Dane BadawczeThe dataset consists of a surface image and topography obtained using a Keyence VK-X1000 confocal laser microscope for (Ce0.80Gd0.20)O1.90 substrate (CGO-20). Imaging was performed to determine surface roughness. The Keyence VK-X1000 uses a 404 nm laser to map and measure the surface of samples via confocal scanning or a wide-field variable focus. The...
-
Optical measurements of LTO:Cu sol-gel derived thin films
Dane BadawczeLithium titanate doped by copper thin films were manufactured by chemical, sol-gel method. Flms were deposited on a Corning glass substrated by spin coater. To calculated optical band gap and other optcal parameters, UV-VIS spectroscopy measurements were performed. For measurements selected samples with various content of Cu.
-
Depth profile of the chemical composition of the Au-Ag multilayers
Dane BadawczeSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Scanning electron microscopy (SEM) images of the boron-doped carbon nanowalls surfaces
Dane BadawczeThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of boron-doped carbon nanowalls electrodes on silicon substrates. The surface is characterized by nano-walled structures. The obtained electrodes were doped with boron at the level of [B]/[C] = 5000ppm in the gas atmosphere during the synthesis.
-
Scanning electron microscopy (SEM) images of the boron-dopied carbon nanowalls surfaces
Dane BadawczeThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of boron-doped carbon nanowalls electrodes on silicon substrates. The surface is characterized by nano-walled structures. The obtained electrodes were doped with boron at the level of [B]/[C] = 1200ppm in the gas atmosphere during the synthesis.
-
Scanning electron microscopy (SEM) images of the boron-doped carbon nanowalls surfaces
Dane BadawczeThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of boron-doped carbon nanowalls electrodes on silicon substrates. The surface is characterized by nano-walled structures. The obtained electrodes were doped with boron at the level of [B]/[C] = 2000ppm in the gas atmosphere during the synthesis.
-
Luminescence properties of TeOx thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. The sol was obtained by vigorously stirring precursor solution at 50°C for 2h, then the temperature was raised...
-
SEM images of dewetted gold films
Dane BadawczeGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
Oxidation of silver nanostructures
Dane BadawczeSilver nanostructures were prepared on Si substrate. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma. The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1 , and the incident power was in the range of 30–40 W. The layer thickness...
-
XRD for molybdenum sulfide modified with nickel or platinum nanoparticles
Dane BadawczeThe presented data showcases the results of XRD analysis conducted on molybdenum sulfide modified with nickel or platinum nanoparticles . The MoS2 was prepared on the TiO2 nanotube substrates via a facile hydrothermal method, followed by the deposition by magnetron sputtering of Ni or Pt nanoparticles on the MoS2 surface. Structural characterization...
-
SEM inwestigation of the silver nanostructures
Dane BadawczeSilver thin films with a thickness of 1nm, 3nm, 5nm, 7nm and 9nm were deposited by a table-top magnetron sputtering unit in a pure argon plasma from a high-purity silver target. Silicon wafers was used as a substrates. As-deposired films were annealed in Ar atmosphere at 550 Celsius degree for 15 minutes.As a result of annealing, Ag nanostructures formed...
-
Luminescence properties of TeOx-Eu thin films
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Tb thin films
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Dy thin films
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
L-Homoserine O-acetyltransferase (CaMet2p) activity and inhibition
Dane BadawczeThe dataset contains the description of methodology and data files with the results obtained spectrophotometrically at 412 nm to determine the rate of fungal enzyme activity. The goal of the study was to obtain conditions optimal for L-homoserine O-acetyltransferase (Met2p) activity as well as evaluation of inhibitory potential of commercially available...
-
SEM micrographs of vanadium oxide nanostructures obtained by V2O5 recrystallization at 1000°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of vanadium oxide nanostructures on quartz glass and silicon substrates obtained by recrystallization of V2O5 thin films at 1000°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
SEM micrographs of vanadium oxide nanostructures obtained by V2O5 recrystallization at 800°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of vanadium oxide nanostructures on quartz glass and silicon substrates obtained by recrystallization of V2O5 thin films at 800°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
SEM micrographs of vanadium oxide nanostructures obtained by V2O5 recrystallization at 1200°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of vanadium oxide nanostructures on quartz glass and silicon substrates obtained by recrystallization of V2O5 thin films at 1200°C under synthetic air. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials.
-
Luminescence properties of TeOx-Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of dysprosium ions were added, the nitrates were used as a source of rare-earth ions....
-
Luminescence properties of TeOx-Tb thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Tb thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of terbium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Luminescence properties of TeOx-Eu thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-Eu thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of europium ions were added, the nitrates were used as a source of rare-earth ions. The...
-
Electrical measurements of the dewetting of metal thin films
Dane BadawczeIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
XPS measurements of the Fe-Pb-Si based glass
Dane BadawczeGlass samples with nominal compositions of xFe2O3-(50-x)PbO–50SiO2, where x = 12.5, 15, 17.5 (mol%) were prepared. Analytical grade substrates were used: Fe2O3, SiO2, and PbO. The appropriate amounts of reagents were mixed in an agate mortar. The powders obtained were melted in porcelain un-enamelled crucibles in an electric furnace at a temperature...
-
Nanoindentation tests of the hydroxyapatite composite coatings applicated on titanium alloys by the electrophoretic method
Dane BadawczeCurrently, there are no metal materials that meet all biomechanical and biochemical requirements needed for long life implantable biomaterials. The main purpose of the study was to functionalize the surface of the titanium alloys used in biomaterial implants.
-
Distance measurement by the low coherent interferometer
Dane BadawczeThe obtained data was acquired by the interferometric fiber-optic sensor of distance. The setup was constructed of a broadband light source working at the central wavelength of 1560 nm, an optical spectrum analyzer and a fiber-optic 2x1 coupler (with the power split 50:50). All elements were connected by standard single-mode optical fibers. The measurement...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-2%Eu1.5%Tb1.5%Tm thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-2%Eu1.5%Tb1.5%Tm thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Luminescence properties of TeOx-1%Eu1.5%Tb2.5%Dy thin films annealing under an oxidizing atmosphere
Dane BadawczeThe DataSet contains the emission and excitation spectra of TeOx-1%Eu1.5%Tb2.5%Dy thin films. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Structural investigations of the Al2O3 ultra thin films
Dane BadawczeUltra-thin layers of Al2O3 were deposited by atomic layer deposition (ALD) (Beneq TFS 200 ALD system). This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2...
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
Distance measurement by the low coherent interferometer with NND layer (the source wavelegth 1310 nm)
Dane BadawczeThe obtained data was acquired by the interferometric fiber-optic sensor of distance. The setup was constructed of a broadband light source working at the central wavelength of 1310 nm, an optical spectrum analyzer, and a fiber-optic 2x1 coupler (with the power split 50:50). All elements were connected by standard single-mode optical fibers. The measurement...
-
Comparison of XPS spectra of Ag3d for silver nanostructures and bulk material
Dane BadawczeAg nanostructures were prepared on borosilicate glass (Corning 1737F) and Si substrates. In both cases, the substrateswere cleaned with acetylacetone and then rinsed in ethanol. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Detection of cellulose production capacity of recombinant Escherichia coli strains BL21(DE3) and AAEC191A
Dane BadawczeBacteria that form biofilms generate an extracellular matrix (ECM), where cellulose stands out as a key constituent. An approach for assessing microorganisms' cellulose production involves using calcofluor white staining on colonies. In this method, a fluorescent dye (calcofluor-white) is introduced to a stable YESCA substrate composed of casamino acids,...
-
Plasmon resonance in gold-silver nanoalloys
Dane BadawczeSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Investigation of plasmon resonance in a silver nanoparticles
Dane BadawczeSilver nanostructures were prepared on borosilicate glass (Corning 1737F) substrates. Thin Ag films (1–9 nm thickness) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma (argon, Air Products 99.999%). The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1, and the incident...
-
Imaging and chemical investigation of silver coating
Dane BadawczeThe recovery of silver from materials such as plates, still used in clinical radiography [1], or scrap jewelery is still very popular. The subject of the research, part of which was microscopic imaging, was to recreate the behavior of an electrochemically deposited silver coating. The copper electrodes were covered with a layer of silver obtained from...
-
Activity assay of O-Acetyl-L-homoserine sulfhydrylase (CaMet15p).
Dane BadawczeThe study aimed to obtain conditions optimal for the activity of O-acetyl-L-homoserine sulfhydrylase (CaMet15p) and a method suitable for its measurement. The selection of appropriate reaction conditions included the identification of the reaction buffer and its pH, substrate and enzyme concentrations. The activity of CaMet15p was measured by the detection...
-
Linear and nonlinear impedance of iron containing silicate glasses
Dane BadawczeThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
Nanostructures fabrication with use of electrical AFM litography
Dane BadawczeIn the last 10 years, one of the nanotechnological trends has been observed, consisting in the development of new variants of computer memory systems with high capacity and speed of access, using quantum dots. One of the techniques for creating nanodots and other nanostructures is based on the use of an atomic force microscope acting as a lithographic...
-
Au nanoparticles identifiction with the use of AFM Volta potential mapping
Dane BadawczeThe specific physical, chemical and electrochemical electrical properties of gold nanoparticles have led to their extensive use as high-performance chemical and biochemical sensors. The described properties relate to surface plasmon resonance, fluorescence quenching or enhancement, high electrical conductivity and light scattering. The described nanoparticles...
-
The surface of the sensor used in the analysis of odorous substances
Dane BadawczeHuman industrial activity usually leads to smaller or larger interference with the ecosystem, contributing to changes affecting the quality of life. An example may be the emission of gaseous substances, not necessarily toxic, but due to their intense smell, they can cause discomfort to people exposed to their inhalation. The problem is so important...
-
Raman data of deuterium and hydrogen grown boron-doped diamond
Dane BadawczeRaman spectra were recorded at room temperature using a micro-Raman spectrometer (Invia, Renishaw) equipped with an edge filter with different excitation wavelengths and lasers: UV λ = 325 nm (HeCd), blue λ = 488 nm (Ar+), green λ = 514 nm (Ar+), and IR λ = 785 nm (IR diode) and 50× microscope objective. To avoid sample heating, the radiation power...
-
Surface modifcation of PMMA polymer detected by XPS
Dane BadawczeIn order to obtain the experimental specimens, four PMMA/PC61BM samples with the following mass proportions were prepared: 10%, 20%, 30%, and 40%. In addition, as a reference, a PMMA sample without PC61BM was prepared as well. For the fabrication process, PC61BM 99.5% (Solenne BV), chloroform HPLC (Sigma Aldrich), and PMMA (commercially available...
-
Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Dane BadawczeLinear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO2, 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O, Li2O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered...
-
Selection of material for infiltration of non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ
Dane BadawczeThe porous electrodes used for the infiltration were prepared from A-site non-stoichiometric Sr0.95Ti0.3Fe0.7O3-δ synthesized by the conventional solid state reaction method. Screen printed electrodes (0.5 cm2) on CGO-20 substrate, were fired at 800 °C for 2 hours in an air atmosphere. Infiltration of the scaffolds was performed by a water-based precursor...
-
XPS data of deuterium and hydrogen grown boron-doped diamond
Dane BadawczeThe high-resolution C1s X-ray absorption spectra of BDD@H and BDD@D samples were measured using the facilities of the HE-SGM beamline (HE-SGM) at the BESSY II synchrotron radiation source of Helmholtz–Zentrum Berlin (HZB).[90] The measurements were carried out under ultra-high vacuum conditions: P ≈ 2×10−9 Torr at T = 300 K. The NEXAFS spectra were...
-
Fingerprint structure studies with semi-contact AFM
Dane BadawczeThe work [1] presents many, sometimes even surprising examples of the use of atomic force microscopy in modern forensics. Some of them are projectile tests using the characteristic scratch patterns created by the firing pin on the primer. There are more and more suggestions in the literature for the use of atomic force microscopy in dactyloscopy [2]....