TEM data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Open Research DataThis Dataset include presentation of summarized TEM investigation of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited...
-
SEM/EDX data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Open Research DataThis Data set include SEM and EDX results of (Mn,Co,Fe,Ni,Cr)3O4 high-entropy spinel oxide prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers were characterised after exposure to temperatures in the range of 400–900 ◦C. The as-deposited layers were amorphous,...
-
Total electrical conductivity data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe
Open Research DataThis dataset includes electrical conductivity measurements results measured by van der pauw technique up to 900oC.
-
XRD data of (Cr,Fe,Mn,Co,Ni)3O4 High-entropy spinel oxide thin films deposited on amorphous SiO2 substrate by spray pyrolysis techniqe, annealed in a range from 400 to 900oC
Open Research DataDataset include collected XRD data of (Cr,Fe,Mn,Co,Ni)3O4 high-entropy spinel oxide thin films deposited by spray pyrolysis technique on amorphous SiO2 substrates and annealed from 400 to 900oC. Samples were prepared in the form of a ~ 500 nm thin film utilising a facile spray pyrolysis technique. The structural and electrical properties of the layers...
-
SEM examination of surface layer of C45 steel after grinding on defferent depth
Open Research DataFerrite examination for the medium carbon structural steel with low content of Mn, Si, Cu, Cr and Ni after its grinding to a depth of 2 µm, 8 µm, 14 µm and 20 µm, at constant wheel circumferential speed of vs = 25 m/s and constant feed rate vft = 1 m/min. It was shown that the grinding of C45 steel causes strong work hardening of ferrite in surface...
-
Microscopic examination of CuNiFeR pipeline
Open Research DataCopper and nickel alloys called cunifers (Cu, Ni, Fe and R – rest of alloy elements) have found wide application in the production of ship pipeline components in contact with sea water, such as, for example, the main engine cooling system. These alloys are characterized by a very high corrosion resistance, which is ensured by appropriately carried out...
-
Macroscopic examination of CuNiFeR pipeline
Open Research DataCopper and nickel alloys called cunifers (Cu, Ni, Fe and R – rest of alloy elements) have found wide application in the production of ship pipeline components in contact with sea water, such as, for example, the main engine cooling system. These alloys are characterized by a very high corrosion resistance, which is ensured by appropriately carried out...
-
Tensile test of part of CuNiFeR pipeline
Open Research DataCopper and nickel alloys called cunifers (Cu, Ni, Fe and R – rest of alloy elements) have found wide application in the production of ship pipeline components in contact with sea water, such as, for example, the main engine cooling system. These alloys are characterized by a very high corrosion resistance, which is ensured by appropriately carried out...
-
Morphology and conductivity investigations of nickel-molybdenium alloy by means of Scanning Spreading Resistance Microscopy
Open Research DataElectrolytically deposited nickel-molybdenum alloys are interesting materials because of their high corrosion resistance and low over-potential for hydrogen evolution. Despite many studies devoted to the deposition of these alloys, the mechanism of co-deposition is not fully understood [1]. The aim of the research was to preserve the electrochemically...
-
Elemental composition of deposited sediments at the tram-route junction
Open Research DataThis data set contains the elemental composition results of deposited sediments collected at the tram-route junction in Gdańsk. Sample collection began in July 2022, when the tram lines were completed and before the rails were scrubbed (27/07/2022). The second sample round was carried out following rail scrubbing in October 2022 (7/10/2022). Since February...
-
The influence of microstructure on the corrosion resistance for some titanium-based alloys
Open Research DataThis dataset contains scanning electron microscopy (SEM) micrographs revealing the microstructure of some Ti-based alloys, namely: Ti-6Al-4V (file name: TiV), Ti-6Al-7Nb (file name: TiNb) and TC21 (file name: TiAlSnZrMoCrNbSi) alloys and their localized corrosion as a result of passive layer breakdown in a corrosive environment, ie. 0.9% NaCl solution...
-
Nanoindentation tests of the hydroxyapatite composite coatings applicated on titanium alloys by the electrophoretic method
Open Research DataCurrently, there are no metal materials that meet all biomechanical and biochemical requirements needed for long life implantable biomaterials. The main purpose of the study was to functionalize the surface of the titanium alloys used in biomaterial implants.
-
Detection of UPEC IH11128 ability to form biofilm in a standard congo red (CR) method of colony staining.
Open Research DataA standard method of testing E. coli's ability to form biofilm is based on the analysis of morphologyof bacterial colonies grown on yeast extract/casamino acids (YESCA) nutrient agar medium containing congored (CR) as an indicator dye of ECM production. The CR dye adsorbed from the culture medium bybacteria binds to the components of the ECM, including...
-
Temperture-programmed reduction (H2-TPR) of Ni-Mo2CTx_Mo2Ga2C and Ni-Mo2CTx_Mo3AlC2 catalysts
Open Research DataThe dataset includes the data for the preparation of plots illustrating the reduction peaks versus the temperature of the catalyst sample.
-
The microstructure of aluminium alloys AA1050 and AA7075 subjected to anodic polarization at 8V in KOH electrolyte
Open Research DataThe dataset contains SEM pictures of the microstructure of aluminum alloy AA1050 and AA7075 exposed in aqueous KOH in the pH range between 14–11. Two sets of samples are presented, revealing the topography of the alloys when exposed to aggressive media under open circuit potential conditions as well as when subjected potentiodynamic polarization ranging...
-
The XRD pattern of CeO2/10wt.%Ni with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor nitrate solution (betacyclodextrin). The dataset includes 5-90 2 theta degree measurement. Nonreduced. Sintered at 400oC for 4h.
-
The XRD pattern of CeO2/10wt.%Ni prepared with BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4h in air.
-
The TPO oxidation profile of CeO2/10wt.%Ni with BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
BET adsorption-desorption isotherm of nano-CeO2 impregnated with Ni
Open Research DataThe dataset includes the isotherms of adortion and desorption of N2 at LN2 temperature. The sorption isotherms were obtained using Quatachrome NovaTouch LX1 equippment. The catalyts powder composed of nanoCeO2 impreganted with Ni oxide nanoparticles with the usage of BCD (Beta-cyclodextrins) and without addition.
-
The XRD diffraction patterns of Ce0.8La0.2O2/Ni prepared using soft template method and impregnation
Open Research DataThe dataset includes XRD patterns of Ce0.8La0.2O2-s nanopowders (nanoparticles,nanocatalyst) prepared using soft template method and further impregnated with 10wt.%Ni using aqueous nitrate solution.
-
The XRD pattern of CeO2/10wt.%Ni prepared without BCD
Open Research DataThe dataset includes the XRD pattern of CeO2/10wt.%Ni. The samples of nanoCeO2 were impregnated without BCD-assisted precursor solution (betacyclodextrin) - pure nitarte solution 1M. The dataset includes the 5-90 2theta degree measurement. Nonreduced. Sintered at 400oC for 4 h in air.
-
The TPO oxidation profile of CeO2/10wt.%Ni without BCD - prereduced
Open Research DataThe dataset includes the TPO oxidation profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes oxidation profile of the prereduced sample.
-
The TPR reduction profile of CeO2/10wt.%Ni with BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated with BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
Ni-based compounds in multiwalled graphitic shell for electrocatalytic oxygen evolution reactions
Open Research DataThis study investigates Ni-based compounds (Ni, NiO, Ni3C) coated with a graphitic shell as electrocatalysts for the oxygen evolution reaction (OER). Electron paramagnetic resonance (EPR) and X-ray diffraction (XRD) are employed to identify the presence and contribution of Nickel ions (Ni0, Ni2+, Ni3+) and determine the phase composition. Electrochemical...
-
The SEM images of Ce0.8La0.2O2 nanocatalyst infiltrated with 10wt.% Ni prepared using soft template method
Open Research DataThe dataset includes SEM images of Ce0.8La0.2O2-s nanopowder (nanoparticles) prepared using soft template method and infiltrated to 10wt.% Ni in the catalyst. CTAB was used as a micelle-based templating agent. The powder was precipitated from aqueous nitrate solution using NaOH solution and 250xCMC (critcal micelle concentration) of CTAB. Precipitate...
-
The TPR reduction profile of CeO2/10wt.%Ni without BCD - 2 cycles
Open Research DataThe dataset includes the TPR reduction profiles of CeO2/10wt.%Ni. The samples of nanoCeO2 impregnated without BCD-assisted precursor solution (betacyclodextrin). The dataset includes two cycles of reduction (samples oxidized in between)
-
SEM images of Ni-Mo2CTx/Mo2Ga2C before and after catalytic dry reforming of methane
Open Research DataThe dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
-
XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials
Open Research DataIn the dataset are included raw data for the preparation of XRD pattern of Mo2Ga2C, Mo2CTx/Mo2GaC and Ni-Mo2CTx/Mo2Ga2C materials.
-
SEM images of Ni-Mo2CTx/Mo3AlC2 before and after catalytic dry reforming of methane
Open Research DataThe dataset includes SEM images of Ni-Mo2CTx/Mo2Ga2C catalysts before and after the dry reforming of methane.
-
Photocatalytic decomposition of acetaldehyde over TiO2 (titanium dioxide) supported on nickel foam and Ni-doped (nickel-doped) TiO2
Open Research DataThis dataset contains chromatograms recorded during the decomposition of acetaldehyde in a high-temperature reaction chamber under UV irradiation using as photocatalytic systems TiO2 (titanium dioxide) supported on nickel foam, TiO2 supported on oxidized nickel foam and TiO2 doped by metallic nickel (Ni) powder. The detailed equipment and measurement...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed in order to force the exsolution process of metallic nanoparticles.
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Fe, Ni) materials were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
Chemical composition of La-Sr-Ce-Ni-Ti ceramics material measured by XPS method
Open Research DataLa-Sr-Ce-Ni-Ti (LSCNT) based ceramics sample was manufactured by standard solid state reaction.Prepared powder was pressed into pilled and sintered in a furnace in air atmosphere for 10h. Annealing temperature was 1200 Celsius degree. To calculate chemical composition and determine valence states of the elements, X-Ray photoemission spectroscopy (XPS)...
-
Selected results of measurements carried out in a ship power station with two generators working in parallel with the use of the NI PXIe-1062Q based measurement system
Open Research DataThe presented dataset is part of research focusing on the assessment of metrological properties of the instrument, Estimator/Analyzer (A/E v.2), developed and made at the Faculty of Electrical Engineering, Department of Marine Electrical Power Engineering, of Gdynia Maritime University. The attached data set contains the results of measurements made...
-
SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe dataset presents SEM images of (La0.3Sr0.6Ce0.1)0.9(Me1Me2Ti)O3-δ (Me1,Me2=Co, Fe, Ni) powder materials after reduction at 1000 deg.C in hydrogen. The powders were synthesized via the Pechini method. The reduction was performed to force the exsolution process of bimetallic nanoparticles.
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co)
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9FexMeyTi(1-x-y)O3-δ materials (Me=Ni,Co) were synthesized via the Pechini method. First, the reagents in the form of nitrates were weighed and dissolved in DI water. In another beaker, a stoichiometric amount of titanium (IV) butoxide (Ti(OBu)4) was mixed together with reagent-grade ethylene glycol (EG), and citric acid (CA)...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 900 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1000 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The XRD diffraction patterns of (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials after reduction at 1100 deg.C in hydrogen
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
The SEM micrographs of the cavitation erosion-corrosion process of selected copper alloys degradation
Open Research DataThe dataset contains Scanning Electron Micrographs of CuZn40Mn3Fe brass compared with Superston and Novoston bronze after cavitation erosion-corrosion exposure using a vibratory transducer (in accordance with ASTM G32). The micrographs compare the topography of samples subjected cavitation erosion in 3% NaCl at room temperature, leading to the surface...
-
SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of nickel (Ni) foam as received, after photocatalysis and after oxidation at 500_C.
Open Research DataThis dataset contains SEM (Scanning Electron Microscopy) and SEM-EDS (Scanning Electron Microscopy with Energy Dispersive X-ray Spectroscopy) images of Ni (nickel) foam as received from the supplier, after photocatalytic treatment and after oxidation at 500C. The detailed equipment and measurement data was described in "readme SEM.txt" file
-
The XRD diffraction patterns of as-prepared (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials synthesized via the solid state reaction method
Open Research DataThe (La0.3Sr0.6Ce0.1)0.9Me0.1Ti0.9O3-δ (Me= Co, Cu, Fe, Mn, Ni) materials were synthesized via the solid state reaction method and examined as a potential anode material. First, the mixed oxide reagents were pressed into pellets and calcined at 1200 °C for 12 hours to decompose most of the organic compounds. The resulting calcined pellet was ground...
-
XRD-Ni foam as received and oxidised at 500_C
Open Research DataThese data contain XRD patterns of porous nickel foam commercial and oxidised in air at 500 C degrees for 8 hours.
-
The scanning spreading resistance microscopy (SSRM) of some CoCrMo alloys subjected to electrochemical litography
Open Research DataThe dataset contains the results of the experiment consisting of performing electrochemical lithography on the surface of the CoCrMo prosthetic alloy. First, by applying local anodic polarization, oxide structures were created on the surface of the material. Next, they were imaged in the SSRM (scanning spreading resistance microscopy) mode to visualize...
-
X-ray Photoelectron Spectroscopy studies of various carboxylic acids adsorption on aluminium alloys in alkaline media
Open Research DataThis dataset contains the results of high-resolution XPS studies obtained during evaluation of high corrosion inhibition efficiency of various carboxylic acids towards aluminium alloy 5754 in bicarbonate buffer pH=11.
-
XPS-Ni foam as received, after photocatalysis and after oxidation at 500_C.
Open Research DataThis dataset contains XPS spectra recorded for nickel foam as received from supplier, after photocatalytic process and after oxidation at 500C. Each set contains: survery spectrum, O1, C1s, Ni2p. The detailed equipment and measurement data was described in "readme XPS.txt" file
-
Chromium FTW dataset
Open Research DataThis dataset contains the results of chromium and nutrients (N and PO4-P) removal in floating treatment wetland microcosm experiment with two cosmopolitan species of parennials: Phragmites australis and Iris pseudacorus.
-
XPS measurements of the iron elements covered by chromium
Open Research DataAnticorrosive coatings are an important issue in modern materials engineering. One of the most commonly used, for that coating materials, is chrome. Three metal elements were measured, named as Turcja, WB Tech and Nomet. Names were given according to producer of elements. XPS measurements of the Cr 2p region give an ansver concering on surface chemical...
-
The luminescence study of LiGa5(1−x)O8:5xCr3+ coumpounds
Open Research DataInfrared luminescent materials have evoked much attention from chemists and material scientists. Although substantial progress is made in materials design, the luminescent mechanism remains ambiguous in the complex structures, presenting major barriers to developing novel infrared luminescent materials. Herein, this study aims to deliberate a complete...
-
Imaging of the effects of pitting corrosion with the use of AFM
Open Research DataPitting corrosion is a local attack on a metal surface, limited to a point or small area, which appears as a hole. Pitting corrosion is one of the most harmful forms of corrosion due to the fact that it is associated with small, difficult to detect damage, that can even lead to perforation of the structure. A single pit may range in size from micrometers...