Structural investigations of the Al2O3 ultra thin films
Open Research DataUltra-thin layers of Al2O3 were deposited by atomic layer deposition (ALD) (Beneq TFS 200 ALD system). This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2...
-
Chemical investigation of the Al2O3 ultra-thin films
Open Research DataUltra-thin layers of oluminum oxide (Al2O3) were deposited by ALD method. Atomic layer deposition provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water. The deposition of the atomic layer was carried out at 200 °C. Samples with a thickness of 2 and 8 nm of alumina...
-
TEM and EDX study of the Al2O3 ultra thin films
Open Research DataThe ultra-thin layers of Al2O3 were deposited on a silicon substrates. The method of atomic layer deposition (Beneq TFS 200 ALD system) was chosen as the proper method of dielectric layer deposition. This method provides precise thickness control down to a single atomic layer. The precursors used were trimethylaluminum (Sigma-Aldrich) and purified water....
-
Ultra-thin film of aluminum oxide influence on the plasmon resonance in gold nanostructures
Open Research DataUltra-thin film of aluminum oxide influence on the plasmon resonance in gold nanostructures was measured by UV-VIS spectroscopy. Ultra thin film of Al2O3 was deposited on a gold nanostructures. Thickness of film was 2nm - 8nm. Shift of plasmon resonance was observed, as a result of various dielectric constant of layer.
-
Measurements of the mechanical system properties of "SpeedLine magnetic" ultra-fast robot prototype for IML labeling
Open Research DataThe mechanical system tests of the high-speed IML labeling robot "SpeedLine Magnetic" were carried out in order to analyze the effects of the drive system's operating parameters on vibration and noise.
-
Measurements of drive system properties of the "Magnetic SpeedLine" ultra-fast robot prototype for IML labeling
Open Research DataTests of the drive system of the ultra-fast robot "SpeedLine magnetic" for labeling with the IML method were carried out in order to analyze the influence of the operating parameters of the drive system on the correctness and quality of the drive system.
-
Au nanostructures coated with a ultrathin film of Al2O3 - measurements and FDTD simulations
Open Research DataGold plasmonic platforms have been coated with an ultra-thin films of aluminium oxide. Optical measurements, showing the influence of the thickness of Al2O3 on plasmon resonance position. The observed red-shift of the resonance location with the increase of the thickness of the Al2O3 film, can be explained by the change in the dielectric function of...
-
Measurements of power supply system properties of "Magnetic SpeedLine" ultra-fast robot prototype for IML labeling
Open Research DataTests of the power supply system of "SpeedLine magnetic" ultra-fast industrial robot for IML labeling were carried out to analyze the effect of the active power filter (APF) parameters on the power quality. at the target duty cycle. Tests were performed with the target duty cycle. Linear synchronous motors with permanent magnets were used to drive...
-
Technology and democracy: the who and how in decision-making. The cases of Estonia and Catalonia. METADATA
Open Research DataThe analysis of the Estonian data comes mainly from studies conducted to analyse the cost-efficiency of the Estonian online voting model (Krimmer; Duenas-Cid; Krivonosova, 2021), as well as from the contagion effect that ensued in other parts of the Estonian administration after the voting system was developed (Krimmer; Duenas-Cid,2019). In both cases,...
-
Technology and democracy: the who and how in decision-making. The cases of Estonia and Catalonia. METADATA 1
Open Research DataThe analysis of the Estonian data comes mainly from studies conducted to analyse the cost-efficiency of the Estonian online voting model (Krimmer; Duenas-Cid; Krivonosova, 2021), as well as from the contagion effect that ensued in other parts of the Estonian administration after the voting system was developed (Krimmer; Duenas-Cid,2019). In both cases,...
-
Low frequency nois of supecapacitor
Open Research DataDataset contains results of low frequency noise observation during discharge of commercially available supercapacitor, type DRL 2.7V 10F, with a nominal capacitance 10 F and a nominal voltage 2.7 V. Supercapacitor was charged to various voltages and discharged through a resistor. In the experiment the 50 Ohm and 200 Ohm resistors were used. The supercapacitor...
-
Full CI ground state potential energy curves and one-electron relativistic corrections for hydrogen molecule in various basis sets
Open Research DataThis dataset consists of Full CI ground state Born-Oppenheimer potential energy curves and one-electron relativistic corrections for hydrogen dimer. Nonrelativistic energies, as well as one electron relativistic corrections (treated perturbatively with help of the Cowan-Griffin Hamiltonian) are presented for internuclear distances between 0.8 and 10...
-
Scanning electron microscopy (SEM) images of the boron-dopied diamond surfaces
Open Research DataThe dataset contains the scanning electron micrographs (SEM), revealing the surface morphology of diamond electrodes on silicon substrates. The diamond surface is characterized by ultra-crystalline diamonds obtained by CVD synthesis.
-
The XAS spectra of O-K edges, M-L edges and Ce-M edges in Ce0.9M0.1O2
Open Research DataThe dataset consists of XAS spectra of O-K edges, M-L edges of Ce0.9M0.1O2 (where M=Mn, Fe, Co, Ni, Cu) synthesised by reverse microemulsion method. XAS spectra were collected at PIRX beamline in SOLARIS National Synchrotron Radiation Centre. Measurements were perfomed under ultra high vacuum in total electron yield (TEY) mode.
-
Numerical optimization of planar antenna structures using trust-region algorithm with adaptively adjusted finite differences
Open Research DataThe dataset contains initial designs and optimization results for three planar structures that include quasi-patch antenna for WLAN applications, compact spline-parameterized monopole dedicated for ultra-wideband applications, as well as rectifier for energy harvesting with enhanced bandwidth. The numerical results for the first two structures are also...
-
SEM micrographs of morphology evolution of V2O5 nanostructures
Open Research DataThe DataSet contains the scanning electron microscopy (SEM) micrographs of morphology evolution of vanadium pentaoxide nanostructures obtained by the sol-gel, depending on annealing temperature under synthetic air. The results show that the morphology dependent on the annealing temperature.
-
The 3d Ce XPS spectra of Ce0.9M0.1O2
Open Research DataThe dataset consists of 3d Ce XPS of Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons were excited by an...
-
The 2p XPS spectra of transition metals in Ce0.9M0.1O2
Open Research DataThe dataset consists of 2p XPS spectra of transition metals in Ce0.9M0.1O2 where (M=Mn, Fe, Co, Ni, Cu). X-ray Photoelectron Spectroscopy analysis (XPS) was performed using X-ray photoelectron spectrometer Omnicron NanoTechnology with 128-channel collector. XPS measurements were undertaken in ultra-high vacuum conditions, below 1.1x10-8 mbar. Photoelectrons...
-
Rain Gardens LC_MS/MS analysis dataset
Open Research DataThis dataset contains the results of samples analysis (target analysis with certified reference materials) using ultra-high performance liquid chromatography tandem mass spectrometry (UHPLC-MS/MS, Shimadzu, Japan).
-
Measurements of no-load and short-circuit parameters of power transformers with taps
Open Research Data1) The Laboratory LINTE^2 is a large research infrastructure operated by the Faculty of Electrical and Control Engineering at Gdańsk University of Technology, to be found in Gdańsk, Poland (54.3690 N, 18.6130 E).
-
Ethylene decomposition on TiO2 under UV
Open Research DataData contain chromatograms recorded during decomposition of ethylene over TiO2 in a flow reactor under UV irradiation. Semilac UV lamp with total power of 72 W was used as a source of UV light. Chromatograms were recorded in Trace GC Ultra chromatograph equipped in FID detector. Sampling was realised via the dosing sample loop. TiO2 was coated on the...
-
Internal legal acts of technical and medical universities in Poland regulating classes conducted in-person during the Covid-19 pandemic
Open Research DataA database of legal acts and other internal documents of medical and technical universities in Poland regulating the way of organizing in-person or hybrid classes during the COVID-19 pandemic from the summer semester 2019/2020 to the winter semester 2020/2021.Documents were encoded in two separate coding systems using the MAXQDA program for qualitative...
-
The XPS spectra of Ce0.8Ni0.2O2 prepared using microemulsion method
Open Research DataThe dataset includes XPS spectra of Ce0.8Ni0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XPS spectra of Ce0.8Cu0.2O2 prepared using microemulsion method
Open Research DataThe dataset includes XPS spectra of Ce0.8Cu0.2O2-s sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods (microemulsion). The XPS spectra were collected for all species.
-
The XPS spectra of LSCNT sintered at 1200C
Open Research DataThe dataset includes XPS spectra of La0.27Sr0.54Ce0.09Ni0.1Ti0.9O3-s sintered at various temperatures under air atmosphere for 12 h. Samples were produced using aqueous soft chemistry methods (Pechini). The XPS spectra were collected for all species.
-
The XPS spectra of Al2O3/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of Al2O3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/1%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of AlOOH/1%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of ZrO2/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of ZrO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of CeO2/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of CeO2/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of SrTiO3/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of SrTiO3/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
The XPS spectra of AlOOH/5%Cu prepared using wet impregnation method
Open Research DataThe dataset includes XPS spectra of AlOOH/5%Cu catalyst sintered under air atmosphere. Samples were produced using aqueous soft chemistry methods and incipient wettness impregnation using nitrate solution. The XPS spectra were collected for all species.
-
3D point cloud as a representation of buildings: the Nanotechnology Center and the Auditorium Novum
Open Research DataThe product presents the point cloud in the collection of a three-dimensional database in spatial order as the representations of the Nanotechnology Center and the Auditorium Novum buildings (located on the campus of the Gdańsk University of Technology) acquired in the laser scanning technology. According to its high accuracy and precision of data acquisition...
-
state aid for sustainable urban development
Open Research DataThe dataset encompassed a choice of important legal acts with respect on the usage of EFRD for urban projects, a list of selected bibliography as well as a list of selected individual notifications of state aid measures being part of the Sustainable Urban Development Programme in the period 2014- 2020. As a comparison, an example of individual EC decision...
-
X-ray Photoelectron Spectroscopy studies of ammonium vanadate
Open Research DataThe DataSet contains the high-resolution XPS studies of the ammonium vanadate nanostructures obtained by the hydrothermal method. XPS analyses were carried out with an X-ray photoelectron spectrometer (Omicron NanoTechnology) with a 128-channel collector. The measurements were performed at room temperature in an ultra-high vacuum condition (below 1.1x10-8...
-
Data from the survey on factors determining the employment of the Gdańsk University of Technology graduates’ in the opinion of entrepreneurs
Open Research DataThe dataset includes data from the survey on factors determining the employment of the Gdańsk University of Technology (GUT) graduates’ in the opinion of entrepreneurs. The survey was conducted in 2017. The research sample included 102 respondents representing various firms from Pomeranian Voivodship. The study concerned i.a. factors determining the...
-
Employee benefits in comparision to the personal payroll fund in 2017-2019 on given example
Open Research DataIn modern employee relations, employers offer employees a whole range of benefits, which usually are required by the relevant regulations on the part of the employer, which serve to create appropriate working conditions.
-
Study of the chemical state of Gd in a Ba-La-Gd-Co based ceramic
Open Research DataBarium, Lanthanum, Gadolinium and Cobaltium precursors were used for production of ceramic materials. Samples were produced by standard solid state reaction. Samples were annealed at 300 Celsius degree in wet and dry atmosphere. Annealing takes 72h or 2h. Results of annealing on a Gadolinum were observed by X-Ray photoemission spectroscopy (XPS), OmicronNanotechnology....
-
Silicon microcantilever with impedance sensor
Open Research DataThe issue of microelectromechanical systems (MEMS) [1] has been enjoying popularity and interest since the 90s of the 20th century. Microcells are one of the simplest devices of this type, but they can be widely used in sensors. There are reports on the possibility of using this type of sensors in the context of such important issues as diagnostics...
-
Structure of the register of immovable monuments by date of individual objects – comparison of 2017 and 2024
Open Research DataThe register of monuments is the primary form of monument protection. The register for monuments in the voivodeship is kept by the voivodeship conservator of monuments in the form of separate books for immovable (book A), movable (book B), and archaeological (book C) monuments. Entries in the register of monuments are made upon application by the owner...
-
A synthetic result of the development of personnel risk factors in the A, B, C, D enterprise
Open Research DataThe data below presents the shape of all the researched personnel risk factors in the A, B, C, D enterprise (which were tested by the author). Further considerations should be started with the presentation of the synthesis of the obtained results, which is presented in this research data.
-
Chemical composition of tellurium oxides thin films deposited by magnetron sputtering method
Open Research DataThin films were prepared by radio frequency reactive magnetron sputtering technique. Metallic Te target was sputtered for about 45 min in argon-oxygen atmosphere what resulted in 300 nm film thickness deposition. The pressure in the chamber was below 0.2 Pa and substrate was heated at 200 °C. The distance between sputtered target and the Corning 1737...
-
Investigations of the valence state of Co in a MnCoO ceramics
Open Research DataMcCoO ceramics materials were produced by solid state reaction and sintred in a furnance in air atmosphere for 20h. Annealing temperature was 600 Celsius degree. For investigations a series of samples, with a various composition was chosen: MnCoO, Mn, Co2O and Mn2CoO. Chemical behaviour of the Cobaltium was measured by XPS method. The analyses were...
-
The luminescence study of Ga1.98–xAlxO3:0.02Cr3+ coumpounds.
Open Research DataA chemical and mechanical pressure-induced photoluminescence tuning method was developed through structural evolution and hydrostatic pressure involving phase transition. A series of Ga1.98−xAlxO3:0.02Cr3+ phosphors were synthesized by collaborators from National Taiwan University. Structural evolution reveals a crystal phase change with the incorporation...
-
The luminescence study of Ga2–x(Al0.68In0.32)xO3:Cr3+ coumpounds.
Open Research DataNear-infrared (NIR) phosphor-converted light-emitting diodes (pc-LEDs) are a highly efficient perspective NIR light source, with application hindered by a narrow emission band. In this work, we broaden the emission of a new series of NIR phosphors by controlling crystal structure disorder through cation cosubstitution. By substituting Ga3+ with (Al0.68In0.32)3+,...
-
Substrate characterization in a electrochemically derived Manganium-Cobaltium thin films
Open Research DataManganium-Cobaltium thin films were electrochemically deposited on a Ni foams subsrates in a one-step process at −1.1 V vs. Ag/AgCl in an aqueous solution of differently concentrated Mn(NO3)2·4H2O and Co(NO3)2·6H2O with the deposition time limited by charges of 60, 120, and 200 mC at 25 °C. The concentration ratios of Mn(NO3)2·4H2O to Co(NO3)2·6H2O...
-
XPS study of the YST ceramics
Open Research DataYttrium-doped strontium titanate was prepared via conventional solid-state reaction method from Y2O3 (Sigma Aldrich, 99,9%), TiO2 (Sigma Aldrich, 99%) and SrCO3 (Sigma Aldrich,98%). For comparision, two other techniques were used for synthesis: Pechini and wet methods. Both kind of samples were measured, after and before reduction process (in a hydrogen)....
-
Chemical analysis of the Au-Ag nanoaloys
Open Research DataThe nanostructures of AuAg nanoalloys were prepared by sequential sputtering of gold and silver thin films. Single layer thickness was usually 2.8 nm were deosted by magnetron sputtering method in a Ar plasma. As deposited layers were annealed in Ar atmosphere at 550 degress for 15 minutes. For XPS measurements five samples were selected: pure gold...
-
Parameters of land reference points in the Gdynia region and the Free-air anomaly grid of the South Baltic
Open Research DataThe data was registered during the campaign to verify the catalog value of the absolute point coordinates [point 5403 (POLREF-GORA DONAS)] of the national gravimetric control network. The data was recorded in two three-hour stationary measurement campaigns at the following points: Rozewie of the EUREF-POL network, Góra Donas POLREF, and mareograph points...
-
Reduction of the strontium titanate doped by Ytrium ceramics observed by X-ray photoemission spectroscopy method
Open Research DataYtrium-doped strontium titanate (YSTF) ceramics materials were manufactured by three various methods: 1) standard solid-state reaction method from Y2O3 (Sigma Aldrich, 99,9%), TiO2 (Sigma Aldrich, 99%) and SrCO3 (Sigma Aldrich,98%), 2) Pechini method, 3) wet method.
-
XPS data of deuterium and hydrogen grown boron-doped diamond
Open Research DataThe high-resolution C1s X-ray absorption spectra of BDD@H and BDD@D samples were measured using the facilities of the HE-SGM beamline (HE-SGM) at the BESSY II synchrotron radiation source of Helmholtz–Zentrum Berlin (HZB).[90] The measurements were carried out under ultra-high vacuum conditions: P ≈ 2×10−9 Torr at T = 300 K. The NEXAFS spectra were...