Search results for: ceramic
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K02
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig:...
-
Optical microsc. images of wear marks on ball (JPG). Reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - DISTILLED WATER. Specim. set K06
Open Research DataOptical microscope images of wear zone on the 5mm diam. ceramic ball used in tests as the fixed specimen.Friction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: DISTILLED WATER. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test...
-
NaCEnCo Nanocrystalline ceramic materials for efficient electrochemical energy conversion
ProjectsProject realized in Department of Biomedical Engineering according to POIR.04.04.00-00-42E9/17-00 agreement from 2018-10-31
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #24 - #25.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #24 (upper, rotating), #25 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #30 - #31.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #30 (upper, rotating), #31 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #20 - #21.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #20 (upper, rotating), #21 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #22 - #23.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #22 (upper, rotating), #23 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #28 - #29.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #28 (upper, rotating), #29 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Specimen running-in. Prep. to sliding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specimen set #26 - #27.
Open Research DataSpecimen running-in procedure. Preparation to sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. Specimen set #26 (upper, rotating), #27 (lower, non-rotating)CZ_PRZYS.MAT - accelerometerMOM_TAR.MAT...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - full run
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09A - full-run
Open Research DataVIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30,...
-
VIbration monitoring in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - pre-run
Open Research DataVIbration monitoring in reciprocating siding friction tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30,...
-
Wear in reciprocating siding friction tests. Ball-on-flat contact. Sintered alumina ceramics (98%). Lubricant - PARAFFIN OIL. Specim. set K09 - pre-run (10s)
Open Research DataFriction and wear tests in ball-on-flat contact. Both specimens made of sintered alumina ceramics (98%) - self-mated contact.Linear reciprocating motion.Lubrication: PARAFFIN OIL. Sliding velocity (peak): 0.1 m/s. Load (normal force): 5N. Test rig: TPZ-1 Tribometer.Running time: progressive increments of 10, 15, 30, 60, 180 and 300s. (stored in separate...
-
POPCECT Positrode Optimization for Protonic Ceramic Electrochemical Cells Technology
ProjectsProject realized in Zakład ceramiki according to PL-TW/IX/42/POPCECT/2022 agreement from 2022-06-14
-
Sposób otrzymywania ceramicznych materiałów nadprzewodzących o porach otwartych
Inventions -
FunKeyCat Functional Grading by Key doping in Catalytic electrodes for Proton Ceramic Cells
ProjectsProject realized in Department of Solid State Physics according to UMO-2018/30/Z/ST5/00915 agreement from 2019-10-01
-
LNO Investigation of high temperature properties of ceramic materials by thermal analysis
ProjectsProject realized in Department of Solid State Physics according to 0513/IP2/2016/74 agreement from 2016-10-19
-
n/d n/d
ProjectsProject realized in Faculty of Chemistry according to Homing Plus/2012-6/16 agreement from 2013-05-22
-
Low-temperature synthesis of silicon carbide powder using shungite
Publication -
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 4-8h.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 4-8h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21, #22-#23, #24-#25, #26-#27,...
-
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 0-4h.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer.Running time: 0 - 4h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21, #22-#23, #24-#25, #26-#27,...
-
Wear in siding friction tests. Ring-on-ring contact. Sintered alumina ceramics (98%). Paraffin oil lubrication. Specim. sets #20-#21, #22-#23, #24-#25, #26-#27, #28-#29,#30 - #31. Run time: 0-4h. High frequency burst recording.
Open Research DataWear in sliding friction tests in ring-on-ring contact. Sintered alumina ceramics (98%) in self-mated contact. Lubrication: paraffin oil. Sliding velocity: 0.2 m/s. Mean contact stress: 10 MPa. Test rig: PT-3 Tribometer. High frequency burst recording.Running time: 0 - 4h.Specimen sets:Specim. sets (# [upper, rotating] - #[lower, non-rotating]):#20-#21,...
-
MiLoSoc Understanding and minimization of ohmic and polarization losses in solid oxide cells by nanocrystalline ceramic and cermet functional layers
ProjectsProject realized in Department of Biomedical Engineering according to UMO-2017/25/B/ST8/02275 agreement from 2018-02-26
-
Sposób otrzymywania materiału ceramicznego do anod i katod ogniw paliwowych, zwłaszcza pracujacych w niskich i średnich temperaturach w zakresie od 500K do 1500K
Inventions -
Balanand Santhosh Ph.D.
PeopleDr. Balanand Santhosh, obtained his Ph.D. (cum laude) in Materials, Mechatronics and Systems engineering from the Department of Industrial Engineering, University of Trento, Italy. He is currently working as Research Assistant Professor at Gdansk Univerity of Technology, Poland. Formerly he was working as a post-doctoral researcher at University of Trento, Italy. His research expertise is mainly in the area of ceramic processing...
-
Aleksandra Dorota Mielewczyk-Gryń dr hab. inż.
People -
Paweł Wierzba dr hab. inż.
PeopleDr Paweł Wierzba, E.E. M.Sc. E.E. received from WETI PG 1994 PhD in optoelectronics (with honours) from WETI PG 2001 Research Stays at VTT Technical Research Centre of Finland from 1997 to 2000 Finnish Academy Scholarship at VTT Technical Research Centre of Finland (12 months) 2002-3 Research interest area covers optical and optical fiber meaurement methods, technology of selected ceramic and liquid crystalline materials relevant...
-
Sebastian Lech Wachowski dr inż.
PeopleBorn in 1987 in Bydgoszcz, Poland. In 2012 graduated MSc in Applied Physics: Nanotechnology and in 2017 finished, with honours, PhD in physics at Gdańsk University of Technology. Since the beginning of his academic journey interested in functional materials, especially in high-tech ceramics. Devoted to the development of high temperature protonic conductors for water vapour electrolyzers and fuel cells. During his career has several...
-
Peculiarities associated with testing polyetheretherketone (PEEK) in a model rolling contact
PublicationPolyetheretherketone (PEEK) was investigated using a modified version of the four-ball tester in which the upper forth ball was replaced by a cone in such a way that kinematics of the four-ball configuration were fully preserved. Rotation of the cone enforced orbiting and rolling of the ceramic balls around the polymer cup. The results produced some unexpected peculiarities in the wear of ceramic balls which, in principle, should...
-
Mariusz Deja dr hab. inż.
PeopleAssistant Professor in the Department of Manufacturing Engineering and Automation. He graduated in 1993, obtaining Master degree at the Faculty of Mechanical Engineering, Gdańsk University of Technology in the field of study: Mechanical Engineering, specialization: Technological Process Design. After graduation he worked for the Department of Manufacturing Engineering and Automation and his main research area was associated with...
-
Badanie właściwości czujników wilgotności na bazie nanocząstek tlenku cynku
PublicationW celu pomiaru wilgotności szeroko stosowane są czujniki elektryczne. Warstwą czynną, zmieniającą swoje właściwości pod wpływem pary wodnej, stanowią najczęściej materiały ceramiczne lub polimerowe. Tlenek cynku jest jednym z materiałów ceramicznych będących dobrym kandydatem do zastosowania go jako warstwy czynną w czujnikach wilgotności. W tej pracy przedstawiono wyniki badań właściwości struktur czujnikowych z warstwą tlenku...
-
Właściwości elektryczne szkło-ceramiki zawierającej ferroelektryczną fazę BiV
PublicationKompozyty szklano - ceramiczne zawierające nanokryształy posiadają właściwości fizyczne, które nie są możliwe do uzyskania w innych materiałach. Dzięki możliwości wytworzenia szkło - ceramik posiadających kryształy o różnej wielkości (nano, mikro...) i różnorodnego typu, można w istotny sposób kontrolować właściwości elektryczne takich materiałów. Stała dielektryczna faz ferroelektrycznych jest bardzo wrażliwa na zmiany rozmiarów...
-
STRUKTURA SZKŁO-CERAMIKI ZAWIERAJĄCEJ FERROELEKTRYCZNĄ FAZĘ BiV
PublicationLiteratura opiusuje próby wytworzenia nanokompozytów, w których skład wchodzą matryca szkła i rozproszone w niej nanokrystality fazy ferroelektrycznej. Najczęstsza metoda wykorzystywana do otrzymywania takiej szkło - ceramiki polega na wytopie szkła, a następnie jego krystalizacji. W literaturze można znaleźć dużo przykładów wytwarzania tego typu materiałów dwu lub więcej składnikowych. Najwięcej badań dotyczy ferroelektrycznych...
-
Silicon oxycarbide-tin nanocomposite derived from a UV crosslinked single source preceramic precursor as high-performance anode materials for Li-ion batteries
PublicationIn this work, we report an innovative and facile UV light-assisted synthesis of a nanocomposite based on silicon oxycarbide (SiOC) and tin nanoparticles. SiOC ceramic matrix, containing a conductive free carbon phase, participates in lithium-ion storage, and buffers the volume changes of Li-alloying/de-alloying material. The reported synthesis procedure through a polymer-derived ceramic route involves the preparation of a single-source...
-
Wpływ posuwu nagniatania na chropowatość powierzchni przedmiotów ze stali w stanie utwardzonym
PublicationPrzedstawiono wyniki badań eksperymentalnych procesu nagniatania stali twardej (62 HRC) narzędziem ceramicznym (kulką) z dociskiem hydrostatycznym. Analizowano wpływ posuwu nagniatania oraz parametrów poprzedzającej obróbki toczeniem na twardo na stan powierzchni opisanej wybranymi parametrami chropowatości.
-
BET adsorption-desorption isotherm of nano-MgO
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric MgO (CA-assisted method of synthesis)
-
BET adsorption-desorption isotherm of nano-ZrO2
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric ZrO2 (CA-assisted method of synthesis)
-
BET adsorption-desorption isotherm of nano-SrTiO3
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric SrTiO3 (CA-assisted method of synthesis)
-
BET adsorption-desorption isotherm of CeO2 pure
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric pure CeO2 (CA-assisted method of synthesis)
-
Mixed ionic-electronic conductivity and structural properties of strontium-borate glass containing nanocrystallites of Bi2 VO5.5
PublicationSamples of strontium borate glass containing bismuth vanadate nanocrystallites were prepared. Nanocomposites containing up to 45mol% of the Bi2VO5.5 phase exhibit electrical properties closer to the strontium-borate glass than to the ferroelectric Bi2VO5.5 ceramic. The glass matrix still may contain some part of bismuth and vanadium ions even after crystallization process and there is too little of crystalline phase to observe...
-
BET adsorption-desorption isotherm of CeO2 prepared using Pechini method
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The ceramic measured powder was composed of nanometric pure CeO2 prepared using modified Pechini method - citric acid and propylene glycol (2:1)
-
Investigation of electrocatalytic gas sensor properties in presence of chlorine
PublicationIn this paper performance of an electrocatalytic sensor in presence of chlorine is investigated. Presented studies concern sensor prepared in ceramic technology based on NASICON as a solid electrolyte with two round shaped platinum electrodes. Measurements in different temperatures have been performed in order to determine optimal sensor working temperature.
-
Krzysztof Zagórski mgr inż.
People -
Assessment of Trace Metals Leaching During Rainfall Events from Building Rooftops with Different Types of Coverage – Case Study
PublicationRunoff water is an important medium transporting various types of pollution originating from the atmosphere and washed out from roofing materials. The study presents a quality assessment of runoff from different roofs in the context of trace metal concentrations. The analysed rooftops were covered with copper, tar paper and ceramic tile. The quality of the rain water collected at the same time satisfies the demands of the first...
-
Electrocatalytic Gas Sensor with Reference Layer
PublicationThis paper presents studies of gas sensors prepared in ceramic technology with Nasicon as a solid electrolyte. Sensors work in the voltammetric mode thus based on the excitation of a sensor with a periodic potential signal while current response is recorded. The main aim is to investigate a Bi8Nb2O17 reference layer influence on sensor properties. Sensors I-V characteristics in different concentration of nitrogen dioxide have been...
-
Development of conductive porous media as packing materials for biotrickling filter – microbial fuel cell system (BTF-MFC system)
Open Research DataDataset presents values of electrical resistance measured for three developed conductive packimg materials for the application in a BTF-MFC system.
-
Characteristics of La 0.8 Sr 0.2 Ga 0.8 Mg 0.2 O 3-δ -supported micro-tubular solid oxide fuel cells with LaCo 0.4 Ni 0.6-x Cu x O 3-δ cathodes
PublicationIn this study, micro-tubular solid oxide fuel cells (T-SOFCs) with extruded La0.8Sr0.2Ga0.8Mg0.2O3-δ (LSGM) electrolyte as the mechanical support and LaCo0.4Ni0.6O3-δ (LCNO) or LaCo0.4Ni0.4Cu0.2O3-δ (LCNCO) as cathodes were prepared and characterized. Partial substitution of Cu for the Ni-ion positions in the LCNO lattices was found to significantly enhance the densification and accelerate the grain growth. The porosity-corrected...
-
Water uptake kinetics and electrical transport in BaCe0.6Zr0.2Y0.1M0.1O3−δ (M = Tb, Pr, Fe) protonic conductors
PublicationBaCe0.6Zr0.2Y0.1M0.1O3−d (M = Fe, Pr, Tb) is a mixed conducting oxide in which three mobile charge carriers – oxygen ion, electron/hole, and protonic defects – are present. These types of materials have gained much interest as electrode materials for protonic ceramic fuel cells (PCFCs) and protonic ceramic electrolysis cells (PCECs). In this study, the water uptake and oxygen transport properties of different BaCe0.6Zr0.2Y0.1M0.1O3−d...