Search results for: SUPER DUPLEX STAINLESS STEEL WELDING CATHODIC PROTECTION
-
TiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A41/#B39
Open Research DataWear tests in sliding friction of TiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiC over TiC . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #A25/#B21
Open Research DataWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 9 min....
-
CrN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #B22/#A23
Open Research DataWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 6 min. The test...
-
SiC coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A33/#B34
Open Research DataWear tests in sliding friction of SiC coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, SiC over SiC. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 3 min. The test...
-
FEM modelling of stress and strain distribution in weld joints of steel sandwich panels
PublicationThe development of laser welding technology has enabled the mass production of thin-walled structures, including steel sandwich panels. The technology of joining plating panels with stiffeners by welding allows us to create joints with a specific geometry and material properties. In comparison with other types of joints, laser welds are characterized by their specific behaviour under cyclic load and, as a consequence, a different...
-
Application of the Barkhausen effect probe with adjustable m agnetic field direction for stress state determination in the P91 ste el pipe
PublicationThe paper presents the results of application of a novel Barkhausen effect (BE) probe with adjustable magnetizing field direction for the stress level evaluation in ferromagnetic materials. The investigated sample was in a form of a pipe, made of P91 steel that was anisotropic due to the production process. The measurements were performed before and after welding, revealing the influence of welding process on the residual stress...
-
The Effect of Increasing the Amount of Indium Alloying Material on the Efficiency of Sacrificial Aluminium Anodes
PublicationAl-Zn-In alloys having 4.2% zinc content and various indium content in the range of 0.02–0.2% were tested with respect to the most important electrochemical properties of sacrificial anodes in a cathodic protection, i.e., the current capacity and potential of the operating anode. The distribution of In and Zn in the tested alloys was mapped by means of the EDX technique, which demonstrated that these elements dissolve well in the...
-
Experimental review of the performances of protective coatings for interconnects in solid oxide fuel cells
PublicationFerritic stainless steel interconnects are used in solid oxide fuel cells; however, coatings are required to improve their performance. Although several types of coatings have been proposed, they have been scarcely investigated under similar conditions. This study compares the characteristics of uncoated Crofer 22 APU and eight different coatings on Crofer 22 APU for up to 3000 h at 800 ◦C. The coatings were deposited at various...
-
The Innovative Faculty for Innovative Technologies
PublicationA leaflet describing Faculty of Electronics, Telecommunications and Informatics, Gdańsk University of Technology. Multimedia Systems Department described laboratories and prototypes of: Auditory-visual attention stimulator, Automatic video event detection, Object re-identification application for multi-camera surveillance systems, Object Tracking and Automatic Master-Slave PTZ Camera Positioning System, Passive Acoustic Radar,...
-
Underwater in situ local heat treatment by additional stitches for improving the weldability of steel
PublicationIn this paper the influence of in situ local heat treatment performed by additional stitches on the weldability of high-strength low-alloy (HSLA) S355J2C+N steel was tested. The investigated steel is characterized by high susceptibility to cold cracking. It is necessary to find a method to improve the quality of welded joints. The local heat treatment was applied as an eect of bead-on plate welding made on the face of a Tekken...
-
CrN coating in ring-on-ring sliding with saline solution (0.9%) lubrication 5MPa, 0.1m/s specimn. #B21/#A21
Open Research DataWear tests in sliding friction of CrN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, CrN over CrN . Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: SALINE SOLUTION (0.9%). Tribometer: PT-3. Overall test time till coating penetration 25 min....
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#A47
Open Research DataWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 20 min. The test...
-
TiN coating in ring-on-ring sliding with distlled water lubrication 5MPa, 0.1m/s specimn. #A45/#B45
Open Research DataWear tests in sliding friction of TiN coating on 1.4021 (EN 10088-1) heat treated stainless steel. Ring - on - ring contact in unidirectional sliding, TiN over TiN. Mean contact stress: 5MPa. Sliding velocity: 0,1 m/s. Mean friction radius: 9.5mm. Lubricant: DISTILLED WATER. Tribometer: PT-3. Overall test time till coating penetration 90 min. The test...
-
Instantaneous Impedance Analysis of Non-Stationary Corrosion Process: a Case Study of Carbon Steel in 1M HCl
PublicationThe paper concerns the problem of evaluation of stationarity of carbon steel corrosion in 1M HCl. Comparison of corrosion rate with addition of corrosion inhibitor to the reference measurement is the most often used way of evaluating inhibitor efficiency. Such an approach is valid only if corrosion rate is a stationary process. Two complementary techniques were used simultaneously: volumetric analysis of evolved hydrogen and instantaneous...
-
Analysis of the Possibility of Using New Types of Protective Coatings and Abrasion-Resistant Linings under the Operating Conditions of the Spiral Classifier at KGHM Polska Miedź S.A. Ore Concentration Plant
PublicationA study was carried out to select the appropriate coatings for corrosion protection of the spiral classifier working at KGHM Polska Miedź S.A. Ore Concentration Plant. The abrasion resistance of selected protective coatings and wear-resistant linings was investigated using a DT-523 rotary abrasion tester with Taber CS-10 rubber abrasive discs. The average weight loss of the coatings after a cycle of 2000 revolutions was determined....
-
Dynamic Nanoimpedance Characterization of the Atomic Force Microscope Tip-Surface Contact
PublicationNanoimpedance measurements, using the dynamic impedance spectroscopy technique, were carried out during loading and unloading force of a probe on three kinds of materials of different resistivity. These materials were: gold, boron-doped diamond, and AISI 304 stainless steel. Changes of impedance spectra versus applied force were registered and differences in the tip-to-sample contact character on each material were revealed. To...
-
Evaluation of organic coating systems for corrosion protection of industrial equipment using impedance spectroscopy
PublicationThe high economic impact of corrosion can be reduced by enhanced corrosion management and prevention based on appropriate means. This applies in particular to the protection of structures with organic protective coatings. Steel is subject to corrosion that reduces its service life and leads to destruction in most severe cases. The application of paints to metallic objects for corrosion control has been known for a long time and...
-
Displacements of bones during bending test of first metatarsophalangeal joint after arthrodesis with medially or dorsally positioned locking plate and lag screw.
Open Research DataThe Dataset contains the values of displacements of bone control points during the bending test of first metatarsophalangeal (MTP1) joint specimens after arthrodesis.
-
Pool boiling of nanofluids on rough and porous coated tubes: experimental and correlation
PublicationThe paper deals with pool boiling of water-Al2O3 and water- Cu nanofluids on rough and porous coated horizontal tubes. Commercially available stainless steel tubes having 10 mm outside diameter and 0.6 mm wall thickness were used to fabricate the test heater. The tube surface was roughed with emery paper 360 or polished with abrasive compound. Aluminium porous coatings of 0.15 mm thick with porosity of about 40% were produced by...
-
NUMERICAL MODEL OF PLASTIC DESTRUCTION OF THICK STEEL STRUCTURAL ELEMENTS
PublicationIn the shipbuilding industry, the risk of brittle fracture of the structure is limited by using certified materials with specified impact strength, determined by the Charpy method (for a given design temperature) and by supervising the welding processes (technology qualification, production supervision, non-destructive testing). For off-shore constructions, classical shipbuilding requirements may not be sufficient. Therefore, the...
-
Effect of Pin Shape on Thermal History of Aluminum-Steel Friction Stir Welded Joint: Computational Fluid Dynamic Modeling and Validation
PublicationThis article studied the effects of pin angle on heat generation and temperature distribution during friction stir welding (FSW) of AA1100 aluminum alloy and St-14 low carbon steel. A validated computational fluid dynamics (CFD) model was implemented to simulate the FSW process. Scanning electron microscopy (SEM) was employed in order to investigate internal materials’ flow. Simulation results revealed that the mechanical work...
-
Imaging of the effects of pitting corrosion with the use of AFM
Open Research DataPitting corrosion is a local attack on a metal surface, limited to a point or small area, which appears as a hole. Pitting corrosion is one of the most harmful forms of corrosion due to the fact that it is associated with small, difficult to detect damage, that can even lead to perforation of the structure. A single pit may range in size from micrometers...
-
New Method of Non-Linear Electrochemical Impedance Spectroscopy with an Amplitude-Modulated Perturbation Signal
PublicationThe paper presents a new method of non-linear electrochemical impedance spectroscopy (NLEIS), which allows fast and nondestructive evaluation of the corrosion rate and determination of the Tafel coefficients values for a corrosion system under investigation. This method employs amplitude modulation of the ac perturbation signal. The study demonstrated that it was possible to obtain impedance characteristic as a function of the...
-
Designate of CTOD for WM and HAZ, report no: WOiO/II/122/2014
PublicationTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability to...
-
CTOD designation for WM and HAZ in butt joint made from S460 ML steel, Expertise No. WOiO/II/82/2015
PublicationTypical (normative) testing of materials and/or welded joints do not answer on all questions about material or welded joint properties. In ship building and off-shore sectors, many strucures requires materials and joint with higher than typical fatigue resistance. Imact tests, which are carried out during welding technology qualification, gives answer about ductility, CTOD tests results about material or welded joint ability to...
-
Właściwości stali S460M napawanej pod wodą metodą lokalnej komory suchej
PublicationW artykule przedstawiono wyniki badań próbek ze stali S460M wykonanych pod wodą metodą lokalnej komory suchej. Pomiary twardości oraz analiza strukturalna wykazały, że dla określonych ilości wprowadzonego ciepła możliwe jest wykonanie złączy bez niezgodności spawalniczych. Stwierdzono formowanie się w pewnych warunkach pęknięć zimnych w SWC wywołanych procesami odprowadzania ciepła z materiału, które są charakterystyczne dla spawania...
-
Influence of Material Thickness on the Ductile Fracture of Steel Plates for Shipbuilding
PublicationIn the shipbuilding industry, the risk of brittle fractures is relatively high because some units operate in arctic or subarcticzones and use high thickness (up to 100 mm) steel plates in their structures. This risk is limited by employing certifiedmaterials with a specific impact strength, determined using the Charpy method (for a given design temperature) and byexercising control over the welding processes (technology qualification,...
-
High-temperature kinetics study of 430L steel powder oxidized in air at 600–850 °C
PublicationThe 430L stainless steel powder with a mean particle size of 95 μm was studied to determine its high-temperature oxidation properties. Continuous thermogravimetric measurements were carried out for 100 h in air at temperatures in the range of 600–850 °C. Even though a considerable amount of Cr (up to ˜5 wt.% Cr) inside the grains was depleted – especially inside small grains – no breakaway oxidation was observed. This indicates...
-
Assesment of (Mn,Co)3O4powders for possible coating material for SOFC/SOEC interconnects
PublicationIn this work (Mn,Co)3O4 spinel powders with different Mn:Co ratio (1:1 and 1:2) and from different commercial suppliers are evaluated for possible powder for production of interconnect coatings. Sinterability of the powders is evaluated on pressed pellets sintered in oxidizing and in reducing/oxidizing atmospheres. For selected powder, coatings are then prepared by the electrophoretic deposition method on Crofer 22 APU stainless...
-
Fe-modified Mn2CuO4 spinel oxides: coatings based on abundant elements for solid oxide cell interconnects
PublicationThe current state of the art steel interconnect coating materials are based on critical raw material - Co-oxide spinels. Replacing Co-oxide spinels with alternative, abundant materials can reduce the dependence on the critical raw materials. Cobalt-free coatings with the general formula Mn2-xCuFexO4, where x = 0, 0.1, 0.3, were electrophoretically deposited on a ferritic stainless-steel support and evaluated. Prior to deposition,...
-
Multilayer coatings based on cerium oxide and manganese cobaltite spinel for Crofer22APU SOC interconnects
PublicationThe current state of the art steel interconnect coating materials are based on critical raw material - Co-oxide spinels. Replacing Co-oxide spinels with alternative, abundant materials can reduce the dependence on the critical raw materials. Cobalt-free coatings with the general formula Mn2-xCuFexO4, where x = 0, 0.1, 0.3, were electrophoretically deposited on a ferritic stainless-steel support and evaluated. Prior to deposition,...
-
The protection and monitoring of a distribution piping network for potable water supply
PublicationPurpose – The purpose of this paper is to implement the corrosion protection method for steel pipes used in a municipal water-pipe network. Results of an inhibitor protection system installed on the system are presented. Inhibitor protection was required due to the high corrosivity of the water collected by a surface intake, which had resulted in a large number of failures and low water quality, due to the presence of corrosion...
-
The Influence of Modelling Material Zones on Strains and Stresses at Weld Toe Notch
PublicationThe latest development in the field of welding technology enabled prefabrication of thin-walled sandwich structures in an industrial scale. Sandwich structures fabricated of steel, or aluminium alloy plates and stiffeners are welded with the use of hi-power CO2 lasers. Strength analysis of such structures with the use of finite element method needs proper material modelling.In this paper the material model of steel sandwich panel...
-
Experimental investigation of forced convection of water/EGAl2O3 nanofluids inside horizontal tube
PublicationIn this paper, forced convection of water/EG-Al2O3 nanofluids inside horizontal stainless steel tube is studied experimentally. As base fluid served water/EG mixture of two ratios (60:50 and 50:50). Nanoparticle mass concentrations was 0.1% or and 1%. Transition and turbulent flow regimes were tested. Average heat transfer coefficient and pressure drop values were determined for nanofluids and compared to base fluids. Deterioration...
-
INFLUENCE OF SURFACE CURVATURE ON SESSILE DROPLET CONTACT ANGLE OF NANOFLUIDS
PublicationThis paper deals with change in contact angle of droplets of three nanofluids, i.e. water-Al2O3, water-TiO2 and water-Cu. Nanoparticles were tested at the concentration of 0.01%, 0.1%, and 1% by weight. Although dispersants were not used to stabilize the suspension, the solutions tested exhibited satisfactory stability. Ultrasonic vibration was used in order to stabilise the dispersion of the nanoparticles. Experimental measurements...
-
3D Printing of Metallic Implants
PublicationThe fabrication of various elements, solid and open porous structures of stainless steel and Ti alloy is described. The process was started with the design of 3D models in CAD/CAM system. The 3D models were transformed into *.stl files and then the manufacturing process of the real structures by means of the selective laser melting with the SLM Realizer 100 3D printer was made. The paper shows the porous specimens made for possible...
-
The influence of core material on strength properties of hybrid sandwich panels
PublicationAlong with high prices of fuels and more restrictive safety and environmental regulations (including environment protection) increased interest in sandwich structures is being observed. One of the solution having growing application potential is steel sandwich panel. The construction consist of very thin steel plates (about 2mm) and stiffeners between them. The main advantage of using such solution is very high strength to weight...
-
The home-made in situ passive flux sampler for the measurement of monoterpene emission flux: preliminary studies
PublicationThe paper presents the construction and metrological characteristics of the home-made in situ passive flux sampler, an analytical tool representing small-scale emission chambers working in situ and passively sampling analytes from the gaseous phase. The sorption element was a cylindrical container made of stainless steel net, packed with a carbon sorbent bed-graphitized charcoal, Carbograph 4 (35/50mesh). The recommended working/exposure...
-
Types of Surface Impurities versus the Quality of Brazed Joints
PublicationBrazing is one of the primary joining processes increasingly often applied in industry. Because of their mechanical properties, overlap joints are particularly popular when making brazed structures. The use of brazed joints in structures of critical importance requires that particular attention be paid to joint quality, e.g. by the appropriate cleaning of surfaces to be joined. The article presents results of non-destructive tests...
-
Zastosowanie techniki ściegu odpuszczającego do spawania mokrego
PublicationW artykule przedstawiono zastosowanie techniki ściegu odpuszczającego do poprawy właściwości złączy ze stali konstrukcyjnych wykonywanych w warunkach mokrego spawania pod wodą. Scharakteryzowano spawanie mokre elektrodami otulonymi zmiany struktury i właściwości złączy spawanych przez nakładanie ściegów odpuszczających. Przedstawiono metodykę oraz wyniki badań metalograficznych i twardości próbek ze stali konstrukcyjnej o podwyższonej...
-
Surface Texture after Turning for Various Workpiece Rigidities
PublicationIn the paper, we present an analysis of the surface texture of turned parts with L/D (length/diameter) ratios of 6 and 12 and various rigidity values. The studies were carried out on samples made of S355JR steel and AISI 304 stainless steel. A detailed analysis of 2D surface profiles was carried out by using a large number of parameters that allowed us to distinguish significant differences in the surface microgeometry, which confirmed...
-
A brief note on monotonic and fatigue fracture events investigation of thin-walled tubular austenitic steel specimens via fracture surface topography analysis (FRASTA)
PublicationThe main objective of this short communication is to show the fracture progression in each loading case and complement knowledge about fracture mechanisms underpinning the tensile and fatigue performance of thin-walled tubes. For this purpose, the fracture surface topography analysis (FRASTA) method was used in the thin-walled tubular austenitic stainless-steel specimens. Two cases were analyzed: monotonic tension, and uniaxial...
-
Ceria Based Protective Coatings for Steel Interconnects Prepared by Spray Pyrolysis
PublicationStainless steels can be used in solid oxide fuel/electrolysis stacks as interconnects. For successful long term operation they require protective coatings, that lower the corrosion rate and block chemical reactions between the interconnect and adjacent layers of the oxygen or the hydrogen electrode. One of the promising coating materials for the hydrogen side is ceria. Using standard sintering techniques, ceria sinters at around...
-
Application of galvanodynamic impedance spectroscopy for studying passive film cracking under mechanical strain
PublicationThe paper reports the results of simultaneous mechanical and electrochemical investigations on austenitic (18/8) stainless steel in a 2 % solution of sulphuric acid. The measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Electrochemical analysis of mechanical passive layer cracking and repassivation conditions during a tensile test was carried out. Application of this methodology allowed...
-
Study on Microstructure and Mechanical Properties of Laser Welded Dissimilar Joint of P91 Steel and INCOLOY 800HT Nickel Alloy
PublicationThis investigation attempts to explore the weld characteristics of a laser welded dissimilar joint of ferritic/martensitic 9Cr-1Mo-V-Nb (P91) steel and Incoloy 800HT austenitic nickel alloy. This dissimilar joint is essential in power generating nuclear and thermal plants operating at 600–650 °C. In such critical operating conditions, it is essential for a dissimilar joint to preserve its characteristics and be free from any kind...
-
Sessile droplet contact angle of water–Al2O3, water–TiO2 and water–Cu nanofluids
PublicationThis work presents measurements of the contact angle of sessile droplets for three nanofluids, i.e. water–Al2O3, water–TiO2 and water–Cu. The plates made of glass, anodized aluminium and stainless steel of different roughness served as substrates. Ultrasonic vibration was used for 30–60 min in order to stabilise the dispersion of the nanoparticles. Nanoparticles were tested at the concentration of 0.01%, 0.1%, and 1% by weight....
-
Electrohydrodynamic flow patterns and collection efficiency in narrow wire-cylinder type electrostatic precipitator
PublicationRecently, narrow electrostatic precipitators (ESPs) have become a subject of interest because of their possible application for the cleaning of the exhaust gases emitted by diesel engines. Diesel engines emit fine particles, which are harmful to human and animal health. There are several methods for decrease particulate emission from a diesel engines, but up to now, these methods are not enough effective or very expensive. Therefore,...
-
Effective yttrium based coating for steel interconnects of solid oxide cells: Corrosion evaluation in steam-hydrogen atmosphere
PublicationThis work describes manufacture, analysis and test of a new well conducting corrosion-protection coating that can be applied on steel types with high chromium content. Electrolytic deposition of yttrium salts is used to form thin (<100 nm) coatings on both flat steel sheets (material: Crofer 22 APU) and its properties are proven on woven wire-meshes (materials from two different sources: SUS316 and SUS316L). The oxide scale on...
-
Risks caused by microbiologically influenced corrosion in diesel fuel storage tanks
PublicationMicrobiologically influenced corrosion (MIC) poses serious problems for the petrochemical and refinery industries. Particularly favourable conditions for MIC arise in storage tanks and transmission pipelines for mixtures of diesel oil with the addition of a biocomponent (in Poland 7%). The best conditions for the development of MIC occur at the fuel-water interface, where microorganisms are provided with a source of food and water,...
-
"Raport z wstępnych badań własności stali trudnościeralnej 460HB",. ang "Report on preliminary tests of the properties of wear-resistant steel 460HB"
PublicationMikrostrukturę badanej stali trudnościeralnej 460HB stanowi drobnoziarnisty martenzyt odpuszczony, który jest właściwy dla stali konstrukcyjnych niskowęglowych, niskostopowych ulepszonych cieplnie. W przypadku blach grubych, do których zalicza się badana stal, struktura może ulec zaburzeniu, jeżeli w hutniczym procesie wytwórczym wystąpiła niejednorodność odkształcenia plastycznego i w konsekwencji tworzenie się pasm segregacyjnych,...