Dissimilar autogenous TIG joint of Alloy 617 and AISI 304H steel for AUSC application
PublicationTo reduce costs and improve high-temperature performance in Advanced Ultra Super Critical (AUSC) boilers, it is necessary to weld austenitic steel to Inconel alloy. In this study, the autogenous tungsten inert gas (TIG) welding process was used to join Alloy 617 and an austenitic AISI 304H steel plate of thickness 5 mm. Microstructural analysis showed that the microstructure formation was uneven along the weldments, with columnar...
-
Guided wave propagation in debonding detection in CFRP-reinforced steel plate-like structures
PublicationThe present study investigates the guided wave propagation in multilayered steel specimens reinforced with carbon fiber reinforced polymer (CFRP) through theoretical, numerical, and experimental means. The effectiveness of externally bonded reinforcement (EBR) relies heavily on the bonding quality between the CFRP and the substrate. Premature debonding, a prevalent and hazardous defect, can arise from suboptimal manufacturing processes,...
-
FRP-based reinforcement coatings of steel with application prospects in ships and offshore structures: a review
PublicationLatest research on novel FRP-based anti-corrosion structural coatings (for enhancing structural capacity and strengthening the coating layer) is discussed with application prospects for ships and offshore structures. In the marine environment, structures constantly face corrosion and fatigue cracks. Combining this with high operational and wave loads, it might cause a structural collapse. Recently, polymer composites have been...
-
Experimental study on models of cylindrical steel tanks under mining tremors and moderate earthquakes
PublicationThe aim of the study is to show the results of complex shaking table experimental investigation focused on the response of two models of cylindrical steel tanks under mining tremors and moderate earthquakes, including the aspects of diagnosis of structural damage. Firstly, the impact and the sweep-sine tests have been carried out, so as to determine the dynamic properties of models filled with different levels of liquid. Then,...
-
The influence of the carbon equivalent on the weldability of high-strength low-alloy steel in the water environment
PublicationFrom many years, the high strength low alloy steels are often used for offshore constructions. This constructions, due to the environment in which they work, require more frequent repairs than the constructions from the land. For economic reasons, repairs take place in the underwater conditions, however water significantly decreases the weldability of steel. The paper presents the results of the CTS weldability test for S460ML...
-
Influence of steel brackets supporting crane runway girders structure on the stress distribution in the brackets
PublicationThe paper presents a numerical analysis of steel brackets supporting a double-span crane runway girders. The purpose of the study was to assess the new structural solution based on the stress distribution in the brackets. In order to simplify the connection, the bottom flange of the crane runway girder is based directly on the upper flange of the bracket. As a result, the support reaction is no longer applied in the plane of the...
-
Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel
PublicationThis paper examined the cyclic deformation behaviour of multiphase low-carbon steel that was subjected to austempering heat treatments at four temperatures (190 °C, 230 °C, 275 °C, and 315 °C) below the martensite start temperature (Ms = 353 °C). The tests were conducted at room temperature, under fully reversed strain-controlled conditions, with strain amplitudes in the range 0.5–1.0%. The microstructure was observed by transmission...
-
Impact of steel grade on a ship colliding with an offshore wind turbine monopile supporting structure
PublicationOffshore wind power is experiencing rapid development around the world. The number of installations and their size is growing. Thousands of monopile support structures with diameters of 10 m and weights of 2000 tons will be installed in the coming years. Offshore wind power installations, often located close to the shore and shipping routes, pose a new challenge to ship safety. The study analyses the damages from an accidental...
-
Complementary study with magnetic and acoustic techniques of A336 steel damage state due to creep
PublicationBadano możliwość detekcji w sposób nieniszczący zmian w mikrostrukturze stali A336 poddanej próbie pełzania. Testowano dwie magnetyczne techniki (klasyczny efekt Barkhausena i emisję magnetoakustyczną) oraz dwie nowe techniki ultradźwiękowe (pomiar współczynnika elasto-akustycznego oraz dwójłomność akustyczną). Wykazano, iż wyniki badań akustycznych są komplementarne do wyników badań magnetycznych.
-
Specific risks for local stability and capacity of verticat doble - shell cylindrical steel tanks
PublicationOmówiono zagrożenia stateczności i nosności płaszczy zbiorników dwupłaszczowych wywołane przez: niefachowo prowadzoną próbę wodną, dużną różnicę temperatury podczas eksploatacji oraz nierównomierne osiadanie. W księdze konferncyjnej opublikowano dwustronicowe streszczenie referatów a na załączonej płycie referaty zamieszczone są w całości.
-
Simulation of fracture process in concrete elements with steel fibres using discrete lattice model
PublicationArtykuł omawia wyniki modelowania procesu zarysowania w elementach betonowych zawierające stalowe włókna przy zastosowaniu dyskretnego modelu kratownicowego. Beton był modelowany na poziomie mezoskali z uwzględnieniem 5 faz: kruszywa, zaczynu cementowego, włókien i obu stref kontaktu. Obliczenia wykonano dla jednoosiowego ściskania, jednoosiowego rozciągania i zginania prostego.
-
Effect of steel fibres on concrete behavior in 2D and 3D simulations using lattice model.
PublicationW artykule przedstawiono wyniki numerycznej symulacji betonu zbrojonego włóknami stalowymi. Beton został opisany w skali mezo jako materiał 3-fazowy przy zastosowaniu modelu sieciowego. Obliczenia wykonano dla rozciągania jednoosiowego. Porównano ze sobą wyniki dwu- i trójwymiarowe.
-
Full-scale experiments on wheat flow in steel silo composed of corrugated walls and columns
PublicationArtykuł omawia wyniki doświadczalne w dużej skali odnośnie przepływu pszenicy w stalowym silosie wykonanym z blachy falistej i słupów. Pomierzono napory poziome i pionowe na ścianie oraz siły pionowe w słupach. Zbadano rodzaj przepływu w zależności od położenia wylotu. Wyniki naporów porównano z Eurokodem.
-
Experimental and numerical investigations of size effects in reinforced concrete beams with steel or basalt bars.
PublicationW artykule przedstawiono wyniki obliczeń efektów skali w belkach betonowych zbrojonych prętami stalowymi i bazaltowymi podczas zginania. Zastosowano model sprężysto-plastyczny z nielokalnym osłabieniem. Rozkład wytrzymałości na rozciąganie był stochastyczny – przestrzennie skorelowany. Belki były geometrycznie podobne. Wyniki porównano z modelem efektu skali Bazanta
-
Hydrogen degradation of high strength weldable steels
PublicationW pracy przedstawiono wyniki badań podatności stali spawalnych o wysokiej wytrzymałości na niszczenie wodorowe. Badano dwa gatunki stali S690Q i ich złącza spawane. Ocenę podatności na niszczenie wodorowe wykonano przy różnych rodzajach obciążeń w środowisku wody morskej przy polaryzacji katodowej.
-
Hydrogen degradation of high strength weldable steels
PublicationW pracy przedstawiono wyniki badań podatności stali spawalnych o wysokiej wytrzymałości na niszczenie wodorowe. Badano dwa gatunki stali S690Q i ich złącza spawane. Ocenę podatności na niszczenie wodorowe wykonano w oparciu o próbę rozciągania z małą prędkością odkształcania w powietrzu i środowisku wody morskiej przy polaryzacji katodowej. Przedstawiono model niszczenia wodorowego badanych stali i ich złączy spawanych.
-
Properties of Vacuum Sintered Duplex Stainless Steels
Publication -
Properties of vacuum sintered duplex stainless steels
Publication -
Properties of Vacuum Sintered Duplex Stainless Steels
Publication -
Sintered Duplex Stainless Steels Corrosion Properties
Publication -
Sintered Duplex Stainless Steels Corrosion Properties
Publication -
Dissimilar underwater wet welding of HSLA steels
PublicationThe high-strength low-alloy S460ML and S460N steels were chosen for underwater wet welding of dissimilar T-joints using covered electrodes. For improving the quality of joints, the temper bead welding (TBW) method was used. The application of TBW in pad welding conditions has been investigated earlier but the possibility of usage of this technique in welded joints was not analyzed. The main aim of the study was to check the influence...
-
IMPACT-TOUGHNESS INVESTIGATIONS OF DUPLEX STAINLESS STEELS
PublicationDuplex stainless steels are very attractive constructional materials for use in aggressive environments because of their several advantages over austenitic stainless steels. Duplex steels have excellent pitting and crevice corrosion resistance, are highly resistant to chloride stress-corrosion cracking and are about twice as strong as common austenitic steels. Better properties are associated with their microstructures consisting...
-
Measurements of the mechanical Barkhausen noise in ferromagnetic steels
PublicationArtykuł ten przedstawia wpływ zmian w mikrostrukturze stali P91, powstałych w skutek obróbki cieplnej, na właściwości mechanicznego efektu Barkhausena (MeBN). Parametry takie jak amplituda obwiedni napięcia skutecznego (RMS) MeBN oraz położenie maksimum tejże obwiedni porównywane są, pod kątem czułości na obróbkę cieplną materiału, z klasycznymi parametrami takimi jak pole koercji magnetycznej czy też twardość mechaniczna HV. Największą...
-
Hydrogen Damage in Superaustenitic 904L Stainless Steels
Publicationresults on the influence of hydrogen on corrosion resistance and of hydrogen embrittlement of 904L superaustenitic stainless steel were investigated. The cracking behavior was studied by performing a slow strain rate test in synthetic seawater under varying cathodic polarization conditions. The results showed that the steel’s plasticity varied with the applied cathodic current density. Significant reductions in ductility were found,...
-
Application of molecularly imprinted polymer pipette tip micro-solid phase extraction of nalidixic acid and acetaminophen from pills and seawater samples and their determination by spectrophotometry
Publication -
Experimental studies on the impact of changing the pipe material on the propagation of the pressure wave during water hammer
PublicationAim of the paper is to present the results studying the water hammer phenomenon in pipes made of different materials, and to show the impact of changing the type of material of the pipe on the velocity of the pressure wave during the transient flow in the pipes. In terms of research material and methods, pipes made of galvanized steel and high-density polyethylene were tested. Measurements were made using strain gauges with a high...
-
state aid for steel sector in the EU
Open Research DataThe dataset encompassed a choice of most important UE and Polish legal acts, a list of selected Polish and foreign bibliography and a list of important individual decisions issued on the topic of state aid for steel industry in the UE. The significance of this topic is undoubted, as the steel industry is one of the most important UE production branches....
-
Strucutral steel - tensile test results
Open Research DataModern floating structures such as ships, oil platforms and offshore wind towers are built mostly of structural steel. It is a material that is subject to requirements which, when met, allows the construction and safe operation of the structure throughout its entire work cycle. One of the basic criteria that a material must meet is its strength. The...
-
Results after grinding C45 steel
Open Research DataThe database contains results from nanoindenter, scanning microscope and also X-ray diffractometer. To determine the residual stresses and the size of the crystallites in the ferrite grains in the grinded surface layer, the Williamson Hall analysis of the X-ray diffraction patterns was performed. XRD diffraction patterns were also used to perform a...
-
The features of steel surface hardening with high energy heating by high frequency currents and shower cooling
Publication -
Numerical Modeling of Steel Surface Hardening in the Process of High Energy Heating by High Frequency Currents
Publication -
Construction and Validation of Simulation Models of Samples Made from 316L Steel by Applying Additive Technique
Publication -
High temperature corrosion of steel equipment in modern rafinery environments with high and low sulphur content
PublicationPrzedstawiono charakterystykę i mechanizmy procesów wysokotemperaturowej korozji elementów ze stali we współczesnych rafineriach ropy naftowej podczas eksploatacji we frakcjach węglowodorowych o niskiej i wysokiej zawartości siarki. Zwrócono uwagę na procesy korozji siarkowej w obecności wodoru i bez obecności wodoru oraz proces pylenia metalu pod wpływem węgla ze środowiska - w wypadku niskiej zawartości siarki w środowisku.
-
Microscopic impact of creep damage incipience and development on the magnetic properties of ferromagnetic Cr-Mo steel
PublicationPokazano wyniki badań emisji magneto-akustycznej (EMA0 oraz magnetostrykcji dla stali P22 w stanie dostawy i po ekploatacji. Wyniki te pokazują, że maksimum EMA jest skorelowane z maksimum pochodnej magnetostrykcji. Badania morfologii wydzieleń w granicach ziarn i w ich wnętrzu potwierdzają tezę, iż te pierwsze są główną przyczyną zmniejszania natężenia EMA. Zaproponowano prosty model tłumaczący ilościowo funkcję zmian natężenia...
-
Post-failure fracture surface analysis of notched steel specimens after bending-torsion fatigue
Publication -
Analysis of fracture roughness parameters of S355J2 steel and EN AW-2017A-T4 aluminium alloy
Publication -
Structural and Microhardness Changes After Turning of the AISI 1045 Steel for Minimum Quantity Cooling Lubrication
Publication -
SURFACE TEXTURE ANALYSIS AFTER BALL END MILLING WITH VARIOUS SURFACE INCLINATION OF HARDENED STEEL
Publication -
Optimisation of machining parameters during ball end milling of hardened steel with various surface inclinations
Publication -
Assessment of Corrosive Behaviour and Microstructure Characterization of Hybrid Friction Stir Welded Martensitic Stainless Steel
PublicationThis study examined the effect of induction heating on the microstructure and corrosion characteristics of hybrid friction stir welded AISI 410 stainless steel. Five joints have been produced with different friction stir welding parameters like welding speed, spindle speed, plunge depth, and induction power. Their microstructures were evaluated using a scanning electron microscope, and chemical composition was examined using...
-
Fracture Areas Quantitative Investigating of Bending-Torsion Fatigued Low-Alloy High-Strength Steel
PublicationIn this study, the impact of pseudo-random non-proportional bending-torsion fatigue loadings proportion on the fatigue life and the fracture surface topography was analyzed. Investigation was carried out for 24 specimens made of S355J2 steel with 11 different ratios of maximum stresses λ. For these cases, after the fatigue tests, the surface topography measurements were carried out using an optical profilometer, using the focus...
-
Experimental analysis of the behaviour of different types of joints in the steel structure model subjected to earthquake loading
PublicationThe present paper reports the results of the experimental study performed to investigate the behaviour of two different types of joints (destroyed and welded ones) in the model of the steel structure under seismic excitations. The structure was subjected to three earthquakes, namely Kobe, Loma Prieta and Northridge, using the shaking table investigation. The results obtained from the study...
-
Stress–strain model of lower corroded steel plates of normal strength for fitness-for-purpose analyses
PublicationThis study investigates the mechanical properties of specimens made of normal strength steel subjected to lower marine immersed corrosion degradation levels (below 25 %). The specimens were corroded in laboratory conditions, and only natural factors were controlled to raise the corrosion rate (reaching the level of 1 mm/year). Three different thicknesses of plates made of normal strength of shipbuilding steel are investigated (between...
-
EXPERIMENTAL AND NUMERICAL INVESTIGATION ON SPECIMEN GEOMETRY EFFECT ON THE CTOD VALUE FOR VL-E36 SHIPBUILDING STEEL
PublicationThere are special cases in the marine industry, where additional material tests, such as the fracture toughness test, must be performed. Additional fracture toughness tests, such as CTOD (Crack Tip Opening Displacement), are typically performed on three-point bend specimens. The dimension that defines all the specimen dimensions is the thickness of the material to be tested. It is recommended by classification societies (e.g. DNVGL)...
-
Glass-ceramic sealants and steel interconnects: accelerated interfacial stability and reactivity tests at high temperature
PublicationHigh-temperature reactions between glass-ceramic sealants and Fe-Cr alloy interconnects may lead to the formation of undesirable phases, and consequently degradation of solid oxide fuel/electrolyser devices. In this work, three different glass-ceramic sealants (Na-containing, Ba-containing, Sr-containing compositions) and Fe22Cr stainless steel powders (raw and pre-oxidised) are considered in order to test their chemical reactivity...
-
Preventing of earthquake-induced pounding between steel structures by using polymer elements – experimental study
PublicationPounding between two, or more, adjacent buildings during earthquakes has been identified as one of the reasons for substantial damage or even total collapse of colliding structures, so it has been the subject of numerous studies in the recent years. A major reason leading to interactions between adjacent, insufficiently separated structures results from the differences in their dynamic properties. A number of different methods...
-
THE COST ANALYSIS OF CORROSION PROTECTION SOLUTIONS FOR STEEL COMPONENTS IN TERMS OF THE OBJECT LIFE CYCLE COST
PublicationSteel materials, due to their numerous advantages - high availability, easiness of processing and possibility of almost any shaping are commonly applied in construction for carrying out basic carrier systems and auxiliary structures. However, the major disadvantage of this material is its high corrosion susceptibility, which depends strictly on the local conditions of the facility and the applied type of corrosion protection system....
-
Improvement of Performance Level of Steel Moment-Resisting Frames Using Tuned Mass Damper System
PublicationIn this paper, parameters of the tuned mass dampers are optimized to improve the performance level of steel structures during earthquakes. In this regard, a six-story steel frame is modeled using a concentrated plasticity method. Then, the optimum parameters of the Tuned Mass Damper (TMD) are determined by minimizing the maximum drift ratio of the stories. The performance level of the structure is also forced to be located in a...
-
The Influence of the Depth of Cut in Single-Pass Grinding on the Microstructure and Properties of the C45 Steel Surface Layer
PublicationThe paper contains the results of a metallographic examination and nanoindentation test conducted for the medium carbon structural steel with low content of Mn, Si, Cu, Cr, and Ni after its grinding to a depth ranging from 2 μm to 20 μm, at constant cutting speed (peripheral speed) of vs = 25 ms−1 and constant feed rate of vft = 1 m/min. Applied grinding parameters did not cause the surface layer hardening, which could generate...