FTIR spectra of gas mixtures from the process of biogas dry reforming using Al2O3/5%Cu catalyst
Open Research DataThe dataset contains the FTIR spectra collected during the catalytic measurements of dry reforming of biogas (60/40 CH4-CO2) using Al2O3 (TMDAR)/5%Cu nanocatalyst. The specatra were collected every 1 minute from 800C to 500C. Reagent flow was set to 20ml/min.
-
Linear impedance of vanadate glasses containing BaTiO3
Open Research DataThe linear impedance of vanadate glasses doped with BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated (573...
-
Linear impedance of 2Si3N4–98(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of 2Si3N4–98(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.
-
Linear impedance of V2O5 nanorods obtained at 923K
Open Research DataThe DataSet contains the linear electrical properties of V2O5 nanorods which were measured by the impedance spectroscopy method. V2O5 nanorods were obtained by the sol-gel method. The information about xerogel powder synthesis is described in the Journal of Nanomaterials. The precursor powder was pressed into the disk-shaped pellets (12mm in diameter...
-
Performance of Haemophilus influenzae impedimetric biosensors based on screen-printed carbon electrodes (SPCE) with boron-doped diamond foils
Open Research DataThis dataset contains electrochemical impedance spectroscopy studies of SPCE electrodes containing boron-doped diamond BDD foils and functionalized towards detection of Protein D and Haemophilus influenzae.
-
Optical properties of MnO-B2O3 based glass
Open Research DataMnO-B2O3 based glass with Au nanoparticles samples were annealing for a various time (in a range of 24-96 hours) at various temperatures (from 340 up to 350 deg.). Presence of silver nanoparticles was detected by UV-VIS measurements. On the basis of change optical bandgap, Ag NPs was detected.
-
Nonlinear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm (after second heat-treatment at 913 K) was measured by impedance spectroscopy method.
-
Effect of Jerusalem artichoke addition on texture profile of bread
Open Research DataThe dataset contains the results of Jerusalem artichoke addition on the texture of wheat bread. The following bread variants were tested: control bread, bread with 15% and 30% Jerusalem artichoke addition. Measurements were made immediately after baking. On the basis of data, the following parameters were determined: hardness, elasticity, cohesion and...
-
AFM (Atomic Force Microscopy) analysis of surface topography loaded with nickel nanoparticles.
Open Research DataThis dataset presents AFM (Atomic Force Microscopy) images depicting the surface topography loaded with nickel powdered nanoparticles. The detailed equipment and measurement data was described in "AFM readme.txt" file
-
Morphology of the sol-gel derived LTO:Cu films
Open Research DataMorphology of the lithium titanate doped by Cu thin films were investigated by SEM microscope. Films were deposited by spin-coater from sol-gel derived sol. SEM images showed a high porous structure, tipaciall for sol-gel based films. For measurements samples with a various content of Cu were selected.
-
The XRD pattern of CeO2/10wt.%Co prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Co. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement.
-
Solar radiation (PAR, UV-B and UV-A) reaching the sea surface - Gdańsk Deep (2001-2005)
Open Research DataSolar radiation reaching the sea surface was measured in spring (2001, 2003, 2005) and autumn (2002, 2004). For measurements of the photosynthetic active radiation - PAR (400-700 nm), the Ejkelkamp SKP 210 / I 0896 13595 sensor was used, the UV-B radiation (280-315 nm) was measured with the Ejkelkamp SKU 430 0497 14854 sensor, while UV-A (315- 380 nm)...
-
Total electrical conductivity data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Open Research DataThis dataset includes electrical conductivity measurements results measured by van der pauw technique up to 900oC.
-
Effects of liquid phase modification on the values of surface tension of trickling liquid
Open Research DataDataset presents the values of surface tension of trickling liquid sampled from three running biotrickling filters.
-
Images of topography and mechanical properties (phase imaging) of cast iron samples from water installations
Open Research DataMeasurements in contact and semi-contact mode. NTEGRA Prima (NT-MDT) device. CSG 10.
-
Linear impedance of 1SiO2–99(40Na2O-20CaO-40P2O5) glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of 1SiO2–99(40Na2O-20CaO-40P2O5) glass was measured by impedance spectroscopy method.
-
The influence of the temperature treatment method on the quality of French fries.
Open Research DataThe video presents instructional work on the temperature treatment of French fries and the assessment of oil changes during frying. The results of the measurements show that placing the fries in cold oil, heating them to the frying temperature compared to the conventional method of frying, reduces the amount of primary oxidation products and free fatty...
-
The effect of the flaxseed addition on the texture of wheat bread
Open Research DataThe dataset contains the results of flaxseed addition on the texture of toasted bread. The following bread variants were tested: control bread, bread with 8% and 12% linseed addition and competitive bread. Measurements were made immediately after baking and after 4 days. On the basis of data the following parameters were determined: hardness, elasticity,...
-
Structural and luminescence properties of B2O3-Bi2O3+10AlF3 glasses doped with Eu3+/Dy3+ ions
Open Research DataThe attached data contains the results of measurements of B2O3-Bi2O3 and B2O3-Bi2O3+10AlF3 glasses doped with Eu3+ and Dy3+ ions in different molar ratios. Glasses were synthesized by the melt quenching technique. On their basis, the structural, optical, and luminescence properties of synthesized samples were characterized. The dataset includes XRD,...
-
UV/VIS Spectroscopy of titanium dioxide coated nickel foams
Open Research DataThe data includes UV-Vis spectra of titanium dioxide coated nickel foams heated at 400, 500 and 600 C in Ar. Jasco V-650 Spectrophotometer was used and Spectra Measurement software.
-
Investigation of temperature changes using a microsphere-based fiber-optic sensor
Open Research DataInvestigation of temperature changes using a microsphere-based fiber-optic sensor with a 200 nm ZnO ALD coating for the purpose of validation the design of the sensor, measurement setup and method of examination of electric cell materials.
-
Sol-gel derived TeO2:RE powders
Open Research DataTellurium dioxide powders doped by Europium or Dysprosium were prepared by sol-gel method. Samples were annealed in ix of Ar and O2 atomosphere at 600 degrees. Presence of rare earth dopants and Te4+ phase was confirmed by X-Ray Photoemission Spectroscopy method (XPS). For XPS measurements samples with 1 atomic % and 5 atomic % of dopand were selected.
-
Optical transmission of the Niobium thin films
Open Research DataNiobium thin films with a thickness of 200nm were deposited n a Corning glass substrate by magnetron sputtering method. The optical transmission spectra in a visible light range were.recorded. Investigations showed a good optical transmission thru the layers for each samples, annealed at various temperatures. For measurements samples annealed at 500,...
-
Raman data of deuterium and hydrogen grown boron-doped diamond
Open Research DataRaman spectra were recorded at room temperature using a micro-Raman spectrometer (Invia, Renishaw) equipped with an edge filter with different excitation wavelengths and lasers: UV λ = 325 nm (HeCd), blue λ = 488 nm (Ar+), green λ = 514 nm (Ar+), and IR λ = 785 nm (IR diode) and 50× microscope objective. To avoid sample heating, the radiation power...
-
Electrical properties of lead-borate glasses and glass-ceramics containing iron ions
Open Research DataElectrical properties were studied for borate-lead glasses and glass-ceramics doped with iron ions. Glass samples of composition of xFe2O3–(100 − x)(B2O3–2PbO) (2.5 b x b 37, in mol%) were prepared by the conventional melt quenching technique. The melting was conducted in alumina crucibles at the temperature of 1523 K. The melts were poured on a preheated...
-
Dielectric properties of barium-vanadate glasses
Open Research DataThe linear impedance of barium-vanadate glasses was measured. Samples of the composition of xBaO-(100-x)V2O5 where x= 30, 40 and 45 (in %mol) were prepared by the conventional melt quenching technique. Appropriate amounts of reagents: BaO (≥99.9%, P.P.H STANLAB Sp.J.) and V2O5 (≥99.9%, POCH) were thoroughly mixed in an agate mortar. The melting was...
-
Linear impedance of vanadate glass-ceramics containing BaTiO3
Open Research DataThe linear impedance of vanadate glass-ceramics containing BaTiO3 was measured. Samples of the composition of x[BaO,TiO2]–(80 − x)V2O5–20Bi2O3 where x = 5, 10 and 15 in mol% were prepared by a conventional melt quenching technique. The melting was performed in alumina crucibles at the temperature of 1273 K–1373 K. The melts were poured on a preheated...
-
Linear impedance of 58(2Bi2O3-V2O5)-42SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 58(2Bi2O3-V2O5)-42SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of 5(2Bi2O3-V2O5)-95SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 5(2Bi2O3-V2O5)-95SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance of 50(2Bi2O3-V2O5)-50SrB4O7 glass measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrcial properties of 50(2Bi2O3-V2O5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Linear impedance as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass measured with impedance spectroscopy method
Open Research DataThe linear electrcial properties as a function of A.C. voltage for 50(2Bi2O3-V2O5)-50SrB4O7 glass was measured by impedance spectroscopy method.
-
Investigations of the valence state of Co in a MnCoO ceramics
Open Research DataMcCoO ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. Chemical behaviour of the Cobaltium was measured by XPS method. The analyses were...
-
Photocatalytic decomposition of ethylene on the TiO2-polystyrene spheres
Open Research DataData contain results from the measurements of the photocatalytic decomposition of ethylene under UV irradiation with using TiO2 coating on the expanded polystyrene spheres (EPS). EPS-SiO2-TiO2 and EPS-TiO2 were used as the photocatalytic beds in the fluidized bed reactor. Both, stationary and fluidized beds were tested. The comparison of ethylene decomposition...
-
Influence of controlled crystallization and SrF2 content on the structure and properties of Eu3+ doped phosphate glasses
Open Research DataThe attached data contains the results of measurements of phosphate glasses and glass-ceramics doped with Eu. On their basis, the new material was characterized and the influence of the SrF2 addition on the glass structure was determined. In addition, the influence of the SrF2 content and controlled crystallization on the luminescent properties of Eu3+...
-
Determination of changes in viscosity of poly(acrylic acid) PAA solutions depending on shear rate.
Open Research DataThe rheological characteristics of poly(acrylic acid) PAA solutions were based on viscosity measurements using a Brookfield viscometer, using LV SC4 - 27 spindles and shear rates from 1,7 to 39 s-1 (Fig. 1). PAA solutions with were prepared in water. The data allowed to characterize the used PAA and assess their functional parameters as rheology modifying...
-
The XAS spectra of O-K edges, M-L edges and Ce-M edges in Ce0.9M0.1O2
Open Research DataThe dataset consists of XAS spectra of O-K edges, M-L edges of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) synthesised by reverse microemulsion method. XAS spectra were collected at PIRX beamline in SOLARIS National Synchrotron Radiation Centre. Measurements were perfomed under ultra high vacuum in total electron yield (TEY) mode.
-
Thermal behaviour of vanadium xerogel powder under different inert atmosphere
Open Research DataThe DataSet contains the results of the thermal behavior of the vanadium xerogel powder. The information about xerogel powder synthesis is described in the Journal of Nanomaterials.
-
Monitoring of Explosive Nitroaromatic Tetryl
Open Research DataSource data used for the publication entitled "sp2-rich Dendrite-like Carbon Nanowalls as Effective Electrode for Environmental Monitoring of Explosive Nitroaromatic Tetryl".1. SEM files2. TEM files3. XPS files4. Electrochemical measurements5. Raman files
-
Mercury intrusion porosimetry (MIP) results of cement pastes containing Bi2O3/Gd2O3 and silica-coated Bi2O3/Gd2O3 structures
Open Research DataMercury intrusion porosimetry (MIP) data - curves of cement pastes containing Bi2O3/Gd2O3 and silica-coated Bi2O3/Gd2O3 structures
-
The XRD pattern of CeO2/10wt.%Ni prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4h in air.
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
The TPR reduction profile of Ce0.9M0.1O2
Open Research DataThe dataset includes the TPR reduction profiles of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) nanopowders prepared by the reverse microemulsion method. After the synthesis powders were dried, then calcined at 500 degrees for 2 h. The measurements were carried out in H2/Ar mixture from 100C to 900C. Gas flow:40ml/min and temperature ramp: 10deg/min.
-
Dilatometry results of SrTi0.50Fe0.50O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.50Fe0.50O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.50Fe0.50O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.65Fe0.35O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.65Fe0.35O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.65Fe0.35O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Dilatometry results of SrTi0.30Fe0.70O3-d powder
Open Research DataThis dataset contains results of dilatometry measurements of SrTi0.30Fe0.70O3-d powder. The investigation of the linear thermal expansion was carried out using a Netzsch DIL402 dilatometer. The SrTi0.30Fe0.70O3-d powder was formed into cylinders and heat up to 1100 °C with a heating rate of 5 °C min−1, dwelled for 15 min, and then cooled at a rate of...
-
Sierakowice 2020- video data
Open Research DataSierakowice 2020- video data
-
The XRD pattern of CeO2/10wt.%Mn prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Mn. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Fe prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Fe. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The XRD pattern of CeO2/10wt.%Ni with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor nitrate solution (betacyclodextrin). The dataset includes 5-90 2 theta degree measurement. Nonreduced. Sintered at 400oC for 4h.