Wyniki wyszukiwania dla: ATMOSPHERIC LIFETIME
-
SPTNO ceramics measured by XPS method
Dane BadawczeSPTNO (Sr-Pr-Ti-Ni-O) ceramic were manufactured by solid state reaction, from oxides compounds. Synthesis conducted in air atmosphere at temperature in a range of 800-900 deg. Chemical composition of prepared materials were measured by XPS (X-Ray photoemision spectroscopy) method. UHV OmicronNanotechnology system with 128 channel Argus hemispherical...
-
SEM inwestigation of the silver nanostructures
Dane BadawczeSilver thin films with a thickness of 1nm, 3nm, 5nm, 7nm and 9nm were deposited by a table-top magnetron sputtering unit in a pure argon plasma from a high-purity silver target. Silicon wafers was used as a substrates. As-deposired films were annealed in Ar atmosphere at 550 Celsius degree for 15 minutes.As a result of annealing, Ag nanostructures formed...
-
XPS study of the NH4-VOx powders
Dane BadawczeVanadium pentoxide samples were prepared by sol-gel method. The starting solution was prepared by mixing vanadium (V) oxytripropoxide (Aldrich) in an anhydrous ethanol as solvent and acetylacetone. By drying the sol at 323 K for 48 h, it transforms via gel into a xerogel powder. Next, the precursor powder was pressed into the disk-shaped pellets. Samples...
-
Data from environmental sensors installed in two locations
Dane BadawczeThe dataset contains data gathered from environmental sensors installed in two locations:
-
DSC measurments of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the thermal behavior of the ammonium vanadate nanostructures obtained by the hydrothermal method with different conditions. Differential scanning calorimetry (DSC) measurement was carried out under an argon atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The results reveal the differences...
-
XRD patterns of VO2 and V6O13 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V6O13 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under a reducing atmosphere (94% Ar, 6% H2) at 500, 600 and 700C for 10h.
-
XRD patterns of V2O5 thin film morphology dependent on substrate types
Dane BadawczeThe DataSet contains the XRD patterns of the V2O5 thin film structure dependent on substrate types. The as-prepared thin films were deposited on alumina, zirconium, zirconium oxide and metallic vanadium substrate, then was annealing under an oxidizing atmosphere at 600C for 10h.
-
XRD patterns of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
XRD patterns of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon atmosphere.
-
Chemical composition of V2O5 nanorods
Dane BadawczeThe DataSet contains the chemical compositions of the V2O5 nanorods on a silicon substrate. The thin films were obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The As-prepared thin films were annealed at 600C under a synthetic air atmosphere.
-
XRD patterns of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the XRD patterns of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (5-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon atmosphere.
-
XRD and electrochemical results for MoO3 films deposited using pulsed laser deposition system
Dane BadawczeThe attached data contains XRD and electrochemical results for MoO3 films deposited on fluorine-doped tin oxide glasses. Films were deposited using a pulsed laser deposition system at different conditions. Part of the samples was deposited at room temperature and then annealed at 575°C for given times (samples labeled PLD_RT_575C_xmin, where x stands...
-
XRD patterns of V2O5 thin films deposited on silicon substrate
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range of 300-600C. The results show that the structure of the films dependent on the annealing temperature.
-
XRD patterns of V2O3 nanostructures
Dane BadawczeThe DataSet contains the XRD patterns of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that crystallinity dependent on the annealing temperature.
-
SEM micrographs of VO2 and V6O13 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V6O13 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under a reducing atmosphere (94% Ar, 6% H2) at 600 and 700C for 10h.
-
SEM micrographs of NH4VO3 crystals - molar concetration factor after annealing
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 nano_crystals obtained by the LPE-IonEx method with different morphology after annealing at 400C under argon atmosphere (with a heating rate of 10 C/min).
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films were deposited on a silicon and quartz glass substrate and were annealing at 1000°C under an argon atmosphere.
-
SEM micrographs of morphology evolution of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-800C. The...
-
Long term measurements of PM1, PM2.5, PM10 and NO2 in open-air at Gdansk (Poland) area using low-cost sensors together with the reference results
Dane BadawczeThe measurements results of open-air measurements made using the following low-cost sensors: particulate matter (PM) sensor SPS30 from Sensirion, NO2 electrochemical sensor SGX-7NO2 from SGX Sensortech, NO2 electrochemical sensor 7E4-NO2 from SemaTech, compact MOS air quality sensor MiCS 2714 from SGX Sensortech, BME280 (Bosch) environmental sensor...
-
XRD patterns of V2O5 thin films deposited on quartz glass
Dane BadawczeThe DataSet contains the XRD patterns of V2O5 thin films deposited on a quartz glass substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range 200-600C. The results show that the structure of the films dependent on the annealing temperature.
-
Electrical measurements of the dewetting of metal thin films
Dane BadawczeIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 700°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 700°C under an argon...
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 1000°C dependent on film thickness
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (2-3 AsP layers) were deposited on a silicon substrate and were annealing at 1000°C under an argon...
-
Nitrogen sorption isotherm for V2CTx
Dane BadawczeData of points for nitrogen sorption isotherm for sample V2CTx (only sorption branch). The V2CTx was prepared via selective etching of aluminium from MAX matrice V2AlC using 50% HF for 96 h at room temperature.
-
SEM micrographs of morphology evolution of VO2 and V2O3 thin films obtained at 500°C
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of VO2 and V2O3 thin films obtained by the sol-gel method. The information about sol synthesis is described in the Journal of Nanomaterials. The thin films with different thicknesses (3-9 AsP layers) were deposited on a silicon substrate and were annealing at 500°C under an argon...
-
Twenty years' (1996-2016) tropospheric parameters for selected EPN stations derived from GPS double-difference processing
Dane BadawczePropagation of global navigation satellite systems (GNSS) signals through the Earth’s atmosphere is affected by its physical properties. Both hydrostatic and wet part of the atmosphere (mostly related with troposphere) causes delays of GNSS signal, which usually are expressed in the zenith direction (zenith hydrostatic delay - ZHD, and zenith wet delay...
-
Twenty years' (1996-2016) tropospheric parameters for selected EPN stations derived from GPS precise point positioning
Dane BadawczePropagation of global navigation satellite systems (GNSS) signals through the Earth’s atmosphere is affected by its physical properties. Both hydrostatic and wet part of the atmosphere (mostly related with troposphere) causes delays of GNSS signal, which usually are expressed in the zenith direction (zenith hydrostatic delay - ZHD, and zenith wet delay...
-
SEM micrographs of morphology evolution of V2O5 thin films on quartz glass
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin films deposited on a quartz glass substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range 200-600C. The results show that the morphology of the films dependent on the annealing temperature.
-
SEM micrographs of morphology evolution of V2O3 nanostructures
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The xerogel powder was annealing under a reducing atmosphere (94% Ar, 6% H2) in the temperature range 350-700C. The results show that the morphology dependent on the annealing temperature.
-
SEM micrographs of V2O5 thin film morphology dependent on substrate types
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin film morphology dependent on substrate types. The as-prepared thin films were deposited on alumina, zirconium, zirconium oxide and metallic vanadium substrate, then was annealing under an oxidizing atmosphere at 600C for 10h. The results show that the morphology of...
-
SEM micrographs of morphology evolution of V2O5 thin films on silicon substrate
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 thin films deposited on a silicon substrate. The as-prepared thin films were annealing under an oxidizing atmosphere in the temperature range 250-600C. The results show that the morphology of the films dependent on the annealing temperature.
-
The XPS spectra of Ce0.8Ni0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Ni0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XPS spectra of Ce0.8Cu0.2O2 prepared using microemulsion method
Dane BadawczeThe dataset includes XPS spectra of Ce0.8Cu0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
Plasmon resonance in a TiO2-Au NPs structures
Dane BadawczeInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
The XPS spectra of LSCNT sintered at 1200C
Dane BadawczeThe dataset includes XPS spectra of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini). The XPS spectra were collected for all species.
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/1%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/1%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of CeO2/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of CeO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
Investigation of the uniformity of TeO2:Eu layer
Dane BadawczeTeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by XPS method. Te-Eu mosaic target with diameter of 50.8 mm was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the deposition chamber was below 0.2 Pa and substrate was heated at 200 oC during...
-
The topography of carbon black-polylactide composite 3D printed electrodes after femtosecond laser ablation
Dane BadawczeThis dataset contains a series of scanning electron microscopy images revealing the topography of 3D printed carbon black-polylactide composite electrodes after laser ablation with a femtosecond laser. Different laser powers were investigated, namely: 10%, 25%, 50%, 75% and 100%. The CB-PLA electrodes were 3D printed using an Ender printer. Femtosecond laser NKT Photonics, Origami XP parameters: power at 100%...
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
Thermal behavior of (NH4)V4O10xH2O
Dane BadawczeThe DataSet contains the results of the thermal behavior of the (NH4)V4O10xH2O obtained by the hydrothermal method using different precursors: microstructured (commercially available) or nanostructured. The information about samples synthesis is described in the Materials.
-
The XPS spectra of AlOOH/5%Cu prepared using wet impregnation method
Dane BadawczeThe dataset includes XPS spectra of AlOOH/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
Long-term hindcast simulation of water temperature and salinity in the Baltic Sea
Dane BadawczeThe dataset contains the results of numerical modelling of water temperature and salinity over a period of 50 years (1958-2007) in the Baltic Sea. A long-term hindcast simulation was performed using a three-dimensional hydrodynamic model PM3D (Kowalewski and Kowalewska-Kalkowska, 2017), a new version of the M3D model (Kowalewski, 1997). The hydrodynamic...
-
FTIR spectra of VO2 and V2O3 nanostructures
Dane BadawczeThe DataSet contains the FTIR spectra of VO2 and V2O3 nanostructures obtained by the sol-gel with different reaction conditions. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The xerogel powder was annealing under argon atmosphere in the temperature range 400-1000C. The results show that the morphology...
-
Oxidation of silver nanostructures
Dane BadawczeSilver nanostructures were prepared on Si substrate. Thin Ag films (2 and 6 nm thickness) were deposited using a tabletop dc magnetron sputtering coater (EM SCD 500, Leica) in pure Ar plasma. The Ag target was of 99.99% purity, the rate of layer deposition was about 0.4 nm·s−1 , and the incident power was in the range of 30–40 W. The layer thickness...
-
The XRD diffraction patterns of as-preapred (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9FexTi(1-x)O3-δ (x=0.1, 0.2 and 0.3) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials
Dane BadawczeThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials
Dane BadawczeThe ((La0.3Sr0.6Ce0.1)0.9Ni0.05Me0.05Ti0.9O3-δ (Me= Co, Fe, Cu) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid...