Experimental and Numerical Investigation of Tensile and Flexural Behavior of Nanoclay Wood-Plastic Composite
PublicationIn this study, the effect of wood powder and nanoclay particle content on composites’ mechanical behavior made with polyethylene matrix has been investigated. The wood flour as a reinforcer made of wood powder was at levels of 30, 40, and 50 wt.%, and additional reinforcement with nanoclay at 0, 1, 3, and 5 wt.%. Furthermore, to make a composite matrix, high-density polyethylene was used at levels of 70, 60, and 50% by weight....
-
Tensile modulus of human orbital wall bones cut in sagittal and coronal planes
PublicationIn the current research, 68 specimens of orbital superior and/or medial walls taken from 33 human cadavers (12 females, 21 males) were subjected to uniaxial tension untill fracture. The samples were cut in the coronal (38 specimens) and sagittal (30 specimens) planes of the orbital wall. Apparent density (ρapp), tensile Young’s modulus (E-modulus) and ultimate tensile strength (UTS) were identified. Innovative test protocols were...
-
Machine learning-based prediction of preplaced aggregate concrete characteristics
PublicationPreplaced-Aggregate Concrete (PAC) is a type of preplaced concrete where coarse aggregate is placed in the mold and a Portland cement-sand grout with admixtures is injected to fill the voids. Due to the complex nature of PAC, many studies were conducted to determine the effects of admixtures and the compressive and tensile strengths of PAC. Considering that a prediction tool is needed to estimate the compressive and tensile strengths...
-
Mechanical response of human thoracic spine ligaments under quasi-static loading: An experimental study
PublicationPurpose This study aimed to investigate the geometrical and mechanical properties of human thoracic spine ligaments subjected to uniaxial quasi-static tensile test. Methods Four human thoracic spines, obtained through a body donation program, were utilized for the study. The anterior longitudinal ligament (ALL), posterior longitudinal ligament (PLL), capsular ligament (CL), ligamenta flava (LF), and the interspinous ligament and...
-
The effect of macro polymer fibres length and content on the fibre reinforced concrete
PublicationThe paper presents studies of a ready-mix concrete containing polymer fibres of three different lengths: 24, 38 and 54 mm. The performed tests allowed to determine the effect of fibre volume fraction and length on the concrete strength. The basic parameters of concrete mixture (consistency, air content and bulk density) were identified. Fibre reinforced concrete belongs to a group of composite materials. The polymer fibres are...
-
Morphology and properties of recycled polyethylene/ground tyre rubber/thermoplastic poly(ester-urethane) blends
PublicationThe growing amount of plastics waste produced every year resulted in development of mechanical and chemical recycling methods of polymers and their blends or composites. From the environmental point of view, the possibility of plastics waste reusing and recycling is desirable. In this study three polymer blends were obtained with using recycled polyethylene (RPE), ground tyre rubber (GTR) and thermoplastic poly(ester-urethane)...
-
Influence of cooling rate and additives on low-temperature properties of asphalt mixtures in the TSRST
PublicationThe paper presents the results and analysis of low-temperature properties of asphalt mixtures according to Thermal Stress Restrained Specimen Test (TSRST) and Indirect Tensile Test methods. Different groups of bitumen were investigated: neat, SBS-modified and highly SBS-modified. Influence of cooling rates (1 C/h, 3 C/h, 5 C/h and 10 C/h) and additives (aramid fibres and crumb rubber) was identified as well. Moreover, for each...
-
Stiffness of cold-recycled mixtures under variable deformation conditions in the IT-CY test
PublicationStiffness modulus belongs to the most important properties describing the cold-recycled mixtures (CRM) in terms of their usability in road pavement structures. Previous research proved that this property is strongly dependent on the scheme and conditions of the test (temperature and time of loading) and the time that has passed since the compaction of the specimen or pavement layer. It is a result of the influence of two different...
-
Mechanical properties of the human stomach under uniaxial stress action
PublicationThe aim of this study was to estimate the range of mechanical properties of the human stomach in order to use the collected data in numerical modelling of surgical stapling during resections of the stomach. The biomedical tests were conducted in a self-developed tensile test machine. Twenty-two fresh human stomach specimens were used for the experimental study of its general strength. The specimens were obtained from morbidly obese...
-
The fracture behaviour of notched PMMA specimens under simple loading conditions – Tension and torsion experimental tests
PublicationThis paper presents the results of experimental testing of flat PMMA specimens during uniaxial loading conditions. Two separate tests were conducted: tensile and torsion. The specimens were weakened with V-type edge notches with different root radii: 0.5; 2 and 10 mm. The specimens were made in two thickness variants: 5 and 15 mm. Monotonic tensile and torsion tests were carried out while keeping the averaged strain rate constant,...
-
The influence of stainless steels microstructure evolution on the mechanical properties of pressure installation elements
PublicationIn this paper results of FEM analysis performed for pipe and 90o elbow, made of super duplex stainless steel, after precipitation of sigma phase (),were presented. Heat treatment conditions simulate accidental overheating that can occur in nuclear installations after cooling circulation fails. For initial and modified microstructure tensile test was performed and numerical description of work hardening curves was done. Verification...
-
The influence of stainless steels microstructure evolution on the mechanical properties of pressure installation elements
PublicationIn this paper results of FEM analysis performed for pipe and 90o elbow, made of super duplex stainless steel, after precipitation of sigma phase (s), were presented. Heat treatment conditions simulate accidental overheating that can occur in nuclear installations after cooling circulation fails. For initial and modified microstructure tensile test was performed and numerical description of work hardening curves was done. Verification...
-
The use of a 4 PB strain sweep fatigue test to evaluate characteristics of carbon grid reinforced asphalt beams
PublicationThe article presents research results concerning pre-bituminized carbon grids for asphalt pavement reinforcement, which are used to prevent cracking and crack reflection thus increasing bearing capacity and durability of pavement. Research program involved testing of large sized double-layer samples, both reinforced and unreinforced. The advantage of using a carbon grid was especially visible after crack initiation. The energy...
-
Wire Arc Additive Manufactured Mild Steel and Austenitic Stainless Steel Components: Microstructure, Mechanical Properties and Residual Stresses
PublicationWire arc additive manufacturing (WAAM) is an additive manufacturing process based on the arc welding process in which wire is melted by an electric arc and deposited layer by layer. Due to the cost and rate benefits over powder-based additive manufacturing technologies and other alternative heat sources such as laser and electron beams, the process is currently receiving much attention in the industrial production sector. The gas...
-
Experimentation, material modelling and simulation of bonded joints with a flexible adhesive
PublicationThe paper deals with material parameters identification of a flexible adhesive and the numerical simulation of its behaviour in a single lap bonded joint. The material modelling was based on the simple shear and tensile-shear laboratory tests of the bonded joints made of thin aluminium and polyurethane plates with the flexible adhesive Terostat MS 9360 manufactured by Henkel AG & Co. The adhesive was considered as a hyperelastic...
-
Mechanical and fracture properties of concrete reinforced with recycled and industrial steel fibers using Digital Image Correlation technique and X-ray micro computed tomography
PublicationPaper presents investigation of fracture phenomenon in plain concrete and in concrete reinforced with both recycled steel fibers (RSF) and industrial steel fibers (ISF). The wedge splitting test (WST), which enables stable crack propagation for quasi-brittle materials, was carried out on 75 75 75 mm cube samples. Initially, fracture process zone development was investigated only on the surface of samples using Digital Image Correlation...
-
High-Temperature Tensile Behaviour of GTAW Joints of P92 Steel and Alloy 617 for Two Different Fillers
PublicationThis study explores the high-temperature (HT) tensile rupture characteristics of a dissimilar gas-tungsten-arc-welded (GTAW) joint between P92 steel and Alloy 617, fabricated using ER62SB9 and ERNiCrCoMo-1 fillers. The high-temperature tensile tests were performed at elevated temperatures of 550 ◦C and 650 ◦C. An optical microscope (OM) and a field emission scanning electron microscope (FESEM) were utilized to characterize the...
-
The Effect of Water and Frost on Fatigue Life of Asphalt Concrete
PublicationThis paper presents testing of fatigue life of asphalt concrete that has been subjected to action of water and frost. Simulation of water and frost action was based on the original AASHTO T283 method and its modification. The original method was modified in such a way that instead of a single freeze-thaw cycle, 50 and 150 cycles were applied. Fatigue life was measured in the indirect tensile fatigue test in the Nottingham asphalt...
-
Microstructure, mechanical properties, and flame retardancy of nanoclay-incorporated polyurethane flexible foam composites
PublicationThe present work seeks to investigate microstructure, mechanical properties, and flame retardancy of polyurethane/nanoclay flexible foam composites. In this regard, we prepared various nanocomposites with and without nanoclay and observed the resulting morphologies to correlate them with the other corresponding characteristics. The results provided support for the fact that tensile strength and compression set will increase with...
-
A constitutive law for concrete with smooth transition from continuous into discontinuous cracks’ description
PublicationPaper presents a constitutive model for concrete that combines a continuous and discontinuous crack’s description to simulate the concrete under tensile dominated loads. In a continuum regime, two different constitutive laws were used. First, a plasticity model with the Rankine failure criterion and an associated flow rule was used. Second, a constitutive law based on isotropic damage mechanics was formulated. Both model alternatives...
-
Application of galvanodynamic impedance spectroscopy for studying passive film cracking under mechanical strain
PublicationThe paper reports the results of simultaneous mechanical and electrochemical investigations on austenitic (18/8) stainless steel in a 2 % solution of sulphuric acid. The measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Electrochemical analysis of mechanical passive layer cracking and repassivation conditions during a tensile test was carried out. Application of this methodology allowed...
-
Study on Microstructural Characterization, Mechanical Properties and Residual Stress of GTAW Dissimilar Joints of P91 and P22 Steels
PublicationThis article deals with the dissimilar joining of two different grade Cr-Mo steel (2.25Cr-1Mo: P22 and modified 9Cr-1Mo: P91) for power plant application. The dissimilar butt-welded joint was produced for conventional V groove design by using the gas tungsten arc welding (GTAW) process with the application of an ERNiCrMo-3 Ni-based super alloy filler. A microstructure characterization was performed to measure the inhomogeneity...
-
Investigation on Mode I Fracture Behavior of Hybrid Fiber-Reinforced Geopolymer Composites
PublicationRecent reports in the literature have shown that fber-reinforced geopolymer composites (FRGC) made with monofbers exhibit a signifcant enhancement in fracture energy. However, many aspects of the fracture performance of hybrid fberreinforced geopolymer composites (HFRGC) remain largely unexploited, and these are predominant for the structures. For the frst time, the mode I fracture energy of HFRGC is investigated. The mode I behavior...
-
Microstructure and mechanical properties of a dissimilar metal welded joint of Inconel 617 and P92 steel with Inconel 82 buttering layer for AUSC boiler application
PublicationThe application of the novel dissimilar metal welded (DMW) joint, utilizing Inconel 617 and P92 steel, was showcased in the advanced ultra-supercritical (AUSC) boiler. The work has been performed to investigate the effect of Inconel 82 (ERNiCr-3) buttering layer on microstructure and mechanical properties (high-temperature tensile strength, impact strength and microhardness) of gas tungsten arc welded (GTAW) dissimilar joint between...
-
Study on Microstructure-Property Relationship of Inconel 617 Alloy/304L SS Steel Dissimilar Welds Joint
PublicationWelding of Inconel 617 (IN617) alloy and austenitic 304L SS steel has been attempted using the autogenous Laser Beam Welding (LBW) process. Characterization of dissimilar weldments was performed on either side of the fusion boundaries. The metallographic results showed that the inhomogeneous microstructure formation for weld metal contained columnar and cellular dendrites near the interface, whilst the columnar, cellular and equiaxed...
-
Assessment of the application of CEM III with exposed aggregate as an alternative to CEM I for road pavements
PublicationThe article presents a results of study on the impact of replacing CEM I SR3/NA by CEMIII/A LH/HSR/NAon the mechanical properties and durability of pavement concrete with exposed aggregate. Was used granite aggregate and washed sand. Water/cement () ratio in the tested concretes constituted 0.35 and 0.4 and part of the cement was replaced with a 5% addition of natural pozzolana – zeolite. Compressive strength tests were performed...
-
Analytical approach for membrane action in laterally-restrained reinforced concrete square slabs under uniformly distributed loads
PublicationLaterally-restrained reinforced concrete slabs can mobilise compressive membrane action and subsequent tensile membrane action under extreme loading conditions, thereby enhancing the load resistance under uniformly distributed loads. Previous analytical study focuses primarily on tensile membrane action in simply-supported slabs. This paper describes an analytical approach for membrane action in laterally-restrained square slabs....
-
Comparative Study of the Reinforcement Type Effect on the Thermomechanical Properties and Burning of Epoxy-Based Composites
PublicationAramid (AF), glass (GF), carbon (CF), basalt (BF), and flax (FF) fibers in the form of fabrics were used to produce the composites by hand-lay up method. The use of fabrics of similar grammage for composites’ manufacturing allowed for a comprehensive comparison of the properties of the final products. The most important task was to prepare a complex setup of mechanical and thermomechanical properties, supplemented by fire behavior...
-
Preparation, morphology and properties of natural rubber composites filled with untreated short jute fibres
PublicationGreen composites were obtained by incorporation of short jute fibres in natural rubber matrix using a laboratory two-roll mill. The influence of untreated fibre content (1, 2.5, 5, 7.5 and 10 phr) on the mechanical properties, dynamic mechanical properties, swelling properties was examined. The behaviour of prepared green composites under cyclic compression was also investigated. Fibre dispersion in rubber matrix was studied by...
-
The Influence of the Aircraft Operating Fluids on the Mechanical Parameters of the Airport Surface Concrete
PublicationThe authors of the article assessed the impact of operating fluids used to service aircraft on changing mechanical parameters of cement concrete intended for airport pavement. The research concerned concrete designed with the use of CEM I 42.5N LH NA low-alkali cement, broken granite aggregate, fine washed aggregate, and admixtures. The analysis included the assessment of changes in dierences in endurance parameters over various...
-
Size effect in concrete under splitting tension
PublicationThe size effect is a fundamental phenomenon in concrete materials. It denotes that both the nominal structural strength and material ductility always decrease with increasing element size under tension. In the paper splitting tensile tests on cylindrical concrete specimens with the different diameter were carried out. Two types of the loading strip (plywood board and steel cylinder) were used. The concrete strength and ductility...
-
Autogenous Fiber Laser Welding of 316L Austenitic and 2304 Lean Duplex Stainless Steels
PublicationThis study presents results of experimental tests on quality of dissimilar welded joints between 316L austenitic and 2304 lean duplex stainless steels, welded without ceramic backing. Fiber laser welded butt joints at a thickness of 8 mm were subjected to non‐destructive testing (visual and penetrant), destructive testing (static tensile test, bending test, and microhardness measurements) and structure observations (macro‐ and...
-
Optymalizacja doboru prawa konstytutywnego membrany o strukturze plecionej
PublicationCelem niniejszej dysertacji jest opracowanie zagadnienia optymalizacyjnego pozwalającego dobrać model konstytutywny opisujący mechaniczne zachowanie membrany technicznej. Do analizy wybrano membrany plecione, stosowane w medycynie, tzw. siatki chirurgiczne. W celu wykonania identyfikacji praw konstytutywnych, wykonano dwuosiowe rozciąganie próbek materiałów, otrzymując wskazanie na nieliniowe anizotropowe zachowanie materiałów....
-
P92 steel and inconel 617 alloy welds joint produced using ERNiCr-3 filler with GTAW process: Solidification mechanism, microstructure, mechanical properties and residual stresses
PublicationThe objective of the current study was to analyse the microstructure, mechanical characteristics, and residual stresses of a dissimilar welded joint (DWJ) made of P92 steel and the Inconel alloy 617 (IN617) using the gas tungsten arc welding (GTAW) method. The ERNiCr-3 filler was selected to produce the conventional V groove (VG) and narrow V groove (NVG) butt joint. The filler deficient zones in the weldments, such as the filler...
-
Evaluation of Mechanical Properties of Two-Stage Concrete and Conventional Concrete Using Nondestructive Tests
PublicationDifferent types of concrete mixtures are used as building materials. The manufacturing process of two-stage concrete (TSC) differs from that of conventional concrete. This study investigated conventional mechanical properties derive empirical relations for estimation of the mechanical parameters of TSC and conventional concrete mixtures. TSC was used to prepare 216 specimens and conventional concrete was used to prepare 108 specimens...
-
The Effect of Surface Treatment with Isocyanate and Aromatic Carbodiimide of Thermally Expanded Vermiculite Used as a Functional Filler for Polylactide-Based Composites
PublicationIn this work, thermally expanded vermiculite (TE-VMT) was surface modified and used as a filler for composites with a polylactide (PLA) matrix. Modification of vermiculite was realized by simultaneous ball milling with the presence of two PLA chain extenders, aromatic carbodiimide (KI), and 4,4’-methylenebis(phenyl isocyanate) (MDI). In addition to analyzing the particle size of the filler subjected to processing, the efficiency...
-
One Year Evaluation of Material Properties Changes of Polylactide Parts in Various Hydrolytic Degradation Conditions
PublicationBiodegradable biocompatible materials are widely used in medical applications. Determining the possibility of using biodegradable materials depends on determining the changes in their parameters over time due to degradation. The current scientific research on biodegradable materials has presented results based on research methods characterized by the different geometry and cross-section size of the specimen, type of degradation...
-
Synthesis and thermal studies of flexible polyurethane nanocomposite foams obtained using nanoclay modified with flame retardant compound
PublicationThis work presents thermal studies of nanocomposites based on the flexible polyurethane (PU) matrix and filled using montmorillonite organically modified with organophosphorus flame retardant compound. Flexible PU nanocomposite foams were prepared in the reaction carried out between reactive alcoholic hydroxyl and isocyanate groups with the ratio of NCO to OH groups equal to 1.05. The amount of an organoclay ranging from 3 to 9...
-
Durability of Asphalt Concrete Subjected to Deteriorating Effects of Water and Frost
PublicationThe paper presents testing of the detrimental effects of water and frost on asphalt pavements. It included laboratory testing of 5 fatigue life of asphalt concrete that was subjected to action of water and frost and field testing of damages caused by water and frost on 6 existing asphalt pavements, such as stripping, raveling, and potholes. Laboratory simulation of water and frost action was based on the 7 original AASHTO T283...
-
Laser Beam as a Precision Tool to Increase Fatigue Resistance in an Eyelet of Undercarriage Drag Strut
PublicationThe article contains the results of tests on a laser-processed eyelet of undercarriage drag strut to increase its fatigue strength. Laser processing concentrated on both sides around the hole of eye for connecting the undercarriage drag strut caused that the material in this area withstood more than twice the number of load cycles established for this material. In order to determine the reasons for the increase in fatigue strength,...
-
Contact with coupled adhesion and friction: Computational framework, applications, and new insights
PublicationContact involving soft materials often combines dry adhesion, sliding friction, and large deformations. At the local level, these three aspects are rarely captured simultaneously, but included in the theoretical models by Mergel et al., (2019). We here develop a corresponding finite element framework that captures 3D finite-strain contact of two deformable bodies. This framework is suitable to investigate sliding friction even...
-
Effect of bio-based components on the chemical structure, thermal stability and mechanical properties of green thermoplastic polyurethane elastomers
PublicationIt seems to be obvious that conditions changes during polyols synthesis have impact on the polyols properties. Even the chemical formula is the same or similar, physicochemical properties and also molecular weight of polyols might be different and are significant in term of future polyurethanes properties and processing. In this work, fully bio-based poly(propylene succinate)s synthesized at different temperature conditions were...
-
Hydrogen Embrittlement and Oxide Layer E ect in the Cathodically Charged Zircaloy-2
PublicationThe present paper is aimed at determining the less investigated effects of hydrogen uptake on the microstructure and the mechanical behavior of the oxidized Zircaloy-2 alloy. The specimens were oxidized and charged with hydrogen. The different oxidation temperatures and cathodic current densities were applied. The scanning electron microscopy, X-ray electron diffraction spectroscopy, hydrogen absorption assessment, tensile, and...
-
Investigations of size effect in concrete at aggregate level - experiments and calculations results using discrete element method
PublicationSize effect is a fundamental phenomenon in concrete. It is characterised by decreasing strength and increasing brittleness of concrete with increasing size. The thesis includes experimental and theoretical elements. The main goal of the thesis were investigations of a size effect at the aggregate level by taking fracture into account with the discrete element method (DEM) for various failure modes. Comprehensive experiments on...
-
Structure versus hydrolytic and thermal stability of bio-based thermoplastic polyurethane elastomers composed of hard and soft building blocks with high content of green carbon
PublicationNowadays, sustainability plays a key role in the design and synthesis of new materials. One of the methods for the preparation of green materials is incorporation into their structure the monomers with a high content of green carbon. Therefore, the aim of this work was to investigate the influence of the type and molecular mass of two bio-based polyester polyols and bio-glycol on the properties of aliphatic partially bio-based...
-
Thermomechanical and Fire Properties of Polyethylene-Composite-Filled Ammonium Polyphosphate and Inorganic Fillers: An Evaluation of Their Modification Efficiency
PublicationThe development of new polymer compositions characterized by a reduced environmental impact while lowering the price for applications in large-scale production requires the search for solutions based on the reduction in the polymer content in composites’ structure, as well as the use of fillers from sustainable sources. The study aimed to comprehensively evaluate introducing low-cost inorganic fillers, such as copper slag (CS),...
-
The Impact of Homogeneity of High Modulus Asphalt Concrete Layer on Low-Temperature Cracking
PublicationDuring winter season of 2012 numerous transverse cracks developed in high-modulus asphalt concrete (HMAC) base of newly constructed motorway. Pavement cracked both in transverse joint locations and in the area between them. Research which was conducted during investigation of the causes and mechanisms of cracking consisted of: field examination, laboratory testing of specimens cored out of the existing pavement, computational analyses...
-
The FEM analysis of pressure installation elements after simulated accidental overheating
PublicationThe paper presents innovative analysis focused on the safety aspects of existing pressure installation operation after overheating accidents. Results presented here can be applied in decision-making process concerning further operation of existing pressure installation after cooling system failure. In this paper the results of FEM analysis performed for a straight pipe and 90 degrees elbow, made of super duplex stainless steel,...
-
Shape memory thin films of Polyurethane: Does graphene content affect the recovery behavior of Polyurethane nanocomposites?
PublicationThin nanocomposite films of polyurethane have received remarkable attention due to their shape memory properties. As most of the reports focus on the beneficial aspects of the presence of nanofillers such as graphene nanoplatelets (GNPs) introduced into shape memory polymers, some research results reveal the opposite trend. The polyether/polyester-based polyurethane was synthesized through a condensation polymerization and the...
-
Influence of the Addition of Recycled Aggregates and Polymer Fibers on the Properties of Pervious Concrete
PublicationThe aim of the study was to check the possibility of reusing aggregate from recycled concrete waste and rubber granules from car tires as partial substitution of natural aggregate. The main objective was to investigate the effects of recycled waste aggregate modified with polymer fibers on the compressive and flexural strength, modulus of elasticity and permeability of pervious concrete. Fibers with a multifilament structure and...