Wyniki wyszukiwania dla: SURFACE COATING
-
TG analyses - content of SiO2 and TiO2 in polystyrene
Dane BadawczeTG analyses were performed for polystyrene spheres coating by SiO2 and then coating by SiO2-TiO2. Thermal analyses of polystyrene spheres only were also performed. The content of inorganic remaining was used for calculation the quantity of coating SiO2 and TiO2 in the polystyrene spheres.
-
The influence of the Cu2O deposition method on the structure, morphology and photoresponse of the ordered TiO2NTs/Cu2O heterojunction
PublikacjaThe increased interest in highly ordered titania structures exhibiting tubular shape that could be directly formed onto the stable substrate is related with the intensive research on their modification enabling absorption of light within the wide solar spectrum and its further conversion into electric or chemical energy. Among others, formation of uniform 3D heterojunctions based on the TiO2 nanotubes attracts attention since porous...
-
Enhanced electrochemical performance of partially amorphous La0.6Sr0.4CoO3-δ oxygen electrode materials for low-temperature solid oxide cells operating at 400 °C
PublikacjaThis work evaluates partially amorphous La0.6Sr0.4CoO3-δ (LSC) as a potential oxygen electrode for lowtemperature solid oxide cells. LSC was deposited using the spin-coating technique onto Ce0.8Gd0.2O2-δ (CGO) substrates. The optimal oxygen electrode thickness was determined as 500 nm. The electrochemical impedance spectroscopy (EIS) study showed a significant improvement in oxygen reduction/oxidation reaction kinetics when annealing...
-
Degradation of protective coatings in steel chimneys of flue gas desulfurisation system
PublikacjaThis paper presents problems associated with corrosion of steel stacks and changes in philosophy of corrosion protection when implemented into flue gas desulphurization systems. In-situ tests were taken by means of electrochemical impedance spectroscopy at the stack which discharges flue gas before wet lime/limestone desulphurization. A very quick electrolyte absorption by the spherical infill vinylester coating was found using...
-
Deterioration and Protection of Concrete Elements Embedded in Contaminated Soil: A Review
PublikacjaCoating materials are considered one of the most antique materials of human civilization; they have been used for decoration and the protection of surfaces for millennia. Concrete structures—due to their permanent exposure to different types of environments and contaminants—require the use of coatings that contribute to its preservation by reducing the corrosion of its components (steel and aggregates). This article intends to...
-
Mechanical Behavior of Bi-Layer and Dispersion Coatings Composed of Several Nanostructures on Ti Substrate
PublikacjaThree coatings suitable for biomedical applications, including the dispersion coating composed of multi-wall carbon nanotubes (MWCNTs), MWCNTs/TiO2 bi-layer coating, and MWCNTs-Cu dispersion coating, were fabricated by electrophoretic deposition (EPD) on Ti Grade II substrate. Optical microscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and nanoindentation were applied to study topography, chemical, and...
-
Low temperature processed MnCo2O4 and MnCo1.8Fe0.2O4 as effective protective coatings for solid oxide fuel cell interconnects at 750 °C
PublikacjaIn this study two materials, MnCo2O4 and MnCo1.8Fe0.2O4 are studied as potential protective coatings for Solid Oxide Fuel Cell interconnects working at 750 °C. First powder fabrication by a modified Pechini method is described followed by a description of the coating procedure. The protective action of the coating applied on Crofer 22 APU is evaluated by following the area specific resistance (ASR) of the scale/coating for 5500...
-
Comparison of Properties of the Hybrid and Bilayer MWCNTs—Hydroxyapatite Coatings on Ti Alloy
PublikacjaCarbon nanotubes are proposed for reinforcement of the hydroxyapatite coatings to improve their adhesion, resistance to mechanical loads, biocompatibility, bioactivity, corrosion resistance, and antibacterial protection. So far, research has shown that all these properties are highly susceptible to the composition and microstructure of coatings. The present research is aimed at studies of multi-wall carbon nanotubes in three different...
-
The influence of chitosan hydrogel cross-linking by agarose on coating physico-chemical properties
Dane BadawczeThis dataset contains various physicochemical analyses showing the effect of different concentration of chitosan and the cross-linking agent agarose. Each sample is labeled by C and A representing chitosan and agarose concentrations, respectively, while the exact amounts are depicted in the attached table. Fourier-transform infrared (FT-IR) spectroscopy...
-
Stratification of nano-pigments in anti-corrosive coatings by means of magnetic field
PublikacjaThe concept of self-stratification of coatings, although attractive, causes difficulties in its practical use, especially when pigments are added to the resins. An alternative way of obtaining a multilayer structure in a single step was presented. Using the inhomogeneous magnetic field and magnetically active components of the coating, the possibility of vertically graded differentiation of the one layer properties has been verified....
-
Performance of organic coatings upon cyclic mechanical load
PublikacjaA number of engineering structures fail due to the fatigue damage resulting from cyclic mechanical stress. However, as far as organic coatings are concerned this degradation factor remains underestimated. In the paper the authors propose a methodology combining global electrochemical impedance spectroscopy and local atomic force microscopy measurements for evaluation of coating resistance to an impact of repetitive mechanical stress. Typical...
-
Applicability of edible Candelilla wax composite blended with Bryophyllumpinnatum extract to prolong shelf life of fruits/vegetables
PublikacjaCandelilla wax (CW) is a natural lipid source that can be used to make biodegradable and edible coatings and films for fruits. However, CW alone does not provide sufficient antimicrobial and antioxidant properties to prevent microbial spoilage and oxidative deterioration of fresh products. This study aims at evaluating the applicability of CW blended with Bryophyllum pinnatum extract (BPE), a plant with medicinal and phytochemical...
-
Solid Phase Microextraction: Apparatus, Sorbent Materials, and Application.
Publikacjahe primary objective of this review article is to strategically screen and highlight the advancements in the area of solid phase microextraction (SPME). The plenty of review articles have been written on different aspects of SPME, this review is dedicated to provide the brief but clear overview of the research footprints so produced from SPME. Some of the key advancements in types and designs, coating materials, coating strategies,...
-
Local properties of organic coatings close to glass transition temperature
PublikacjaAcrylic coating applied on copper substrate has been investigated at different temperatures starting from the ambient one up to the level above the glass transition temperature. Its local topographic and electric properties have been examined with the atomic force microscopy (AFM) based approach including dc current mapping and local impedance spectroscopy. The local findings have been compared with the information from global...
-
Effect of plasma sprayed and laser re-melted Al2O3 coatings on hardness and wear properties of stainless steel
PublikacjaCommercially available austenic stainless steel substrate was coated with commercially available, raw Al2O3 powder applied by means of plasma spraying method and then re-melted with CO2 laser beam of various parameters. Tribological and mechanical properties of the 120 J/mm and 160 J/mm laser re-melted coatings were compared with the tribological and mechanical properties of the “as-sprayed” coating. The influence of the laser...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B37/#A35
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A39/#B41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
SiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A35/#B37
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 3 min.Secimen...
-
The analysis of the influence of the corrosion protection method of selected steel elements on the steel structure life cycle costs
PublikacjaSteel products are widely used in the construction for the performance of essential and additional elements of engineering structures. They are characterized by high tensile strength, compression and bending, the structure homogeneity, the possibility of assembly regardless of the season and climatic conditions, ease of processing and the possibility of almost any shape. The main disadvantage of steel structures is their high susceptibility...
-
High-temperature oxidation of the Crofer 22 H ferritic steel with Mn1.45Co1.45Fe0.1O4 and Mn1.5Co1.5O4 spinel coatings under thermal cycling conditions and its properties
PublikacjaThe aim of the presented study was to deposit protective-conducting Mn1.45Co1.45Fe0.1O4 and Mn1.5Co1.5O4 spinel coatings on the Crofer 22 H ferritic steel by means of electrophoresis and to evaluate their physicochemical properties after high-temperature oxidation under thermal cycling conditions. When the Crofer 22 H steel – whether uncoated or coated with the two spinels – was oxidized in 48-h cycles involving a temperature of...
-
PROBLEMS WITH CORROSION PROTECTION STEEL STACKS IN FGD SYSTEMS
PublikacjaThis paper presents problems associated with corrosion of steel stacks and changes in philosophy of corrosion protection when implemented into flue gas desulphurization systems. In-situ tests were taken by means of electrochemical impedance spectroscopy at a stack which discharges flue gas before wet lime/limestone desulphurization. A very rapid soaking of spherical infill vinylester coating with electrolyte has been observed....
-
Improvement of electrochemical action of zinc-rich paints by addition of nanoparticulate zinc
PublikacjaThe influence of nanosized particles on electrochemical action of standard zinc-rich paints by means of SEM as well as potential and impedance measurements has been investigated. The motivation for doing this was to obtain additional electrical connection between the spherical microparticles themselves and zinc particles and steel substrate. Overall zinc content was at the level of 92% by weight. Samples with different concentration...
-
The influence of chitosan hydrogel coating on different redox probes kinetics
Dane BadawczeThis dataset contains cyclic voltammetry studies of three redox probes: 1 mM K3[Fe(CN)6], [K4Fe(CN)6], C12H14FeO2, and [Ru(NH3)6]Cl2 dissolved in 0.1 M KCl or PBS as the primary electrolyte. The studies are made for glassy carbon electrode (GC) and glassy carbon electrode covered with thin chitosan hydrogel membrane (C2A2). Cyclic voltammograms were...
-
Investigation of temperature changes using a microsphere-based fiber-optic sensor
Dane BadawczeInvestigation of temperature changes using a microsphere-based fiber-optic sensor with a 200 nm ZnO ALD coating for the purpose of validation the design of the sensor, measurement setup and method of examination of electric cell materials.
-
Recovery and re-use of photovoltaic solar cells from crystalline silicon
PublikacjaCrystalline silicon-type PV modules consist, in order of mass, of glass, an aluminium frame, an EVA coating, solar cells, a terminal box, back film and tapping screws. From the economic point of view, pure silicon, recoverable from spent cells, is the most important material owing to its cost and shortage. For crystalline, silicon-based PV cells, the following chemical treatments were performed: removal of the metal coating, followed...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B48/#A45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiC coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B41/#A39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A23/#B22
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 12 min. The...
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B39/#A41
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B34/#A33
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
TiN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A45/#B48
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 12 min....
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A41/#B39
Dane BadawczeWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A25/#B21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B22/#A23
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 6 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A33/#B34
Dane BadawczeWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
Deposition and growth of thin ceramic films
Publikacja: Thin ceramic films play an important role in modern technology. One of the more utilized methods of deposition of ceramic films is spin coating. In this paper we investigate optimal deposition parameters for LaNi0.6Fe0.4O3−δ thin layers spin coated from a polymeric precursor. The quality of the obtained layers is checked using scanning electron microscopy. Additionally, we investigate the growth of grains in ceramic films annealed at...
-
Microcapsules and their applications in pharmaceutical and food industry.
PublikacjaMicroencapsulation is a process in which tiny particles or droplets are surrounded by a coating or embedded in a homogeneous or heterogeneous matrix, to generate small capsules in size range from a few to few thousand micrometers. The material inside the microcapsule is referred to as the core, internal phase, or fill, whereas the wall is sometimes called shell, coating, wall material, or membrane. It has found application in...
-
Application of optical microsphere in fiber optic sensors for measurement of electrochemical processes
Dane Badawczeinvestigation of the electrochemical processes using micro-sphere fiber-optic sensor with a zinc oxide (ZnO) coating applied by Atomic Layer Deposition method (ALD). The measurements were performed in 1M KNO3 during a decomposition of Bisphenol-A
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21
Dane BadawczeWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 25 min....
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 20 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#B45
Dane BadawczeWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 90 min. The test...
-
Fabrication methods of smart composite coatings - review
PublikacjaPostoperative bacterial infections are one of the main reasons for unsuccessful implantation of long-term implants. The development of bacterial infection requires antibiotic therapy, in extreme cases a reimplantation procedure is necessary. In order to provide materials for implants with antibacterial properties, they are subjected to modifications to create a coating that will release the drug substance, when the inflammation...
-
Protective and Suppressing Electromagnetic Interference Properties of Epoxy Coatings Containing Nano-Sized NiZn Ferrites
PublikacjaNano-crystalline ferrites with the chemical formula NixZn(1−x)Fe2O4, where x = 0, 0.2, 0.4, 0.6, 0.8, 1.0, were synthesized using a co-precipitation method. The obtained ferrites were investigated by X-ray diffraction (XRD). The corrosion inhibiting behavior of nano-sized ferrites was tested using carbon steel samples and 10% aqueous ferrite extracts. Results were compared with previous data obtained for micro-sized ceramic ferrites....
-
Annealing of indium tin oxide (ITO) coated optical fibers for optical and electrochemical sensing purposes
PublikacjaGlass and fiber structures with Indium Tin Oxide (ITO) coating were subjected to annealing in order to identify impact of the thermal treatment on their optical and electrochemical properties. It is shown that the annealing process significantly modifies optical properties and thickness of the films, which are crucial for performance of optical fiber sensors. Moreover, it visibly improves electrochemical activity of ITO on glass...
-
Electrophoretic co-deposition of Fe2O3 and Mn1,5Co1,5O4: Processing and oxidation performance of Fe-doped Mn-Co coatings for solid oxide cell interconnects
PublikacjaThe “in-situ” Fe-doping of the manganese cobalt spinel was achieved by electrophoretic co-deposition of Mn1,5Co1,5O4 and Fe2O3 powders followed by a two-step reactive sintering treatment. The effects on the coating properties of two different Fe-doping levels (5 and 10 wt.% respectively) and two different temperatures of the reducing treatment (900 and 1000 °C) are discussed. Samples with Fe-doped coatings demonstrated a lower...
-
Application of Electrochemical Impedance Spectroscopy to evaluate cathodically protected coated steel in seawater
PublikacjaTwo types of organic coated carbon steel (S235JR2 grade) electrodes were exposed to artificial seawater environment. One prepared type was defect free while the other one had an intentionally introduced φ0,5 cm coating defect. Both kinds of samples were polarized during the exposure to four potentials corresponding to four different cathodic protection levels. Evolution of their EIS spectra is presented in this paper. Results obtained...
-
Depth XPS profile of vanadium pentoxide
Dane BadawczeVanadium pentoxide sample was manufactured by sol-gel method and deposited on a substrate by spin coating technique. To determine depth profile of chemical composition of thin film, etching by Argon ion gun was used. Thin film was etched three times. Chemical composition was measured by XPS method.
-
Impedance spectroscopy of the lithium titanate doped by copper thin films
Dane BadawczeLithium titanate doped by copper thin films were derived by sol-gel method. Prepared gel was deposited by spin-coating technique. Samples with various content of Cu were measured by impedance spectroscopy method in a wide range of temperature, from -120 up to 150 deg.
-
Iron doped manganese cobaltite spinel coatings produced by electrophoretic co-deposition on interconnects for solid oxide cells: Microstructural and electrical characterization
PublikacjaWe report a systematic microstructural and electrical characterization of iron doped Mn–Co spinel coatings processed by electrophoretic co-deposition of Mn1.5Co1.5O4 and Fe2O3 powders on Crofer 22 APU and AISI 441 steel substrates. Iron addition to Mn–Co spinel coating leads to a reduction of the area specific resistance on both substrates, after 3200 h at 750 °C. The Fe doped Mn–Co coating both leads to a thinner oxide scale and...
-
Functional Bi2O3/Gd2O3 Silica-Coated Structures for Improvement of Early Age and Radiation Shielding Performance of Cement Pastes
PublikacjaThis study presents a new approach towards the production of sol-gel silica-coated Bi2O3/Gd2O3 cement additives towards the improvement of early mechanical performance and radiation attenuation. Two types of silica coatings, which varied in synthesis method and morphology, were used to coat Bi2O3/Gd2O3 structures and evaluated...