Pre-oxidation of porous ferritic Fe22Cr alloys for lifespan extension at high-temperature
PublicationPre-oxidation of porous ferritic Fe22Cr alloys was extensively studied in this paper. Weight gain measurements and SEM analysis revealed that pre-oxidation performed at 900◦C for 40 min increased the lifespan of the alloy. A Cr evaporation study did not disclose any significant influence of the pre-oxidation process on the Cr content in the alloy. For a more detailed assessment, TEM imaging and X-ray tomography measurements of...
-
Investigations of Titanium Implants Covered with Hydroxyapatite Layer
PublicationTo reduce unfavorable phenomena occurring after introducing an implant into human body various modifications of the surface are suggested. Such modifications may have significant impact on biocompatibility of metallic materials. The titanium and it's alloys are commonly used for joint and dental implants due to their high endurance, low plasticity modulus, good corrosion resistance as well as biocompatibility. Special attention...
-
Adhesion of organic coatings to hot-dip galvanized steel
PublicationDuplex systems provide long-time corrosion protection, much longer than the sum of the lifetimes of zinc and paint used individually. However loss of adhesion between coating and zinc substrate is often found in practice. Different methods of zinc surface preparations are used in the fi eld. The aim of this study was to examine and compare coating protection when the old zinc surface, stored during long-time period (15 years) in...
-
Biocompatibility and Bioactivity of Load-Bearing Metallic Implants
PublicationThe main objective of here presented research is to develop the titanium (Ti) alloy base composite materials possessing better biocompatibility, longer lifetime and bioactivity behaviour for load-bearing implants, e.g. hip joint and knee joint endoprosthesis. The development of such materials is performed through: modeling the material behaviour in biological environment in long time and developing of new procedures for such evaluation;...
-
Deterioration and Protection of Concrete Elements Embedded in Contaminated Soil: A Review
PublicationCoating materials are considered one of the most antique materials of human civilization; they have been used for decoration and the protection of surfaces for millennia. Concrete structures—due to their permanent exposure to different types of environments and contaminants—require the use of coatings that contribute to its preservation by reducing the corrosion of its components (steel and aggregates). This article intends to...
-
Ceria Based Protective Coatings for Steel Interconnects Prepared by Spray Pyrolysis
PublicationStainless steels can be used in solid oxide fuel/electrolysis stacks as interconnects. For successful long term operation they require protective coatings, that lower the corrosion rate and block chemical reactions between the interconnect and adjacent layers of the oxygen or the hydrogen electrode. One of the promising coating materials for the hydrogen side is ceria. Using standard sintering techniques, ceria sinters at around...
-
Application of galvanodynamic impedance spectroscopy for studying passive film cracking under mechanical strain
PublicationThe paper reports the results of simultaneous mechanical and electrochemical investigations on austenitic (18/8) stainless steel in a 2 % solution of sulphuric acid. The measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Electrochemical analysis of mechanical passive layer cracking and repassivation conditions during a tensile test was carried out. Application of this methodology allowed...
-
Morphology and conductivity investigations of nickel-molybdenium alloy by means of Scanning Spreading Resistance Microscopy
Open Research DataElectrolytically deposited nickel-molybdenum alloys are interesting materials because of their high corrosion resistance and low over-potential for hydrogen evolution. Despite many studies devoted to the deposition of these alloys, the mechanism of co-deposition is not fully understood [1]. The aim of the research was to preserve the electrochemically...
-
Imaging and chemical investigation of silver coating
Open Research DataThe recovery of silver from materials such as plates, still used in clinical radiography [1], or scrap jewelery is still very popular. The subject of the research, part of which was microscopic imaging, was to recreate the behavior of an electrochemically deposited silver coating. The copper electrodes were covered with a layer of silver obtained from...
-
AFM-assisted investigation of conformal coatings in electronics
PublicationPurpose – This paper aims to presents a new method of investigation of local properties of conformal coatings utilized in microelectronics. Design/methodology/approach – It is based on atomic force microscopy (AFM) technique supplemented with the ability of local electrical measurements, which apart from topography acquisition allows recording of local impedance spectra, impedance imaging and dc current mapping. Potentialities...
-
IN VIVO DEGRADATION OF BIOMATERIALS
PublicationThe material designed to be introduced into the human tissue should be biocompatible and biofunctional. Unless it is so, the body may respond to the implant in different ways. An inflammation reaction may appear such as: parting of items of the implant surface resulting from fraction or pressure. The condition of the surface has an important influence on the usefulness of the implant. The required values depend on the implant function...
-
Mathematical modeling and prediction of pit to crack transition under cyclic thermal load using artificial neural network
PublicationThe formation of pitting is a major problem in most metals, which is caused by extremely localized corrosion that creates small holes in metal and subsequently, it changes into cracks under mechanical load, thermo-mechanical stress, and corrosion process factors. This research aims to study pit to crack transition phenomenon of steel boiler heat tubes under cyclic thermal load, and mathematical modeling...
-
Formation of Porous Structure of the Metallic Materials Used on Bone Implants
PublicationResearch on improvement of structure and fabrication methods of the bone implants are carried out for many years. Research are aimed to shape the structures, that will have a Young's modulus value similar to the value of the human bones Young's modulus. Depending on theporosity, Young's moduli can even be tailored to match the modulus of bone closer than solid metals can, thus reducing the problems associated with stress shielding...
-
COMPARISON OF TWO MODELS OF CONDENSATION
PublicationIn the low-pressure part of steam turbine, the state path usually crosses the saturation line in penultimate stages. At least last two stages of this part of turbines operate in two –phase region. The liquid phase in this region in mainly created in the process of homogeneous and heterogeneous condensation. Several observations confirm however, that condensation often occurs earlier than it is predicted by theory i.e. before the...
-
Structural Reliability Assessment Of Corroded Tanker Ship Based On Experimentally Estimated Ultimate Strength
PublicationThis work deals with the reliability assessment of a tanker ship hull structure subjected to a vertical bending moment and corrosion degradation. The progressive collapse and ultimate load carrying capacity are estimated based on experimentally tested scaled box-shaped-specimens. The translation of the strength estimate of the scaled specimen to the real tanker ship hull structure is performed based on the dimensional theory developing...
-
Zabezpieczenia antykorozyjne stalowych barierek ochronnych na obiektach mostowych w ujęciu kosztów cyklu ich życia
PublicationThe article presents the Life Cycle Costs analysis of steel safety barriers operated in road lane conditions, located on a selected bridge structure. Three corrosion protection systems were proposed, analyzing them in terms of the cost of initial and planned outlays related to maintenance. Based on the LCC analysis for three options, taking into account the 25-year lifetime of the barriers, the optimal solutionwas indicated, i.e....
-
The impact of material degradation on the resistance and reliability of truss structures
PublicationThe paper analyses limit load-carrying capacity and buckling load of truss towers used to support high voltage power lines. The analysed typical structure was subjected to characteristic loads and their combinations. The results were applied to assess structural resistance with regard to steel corrosion in the long-term operation. The extent of structural deterioration was assessed due to Young's modulus decrement in the course...
-
Types of wear and tear of biomaterials used in orthopaedic surgery
PublicationPurpose of this paper is presentation of observations on different kinds of wear and tear of biomaterials used in contemporary orthopaedic surgery. Types of prosthesis damage, encountered in medical practice, and their causes have been described. Results of many clinical studies were analysed to review prosthesis damage from the stage of implanting (such as intrusion of a foreign object between its components) to their natural...
-
Measurements of flicker noise in supercapacitor cells
PublicationFlicker noise (1/f-like noise) is often used to assess the quality of various materials and devices. This phenomenon has been observed in different electrochemical devices or reactions (e.g., smart windows, pitting corrosion events). In our exploratory studies we consider how to measure and utilize 1/f noise for the quality assessment of supercapacitors. This task requires special attention because of enormous capacitance of the...
-
Localized impedance measurements of AA2024 and AA2024-T3 performed by means of AFM in contact mode
PublicationPurpose: The purpose of this paper is to present the results of an atomic force microscopy (AFM) based approach to local impedance spectroscopy (LIS) measurement performed on AA2024 and AA2024-T3 aluminium alloys. Design/methodology/approach: AFM-LIS measurements were performed ex-situ without the electrolyte environment, so in fact the electrical not electrochemical impedance was obtained. Findings: Relative local impedance values...
-
Inspection of Gas Pipelines Using Magnetic Flux Leakage Technology
PublicationMagnetic non-destructive testing methods can be classified into the earliest methods developed for assessment of steel constructions. One of them is the magnetic flux leakage technology. A measurement of the magnetic flux leakage is quite commonly used for examination of large objects such as tanks and pipelines. Construction of a magnetic flux leakage tool is relatively simple, but a quantitative analysis of recorded data is a...
-
Debonding Detection in Reinforced Concrete Beams with the Use of Guided Wave Propagation
PublicationOne of the most frequent damage of the reinforced concrete structures is debonding between steel bar and concrete cover. In the case of debonding occurrence not only the strength of the structure decreases, but also it is more vulnerable to corrosion damages. For this reason fast and effective methods of debonding detection in an early stage of its development need a significant boost. The paper presents analytical and experimental...
-
THE ROLE OF THIN FUNCTIONAL LAYERS IN SOLID OXIDE FUEL CELLS
PublicationWidespread commercialization of solid oxide fuel cells requires lowering its cost. It is generally accepted that to lower the cost of solid oxide fuel cells it is necessary to use metal alloys as interconnectors and, consequently, lower its operating temperature to slow down interconnectors degradation. As a result the area specific resistance of the cathodes should be lowered to sustain the performance of the cells. In order to...
-
Experimental and numerical investigations of ultimate strength of imperfect stiffened plates of different slenderness
PublicationThe objective of this study is to analyse the behaviour of compressed stiffened plates of different slenderness using experimental and numerical methods. The presented results are part of a long-term project to investigate the ultimate strength of geometrically imperfect structures subjected to different degradation phenomena, including corrosion degradation and locked cracks. Several specimens were subjected to a uniaxial compressive...
-
Mn-Co spinel coatings on Crofer 22 APU by electrophoretic deposition: Up scaling, performance in SOFC stack at 850 °C and compositional modifications
PublicationCeramic coatings for metallic interconnects play a key role in limiting corrosion and chromium evaporation in solid oxide cells. This study presents the upscaling of the electrophoretic deposition (EPD) technique to process Mn-Co spinels on real-dimension Crofer 22 APU interconnects and the test in a SOFC stack. Area specific resistance of long-term test conducted for 5000 h at 850 °C demonstrated that two-steps sintering has a...
-
Failure mode prediction for composite structural insulated panels with MgO board facings
PublicationSandwich panels are readily used in civil engineering due to their high strength to weight ratio and the ease and speed of assembly. The idea of a sandwich section is to combine thin and durable facings with a light-weight core and the choice of materials used allows obtaining the desired behaviour. Panels in consideration consist of MgO (magnesium oxide) board facings and expanded polystyrene core and are characterized by immunity...
-
Enhanced photoelectrochemical performance of inorganic-organic hybrid consisting of BiVO4 and PEDOT:PSS
PublicationThe PEDOT:PSS (poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate)) was electrodeposited on a thin layer of bismuth vanadate (BiVO 4 ) prepared using the pulsed laser deposition technique onto FTO. The inorganic-organic junction was characterized by Raman spectroscopy, UV-Vis spectroscopy and sc anning electron microscopy. Chronoamperometry curves, recorded under simulated solar light illumination,...
-
Materials Design for the Titanium Scaffold Based Implant
PublicationThe main objective of here presented research is a design the scaffold/porous titanium(Ti) alloy based composite material demonstrating better biocompatibility, longer lifetime andbioactivity behaviour for load-bearing implants. The development of such material is proposed bymaking a number of consecutive tasks. Modelling the mechanical, biomechanical and biologicalbehavior of porous titanium structure and an elaboration of results...
-
Materials Design for the Titanium Scaffold Based Implant
PublicationThe main objective of here presented research is a design the scaffold/porous titanium(Ti) alloy based composite material demonstrating better biocompatibility, longer lifetime andbioactivity behaviour for load-bearing implants. The development of such material is proposed bymaking a number of consecutive tasks. Modelling the mechanical, biomechanical and biologicalbehavior of porous titanium structure and an elaboration of results...
-
Synthesis of 5-Substituted 1H-Tetrazoles from Nitriles in the Presence of Heterogeneous Catalyst
PublicationTetrazoles are five-membered heterocyclic compounds containing in their rings four nitrogen atoms. They have wide applications as corrosion inhibitors, analytical reagents, high-energy materials and gas generating compositions. Tetrazoles also play important role in coordination chemistry as ligands and in medicinal chemistry as metabolically stable surrogates for carboxylic acids. In recent years, investigation of new method of...
-
A simplified method to assess the impact of ship-to-ship collision on the risk of tanker ship hull girder breaking accounting for the effect of ageing
PublicationOne of the most critical structural failures is the exceedance of the ship hull girder’s ultimate strength, which may result in hull breaking, and subsequent severe consequences, including loss of life and property as well as environmental damage in case of an oil spill. A cause for such loss of structural continuity can be triggered by a collision with another vessel. In addition, the ageing mechanisms of the hull structure could...
-
Methods of trend removal in electrochemical noise data – overview
PublicationIn this paper we shall review popular methods of trend removal from electrochemical noise time records. The basic principles of operation of the six most popular methods are explained. The proposed methods are: high - pass filtering, Moving Average Removal, polynomial detrending, wavelet detrending, Empirical Mode Decomposition and Variational Mode Decomposition. Estimation of trend removal quality...
-
In-situ Cu-doped MnCo-spinel coatings for solid oxide cell interconnects processed by electrophoretic deposition
PublicationThe Cu doping of the Mn–Co spinel is obtained “in-situ” by electrophoretic co-deposition of CuO and Mn1.5Co1.5O4 powders and subsequent two-step reactive sintering. Cu-doped Mn1.5Co1.5O4 coatings on Crofer22APU processed by electrophoretic co-deposition method are tested in terms of long term oxidation resistance and area specific resistance tests up to 3600 h. The introduction of Cu in the spinel lead to higher level of densification...
-
Visualization of the surface of the Nafion membrane
Open Research DataFuel cells use the chemical energy of hydrogen or other fuels to produce electricity. If the fuel is hydrogen, the only products are electricity, water and heat. Fuel cells are unique in the variety of their potential applications, they can use a wide variety of fuels. They are also highly scalable devices that can power both cars and mobile phones....
-
Investigation of the electrochemical behaviour of AA1050 aluminium alloy in aqueous alkaline solutions using Dynamic Electrochemical Impedance Spectroscopy
PublicationThe paper presents the electrochemical behaviour of aluminium alloy AA1050 in aqueous alkaline media in the pH range 14–8.5. Electrochemical study was applied in order to obtain comprehensive information on the mechanism and kinetics of the process of anodic dissolution of aluminium, supplemented by monitoring of surface topography using an electron microscope. The corrosion rate of AA1050 increases with increasing concentration...
-
Assessment of Supercapacitor’s Quality by Means of Low Frequency Noise
PublicationLow frequency noise is a well-known tool for quality and reliability assessment of electronic devices. This phenomenon is observed in different electrochemical devices as well (e.g., smart windows, electrochemical corrosion processes). Thus, we can assume that the same tool can be used to asses quality of supercapacitors. Their quality is usually determined only by capacitance and/or equivalent series resistance (ESR), or impedance....
-
X-Ray Computer Tomography Study of Degradation of the Zircaloy-2 Tubes Oxidized at High Temperatures
PublicationThe investigations of high-temperature oxidation of zirconium alloys, applied for fuel pellets in nuclear power plants, are usually limited to oxidation kinetics, phase transformations and microstructural characterization. The purpose of this research was to characterize the degradation phenomena occurring within oxide layer and at the interface oxide/metal, on internal and external Zircaloy-2 tube...
-
Effect of wet Hydrogen Sulfide on Carbon Steels Degradation in Refinery Based on Case Study
PublicationMaterial degradation caused by wet hydrogen sulfide (Wet H2S) is one of the major issues in refineries. Carbon steel is the main construction material used in refineries and is subjected not only to thickness loss but the hydrogen is the major concern. H2S leads to high atomic hydrogen penetration in steel which causes degradation in the form of blistering and/or cracking (HIC/SOHIC) and stress cracking in the area of welds and...
-
Determination of stepped plate thickness distribution using guided waves and compressed sensing approach
PublicationGuided waves recently have attracted significant interest as a very promising research area. The signals registered by a specially designed sensor network are processed to assess the state of the tested structure. Despite the constant development of novel damage detection algorithms employing guided waves, the phenomenon of wave propagation still needs detailed recognizing and understanding for the further progress of non-destructive...
-
On the mechanism of photocatalytic reactions on CuxO@TiO2 core–shell photocatalysts
PublicationTitania (titanium(IV) oxide) is a highly active, stable, cheap and abundant photocatalyst, and is thus commonly applied in various environmental applications. However, two main shortcomings of titania, i.e., charge carrier recombination and inactivity under visible-light (vis) irradiation, should be overcome for widespread commercialization. Accordingly, titania has been doped, surface modified and coupled with various ions/compounds,...
-
Nonlocal Models of Plates and Shells with Applications in Micro- and Nanomechanics
PublicationNowadays, the use of small-scale structures in micro/nanomachines has become more and more widespread. The most important applications of such small-sized parts are in micro-electro-mechanical systems (MEMS) as well as nano-electro-mechanical systems (NEMS) as actuators, sensors, energy harvesters. For example, nanosensors are nanoscale devices that measure physical quantities and convert these to signals that can be detected and...
-
Composite as a Material of the Future in the Era of Green Deal Implementation Strategies
PublicationComposite materials have become synonymous with modernity, desired in nearly every aspect of our daily lives, from simple everyday objects to sanitary facilities, pipelines, the construction of modern sewer networks, their renovation, water supply, and storage reservoirs, to complex structures—automotive, planes, and space science. Composites have seen a considerable rise in attention owing to their characteristics, durability,...
-
Guided waves for nondestructive diagnostics of embedded waveguides
PublicationThe thesis concentrates on comprehensive theoretical, numerical and experimental analysis of guided wave propagation in bars embedded in concrete or mortar. The investigations are focused on a particular type of objects representing a laboratory model of a ground anchor. Complex description of wave propagation phenomena in partially embedded bars is given and its application in...
-
Application and modelling of Shape-Memory Alloys for structural vibration control: State-of-the-art review
PublicationOne of the most essential components of structural design for civil engineers is to build a system that is resistant to environmental conditions such as harsh chemical environments, and catastrophic disasters like earthquakes and hurricanes. Under these circumstances and disturbances, conventional building materials such as steel and concrete may demonstrate inadequate performance in the form of corrosion, deterioration, oxidizing,...
-
Analysis of the Possibility of Using New Types of Protective Coatings and Abrasion-Resistant Linings under the Operating Conditions of the Spiral Classifier at KGHM Polska Miedź S.A. Ore Concentration Plant
PublicationA study was carried out to select the appropriate coatings for corrosion protection of the spiral classifier working at KGHM Polska Miedź S.A. Ore Concentration Plant. The abrasion resistance of selected protective coatings and wear-resistant linings was investigated using a DT-523 rotary abrasion tester with Taber CS-10 rubber abrasive discs. The average weight loss of the coatings after a cycle of 2000 revolutions was determined....
-
Cathodic activation of synthesized highly defective monoclinic hydroxyl‐functionalized ZrO2 nanoparticles for efficient electrochemical production of hydrogen in alkaline media
PublicationThe high electrochemical stability of Zirconia (ZrO2) at high potentials strongly suggested it as an alternative to carbon supports, which experience reduced efficiency due to some corrosion problems particularly during prolonged electrocatalysis activity. However, the use of ZrO2 was limited by its low electrical conductivity and surface area. In this work, we developed a methodology for synthesizing monoclinic ZrO2 NPs with increased...