Cyclic voltammetry curves of the V2O5 nanorods (Na-ion batteries)
Open Research DataThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanorods obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanorods (Li-ion batteries)
Open Research DataThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Na-ion batteries)
Open Research DataThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Na/Na+ at a scan rate of 1 mV/s. As an electrolyte 1M NaPF6 was applied.
-
Cyclic voltammetry curves of the V2O5 nanocrystals (Li-ion batteries)
Open Research DataThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Cycling performances of the V2O5 nanorods as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. The...
-
Cycling performances of the V2O5 nanocrystals as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 and 2C current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1. ...
-
Cycling performances of the V2O5 nanostructures as cathode material in Na-ion batteries
Open Research DataThe DataSet contains the next one hundred galvanostatic charge/discharge curves of the V2O5 nanostructures with different morphology obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with C/5 current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here...
-
SEM micrographs of V2O5 nanorods as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 nanorods as cathode materials before and after the galvanostatic charge/discharge curves.
-
Rate performance of the V2O5 nanocrystals as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanocrystals obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
SEM micrographs of V2O5 nanocrystals as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of V2O5 nanocrystals as cathode materials before and after the galvanostatic charge/discharge curves.
-
Rate performance of the V2O5 nanorods as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the galvanostatic charge/discharge curves of the V2O5 nanorods obtained by the sol-gel method. The battery tests of the samples were performed using the Atlas-Sollich 0961 (Atlas-Sollich, Poland) with different current densities in the voltage range between 2.0 V and 4.0 V vs. Li/Li+. Here 1C is 294 mAh g-1.
-
Rate performance of (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method under an initial pressure of 50 bar ((NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities in the voltage...
-
Rate performance of mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O as cathode material in Li-ion batteries
Open Research DataThe DataSet contains the galvanostatic charge/discharge curves of the ammonium vanadate nanostructures obtained by the hydrothermal method without initial pressure (mixture (NH4)2V6O16 and (NH4)2V10O25·8H2O). The battery tests of the samples were performed using the ATLAS 0961 MBI multichannel battery testing system with different current densities...
-
Total Ionization Cross Sections of Selected Amino Acids
Open Research DataThe data set contains tabulated values of cross-sections for a single electron-impact ionization of selected amino acids (glycine, alanine, phenylalanine, proline and tryptophan) calculated using binary-encouter-Bethe method. The data have been published in graphical form (figure 1) in the following paperA.M. Sheer, P. Mozejko, G.A. Gallup, P.D. Burrow...
-
Structure of ammonium vanadate synthesis by LPE-IonEx method
Open Research DataThe DataSet contains the XRD patterns, FTIR spectra of NH4VO3 crystals with different morphology obtained by the LPE-IonEx method.
-
THERMION-C2S_10 Ionic thermoelectri effect in the phase transition in Cu2Se
Open Research DataThe dataset contains results of measurements of the ionic thermoelectric effect in copper selenide with Cu1.99Se and Cu1.8Se compositions. X-Ray diffraction data, SEM images and EDX spectra of the samples are also in the dataset.
-
Influence of the presence of rhamnolipids and ionic cross-linking conditions on the mechanical properties of alginate hydrogels.
Open Research DataThe dataset contains the results of determination the effect of rhamnolipids concentration, calcium chloride concentration and ionic cross-linking time on the mechanical properties of alginate hydrogels prepared by immersing the alginate mixture limited by the dialysis membrane in an appropriate cross-linking solution containing calcium ions. The mechanical...
-
Optical properties TeOx gels doped with the rare-earth ions
Open Research DataThe DataSet contains the UV-Vis spectra of TeOx gels doped with the rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of the rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Tellurite based glass doped by Eu3+ ions - XPS measurements
Open Research DataEu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after...
-
Optical properties of TeOx gels doped with a mix of rare-earth ions
Open Research DataThe DataSet contains the UV-Vis spectra of the TeOx gels doped with a mix of rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the different molar concentration of rare-earth ions was added, nitrates were used...
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Open Research DataElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
Structural and luminescence properties of B2O3-Bi2O3+10AlF3 glasses doped with Eu3+/Dy3+ ions
Open Research DataThe attached data contains the results of measurements of B2O3-Bi2O3 and B2O3-Bi2O3+10AlF3 glasses doped with Eu3+ and Dy3+ ions in different molar ratios. Glasses were synthesized by the melt quenching technique. On their basis, the structural, optical, and luminescence properties of synthesized samples were characterized. The dataset includes XRD,...
-
Luminescence and FTIR measurements of B2O3-Bi2O3-SrF2 glass and glass-ceramics doped with Eu3+ ions
Open Research DataLuminescence and FTIR measurements of B2O3-Bi2O3-xSrF2+2Eu (x=10,20) glass and glass-ceramics. The emission and excitation spectra of the samples depend on the composition and annealing time.
-
XRD, DTA and luminescence measurements of B2O3-Bi2O3-AlF3 glasses doped with Eu3+, Tb3+ and Tm3+ ions
Open Research DataThe DataSet contains the XRD,DTA and luminescence measurements for the B2O3-Bi2O3-AlF3 glass system. Samples were prepared by the conventional melt quenching technique. Starting materials were melted in porcelain crucibles at 950 oC for 20 min. XRD and DTA data were collected for 50B2O3-50Bi2O3,45B2O3-45Bi2O3+10AlF3 and 40B2O3-40Bi2O3+20AlF3 glasses....
-
Raman data of based on BDD, Mn-BDD, Mn-BDD(AN) electrodes
Open Research DataRaman spectra of samples : ion implanted BDD (Mn-BDD) films; prepared by high dose (1015-1017 ions/cm2) Mn ion implantation and post-annealing treatment.
-
Depth profile of the gold-silver bimetallic structures
Open Research DataSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
Depth profile of the chemical composition of the Au-Ag multilayers
Open Research DataSilver and gold multilayers were deposited on a silicon substrate by magnetron sputtering method. Both type, Au and Ag thin films had 2 nm of thickness. Totally structure had thickness of 6 nm (Au-Ag-Au). That prepared multilayers were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching...
-
Depth XPS profile of Fe-S layers on a titanium substrate
Open Research DataDepth XPS profile of Fe-S layers on a titanium substrate was measured. Material was etched by Argon ion gun and measured by XPS method. For each sample, three times per 10 minutes each was sputtered.
-
Depth XPS profile of vanadium pentoxide
Open Research DataVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
The luminescence study of SrAl11.88−xGaxO19:0.12Cr3+ coumpounds.
Open Research DataPortable near-infrared (NIR) light sources are in high demand for applications in spectroscopy, night vision, bioimaging, and many others. Typical phosphor designs feature isolated Cr3+ ion centers, and it is challenging to design broadband NIR phosphors based on Cr3+–Cr3+ pairs. Here, we explore the solid-solution series SrAl11.88–xGaxO19:0.12Cr3+...
-
Valorisation of bioplastics synthesised by liquefaction of celluloseusing hetero- and homogeneous catalysts
Open Research DataThe purpose of the present study was to test the effectiveness of a heterogeneous catalyst such as Nafion ion-exchange resin on the cellulose liquefaction process. The results obtained were compared with the bio-polyols obtained in a conventional way, using a homogeneous catalyst (sulfuric acid (VI)). Depending on the catalyst used and the temperature...
-
Results of the effect of mixtures of ketoprofen with three cations on the germination of Sorghum bicolor (sorghum) seeds
Open Research DataThe research data includes an attempt to verify whether the addition of cations (sodium, ammonium and potassium) at levels found in the environment would affect the toxicity of pharmaceuticals to Sorghum Bicolor grain. Ion concentrations were selected based on studies of water samples collected in water bodies receiving wastewater from wastewater treatment...
-
Results of the effect of mixtures of ketoprofen with three anions on the germination of Sorghum bicolor (sorghum) seeds
Open Research DataThe research data includes an attempt to verify whether the addition of anions (bromide, chloride and fluoride) at levels found in the environment would affect the toxicity of pharmaceuticals to Sorghum Bicolor grain. Ion concentrations were selected based on studies of water samples collected in water bodies receiving wastewater from wastewater treatment...
-
The chemical and mechanical pressure influence on chromium luminescence
Open Research DataIn this study, we aim to compare the changes in the luminescence properties of Ga2O3:Cr3+ modified by Al or Sc ion substitution (chemical pressure) and hydrostatic pressure. We find the same behavior for Ga2–xAlxO3:Cr3+ and different behavior for Ga2–xScxO3:Cr3+ in terms of the optical properties under chemical and mechanical pressure. We consider Al...
-
Investigation of the uniformity of TeO2:Eu layer
Open Research DataTeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by XPS method. Te-Eu mosaic target with diameter of 50.8 mm was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the deposition chamber was below 0.2 Pa and substrate was heated at 200 oC during...
-
Raman spectroscopy analysis of poly(lactic acid)-carbon black composite treated by femtosecond laser
Open Research DataThe dataset contains the Raman spectroscopy measurements of commercially available carbon black-filled poly(lactic acid) 3D printed electrodes after femtosecond laser ablation. These results were utilized in the manuscript published in Electrochimica Acta: 10.1016/j.electacta.2022.140288
-
Thermal behaviour of NH4VO3 microcasketoids
Open Research DataThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microcasketoids under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 nanoflowers
Open Research DataThe DataSet contains the results of the thermal behavior of the ammonium metavanadate nanoflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 elongated microcrystals
Open Research DataThe DataSet contains the results of the thermal behavior of the ammonium metavanadate elongated microcrystals under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass...
-
Thermal behaviour of commercial avaible NH4VO3
Open Research DataThe DataSet contains the results of the thermal behavior of the commercially available ammonium metavanadate (CAS 7803-55-6) under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also...
-
Thermal behaviour of NH4VO3 microflowers
Open Research DataThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of ammonium vanadate nanocrystals
Open Research DataThe DataSet contains the thermal behavior of the ammonium vanadate nanostructures obtained by the hydrothermal method with different conditions. Thermogravimetric analysis (TG) was carried out under an argon atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Chromium Cluster Luminescence: Advancing Near‐Infrared Light‐Emitting Diode Design for Next‐Generation Broadband Compact Light Sources
Open Research DataIn modern technology devices, an energy-saving miniature near-infrared (NIR) light source plays a critical role in non-destructive, non-invasive sensing applications and further advancement of technology. This dataset reports the broadband NIR luminescence of Cr3+ clusters for designing phosphor-converted NIR light-emitting diodes as an alternative...
-
Depth profile of the composition of 8 nm Al2O3 thin film
Open Research Data8 nm layer of aluminum oxide (Al2O3) was deposited by ALD method on a s. Atomic layer deposition provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. To investigate the profile of concenration of...
-
Opposite pressure impact on electron-phonon coupling in Eu2+ and Ce3+ doped AlN
Open Research DataThis data analyzes the influence of pressure on electron–lattice interactions in the 5d excited states of Ce3+ and Eu2+ in the AlN host based on pressure-dependent photoluminescence and photoluminescence excitation spectra. High-pressure measurements on AlN samples doped with Eu2+ and Ce3+ ions reveal that the Stokes shift increases with pressure for...
-
Influence of the annealing condictions on the chemical structure of LaBaGdCo ceramics
Open Research DataCeramic samples based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by solid state reaction. After sintring in a furnance, samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology. XPS analysis...
-
The profiles and spectrum of aqua solution of tannic acid by HPLC-DAD-MS analysis.
Open Research DataThe profiling of tannic acid is determined by examining the content and proportion / ratio of gallotannins [Aras et al. 2016, Clifford et al. 2007, Gauri et al. 2012, Nishizawa et al. 1982]. In order to check the ion mass distribution (TIC) in an aqueous solution of commercial tannic acid, a direct sample injection (TA) was performed into the mass spectrometer....
-
Valence state of Manganium in a MnCoO ceramics
Open Research DataManganium -cobalt based ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. In order to determine valence states of the Mn, X-Ray photoemission...
-
Lanthanum investigations in ceramics annealed in a dry and wet atmosphere
Open Research DataCeramics based on Barium, Lanthanum, Gadolinium and Cobaltium were produced by standard solid state reaction from oxides and carbonate powders. After sintring, samples were annealed for 2 hours or 72 hours at 300 Celsius degree in a both: wet and dry atmosphere. Results of annealing on a chemical composition and valence state of lanthanum were observed...
-
Potential energy curves of the doublet Sigma gerade plus states of the Lithium dimer cation
Open Research DataAdiabatic potential energy curves of the doublet Sigma gerade plus (dSg+) states have been calculated for the Lithium dimer cation (Li2+). The results of the ground state and four excited states of the symmetry doublet Sigma gerade plus have been obtained by the nonrelativistic multireference configuration interaction (MRCI) method used with pseudopotentials...