Morphology of the gold nanoislands
Open Research DataDewetting of the thin metallic films leads to formation of an isolated islands. morphology of nanostructures was measured by SEM microscope. Thin gold films with a thickness of 1.2 nm, 1.5 nm and 3.4 nm were anealed at 550, 600 and 650 Celcius degress.
-
SEM images of dewetted gold films
Open Research DataGold nanostructures were prepared on silicon - Si(111) as a substrate. as a result of dewetting process. Thin golds films were deposited using a table-top dc magnetron sputtering coater under pure Ar plasma conditions . The Au target had 99.99% purity, the rate of Au layer deposition was about 0.4 nm·s−1 and the incident power was 32 W. The thickness...
-
Plasmon resonance in gold-silver nanoalloys
Open Research DataSurface plasmon resonance (SPR) can lead to improve or formation a new linear or nonlinear optical phenomena. Especially it can enhance a light emission from luminescence materials. The presence of metal nanostructures or nanoparticles is necessary to excitation of the SPR. It is well known that gold and silver nanostructures exhibit plasmon resonance...
-
Gold nanocubic structures functionalization with organic layers
Open Research DataThis dataset contains the XPS spectra obtained for gold nanocubes (AuNC), which were deposited at the gold electrode surface and dried. The AuNC's were first functionalized with either cysteamine in EtOH or mercaptopropionic acid in EtOH. The concentration of these compounds was 20 mM. The interaction of the functionalized with the AuNC surface was...
-
Formation of gold anostructures detected by SEM microscope
Open Research DataGold nanostructures were prepared on silicon - Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air...
-
SEM images of tge gold nanostructures on silicon
Open Research DataAu nanostructures were prepared on Si(111) as a substrate. The substrates (1 × 1 cm2 of area) were cleaned with acetylacetone and then rinsed in ethanol. Thin Au films (with thicknesses in a range of 1.7–5.0 nm) were deposited using a table-top dc magnetron sputtering coater (EM SCD 500, Leica) under pure Ar plasma conditions (Argon, Air Products 99.999%)....
-
The AFM micrographs of gold nanoparticles on silicon substrate
Open Research DataThe dataset contains the first approach towards AFM topographic imaging of gold nanoparticles synthesized and immobilized on the silicon surface. Measurements were made in the semi-contact mode on the NTEGRA Prima device, manufactured by NT-MDT. Scans were performed with amplitude detection at an operating value of 60% of the free oscillation amplitude....
-
Depth profile of the gold-silver bimetallic structures
Open Research DataSilver and gold bimetallic layers were deposited on a silicon substrate by magnetron sputtering method. Both, Au and Ag layers had 3 nm of thickness. That prepared nanostructures were measured by XPS method. To obtain a depth profile of chemical composition, an Argon ion (Ar+) gun was used for etching surface of sample. Each cycle of etching takes 30...
-
Formation of gold nanostructures detected by XPS method
Open Research DataGold nanostructers were manufactured by thermal dewetting of thin film. Film with thickness of 2.8 nm was deposited by magnetron sputtering method. As a result of annealing at 550 deg, nanostructures appear. Bulk gold, as-deposited gold film and metallic nanostructures were measured by XPS method.
-
Technical fabrics old sample
Open Research DataThe data presented here includes video of technical fabric strength testing. The included movie is in .cine format, and an external program with a viewer for such movies is required.
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains SEM images of gold nanocubes (AuNC), which were deposited at the conductive Si wafer surface and dried. The deposition method, the solvent used and AuNC concentration have a significant influence on the homogeneous distribution and their agglomeration at the surface, further influencing the electrochemical characteristics of the...
-
Gold nanocubic structures agglomeration when put on conductive surfaces
Open Research DataThis dataset contains Dynamic EIS results obtained for the gold electrodes with non-functionalized gold nanocubes (AuNC) deposited at its surface. The deposition was the following: 2 uL of the solvent containing CTAB as the surfactant was put on the electrode and dried, the same procedure was applied 5 times. Afterward, the electrode was immersed in...
-
Effect of process parameters on food waste conversion - dataset 1
Open Research DataData obtained during studies (food waste pretreatment and conversion), describing the effect of process parameters (sonocavitation) on food waste conversion.
-
Elgold: gold standard, multi-genre dataset for named entity recognition and linking
Open Research DataThe dataset contains 276 multi-genre texts with marked named entities, which are linked to corresponding Wikipedia articles if available. Each entity was manually verified by at least three people, which makes the dataset a high-quality gold standard for the evaluation of named entity recognition and linking algorithms.
-
Maximum temperature of 0.5-W infrared laser-Illuminated gold nanorod platforms
Open Research DataData concern a system consisted of two pieces of borosilicate glass surrounded by air and joined together by a transparent glue, which is to serve as a thermal transducer. On the top and bottom sides of the smaller piece, gold nanorods are dislocated. Glass is prepared here due to its high transparency, facilitating heat to be produced within the system....
-
Ultra-thin film of aluminum oxide influence on the plasmon resonance in gold nanostructures
Open Research DataUltra-thin film of aluminum oxide influence on the plasmon resonance in gold nanostructures was measured by UV-VIS spectroscopy. Ultra thin film of Al2O3 was deposited on a gold nanostructures. Thickness of film was 2nm - 8nm. Shift of plasmon resonance was observed, as a result of various dielectric constant of layer.
-
Determination of the total number of microorganisms in a model food product preserved by CS-2a and CS-2b.
Open Research DataThe dataset contains the results of determination of the total number of microorganisms in a model food product after the use of the innovative preservatives: CS-2a and CS-2b and control (K) after seven days of refrigerated storage of the product. The test was performed using the surface inoculation method.
-
Energy, water detailed usage. Living lab testing for sustainable urban food-water-energy cycle.
Open Research DataData set contains detailed, continuous measurements of the usage of water and electrical energy (AC power) in an experimental facility set up in a scientific laboratory (Laboratorium im. B.Niemkiewicza) at the Faculty of Mechanical Engineering and Ocean Technology of the Gdansk University of Technology. The test bed was established in co-operation...
-
Energy, water detailed usage. Living lab testing for sustainable urban food-water-energy cycle. Jan. 2022
Open Research DataData set contains detailed, continuous measurements of the usage of water and electrical energy (AC power) in an experimental facility set up in a scientific laboratory (Laboratorium im. B.Niemkiewicza) at the Faculty of Mechanical Engineering and Ocean Technology of the Gdansk University of Technology. The test bed was established in co-operation...
-
Energy, water detailed usage. Living lab testing for sustainable urban food-water-energy cycle. Dec. 2021
Open Research DataData set contains detailed, continuous measurements of the usage of water and electrical energy (AC power) in an experimental facility set up in a scientific laboratory (Laboratorium im. B.Niemkiewicza) at the Faculty of Mechanical Engineering and Ocean Technology of the Gdansk University of Technology. The test bed was established in co-operation...
-
The analysis of the expression of hTERT in anthraquinone-treated NSCLC cells
Open Research DataThe datasets showcase an analysis of hTERT relative gene expression in NSCLC cells treated with anthraquinone, quantified as fold change compared to DMSO-treated control cells, using the comparative CT method.
-
Forecast of basic fuel prices in imports to Poland (constant prices in USD in 2007)
Open Research DataThis dataset presents price growth forecasts for conventional energy sources. It should be noted that the Ministry of Economy forecasts a more than two-fold increase in oil prices (although these forecasts may be greatly underestimated) over 23 years, an almost two-fold increase in natural gas prices and a 40% increase in coal prices.
-
SEM images of 8YSZ sintered using flash sintering programme
Open Research DataThe dataset contains the SEM images of 8YSZ (8mol% Y2O3-ZrO2) sintered using the flash technique in the muffle furnace. The programme was as follows: 3oC/min to 1000C - 1h hold- 3oC/min 1100C - 1h hold- 3oC/min 1200C - 2h hold- 3oC/min 1400- 30 min hold- 5oC/min 1200C - 15h hold- 4oC/min RT
-
Wyniki sulfammox (SRAO)
Open Research DataTwo granular sequencing batch reactors were operated for 160 days under anammox conditions, comparing the Anammox process and Sulfate Reduction Ammonium Oxidation process. The study aimed to investigate whether increasing the concentration of SO42- could enhance N removal rates under anaerobic conditions, and whether SO42- reduction and anammox processes...
-
D.C. electrical measurements of Bi2VO5.5 ceramic measured at high temperature region
Open Research DataD.C. electrical properties of Bi2VO5.5 ceramic was measured.
-
X-Ray diffraction of the metallic nanostructures
Open Research DataMetallic nanostructures (gold and silver) were manufactured as a thermal annealing of gold or silver thin film. Gold films with thickness of 2.8 nm were deposited on a silicon substrates using a table-top dc magnetron sputtering coater (EM SCD 500, Leica), equipped with quartz microbalance for in-situ thickness measurements. Films were deposited from...
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.88 mm measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Linear impedance of Bi2VO5.5 ceramic of thickness 2.52 mm measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
The topography of Bi2VO5.5 ceramic measured with SEM and confocal microscope
Open Research DataThe topography of Bi2VO5.5 ceramics was measured by SEM and confocal microscope.
-
Linear impedance of Bi2VO5.5 ceramic prepared by traditional melt quenching technique measured with impedance spectroscopy method at low temperature region
Open Research DataThe linear electrical properties of Bi2VO5.5 ceramic prepared by traditional melt quenching technique was measured by impedance spectroscopy method.
-
Electrical measurements of the dewetting of metal thin films
Open Research DataIn situ observations of dewetting of thin films is very complicated. One of the method, that helps to observe it, could be electrical measurements. For experiments, thin gold, silver and gold-silver nanoalloy films were deposited by magnetron sputtering method. Films were deposited on a Corning glass substrates. Samples were measured by four point method...
-
Top 10 Iran Export Goods in 2011
Open Research DataIn the structure of Iranian exports the dominant position are different types of fuel (including chemical industry products). The structure of imports is much more fragmented. Positions worth of consideration are machinery and equipment, steel, vehicles parts, cereals and food.
-
TEM imaging of metal nanoparticle cross section
Open Research DataTEM microscope was used for a imaging of metallic nanostructures. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
Interface diffusion between metallic nanoparticles and silicon substrate
Open Research DataInterface diffusion between metallic nanoparticles and silicon substrate was detected by EDX method. Metallic nanostructures were manufactured by thermal annealing of thin films. Gold and silver nanostructures were chosen for measurements. Samples were annealed for 15 and 60 minutes at 550 deg.
-
Revenues to the state budget from the sale of shares in state-owned banks in 1994-2000
Open Research DataOn June 14, 1996, a special law was passed on the merger and grouping of certain banks in the form of joint-stock companies. Pursuant to these regulations, the PeKaO S.A. banking group was established, which was the only entity of this type established in this way. Additionally, by the end of 1996, four out of nine regional banks were sold, i.e. Wielkopolski...
-
Dewetting of silver films detected by XPS method
Open Research DataDewetting of silver thin films was detected by XPS method. Thin metallic films were deposited by magnetron sputtering method. Formation of nanostructures , as a result of thermal annealing, was confirmed by SEM microscope. For comparision three samples were measured. Bulg gold, as-deposited silver film with thickness of 3 nm and nanostructures.
-
Plasmon resonance in a TiO2-Au NPs structures
Open Research DataInvestigated structures were deposited on a pre cleaned Corning 1737 glass substrates, which provided flat optical transmission characteristics and high transmission coefficient in a visible light range. Plasmonic nanostructures were formed as a result of thermal annealing. For gold films with thickness of 2.8 nm depiction a table-top dc magnetron sputtering...
-
The influence of the temperature treatment method on the quality of French fries.
Open Research DataThe video presents instructional work on the temperature treatment of French fries and the assessment of oil changes during frying. The results of the measurements show that placing the fries in cold oil, heating them to the frying temperature compared to the conventional method of frying, reduces the amount of primary oxidation products and free fatty...
-
Au nanostructures coated with a ultrathin film of Al2O3 - measurements and FDTD simulations
Open Research DataGold plasmonic platforms have been coated with an ultra-thin films of aluminium oxide. Optical measurements, showing the influence of the thickness of Al2O3 on plasmon resonance position. The observed red-shift of the resonance location with the increase of the thickness of the Al2O3 film, can be explained by the change in the dielectric function of...
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.88 mm was measured at 693 K with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of temperature and frequency for Bi2VO5.5 ceramic of thickness 2.52 mm was measured at different A.C. voltage with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 1.63 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 1.63 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 4.03 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 4.03 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage of Bi2VO5.5 ceramic of thickness 2.91 mm was measured with impedance spectroscopy method at high temperature region
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.91 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of frequency for Bi2VO5.5 ceramic of thickness 2.88 mm was measured at high temperature range with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.88 mm was measured by impedance spectroscopy method.
-
Nonlinear impedance as a function of A.C. voltage and temperature for Bi2VO5.5 ceramic of thickness 2.52 mm (after first heat-treatment at 913 K) was measured at different frequencies with impedance spectroscopy method
Open Research DataThe nonlinear electrical properties of Bi2VO5.5 ceramic of thickness 2.52 mm was measured by impedance spectroscopy method.
-
Chemical analysis of the Au-Ag nanoaloys
Open Research DataThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...