Katalog Danych Badawczych
-
Magnetic flux leakage signals of near side defects measured with different velocities
Dane BadawczeThe dataset contains raw signals measured with the use of the magnetic flux leakage (MFL) technique. Linear Hall effect sensors A1324 were used to measure magnetic flux leakage. Three voltage signals were measured: Bx sensor output, Bz1 sensor output, and difference of Bz1 and Bz2 outputs. An output of a Bx sensor was directly proportional to the tangential...
-
Temperature of formation of Au nanostructures
Dane BadawczeNanostructures were obtained via annealing of thin Au films. In order to determine possible nanoislands formation mechanisms, dependence on initial film thickness was examined. For the surface morphology studies, nanograin structure and chemical composition analysis, SEM, HR TEM and EDS measurements were performed, respectively. Morphology studies shown...
-
Structure and optical measurements of Eu doped tellurium oxide thin films
Dane BadawczeThin films were deposited by magnetron sputtering method and simultaneously heated at 200 oC. Presence of Eu ions and their valence states was confirmed by X-ray photoemission spectroscopy measurements. The structure of the films as well as the influence of europium dopant on crystalline structure of the films was examined by X-ray diffraction method. ...
-
The structure of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
The structure of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All samples were prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
The structure of lead-borate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe structure of iron-doped glasses and glass-ceramics were studied. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate and...
-
The morphology of lead-borate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped borate glasses and glass-ceramics were studied. Samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 < x < 37 in mol%) were prepared by the conventional meltquenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated (573 K) brass plate...
-
Magnetic properties of of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeMagnetic properties of iron-doped glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15 and 20 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere...
-
Electrical properties of nanostructures in lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeElectrical properties of iron oxide nanostructures observed in silicate glasses and glass-ceramics were studied. Two different sets of glass samples were prepared. The first group of samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO– xFe2O3, where x = 15, 20 and 25 (in mol%). Composition of the second group was 50SiO2–(50−x)PbO–xFe2O3, where...
-
The morphology of lead-silicate glasses and nanocomposites doped with iron oxide
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of 50SiO2–(50−x)PbO–xFe2O3, where x=15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass plate preheated to 573...
-
The morphology of lead-silicate glasses containing nanocrystallites of iron oxides
Dane BadawczeThe topography of iron-doped glasses and glass-ceramics were studied. Samples has the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in air at 1623 K in alumina crucibles. The melts were poured on a brass...
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Dane BadawczeElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
Linear and nonlinear impedance of alkali and iron doped silicate-lead glasses
Dane BadawczeLinear and nonlinear impedance was studied for lead-silicate glass samples doped with iron ions and alkaline oxides. The compositions of glasses were as follows: (in %mol) 50% SiO2, 25% PbO, 15% Fe2O3 and 15% one of alkaline oxides: Na2O, K2O, Li2O. All samples were prepared by the conventional melt quenching technique. The substrates were powdered...
-
Electrical properties of silicate-lead glasses containing nanostructures of iron oxides.
Dane BadawczeElectrical properties of silicate-lead glasses doped with different content of iron oxide was studied. The set of glass samples were prepared with the composition of (50 − 0.5x)SiO2–(50 − 0.5x)PbO–xFe2O3, where x = 2, 5, 10, 15, 20 and 25 (in mol%). All sampleswere prepared by the conventional melt quenching technique; the melting was conducted in...
-
Linear and nonlinear impedance of iron containing silicate glasses
Dane BadawczeThe linear and nonlinear impedance ofglasses doped with iron oxide were measured. Glass samples (50 SiO2-50-xPbO-xFe2O3 in mol%) were prepared by the conventional melt quenching technique. The substrates were powdered in a mortar and melted in Al2O3 crucibles. The melting was conducted in air at 1623K. The melts were poured out on plate heated up to...
-
SEM micrographs of NH4VO3 crystals
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 crystals obtained by the LPE-IonEx method. The SEM images clearly show that the morphology of the end product can be nicely tuned by changing the type of ammonium salt and the solvent. It can be concluded that the used solvent affected crystal shapes and their size was...
-
Thermal behaviour of NH4VO3 elongated microcrystals
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate elongated microcrystals under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass...
-
Thermal behaviour of NH4VO3 microcasketoids
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microcasketoids under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 microflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate microflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Thermal behaviour of NH4VO3 nanoflowers
Dane BadawczeThe DataSet contains the results of the thermal behavior of the ammonium metavanadate nanoflowers under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also studied with mass spectrum...
-
Structure of ammonium vanadate synthesis by LPE-IonEx method
Dane BadawczeThe DataSet contains the XRD patterns, FTIR spectra of NH4VO3 crystals with different morphology obtained by the LPE-IonEx method.
-
Morphology and structure of ammonium vanadates synthesis by hydrothermal method
Dane BadawczeThe DataSet contains the XRD patterns, FTIR spectra, and scanning electron microscopy (SEM) micrographs of ammonium vanadates synthesis by hydrothermal method from different NH4VO3 precursors. The results reveal that a mixture of (NH4)V4O10xH2O and(NH4)0.76V4O10 was obtained for both precursors, however the contribution of each phase was different for...
-
Thermal behaviour of commercial avaible NH4VO3
Dane BadawczeThe DataSet contains the results of the thermal behavior of the commercially available ammonium metavanadate (CAS 7803-55-6) under argon and nitrogen atmosphere. Thermogravimetric analysis (TG) was carried out under argon or nitrogen atmosphere from 40C to 560C (with a heating rate of 10 C/min) using Netzsch STA 449 F1. The thermal behavior was also...
-
TEM micrographs of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the TEM images of ammonium vanadate nanobelts obtained by the hydrothermal method with different conditions. The results show that the microstructure of an ammonium vanadate single nanobelt dependent on reaction condition.
-
SEM micrographs of NH4VO3 crystals - molar concetration factor
Dane BadawczeThe DataSet contains the scanning electron microscopy (SEM) micrographs of NH4VO3 nano_crystals obtained by the LPE-IonEx method. The SEM images clearly show that the morphology of the end product can be nicely tuned by changing the molar concentration of ammonium salt in the solvent.
-
XRD patterns of ammonium vanadate nanocrystals
Dane BadawczeThe DataSet contains the XRD patterns of ammonium vanadate nanobelts obtained by the hydrothermal method with different conditions. The results show that the structure and phase compositions of samples dependent on reaction conditions.
-
Raw data for the paper "Mutually polarizable QM/MM model with in situ optimized localized basis functions"
Dane BadawczeThis dataset contains raw data used to generate plots in the paper Mutually polarizable QM/MM model with in situ optimized localized basis functions. The paper is devoted to a second generation of the TINKTEP model -- an QM/MM approach combining linear-scaling DFT (ONETEP) and a polarizable force field (AMOEBA).
-
AFM images of the platinum (111) single crystal surface as delivered, without the polishing treatment
Dane BadawczePlatinum (111) single crystal surface images as delivered, without polishing treatment. Topographic measurements in contact mode. NTEGRA Prima (NT-MDT) device. CSG probe 10.
-
Images of topography and mechanical properties (phase imaging) of cast iron samples from water installations
Dane BadawczeMeasurements in contact and semi-contact mode. NTEGRA Prima (NT-MDT) device. CSG 10.
-
The Mott-Schottky characteristics of microwave pulsed-plasma polymerized allylamine by DEIS analysis
Dane BadawczeThe dataset contains the results obtained for the Mott-Schottky analysis of the microwave pulsed-plasma polymerized allylamine using the multifrequency perturbation signal with Dynamic Electrochemical Impedance Spectroscopy (DEIS) technique. The results were obtained using the perturbation composed of the elementary signals with a frequency range between...
-
Results of calibration of the piezoelectric scanner using the probe TGQ1
Dane BadawczeTeaching file. Results of calibration of the piezoelectric scanner using the probe TGQ1. Scanning in contact mode. NTEGRA Prima (NT-MDT) device. CSG probe 10.
-
The surface of a fragment of the structure of an integrated circuit in the semi-contact mode.
Dane BadawczeThe surface of a fragment of the structure of an integrated circuit. Topographic measurements in the semi-contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
Atomic force microscopy images of copper electrical contacts wear under the influence of friction
Dane BadawczeMeasurement of wear of copper electrical contacts under the influence of friction. Imaging in contact mode in the variant of scanning spreading resistance microscopy. Additionally, there are spectroscopic current-voltage curves showing local changes in electrical conductivity. NTEGRA Prima (NT-MDT) device. Probe NSG 01Pt.
-
Topographic AFM imaging of the leaf surface with magnification of details of its morphological structure
Dane BadawczeTopographic imaging of the leaf surface with magnification of details of its morphological structure. Measurements in semi-contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
The AFM topographic measurements of the surface heterogeneity of iron hexacyanoferrate on a steel surface
Dane BadawczeMeasurements in semi-contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
Mechanical lithography in a polymer substrate using AFM in contact mode
Dane BadawczeMechanical lithography in a polymer substrate. Contact mode. NTEGRA Prima (NT-MDT) device. NSG 01 probe.
-
Integrated circuit structure surface images obtained with contact capacitive imaging technique
Dane BadawczeThe measurements were done using NTEGRA Prima (NT-MDT) device. CSG 10Pt probe.
-
Acoustic emission studies of the 7075 aluminium alloy pitting corrosion process
Dane BadawczeThe dataset contains the cyclic polarization studies and corresponding acoustic emission measurements, revealing the pitting corrosion process of the passive layer at the surface of the 7075 aluminum alloy in the borate buffer with different chloride ions concentrations, in the range between 0.05 and 25 mM.
-
Thermogravimetric measurement (TG) of 20wt.% Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC
Dane BadawczeThe daataset includes the thermogravimetric measurement (TG) of Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC. The mesurement was performed under synthestic air atmosphere. The anode was composed of NiO-YSZ cermet composite (80 wt%) and Ce0.8La0.2O2-s additive (20wt%) with the addition of poroformer - PMMA granules 8um diameter (40 vol.% of whole powder volume)....
-
The changes of outlet gases concentrations from SOFC with Ce(Pr,Sm)O2-s layers
Dane BadawczeThe dataset includes The changes of outlet gases concentrations from SOFC with Ce(Pr,Sm)O2-s layers. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Sm0.2O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Sm0.2O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
Thermogravimetric measurement (TG) of 10 wt.% Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC
Dane BadawczeThe daataset includes the thermogravimetric measurement (TG) of Ce0.8La0.2O2-NiO-YSZ anode for DIR-SOFC. The mesurement was performed under synthestic air atmosphere. The anode was composed of NiO-YSZ cermet composite (90 wt%) and Ce0.8La0.2O2-s additive (10wt%) with the addition of poroformer - PMMA granules 8um diameter (40 vol.% of whole powder volume)....
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.05Sm0.15O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.05Sm0.15O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
Change of reaction quotients for SOFC fueled by biogas mixture at 750 C
Dane BadawczeThe dataset contains the Change of reaction quotients for SOFC fueled by biogas mixture at 750 C (60:40 CH4:CO2). The outlet concentration of the gases from SOFC were measured using novel FTIR-based unit.
-
Electrical measurement data for SOFC fueled by H2 and biogas mixture at 750 C
Dane BadawczeThe dataset contains the Electrical measurement data for SOFC fueled by H2 (30h) and biogas mixture at 750 C (60:40 CH4:CO2). The investigation of long-term electrical stability was performed during initial SOFC feeding with hydrogen (for 30 h) and further with biogas (for 90 h). The electrical properties of the fuel cell were measured using the HAMEG...
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.2O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.2O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.15Sm0.05O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.15Sm0.05O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
Change of catalytic parameters for SOFC fueled by H2 and biogas mixture at 750 C
Dane BadawczeThe dataset contains the Change of catalytic parameters for SOFC fueled by H2 and biogas mixture at 750 C (60:40 CH4:CO2). The outlet concentration of the gases from SOFC were measured using novel FTIR-based unit. The parameters are conversion rates, selectivities and yields of products
-
The electrical properties mesurements of SOFC with Ce0.8Pr0.1Sm0.1O2-s layer
Dane BadawczeThe dataset includes The electrical properties mesurements of SOFC with Ce0.8Pr0.1Sm0.1O2-s layer. Samples were produced using aqueous soft chemistry methods (microemulsion method) and applied in form of a layer onto the anode of the commercial SOFC. The SOFC was working under biogas feeding.
-
Change of exhaust gases concentration for SOFC fueled by H2 and biogas mixture at 750 C
Dane BadawczeThe dataset contains the Change of exhaust gases concentration for SOFC fueled by H2 (for 12h) and biogas mixture at 750 C (60:40 CH4:CO2). The outlet concentration of the gases from SOFC were measured using novel FTIR-based unit.