Rok 2016
-
Novel method for metal-oxide glass composite fabrication for use in thermoelectric devices
PublikacjaA novel method for thermoelectric materials fabrication using a reduction of oxide precursors in hydrogen was reported. On the example of Bi-Sb, Bi-Sb-Te and Te-Ag-Ge-Sb compounds it was shown that this simple and easy method is suitable for fabrication of two-, three- and even multicomponent thermoelectric materials. It allows controlling a composition, microstructure and even type a of electrical charge carriers. As a result...
-
Structure and thermoelectric properties of Te/Ag/Ge/Sb (TAGS) materials obtained by reduction of melted oxide substrates
PublikacjaThe Ge0.77Ag0.1Sb0.13Te1alloy was fabricated by a novel two step route. For that purpose firstly the oxide reagents were melted at high temperature and quenched into pellets. After that pellets were milled to the powder and then reduced in hydrogen at various temperatures and for various periods of time. Energy dispersive X-ray analysis indicated the possibility of successful fabrication of stoichiometric thermoelectric materials...
-
Synthesis and structural properties of (Y, Sr)(Ti, Fe, Nb)O3−δ perovskite nanoparticles fabricated by modified polymer precursor method
PublikacjaThe yttrium, iron and niobium doped-SrTiO3 powders have been successfully fabricated by a modified low–temperature synthesis method from a polymer complex. The usage of strontium hydroxide precursor instead of conventional strontium nitrate or strontium carbonate provides to the possibility of significant decrease of annealing temperature. It allows to prepare a material with sphere-shape grains of nanometric size (15–70 nm). The...
-
Thermoelectric properties of bismuth-antimony-telluride alloys obtained by reduction of oxide reagents
PublikacjaThe BieSbeTe alloys with different Bi/Sb/Te ratio were fabricated by an innovative method. For that purpose the oxide reagents were melted at high temperature, then quenched to form pellets, milled to a powder and finally reduced in hydrogen at various temperatures. Complex structures consisting of connected thin layers forming a continuous path between nano- and micrometer size grains have been obtained. The electrical conductivity,...
Rok 2012
-
Optimization of microstructure and properties of acceptor-doped barium cerate
PublikacjaThe presented research concerns acceptor doped barium cerate and the attempts of improvement of its production method that would allow obtaining the solid electrolyte characterized by the particular properties. The authors suggest combining two production methods, molten salt synthesis and self-combustion, in order to achieve the compound material that has some of the advantages of both of the initial methods. An impact of nickel...
-
Perovskites in Solid Oxide Fuel Cells
PublikacjaPrzeglądowa publikacja dotycząca wykorzystania ceramicznych materiałów perowskitowych w tlenkowych ogniwach paliwowych.
-
Solid Oxide Fuel Cells with Ni infiltrated perovskite anode
PublikacjaNiobium-doped strontium titanate was used as the anode for a solid oxide fuel cell. Electrolyte-supported cells were prepared with pure perovskite and composite perovskite–yttria–stabilized-zirconia (YSZ) anodes. Fuel cell tests demonstrated significant improvement in power density after infiltration with a small amount of Ni. The obtained values of power densities are comparable with conventional Ni/YSZ cermet anode. In addition,...
-
Solid oxide fuel cells with Ni-infiltrated perovskite anode
PublikacjaWytworzono próbki na bazie tytanianu strontu domieszkowanego niobem i przebadano wpływ nasączania niklem na właściwości tych materiałów.
-
Structural and electrical properties of Sr(Ti,Fe)O3-δ materials for SOFC cathodes
PublikacjaW niniejszym artykule, dwa związki SrTiO3 domieszkowanego Fe przebadano pod względem przydatności na katody w tlenkowych ogniwach paliwowych. SrTi0.65Fe0.35O3 i SrTi0.5Fe0.5O3 zostały przebadane pod względem reaktywności chemicznej z elektrolitem YSZ. Stwierdzono, że przewodnictwo elektryczne tych związków jest stosunkowo niskie: 0,4 S/cm i 2 S/cm odpowiednio dla STF35 i STF50.
-
The comparison of SrTi0.98Nb0.02O3–δ-CeO2 and SrTi0.98Nb0.02O3–δ-YSZ composites for use in SOFC anodes
PublikacjaComposites of Nb-doped strontium titanate mixed with yttria-stabilized zirconia or cerium oxide in 50:50, 70:30 and 85:15 weight ratios were evaluated as possible anode/electrolyte interface materials for solid oxide fuel cells in terms of chemical compatibility, electrical conductivity and mechanical properties. It has been shown that composite samples prepared by typical powder-mixing methods remain single-phase up to 1400°C....
-
The comparison of SrTi0.98Nb0.02O3-δ-CeO2 and SrTi0.98Nb0.02O3-δ-YSZ composites for use in SOFC anodes
PublikacjaWytworzono i przebadano właściwości strukturalne i elektryczne kompozytów SrTi0.98Nb0.02O3-δ-CeO2 i SrTi0.98Nb0.02O3-δ-YSZ. Przeprowadzono testy materiałów zastosowanych jako anody w tlenkowych ogniwach paliwowych.
Rok 2017
-
Oxygen biosensor based on carbon nanotubes directly grown on graphitic substrate
PublikacjaFilms of carbon nanotubes were synthesized on the graphitic substrates by CVD method in the presence of catalyst. Two different catalysts were used, that is nickel and iron, supported on graphitic substrates. The as-obtained nanotubes were analyzed by SEM imaging with EDX and Raman spectroscopy. The results revealed their multi-walled morphology. Free radical reaction was carried out in order to chemically functionalize synthesized...
-
Structure and electrical properties of Y, Fe-based perovskite mixed conducting composites fabricated by a modified polymer precursor method
PublikacjaIn this work, samples of Y0.07Sr0.93Ti1-xFexO3-d with 20, 40, 60 and 80 mol% of iron amount were prepared by a low-temperature polymer precursor method. The SEM-EDS analysis proved that analyzed Y0.07Sr0.93Ti1-xFexO3-d samples were composites of two Ti- and Fe-rich perovskite samples. This kind of composite consists of two phases in which one has a good ionic and the other electronic conductivity, which makes such a composite a...
-
Structure and thermoelectric properties of Cs-Bi-Te alloys fabricated by different routes of reduction of oxide reagents
PublikacjaCesium-bismuth-telluride polycrystalline materials were fabricated using a cost-effective method based on a reduction of oxide reagents, leading to a production of a material with good thermoelectric properties. Several samples with various initial stoichiometry were prepared by melting of oxide powders at 1050 °C, quenching, milling to powders and then reducing in pure hydrogen at 400 °C. Another concept was to obtain the CsBi4Te6...
Rok 2015
-
Planowanie eksperymentu
PublikacjaW pracy przedstawiono schemat postępowania przy planowaniu eksperymentu naukowego
-
Structure and thermoelectric properties of Bi–Te alloys obtained by novel method of oxide substrates reduction
PublikacjaA novel method of thermoelectric materials fabrication has been developed. Oxide reagents have been melted at high temperature in air, quenched, milled to powder and reduced in hydrogen to form Bi–Te alloys. Structural and thermoelectric properties of samples have been investigated depending on initial composition and temperature of reduction process. Sample 25Bi2O3–75TeO2 reduced at 340 °C for 10 h has been found to be a p-type...
Rok 2002
-
Positron Annihilation Studies of Silicon Oxides and Oxygen Precipitates in Silicon
PublikacjaTechniki pozytonowe dają możliwości badania defektów i zmian strukturalnych nie obserwowanych innymi metodami. W tej pracy zastosowano 3 różne techniki pozytonowe do badania zmian strukturalnych i tworzenia wydzieleń SiOx w krzemie.
Rok 2004
-
Positron-annihilation monitoring of reduction processes in conducting glasses.
PublikacjaW publikacji podano wyniki badań metodą anihilacji pozytronów szkieł bizmutowo-krzemianowych, bizmutowo-germanianowych i ołowiowo-krzemianowych. Stwierdzono istnienie defektów wywołanych redukcją w atmosferze wodoru. Przeprowadzono analizę głębokości występowania defektów oraz ich rozmiarów.
Rok 2008
-
Protective coatings for stainless steel for SOFC applications
PublikacjaW pracy przedstawiono badania związane z warstwami antykorozyjnymi stali nierdzewnych stosowanych w tlenkowych ogniwach paliwowych. Warstwy przygotowana z użyciem prekursorów polimerowych na bazie Y i Co. Użyta stal to Crofer 22 APU.
-
Structure and electric conductivity of reduced lead-germanate, bismuth-germanate and bismuth-silicate glasses modified with potassium
PublikacjaZbadano szkła germanianowo-ołowiowe i krzemianowo+bizmutowe. Warstwy metalicznych granul wytwarzano w nich poprzez redukcję powierzchni w atmosferze wodoru. Praca dotyczy wpływu potasu na właściwości szkła. Przeprowadzono badania metodami mikroskopii sił atomowych, DSC oraz pomiary przewodności elektrycznej. Stwierdzono, że obecność potasu poprawia mechaniczne i technologiczne właściwości szkła.
Rok 2022
-
Pyrolysis of RDF and Catalytic Decomposition of the Produced Tar in a Char Bed Secondary Reactor as an Efficient Source of Syngas
PublikacjaOne of the technical limitations of refuse-derived fuel (RDF) pyrolysis is the high content of tar in its gas products. In order to resolve this problem, a two-stage RDF pyrolysis with a catalyst based on char from RDF pyrolysis is proposed. This paper presents the results of municipal waste pyrolysis beginning in an oven heated to 480 °C and ending with catalytic tar cracking carried out in the temperature range from 800 to 1000...
Rok 2003
-
Structural and electrical transport studies of reduced in hydrogen surfaceof bismuth germanate glass
PublikacjaOtrzymano nanostruktury krystalicznego bizmutu w matrycy szkła germanowegooraz warstwę nanostruktur krystalicznego bizmutu na powierzchni redukowanegow atmosferze wodoru szkła Bi0.33Ge0.67O1.83. Zaproponowano prosty model bu-dowy zredukowanych szkieł bizmutowo-germanowych potwierdzony wynikami badańAFM i XRD. Zbadano wpływ czasu i temperatury redukcji oraz topnienia bizmu-tu na własności elektryczne badanych szkieł. Przeanalizowano...
-
Structural studies and melting of bismuth nanocrystals in reduced bismuthgermanate and bismuth silicate glasses.
PublikacjaOtrzymano nanostruktury krystalicznego bizmutu w matrycy XO2 (X=Si,Ge) oraz warstwę nanostruktur krystalicznego bizmutu na powierzchni redukowanych w atmosferze wodoru szkieł Bi0.33Ge0.67O1.84 i Bi0.57Si0.43O1.72. Kompozyt Bi-szkło badano metodą DSC, XRD oraz AFM. Zaobserwowano zmniejszenie temperatury topnienia nanokrystalicznego bizmutu znajdującego się w matrycy szkła z 544 K do 387 K oraz do 502 K w przypadku powierzchniowej...
-
Structural studies of bismuth nanocrystals embedded in SiO2 or GeO2 matrices.
PublikacjaW wyniku wygrzewania w atmosferze wodoru szkieł bizmutowych i germanowych otrzymano warstwę nanogranul bizmutu w otoczeniu amorficznej matrycy oraz powierzchniową warstwę bizmutowych granul. Grubość i struktura tak otrzymanych warstw silnie zależy od czasu i temperatury redukcji.
-
Structure and morphology of hydrogen reduced surface of bismuth germanateand bismuth silicate glasses.
PublikacjaOtrzymano nanostruktury krystalicznego bizmutu w matrycy XO2(X=Si,Ge) oraz warstwę nanostruktur krystalicznego bizmutu na powierzchni redukowanych w atmosferze wodoru szkieł Bi0.33Ge0.67O1. i Bi0.57Si0.43O1.72. Zaproponowano prosty model budowy zredukowanych szkieł bizmutowo-germanowych potwierdzony wynikami badań AFM i XRD. Obserwowane zmiany przewodnictwa elektrycznego redukowanych szkieł wyjaśniono na podstawie modelu.
-
Structure changes in (Bi-Pb)-Sr-Ca-Cu-O glass ceramics during the first minutes of crystallization.
Publikacja(Bi0.8Pb0.2)4Sr3Ca3Cu4Ox szkło otrzymano standardową metodą chłodzenia stopionych substratów. Częściowo skrystalizowane próbki otrzymano poprzez wygrzewanie szkła w temperaturze między 700stC i 870stC. Obecność faz krystalicznych badano metodą dyfrakcji rentgenowskiej w temperaturze pokojowej oraz w temperaturze krystalizacji. Stwierdzono obecność faz nadprzewodzących (Bi0.8Pb0.2)2Sr2CuOx, (Bi0.8Pb0.2)2Sr2CaCu2Ox i (Bi0.8Pb0.2)2Sr2Ca2Cu3Ox...
Rok 2010
-
Structure and electric properties of double magnesium zirconium orthophosphate
PublikacjaPublikacja przedstawia wyniki pomiarów elektrycznych i strukturalnych ortofosforanu magnezowo-cyrkonowego.
-
Structure and electrical properties of ceramic proton conductors obtained with molten-salt and solid-state synthesis methods
PublikacjaPublikacja omawia wyniki badań niobanu lantanu domieszkowanego akceptorowo pod kątem właściwości elektrycznych i strukturalnych.
-
Synthesis of acceptor-doped Ba-Ce-Zr-O perovskites
PublikacjaPublikacja przedstawia wyniki badań stukturalnych i elektrycznych domieszkowanego akceptorow cerianu baru.
Rok 2009
-
Structure and electrical properties of nitrided NbN-TiN sol-gel derived films
PublikacjaW pracy przedstawiono rezultaty badań struktury oraz właściwości elektrycznych warstw NbN-TiN (o różnym stosunku molowym NbN/TiN)otrzymanych w wyniku termicznego azotowania warstw tlenkowych otrzymanych metodą zol-żel. Badania struktury przeprowadzono metodami AFM, XRD oraz XPS. Wynika z nich, iż głównymi fazami w wartstwach są NbN i TiN o rozmiarach ziaren około 100 nm. Jednakże zaobserwowano również istnienie niewielkiej ilości...
Rok 2018
-
Structure and thermoelectric properties of bismuth telluride—Carbon composites
PublikacjaCarbon nanotubes and amorphous carbon have been introduced into a bismuth telluride matrix (0.15 and 0.30 wt.% ratio) to investigate the influence of the carbon on the composite’s thermoelectric properties. Composites with well-dispersed additives have been obtained by sonication and ball-milling methodology. Carbon nanotubes and an amorphous carbon addition led to a decrease in electric conductivity from 1120 S/cm to 77 S/cm....
Rok 2021
-
Structure and thermoelectric properties of nickel-doped copper selenide synthesised in a hydrogen atmosphere
PublikacjaNickel-doped copper selenide—Cu2-xNixSe (x = 0; 0.01; 0.02; 0.03)—materials with high thermoelectric properties were synthesised through reduction of reagents in hydrogen. The impact of the nickel content on both the microstructure and thermoelectric properties was examined. The nickel-doped samples’ microstructure differed significantly from pristine copper selenide. Besides Cu2Se, copper precipitations were present in the materials....
-
The unstable thermoelectric effect in non-stoichiometric Cu2Se during the non-equilibrium phase transition
PublikacjaThe superionic α ↔ β phase transition in Cu1.96Se thermoelectric material is investigated by means of thermal analysis (DSC) and measurements of Seebeck coefficient and electrical conductivity. Results of the DSC measurements with 1–10 K/min heating and cooling rates show that the material is close to the equilibrium phase composition during the transformation. However, the kinetic limitation of the process exists, which is indicated...
Rok 2006
-
Superconducting lead granular layer prepared by reducting in hydrogen lead of germanate glass
PublikacjaCienka warstwa granul Pb została wytworzona poprzez wygrzewanie w wodorze, w wysokiej temperaturze. Struktura i nadprzewodzące właściwości warstwy ołowiu zależą od temperatury i czasu redukcji. Artykuł analizuje wpływ warunków redukcji na wytworzoną warstwę granul Pb.
-
Superconducting transition in granular Bi-Sr-Ca-Cu-O superconductors
PublikacjaW układzie(Bi,Pb)-Sr-Ca-Cu-O poprzez krystalizację w fazie stałej można wytworzyć materiały o bardzo różnych właściwościach elektrycznych i nadprzewodzących. W zależności od warunków krystalizacji, można wytworzyć nadprzewodnik o temperaturze krytycznej między 8 a 105 st. K lub materiał nie przechodzący do stanu nadprzewodzącego. Przejście do stanu nadprzewodzacego w materiałach granulastych ma charakter dwustopniowy. Zbadano wpływ...
-
The structure and melting of lead nanocrystalline layer in reduced lead-germanate glass
PublikacjaNanokrystaliczna warstwa granul Pb na powierzchni szkieł ołowiowo-germanianowych została wytworzona poprzez wygrzewanie w wysokich temperaturach, w atmosferze wodoru. Właściwości tej warstwy silnie zależą od temperatury i czasu redukcji. Artykuł prezentuje rentgenowskie i mikroskopowe badania struktury warstwy oraz wpływ topnienia i krzepnięcia granul Pb na jej przewodnictwo.
Rok 2014
-
The properties of reduced Bi-Ge-O glasses for thermoelectric devices
PublikacjaThe bismuth-germanate glasses have been investigated to examine their applicability for thermoelectric devices. In order to increase their electrical conductivity, the 25Bi2O3–75GeO2 glass samples have been reduced at 340-380°C for 10 hours in hydrogen. It has been shown that such heat treatment in H2 leads to the reduction of metal ions Bi3+ and Ge4+ into neutral atoms and the formation of metal grains both in an amorphous glass...
-
The properties of reduced Ge-Sb-O glasses for thermoelectric devices
PublikacjaThe structural and electrical properties of germanium-antimonate glasses after heat treatment in hydrogen have been determined. In the case of 50GeO2-50Sb2O3 glass reduced at 340°C even for less than 1 hour a continuous layer of antimony granules is formed and its electrical properties determine the surface conductivity of the reduced sample. The bulk electrical conductivity at 100°C of this sample was determined as 1000 Scm-1...
-
Wiedza ogólna o eksperymencie naukowym
PublikacjaW pracy przedstawiono podstawowe pojęcia z zakresu metodologii badań w nauce i w technice
Rok 2013
-
YSZ Thin film deposited on porous substrate by spray pyrolysis
PublikacjaIn this work the results of deposition of YSZ layer on a porous substrate using an ultrasonic Spray Pyrolysis are presented.