Search results for: CHARACTERISTIC IMPEDANCES
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.50Fe0.50O3-d oxygen electrode sintered at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.50Fe0.50O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.65Fe0.35O3-d oxygen electrode sintered at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.65Fe0.35O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
Electrochemical impedance spectroscopy spectra measured at 800 °C, 750 °C and 700 °C on porous SrTi0.30Fe0.70O3-d oxygen electrode sintered at 800 °C
Open Research DataThis dataset contains results electrochemica impedance spectroscopy (EIS) of symmetrical cells with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C; 750°C and 700 °C (synthetic air). Results converted to electrode surfaces area and dived by two electrodes.
-
SEM micrographs of 3D printed CB-PLA samples topography after microwave treatment
Open Research DataThis dataset contains the electrochemical studies on microwave-activated carbon-black doped polylactic acid 3D printed electrodes.
-
Electrical and noise responses of graphene back-gated field-effect transistors enhanced by UV light for organic vapors sensing
Open Research DataBack-gated field-effect transistors with graphene channels (GFETs) were investigated toward organic vapors sensing. Two methods were used for sensing experiments including DC characteristics measurements and fluctuation-enhanced sensing by low-frequency noise studies. The data set consists of raw and modified data on GFET responses to acetonitrile,...
-
Determination of viscosity changes in dietary supplement solutions depending on temperature.
Open Research DataThe rheological characteristics of dietary supplement solutions were made based on viscosity measurement using a Brookfield viscometer, using the LV SC4 - 18 spindle and a shear rate of 53 s-1 (Fig.1).
-
X-ray diffraction spectra of nitrogen-doped carbon in hybrid materials containing praseodymium oxide
Open Research DataX-ray powder diffraction patterns of samples were carried out by Philips X’Pert diffractometer, which was radiated by graphite monochromatized Cu Kα (l equal 1.540598). The operating voltage was maintained at 40 kV, the current was maintained at 30 mA and analyzed in the range from 20° to 90°. The data presented confirmed the presence of the PrBSCF...
-
GSADF test results for national art market (G-7 group) + selected investments
Open Research DataThe dataset contains data illustrating the results of detecting and data-stamping price explosivity periods in national art markets in G-7 countries with additional investments from a second group (MSCI, S&P 500, crude oil, gold and silver). The files contain:• 01_diagnostics_gsadf – summary of results for analysed time series.• 02_st_value...
-
Electrical and noise responses of Graphene-Silicon Schottky diodes decorated with Au nanoparticles for light-enhanced sensing of organic gases
Open Research DataGraphene-Silicon Schottky junctions decorated with Au nanoparticles were used for light-enhanced detection of organic tetrahydrofuran and chloroform. Au nanoparticles exhibited localized surface plasmon resonance (LSPR) in the range of yellow light; thus yellow LED (wavelength of 592 nm) was utilized to induce the plasmonic effect, that increased the...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 800 °C and 15% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 800 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 100% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 100% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 20% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 20% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 5% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 5% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 600 °C and 15% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 600 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included. Results converted...
-
Electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for porous SrTi0.30Fe0.70O3-d oxygen electrode measured at 700 °C and 15% oxygen partial pressure
Open Research DataThis dataset contains electrochemical impedance spectroscopy and Distribution of Relaxation Times analysis results for symmetrical cell with porous SrTi0.30Fe0.70O3-d oxygen electrodes sintered at 800 °C. EIS spectra were measured at 700 °C and 15% of oxygen partial pressure. Spectra of two RCPE elements from equivalent circuit , are also included....
-
Carbonized Metal-Organic Frameworks-based strucutres with aluminium, phosphorus and nitrogen
Open Research DataThe dataset includes Raman spectra of carbonized Metal-Organic Frameworks (MOF) [acquired on Renishaw] and electrochemical properties of the materials [acquired on EC Lab], which includes techniques such as Linear Sweep Voltammetry (LCV), Electrochemical Impedance Spectroscopy (EIS), Taffel slope and Chronopotentiometry (CP).
-
Optical properties of TeOx gels doped with a mix of rare-earth ions
Open Research DataThe DataSet contains the UV-Vis spectra of the TeOx gels doped with a mix of rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the different molar concentration of rare-earth ions was added, nitrates were used...
-
Optical properties TeOx gels doped with the rare-earth ions
Open Research DataThe DataSet contains the UV-Vis spectra of TeOx gels doped with the rare-earth ions. The material was obtained by the sol-gel method. The starting solution was prepared by mixing telluric acid (precursor) with thetraetylene glycol, water, and ethanol. Next, the 5% mol of the rare-earth ions were added, the nitrates were used as a source of rare-earth...
-
Floating treatment wetland with Equisetum hyemale - performance in nutrients and potentially toxic elements removal
Open Research DataThis data set contains the results of a microcosm experiment with floating treatment wetlands (FTW) conducted under artificial conditions. The goal of this experiment was to determine the effect of stress factors (Pb, As, increased salinity) on the nutrient uptake capacity of Equisetum hyemale in FTW. The ability of E.hyemale to uptake Pb and As was...
-
Electrochemical data for carbonized metal-organic framworks with cobalt
Open Research DataThe data includes the Metal-Organic Frameworks (MOF) measurements, where cobalt was added. The research focuses on the impact of aluminium on Oxygen Evolution Reaction (OER). The measurements were conducted on [EC Lab]. The techniques included are Linear Sweep Voltammetry (LSV), Tafel slope, Chronopotentiometry (CP) and Electrochemical Impedance Spectroscopy...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Frequency of neoplasia in the baltic clam Limecola balthica from the Gulf of Gdańsk between 1999-2002
Open Research DataThe presented dataset contains data describing the frequency of neoplasia in one of the most common bivalve species inhabiting the Baltic Sea, the baltic clam Limecola balthica. The frequency of neoplasia was assessed at various locations of the Gulf of Gdańsk between years 1999 - 2002. The dataset contains information describing the sampling areas...
-
Dielectric properties of barium-vanadate glasses
Open Research DataThe linear impedance of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was...
-
X-ray images of Baltic herring. Data analysis
Open Research DataBased on the developed methodology for the: (i) optimal method of catching, (ii) transporting and storing fish, (iii) measuring and (iv) analyzing X-rays images, the existing collection of X-ray images of Baltic herring, caught in October 2002 during the Swedish component of the Baltic International Acoustic Survey (BIAS) in the Baltic proper (ICES...
-
Tellurite based glass doped by Eu3+ ions - XPS measurements
Open Research DataEu3+ doped tellurite glass ceramics containing SrF2 nanocrystals were prepared using melt quenching technique and subsequent heat treatment of glass in 370 °C for different time periods. Thermal properties of glass matrix have been determined based on DSC measurements. XRD and XPS results confirmed formation of SrF2 nanocrystals in glass matrices after...
-
Correction of far-field measurements obtained in non-anechoic test site
Open Research DataThe dataset contains raw and processed measurements of radiation pattern characteristics performed in non-anechoic regime for two geometrically small antenna structures: a spline-parameterized Vivaldi structure and a compact spline-based monopole. The responses have been obtained at the selected frequencies of interest as a function of mentioned structures...
-
Optical properties of tellurium dioxide thin films
Open Research DataTeO2 and TeO2 doped by Eu thin films manufactured by magnetron sputtering method were measured by optical spectroscopy. Metallic Te target and Te-Eu mosaic target with diameter of 50.8 mm were sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Oxygen partial pressure and temperature dependence of Gerischer element of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of Gericher element at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C)and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent circuit...
-
Oxygen partial pressure and temperature dependence of low frequency capacitance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of low frequency capacitance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency capacitance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of middle frequency capacitance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of low frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of low frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of series resistance (R) at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Oxygen partial pressure and temperature dependence of middle frequency resistance of symmetrical porous Sr0.86Ti0.65Fe0.35O3 electrode on CGO substrate
Open Research DataThis dataset contains values of middle frequency resistance at different temperatures (800 °C, 750 °C, 700 °C, 650 °C and 600 °C) and oxygen partial pressures (20%, 10%, 5%, 1%, 0.1% and 0.01% pO2) of symmetrical Sr0.86Ti0.65Fe0.35O3 electrode sintered at 1000 °C. This values were obtained by fitting each measured impedance spectra by electrical equivalent...
-
Imaging of graphene surface by means of tapping mode AFM
Open Research DataGraphene [1] is a material consisting of carbon planes with a hexagonal structure. One of the facts of interest from a purely scientific point of view is the very high mobility of electrons in the described material, allowing the study of relativistic effects inside a solid sample. Other features, such as bactericidal activity, make graphene an interesting...
-
Sliding friction of alumina (Al2O3) with friction induced vibrations
Open Research DataTest files containing data on experiments in self mated sliding contact of alumina Al2O3 lubricated with either water or paraffin oil. Tests run in variable load/velocity conditions and with different dynamic settings of the test rig (PT-3 tribometer). The aim of the research was to attempt in finding correlations between the dynamic characteristics...
-
Radiation pattern measurements of geometrically small antennas performed in non-anechoic environments
Open Research DataThe dataset contains unprocessed measurements of radiation pattern characteristics performed in non-anechoic regime for three geometrically small antenna structures: a spline-parameterized Vivaldi structure, a compact spline-based monopole, and a quasi-Yagi geometry with enhanced bandwidth. The responses have been obtained over broad frequency ranges...
-
Measurements of electrically small antenna radiation patterns in non-anechoic environments using TGM
Open Research DataThe dataset contains raw and processed measurements of radiation pattern characteristics performed in non-anechoic regime for four antenna structures: a spline-parameterized Vivaldi structure, a compact spline-based monopole, super-ultrawideband antenna, and a quasi-Yagi component. The responses have been obtained at the selected frequencies of interest...
-
Data on wages, gender wage gap and global value chains measured on the European Structure of Earnings Survey and World Input-Output Database.
Open Research DataThis data article describes the data and merging procedure used by Nikulin and Wolszczak-Derlacz (Nikulin and Wolszczak-Derlacz, 2022).
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Oxygen partial pressure and temperature dependence of series resistance of symmetrical porous SrTi0.30Fe0.70O3 electrode on CGO substrate
Open Research DataThis dataset contains values of equivalent circuit element series resistance at different temperatures (800 °C, 700 °C, 600 °C and 500 °C) and oxygen partial pressures (100%, 80%, 50% 30%, 20%, 15%, 10%, 5%, 2.5%, 1%, and 0.3% pO2) of symmetrical SrTi0.30Fe0.70O3 electrode sintered at 800 °C. This values were obtained by fitting each measured impedance...
-
The profiles and spectrum of aqua solution of tannic acid by HPLC-DAD-MS analysis.
Open Research DataThe profiling of tannic acid is determined by examining the content and proportion / ratio of gallotannins [Aras et al. 2016, Clifford et al. 2007, Gauri et al. 2012, Nishizawa et al. 1982]. In order to check the ion mass distribution (TIC) in an aqueous solution of commercial tannic acid, a direct sample injection (TA) was performed into the mass spectrometer....
-
Biomass of macrophytobentos in the Puck Bay in 2010-2018
Open Research DataThe database contains data on qualitative composition and biomass of macrophytobenthos (flower plants and macroalgae) in samples collected in the Puck Bay area (Gulf of Gdańsk, southern Baltic Sea) at 20 stations between 2010-2018. The database contains information on sampling sites (region, geographical coordinates, depth), sample characteristics (date,...
-
Simulation of perovskite-based CuI/CH3NH3PbI3/TiO2 solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/TiO2 model structure (Model 1) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/SnO2 solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/SnO2 model structure (Model 2) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
Simulation of perovskite-based CuI/CH3NH3PbI3/ZnO solar cell performance
Open Research DataThe presented data set is part of the theoretical research on novel thin-layer lead-halide perovskite solar cells with different inorganic transparent conductive oxides used as charge transport layers. In this study CuI/CH3NH3PbI3/ZnO model structure (Model 3) was investigated by the use of the SCAPS-1D simulation method (https://scaps.elis.ugent.be/).
-
The electrochemical response to BDD electrode functionalization with CD147 receptor
Open Research DataThis dataset contains the results of the electrochemical impedance spectroscopy (EIS) measurements of the boron-doped diamond (BDD) electrode functionalization with CD147 receptor. The functionalized electrode was then used for the electrochemical detection of the SARS-CoV-2 virus S1 protein.
-
The electrochemical response to BDD electrode functionalization with ACE2 receptor
Open Research DataThis dataset contains the results of the electrochemical impedance spectroscopy (EIS) measurements of the boron-doped diamond (BDD) electrode functionalization with ACE2 receptor. The functionalized electrode was then used for the electrochemical detection of the SARS-CoV-2 virus S1 protein.
-
The electrochemical response to BDD electrode functionalization with IgG2B receptor
Open Research DataThis dataset contains the results of the electrochemical impedance spectroscopy (EIS) measurements of the boron-doped diamond (BDD) electrode functionalization with IgG2B receptor. The functionalized electrode was then used for the electrochemical detection of the SARS-CoV-2 virus S1 protein.
-
Electrochemical studies for screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Open Research DataThis dataset contains electrochemical examination of SPCE paste and SPCE containing boron-doped diamond BDD foils. The studies include kinetics analyses with cyclic voltammetry and electrochemical impedance spectroscopy with different redox probes: hexacyanoferrate(III) and Hexaammineruthenium(III) and potentiostatic open circuit potential at different...