Mechanical properties of single V2O5 nanocrystal - nanoindentation measurement in control of the max-depth
Dane BadawczeThe DataSet contains the nanoindentation curves (indentation force Fn vs penetrationPd) for a single V2O5 nanocrystal supported on a substrate. The measurements were performed in control of the maximum depth of Berkovich indenter penetration: 60, 70, and 100 nm.
-
Electrical properties and structure of lead-borate glass containing iron ions.
PublikacjaThe ac and dc conductivity in iron–lead-borate glass samples was investigated in the frequency range from 1 mHz to 1 MHz and in the temperature range from 153 K to 423 K. The structure was investigated by the means of atomic force microscopy (AFM) and the crystalline phases (if present) were identified by the means of X-ray diffractometry. Two types of ac electrical behaviour were observed. The first group of glass samples which...
-
From Structure to Luminescent Properties of B2O3-Bi2O3-SrF2 Glass and Glass-Ceramics Doped with Eu3+ Ions
PublikacjaGlass-ceramics with the composition B2O3 -Bi2O3 -SrF2 were synthesized by the conventional melt-quenching technique and subsequent crystallization of the parental glasses. The temperature at which the ceramization was carried out was selected based on differential scanning calorimetry (DSC) analysis. The structure of the studied materials and the formation of SrF2 nanocrystals were confirmed by the Fourier-transform infrared spectroscopy...
-
Tellurite based glass doped by Eu3+ ions - XPS measurements
Dane BadawczeEu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after...
-
Application of Impedance Spectroscopy for Bi1−xNdxFeO3 Ceramics Characterization
PublikacjaIn the present paper the synthesis conditions for fabrication of Bi1−xNdxFeO3 ceramics are reported. The single phase polycrystalline samples of Bi1−xNdxFeO3 were prepared by standard solid state reaction method from the mixture of oxides viz.: Bi2O3, Fe2O3 and Nd2O3. The samples were characterized by impedance spectroscopy in the frequency range 10Hz – 1MHz at room temperature.
-
Preliminary evaluation of selected mineral adsorbents used to remove phosphorus from domestic wastewater = Wstępna ocena przydatności wybranych adsorbentów mineralnych do usuwania fosforu ze ścieków bytowych
PublikacjaFour grinded mineral materials were studied for their ability of P sorption from the aq. phosphate solns. in 24-h tests by using equations of Langmuir and Freundlich isotherms. The particular sorbents contained mainly SiO254,5% Ca) 29.6%, Fe2O3 69,4% and showed the sorption capacities 56, 159, 285 or 2.4 mg/g resp.
-
A white phosphor based on oxyfluoride nano-glass-ceramics co-doped with Eu3+ and Tb3+: Energy transfer study
PublikacjaStrontium fluoride nanocrystals doped separately with Ln3+ = Eu3+ or Tb3+ ions (95SrF2·5LnF2), as well as co-doped with both the ions (95SrF2·Eu4Tb) were synthesized for comparison. Then, glass-ceramics consisting of the mono-doped or di-doped SrF2 nanocrystals incorporated into amorphous silica (90SiO2·9.5SrF2·0.5Ln or 90SiO2·9.5SrF2·0.1EuF3·0.4Tb) were prepared by sol-gel procedure. The studied materials were characterized by...
-
Cyclic voltammetry curves of the V2O5 nanorods (Li-ion batteries)
Dane BadawczeThe DataSet contains the next thirty cycles voltammetry curves for the V2O5 nanocrystals obtained by the sol-gel method. The cyclic voltammetry was measured using the AUTOLAB 302N potentiostat-galvanostat. The measurements were carried out in a voltage range of 2 V to 4 V vs. Li/Li+ at a scan rate of 1 mV/s. The results show that in the subsequent cycles,...
-
Comparative X-ray diffraction and Mössbauer spectroscopy studies of BiFeO3 ceramics prepared by conventional solid-state reaction and mechanical activation
PublikacjaThe aim of this work was to prepare BiFeO3 by modified solid-state sintering and mechanical activation processes and to investigate the structure and hyperfine interactions of the material. X-ray diffraction and Mössbauer spectroscopy were applied as complementary methods. In the case of sintering, BiFeO3 phase was obtained from the mixture of precursors with 3 and 5 % excess of Bi2O3 during heating at 1023 K. Small amounts of...
-
SEM micrographs of NH4VO3 crystals - molar concetration factor after annealing
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 nano_crystals obtained by the LPE-IonEx method with different morphology after annealing at 400C under argon atmosphere (with a heating rate of 10 C/min).
-
Characterization of Bi6Fe2Ti3O18 Ceramics with Impedance Spectroscopy
PublikacjaIn the present research the tool of impedance spectroscopy was utilized to characterize dielectric behavior of Aurivillius-type ceramics of Bi6Fe2Ti3O18 composition fabricated by hot pressing method from the stoichiometric mixture of oxides Bi2O3, TiO2 and Fe2O3. Impedance spectroscopy was applied to characterize dielectric response of bulk, grain boundary, and material/electrode interfaces of the fabricated polycrystalline ceramic...
-
SEM micrographs of NH4VO3 crystals - molar concetration factor
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 nano_crystals obtained by the LPE-IonEx method. The SEM images clearly show that the morphology of the end product can be nicely tuned by changing the molar concentration of ammonium salt in the solvent.
-
Thin LSFO films for bolometers
PublikacjaPrzedstawiono metodę produkcji oraz temperaturowe zależności rezystancji cienkich warstw niestechiometrycznych tlenków (La,Sr)FeO3 (LSFO) przeznaczonych do zastosowań na detektory podczerwieni
-
Electrical properties of nanostructures in lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeElectrical properties of iron oxide nanostructures observed in silicate glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15, 20 and 25 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where...
-
Magnetic properties of of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeMagnetic properties of iron-doped glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15 and 20 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere...
-
Fabrication of Bi6Fe2Ti3O18 Ceramics by Mixed Oxide Method
PublikacjaIn the present study Bi6Fe2Ti3O18 (BFTO) ceramics has been fabricated by solid state reaction from the mixture of simple oxides viz. Bi2O3, TiO2 and Fe2O3. Stoichiometric mixture of the powders was thermally analyzed so parameters of the thermal treatment were determined. The EDS measurements have shown conservation of the chemical composition of the ceramic powder after calcination. Hot-pressing method was used for final densification...
-
New Unsymmetrical Bisacridine Derivatives Noncovalently Attached to Quaternary Quantum Dots Improve Cancer Therapy by Enhancing Cytotoxicity toward Cancer Cells and Protecting Normal Cells
PublikacjaThe use of nanoparticles for the controlled drug delivery to cells has emerged as a good alternative to traditional systemic delivery. Quantum dots (QDs) offer potentially invaluable societal benefits such as drug targeting and in vivo biomedical imaging. In contrast, QDs may also pose risks to human health and the environment under certain conditions. Here, we demonstrated that unique combination of nanocrystals core components...
-
Study of Phase and Chemical Composition of Bi1-xNdxFeO3 Powders Derived by Pressureless Sintering
PublikacjaIn the present paper studies on Bi1xNdxFeO3 for x =0.1-0.4 are reported. The mixed oxide method followed with pressureless sintering was employed for ceramics fabrication. Thermal behavior of stoichiometric mixtures of simple oxide powders, viz. Bi2O3, Nd2O3 and Fe2O3 was studied by simultaneous thermal analysis. It was found that with an increase in neodymium content the weight loss increased from 0.75% to 3.16% for x =0.1 and...
-
X-RAY DIFFRACTION STUDY OF BISMUTH LAYER-STRUCTURED MULTIFERROIC CERAMICS
PublikacjaGoal of the present research was to apply a solid state reaction route to fabricate bismuth layer-structured multiferroic ceramics described with the formula Bi5FeTi3O15 and reveal the influence of processing conditions on its crystal structure and phase composition. Simple oxide powders Bi2O3, TiO2 and Fe2O3 were used to fabricate Aurivillius-type bismuth layer-structured ferroelectrics. Pressureless sintering in ambient air was...
-
Design, Synthesis, and Enzymatic Evaluation of Novel ZnO Quantum Dot-Based Assay for Detection of Proteinase 3 Activity
PublikacjaHerein, the synthesis and application of functionalized quantum dot-based protease probes is described. Such probes are composed of nontoxic ZnO nanocrystals decorated by amino groups followed by linker and labeled peptide attachment. Spherical NH2-terminated ZnO quantum dots (QDs) with the average size ranging from 4 to 8 nm and strong emission centered at 530 nm were prepared using the sol−gel method. The fluorescence of ZnO...
-
In Situ Random Microseeding and Streak Seeding Used for Growth of Crystals of Cold-Adapted beta-D-Galactosidases: Crystal Structure of betaDG from Arthrobacter sp. 32cB
PublikacjaThere is an increasing demand for cold-adapted enzymes in a wide range of industrial branches. Nevertheless, structural information about them is still scarce. The knowledge of crystal structures is important to understand their mode of action and to design genetically engineered enzymes with enhanced activity. The most difficult task and the limiting step in structural studies of cold-adapted enzymes is their crystallization,...
-
Quantum dots conjugates with unsymmetrical bisacridines enhance cytotoxicity of these antitumor compounds in lung cancer cells and have protecting effects on normal cells
PublikacjaBackground: In recent years, with the rapid development of nanotechnology and its extensive applications in the medicine, nanocarriers for anticancer drug delivery have gained a great importance. Spherical semiconductor nanocrystals, frequently called quantum dots (QDs) are very attractive nanomaterials for bioimaging applications and they possess properties as potential candidates for drug carrier. Unsymmetrical bisacridines (UAs),...
-
TiO2-C nanocomposite synthesized via facile surfactant-assisted method as a part of less energy-consuming LED-based photocatalytic system for environmental applications
PublikacjaA novel facile method was used to incorporate carbon into the titania structure. An alternative synthesis method of carbon-doped TiO2 has been proposed by using a widely used and cheap surfactant. During the process, cetyltrimethylammonium bromide plays a dual role, as a morphology modifier and as a carbon source. The presented approach allows obtained TiO2-C nanostructures to be anatase nanocrystals with carbon being deposited...
-
Fluctuation-enhanced and conductometric gas sensing with nanocrystalline NiO thin films: A comparison
PublikacjaNanocrystalline thin films of NiO were prepared by advanced reactive gas deposition, and their responses to formaldehyde, ethanol and methane gases were studied via fluctuation-enhanced and conductometric methods Thin films with thicknesses in the 200–1700-nm range were investigated in as-deposited form and after annealing at 400 and 500 °C. Morphological and structural analyses showed porous deposits with NiO nanocrystals having...
-
Linear and nonlinear impedance in iron oxide glasses containing alkaline ions and alkali free
PublikacjaThe linear and nonlinear impedance spectra of oxide glasses were measured in the frequency range of 1 mHz to 1 MHz and in the temperature range of 153K to 483K. Two groups of iron oxide glass samples were prepared, the first one containing alkaline ions and the second one without alkali. In the first group, compositions of glasses were as follows: (in %mol) 50% SiO2 , 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O,...
-
The influence of nanostructures size on V2O5 electrochemical properties as cathode materials for lithium ion battery
PublikacjaIn this paper, V2O5 nanostructures with a size depending on the annealing temperature are successfully synthesized by a sol-gel method. The crystal structure and morphology of samples are characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), selected area electron diffraction (SEAD) and scanning electron microscopy (SEM), respectively. Electrochemical testing such...
-
Chitin and derivative chitosan-based structures — Preparation strategies aided by deep eutectic solvents: A review
PublikacjaThe high molecular weight of chitin, as a biopolymer, challenges its extraction due to its insolubility in the solvents. Also, chitosan, as the N-deacetylated form of chitin, can be employed as a primary material for different industries. The low mechanical stability and poor plasticity of chitosan films, as a result of incompatible interaction between chitosan and the used solvent, have limited its industrialization. Deep eutectic...
-
Immittance Studies of Bi6Fe2Ti3O18 Ceramics
PublikacjaResults of studies focusing on the electric behavior of Bi6Fe2Ti3O18 (BFTO) ceramics are reported. BFTO ceramics were fabricated by solid state reaction methods. The simple oxides Bi2O3, TiO2, and Fe2O3 were used as starting materials. Immittance spectroscopy was chosen as a method to characterize electric and dielectric properties of polycrystalline ceramics. The experimental data were measured in the frequency range D = (101–107)...
-
The structure of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
The morphology of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
High resolution X-ray diffractometry and reflectometry of semiconductor nano- and micro- structures based on X-ray refractive optics
PublikacjaIn this thesis proposed, discussed and studied novel synchrotron X-ray diffractometry and reflectometry methods based on a refractive optics. The experimental results obtained from the ID06 beamline at ESRF, Grenoble, France are presented and analyzed in this work to demonstrate a high angular and space resolution in addition to the opportunity to manage in situ and on operando experiments with the help of proposed X-ray optical...
-
Iron doped manganese cobaltite spinel coatings produced by electrophoretic co-deposition on interconnects for solid oxide cells: Microstructural and electrical characterization
PublikacjaWe report a systematic microstructural and electrical characterization of iron doped Mn–Co spinel coatings processed by electrophoretic co-deposition of Mn1.5Co1.5O4 and Fe2O3 powders on Crofer 22 APU and AISI 441 steel substrates. Iron addition to Mn–Co spinel coating leads to a reduction of the area specific resistance on both substrates, after 3200 h at 750 °C. The Fe doped Mn–Co coating both leads to a thinner oxide scale and...
-
Nanostructured biocatalysis for biotechnological applications
PublikacjaThe purpose immobilization process is to enhance the performance of an enzyme for commercial processes. A large number of structures have been reported in the literature to boost the effectiveness of immobilized enzymes. The nanomaterials have the optimal properties for equilibrating key parameters that govern the performance of biocatalysts, such as high enzyme loading ability, specific surface area, and mass transfer resistance....
-
Enhancing electrical properties through in-situ controlled nanocrystallization of V2O5–TeO2 glass
PublikacjaV2O5–TeO2 glass–ceramics (VTGC) were prepared by controlled annealing of the V2O5–TeO2 glass (VTG), which illustrates a parent glass matrix with a single charge carrier. The annealing proceeded at six temperatures selected between the glass transition and the maximum of the frst crystallization process to obtain various nanocrystallite sizes. Heat treatment caused an increase in DC conductivity by 2.5–3.5 (250–285 °C) order of...
-
X-ray diffraction patterns of BaCe0.6Zr0.2Y0.1M0.1O3-δ (M = Fe, Pr, Tb)
Dane BadawczeThe dataset consists of three raw X-ray diffraction (XRD) files collected using a Phillips X’Pert Pro diffractometer (CuKα radiation (𝜆 = 1.541 Å), under 40 kV and 30 mA). The diffraction patterns of BaCe0.6Zr0.2Y0.1Fe0.1O3-δ (BCZYFe), BaCe0.6Zr0.2Y0.1Pr0.1O3-δ (BCZYPr), and BaCe0.6Zr0.2Y0.1Tb0.1O3-δ (BCZYTb) were collected at room temperature. Collected...
-
Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Dane BadawczeLinear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO2, 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O, Li2O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered...
-
Topography of iron-phosphate glasses doped with niobium and titanium tested by confocal microscope
Dane BadawczeThe topography of phosphate-iron glasses containing niobium and titanium were investigated with the use of confocal miscroscope. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5, 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 and 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents...
-
Bis(ammonium) Zoledronate Dihydrate
PublikacjaNeutralization of 2-(1-imidazole)-1-hydroxyl-1,1`-ethylidenediphosphonic acid (zoledronic acid) by an excess of ammonia yielded bis(ammonium) zoledronate dihydrate, {C5H8N2O7P2 2−, 2(H4N+), 2(H2O)}. The product is readily soluble in water and forms monocrystals for which the X-ray structural analysis was carried out. The zoledronic anion is of double negative charge due to deprotonation of three P–OH groups and protonation of the...
-
The structure of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
The morphology of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
Linear impedance of 35P2O5-30Fe2O3-20Nb2O5-15TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...
-
Linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and...
-
Linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Dane BadawczeThe electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2 (≥99.9%, anatase...
-
The morphology of lead-borate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional meltquenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate...
-
The structure of lead-borate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and...
-
Magnetic photocatalysts for water treatment
PublikacjaThe concept of magnetic photocatalysts with separation function requires ferromagnetic material with high magnetic susceptibility to an external magnetic field to enable recycling of composite nanoparticles. Currently, much attention is devoted to functionalization of photocatalyst using MFe2O3, where M =Fe, Zn, Co, Mn. However direct contact between photocatalyst and magnetic iron oxide particles leads to photodissolution of iron...
-
A new simple approach to prepare rare-earth metals-modified TiO2 nanotube arrays photoactive under visible light: Surface properties and mechanism investigation
PublikacjaApplication of Ti90RE10 alloys (RE = Ho, Er, Nd, Y, Ce, Tm) as a working electrode, instead of Ti pure foil in anodic oxidation in a fluoride-based electrolyte, resulted in formation of well-ordered nanotubes made of TiO2 and RE2O3 mixture, which could be efficiently used for pollutant removal from water and air phase upon UV and visible irradiation and easily separable from the reaction mixture to recycle. The as-prepared NTs...
-
High temperature linear impedance of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-27.5Nb2O5-7.5TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG)...
-
High temperature linear impedance of 35P2O5-30Fe2O3-25Nb2O5-15TiO2
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium and titanium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-20Nb2O5-15TiO2 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%,...
-
High temperature linear impedance of 35P2O5-30Fe2O3-35Nb2O5
Dane BadawczeThe high temperature electrical properties of phosphate-iron glasses containing niobium were investigated. Glass samples of the composition of 35P2O5-30Fe2O3-35Nb2O5 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents ((NH4)2HPO4 (≥99.9%, POCH), Fe2O3 (≥99.9%, POCH), Nb2O5 (≥99.9%, PLUKA AG) and TiO2...