems. In-situ tests were taken by means of electrochemical impedance spectroscopy at the stack which discharges flue gas before wet lime/limestone desulphurization. A very quick electrolyte absorption by the spherical infill vinylester coating was found using...
-
Evaluation of organic coating systems for corrosion protection of industrial equipment using impedance spectroscopy
PublicationThe high economic impact of corrosion can be reduced by enhanced corrosion management and prevention based on appropriate means. This applies in particular to the protection of structures with organic protective coatings. Steel is subject to corrosion that reduces its service life and leads to destruction in most severe cases. The application of paints to metallic objects for corrosion control has been known for a long time and...
-
Electrochemical investigations on corosivity of de-icing liquids for railway infrastructure
PublicationThe paper presents the results of electrochemical tests of the de-icing fluid for railway infrastructure. DC and AC electrochemical tests were performed to determine the corrosion rates of structural steel, cast iron and aluminium in the newly produced fluid. The results were compared with the corrosion rates of the same materials in the fluid without corrosion inhibitors. The obtained test results indicate a low corrosion risk...
-
Corrosion behavior of concrete produced with diatomite and zeolite exposed to chlorides
PublicationChloride induced reinforcement corrosion is widely accepted to be the most frequent mechanism causing premature degradation of reinforced concrete structures. The electrochemical impedance of reinforcing steel in diatomite- and zeolite-containing concrete exposed to sodium chloride was assessed. Chemical, physical and mineralogical properties of three concrete samples (20% diatomite, 20% zeolite, and a reference containing neither)...
-
An experimental study of high-hydrogen welding processes
PublicationThis paper presents investigation results of determination of the diffusible hydrogen content in deposited metal obtained by means of two most often used methods-the glycerin method and the mercury method. Relation has been defined between results of those methods in the area characteristic of low-hydrogen as well as high-hydrogen welding processes. Relations available in the literature do not include the diffusible hydrogen content...
-
Improved Performance of 1-Ethyl-3-Methylimidazolium Tetrafluoroborate at Steel/HCl Interface by Iodide Ions
PublicationThe corrosion and corrosion inhibition of St37 steel in 0.1 M HCl solution by 1-ethyl-3-methylimidazolium tetrafluoroborate (EMITFB) and the effect of addition of KI on the inhibitive performance of EMITFB have been examined by electrochemical [electrochemical impedance spectroscopy, potentiodynamic polarization, and dynamic electrochemical impedance spectroscopy (DEIS)] and surface examination [scanning electron microscope (SEM)...
-
Corrosion process monitoring by AFM higher harmonic imaging
PublicationThe atomic force microscope (AFM) was invented in 1986 as an alternative to the scanning tunnelling microscope, which cannot be used in studies of non-conductive materials. Today the AFM is a powerful, versatile and fundamental tool for visualizing and studying the morphology of material surfaces. Moreover, additional information for some materials can be recovered by analysing the AFM's higher cantilever modes when the cantilever...
-
Analisys of the failure of fixator used in bone surgery
PublicationThe Gamma nail (fixator) made of stainless steel, which has broken in the body, was subjected to examination. The fixator was removed from the patient femur. The fracture occurred in the area of the nail hole after two months' stay in the organism. The research included chemical composition, hardness of the Gamma nail material and the observation and analysis of the type of fracture. The research showed the fatigue failure of the...
-
Evaluation of cathode materials for electrochemical photocatalyst deposition
PublicationElectrochemical deposition of photocatalyst, especially TiO2, onto several cathode materials was investigated and evaluated. The deposited films were characterized by scanning electron microscopy (SEM), energy dispersive X-ray spectrometer (EDX) and electrochemical measurements. Photocatalytic activity was determined by the decomposition of cyclohexane in air by irradiation with ultraviolet light emitting diodes. It was found that...
-
Wear of Ultra-thin DLC or Tungsten-modified DLC Coatings under Reciprocating Sliding
PublicationIn the paper results are presented from tests in reciprocating sliding of self mated specimens of DLC and tungsten modified DLC coatings on stainless steel substrate. The contact geometry chosen for the research task was ball on flat. The contacts were lubricated either with distilled water or medical saline solution. Results are presented with regard to wear resistance as a function of material type and lubricant used.
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35
Open Research DataWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41
Open Research DataWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37
Open Research DataWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
RESEARCH ON ORGANIC COATINGS DESIGNED FOR UNDERWATER APPLICATIONS
PublicationUnderwater steel structures require periodic maintenance. In the case of vessels, anti-corrosion works are carried out in the shipyard, where very good conditions for applying organic protective coatings can be provided. Very good surface preparation can be obtained by the use of abrasive blasting. The well-prepared metal surface is free from impurities (particularly inorganic salts). Suitable conditions for the application and...
-
Indoor accelerated controlled corrosion degradation test of small- and large-scale specimens
PublicationThe work presented here is a part of a long-term project analysing the structural behaviour of ageing marine structures. An accelerated corrosion degradation set-up was developed to reproduce corroded marine structural specimens of different degrees of degradation, controlling various natural factors, i.e., temperature, oxygen content, salinity, and flow velocity. The nine stiffened plates of 1.2 m length and 30 small scale specimens...
-
The protection and monitoring of a distribution piping network for potable water supply
PublicationPurpose – The purpose of this paper is to implement the corrosion protection method for steel pipes used in a municipal water-pipe network. Results of an inhibitor protection system installed on the system are presented. Inhibitor protection was required due to the high corrosivity of the water collected by a surface intake, which had resulted in a large number of failures and low water quality, due to the presence of corrosion...
-
Opracowanie ekspertyzy dotyczącej przyczyn pękania łopatek wirnika SP turbiny PG1 typu 13UP55
PublicationZakres badań i analiz dotyczył ustalenia przyczyn pękania elementów łopatek wirnika SPA5 turbiny TG1 typu 13UP55 obejmował: 1. wykonanie badań składu chemicznego stali, z której wykonano łopatki dostarczone przez Zleceniodawcę dwoma metodami, 2. badania mikroobszarów zniszczenia łopatek na mikroskopie elektronowym skaningowym z mikroanalizatorem EDS, 3. badania metalograficzne makroskopowe i mikroskopowe fragmentów...
-
Manganese Phosphatizing Coatings: The Effects of Preparation Conditions on Surface Properties
PublicationManganese phosphate coating could be used to protect the surface of steel products. However, it is essential to determine the effects which process parameters, as well as the types of additives used, have on the efficiency of coating deposition. Thus, we present here a process of phosphatization of low-alloy steel (for 15 min at 95 ◦C) in manganese/nickel baths followed by a passivation process with the use of a silicon and zircon...
-
Problemy z powłokami antykorozyjnymi na elementach wyposażenia obiektów mostowych
PublicationOpisano problem wadliwości zabezpieczenia antykorozyjnego w zakresie malarskich powłok ochronno-dekoracyjnych wykonywanych na stalowych elementach barier zabezpieczonych uprzednio poprzez ocynkowanie metodą zanurzeniową na gorąco. Wykorzystując przykłady pochodzące z różnych obiektów przedstawiono powtarzający się problem delaminacji powłok malarskich, niezależny od rodzaju zastosowanych wyrobów lakierniczych oraz znacznego rozwoju...
-
Problemy z powłokami antykorozyjnymi na elementach wyposażenia obiektów mostowych
PublicationPrzedstawiono problem wadliwości zabezpieczenia antykorozyjnego w zakresie malarskich powłok ochronno - dekoracyjnych wykonywanych na stalowych elementach barier zabezpieczonych uprzednio poprzez ocynkowanie metodą zanurzeniową. Wykorzystując przykłady pochodzące z różnych obiektów przedstawiono powtarzający się problem delaminacji powłok malarskich, niezależny od rodzaju zastosowanych wyrobów lakierniczych oraz znacznego rozwoju...
-
Analysis of the Surface Stereometry of Alloyed Austenitic Steel after Fibre Laser Cutting using Confocal Microscopy
PublicationThe paper extends the concept of cut edge quality and examines the fibre laser cutting process. A Prima Power Platino Fiber Evo device with a reference speed (RS) of 3500 mm/min was used for laser cutting. In order to analyse the influence of the laser cutting speed on the cut edge quality of X5CrNi18-10 stainless steel sheets, macroscopic studies were conducted on a stereoscopic microscope and surface stereometry on a confocal...
-
Finite element simulation of cross shaped window panel supports
PublicationThe aim of the work is to verify suitability of cross-shaped window panel supports for mullion-transom wall systems. The Finite Element Method (FEM) is chosen to determine the behaviour of stainless steel elements under loading. The advanced non-linear numerical simulations are carried out using an implicit FEM software package MSC.Marc. This study is proposed to initiate the comprehensive investigation of mechanical properties...
-
Influence of water salinity on corrosion risk - the case of the southern Baltic Sea coast.
PublicationWater corrosivity in Gdansk Bay, Poland, the southern part of the Baltic Sea, was investigated. The analysed region is heavily industrialized, and the coastline is very diverse. Twenty-seven test points along the coastline were selected. Water parameters such as salinity, total dissolved solids content, resistivity, conductivity, oxygenation, pH and corrosion rate were determined. The results of the investigation are presented....
-
Protective and Suppressing Electromagnetic Interference Properties of Epoxy Coatings Containing Nano-Sized NiZn Ferrites
PublicationNano-crystalline ferrites with the chemical formula NixZn(1−x)Fe2O4, where x = 0, 0.2, 0.4, 0.6, 0.8, 1.0, were synthesized using a co-precipitation method. The obtained ferrites were investigated by X-ray diffraction (XRD). The corrosion inhibiting behavior of nano-sized ferrites was tested using carbon steel samples and 10% aqueous ferrite extracts. Results were compared with previous data obtained for micro-sized ceramic ferrites....
-
3D X-ray Micro-CT Analysis of Rebar Corrosion in Reinforced Concrete Subjected to a Chloride-Induced Environment
PublicationThe paper presents experimental investigations of the concrete cover protective ability to coun-teract rebar corrosion in reinforced concrete cubes. To study and quantify the consequences of corrosion a reinforced concrete sample was subjected to chloride-induced environment in order to get corroded and combined with un-corroded sample. Chloride-accelerated technique can in-duce a high degree of corrosion within at a controlled...
-
PA32 aluminum alloy - tensile properties
Open Research DataIn addition to steel, aluminium alloys are the main building material used in the shipbuilding industry. Due to its undoubted advantages, such as low density (nearly three times lower than in the case of steel for shipbuilding) and high corrosion resistance, it is often used for hulls of yachts and small vessels as well as superstructures. For safety...
-
High temperature corrosion of evaporator tubes with thermal sprayed coatings
PublicationDegradation examinations of outer surface of low-emission steam boiler evaporator tubes are presented in the paper. Metallographic evaluation of scale morphology, its micro sites chemical composition analysis and distribution of elements on cross sections have been performed. Water-wall tubes were exposed in steam boiler for up to two years period. Common tubes made of 16Mo3 steel suffered sulphide and molten salts corrosions....
-
FRP-based reinforcement coatings of steel with application prospects in ships and offshore structures: a review
PublicationLatest research on novel FRP-based anti-corrosion structural coatings (for enhancing structural capacity and strengthening the coating layer) is discussed with application prospects for ships and offshore structures. In the marine environment, structures constantly face corrosion and fatigue cracks. Combining this with high operational and wave loads, it might cause a structural collapse. Recently, polymer composites have been...
-
Influence of nanoparticle concentration on convective heat transfer of water-Al2O3 nanofluids inside horizontal tubes
PublicationNanofluids came to be seen as a new generation of coolants, especially in single-phase systems. Conducted experiments indicate that the increase in thermal conductivity is not the only reason for the intensification of heat transfer when using nanofluids. Preliminary results of the experimental investigation of the forced convection heat transfer of water-Al2O3 nanofluids inside stainless steel tube with 8 mm internal diameter...
-
Comparison of strain results at a laser weld notch obtained by numerical calculations and experimental measurements
PublicationIn the development of ship structures applying new materials and it’s purposeful placement play an important role. During the last years, especially in a construction of ro-ro type vessels, the usage of novel sandwich structures in cargo decks is profitable. Steel sandwich panel is an innovative solution which at a todays state of development can be used for the construction of any members not taking part in a global bending of...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45
Open Research DataWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B41/#A39
Open Research DataWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22
Open Research DataWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41
Open Research DataWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B34/#A33
Open Research DataWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A45/#B48
Open Research DataWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....