COLD CRACKING OF S460N STEEL WELDED IN WATER ENVIRONMENT
PublikacjaThis paper shows results of weldability testing of fine-grained high -strength low- alloy S460N steel welded in water environment by covered electrodes. The tests were carried out by using the CTS test specimens with fillet welds. Four specimens were welded under water and one specimen in air. Welded joints were subjected to non-destructive visual and penetration tests. The accepted joints were then subjected to macroscopic and...
-
Resistance to cold cracking of steel joints of P460NL1 steel
PublikacjaPrzedstawiono wyniki badań odporności na zimne pękanie złączy spawanych ze stali przeznaczonej do pracy pod ciśnieniem. Badano równoczesny wpływ zawartości wodoru dyfundującego i energii liniowej na naprężenie krytyczne w próbie implant dla złączy spawanych elektrodami otulonymi i drutem proszkowym w osłonie gazów ochronnych. Stwierdzono wpływ energii liniowej jak i zawartości wodoru dyfundującego na odporność na zimne pękanie...
-
Hydrogen delayed cracking of high-strength weldable steels
PublikacjaOceniano podatność na niszczenie wodorowe stali 14HNMBCu o wysokiej wytrzymałości i jej połączeń spawanych przy obciążeniu stałym w wodzie morskiej. Badania przeprowadzono w powietrzu, oraz w środowisku wody morskiej przy potencjale korozyjnym i przy polaryzacji katodowej. Obecność lub brak opóźnionych pęknięć próbek z karbem przyjęto za miarę odporności na niszczenie wodorowe przy stałym obciążeniu.
-
Influence of burnishing on stress corrosion cracking susceptibility of duplex steel
PublikacjaNa próbkach ze stali duplex poddanych procesom nagniatania przeprowadzono badania podatności do naprężeniowego pękania korozyjnego. Przeprowadzono testy odkształcania z małą prędkością w środowisku wrzącego 35% MgCl2 i środowisku obojętnym- glicerynie. Stwierdzono zwiększoną odporność korozyjną stali po procesach nagniatania z niewielkim stopniem zgniotu. Stwierdzono, że zgniot powierzchniowy ma wpływ na przebieg procesu korozyjnego...
-
Surface cracking of laser melted Ti-6Al-4V alloy
PublikacjaOpisano charakterystyczne cechy pękania powierzchniowego obserwowanego po nadtapianiu laserem CO2 i Nd:YAG stopu Ti-6Al-4V. Obserwowano pęknięcia niezależnie od sposobu nadtapiania, penetrujące głęboko strefę przetopioną i w niewielkim stopniu zależne od sposobu nadtapiania. Przypisano obserwowane zjawisko przemianie martenzytycznej i (lub) naprężeniom cieplnym powstającym podczas gwałtownego chłodzenia.
-
Investigation of transverse cracking of asphalt pavements in the north-eastern Poland
PublikacjaSpękania poprzeczne są jednym z najczęstszych typów uszkodzeń występujących na polskich drogach. Artykuł przedstawia wyniki badań spękań poprzecznych dróg zlokalizowanych w Polsce północno-wschodniej. Na podstawie badań terenowych podjęto próbę wyznaczenia związków pomiędzy częstotliwością spękań, zdefiniowaną indeksem spękań, a wybranymi cechami nawierzchni. Analizowane były następujące cechy nawierzchni: typ podbudowy (podbudowa...
-
Pitting corrosion and stress-corrosion cracking of buffer tanks in a brewery
PublikacjaW pracy przedstawiono wyniki ekspertyzy zbiornika magazynowego na ciepłą wodę do produkcji piwa w browarze. Zbiornik uległ przyśpieszonym procesom korozyjnym, które doprowadziły do jego perforacji. Podczas eksploatacji zbiornika wystąpił proces korozji wżerowej oraz pękania korozyjnego. Przyśpieszone procesy korozyjne zbiornika związane były z wysoką zawartością jonów chlorkowych w wodzie oraz statycznymi naprężeniami mechanicznymi....
-
Applications of electrochemical noise technique in stress corrosion cracking diagnosis
PublikacjaW pracy przedstawione zostały rezultaty analizy prądowego szumu elektrochemicznego, generowanego podczas korozji naprężeniowej próbek stali stopowej. W przeciwieństwie do tradycyjnych metod analizy nie zakładano stacjonarności analizowanych sygnałów. Zamiast tego analizie poddana została zmodyfikowana widmowa odpowiedź szumowa o charakterze zależnym od czasu. Rezultaty badań skonfrontowano z wynikami otrzymanymi za pomocą techniki...
-
Hydrogen delayed cracking of high-strength 14hnmbcu steel in seawater
PublikacjaOceniano podatność na niszczenie wodorowe stali o wysokiej wytrzymałości i jej połączeń spawanych przy stałym obciążeniu w wodzie morskiej. Badania przeprowadzono na próbkach okrągłych z karbem w środowisku wody morskiej przy potencjale korozyjnym oraz przy polaryzacji katodowej. Badano stal gatunku 14HNMBCu o minimalnej granicy plastyczności 690 MPa oraz jej połączenia spawane automatycznie łukiem krytym i ręcznie łukowo elektrodą...
-
Evaluation of susceptibility of high-strength steels to hydrogen delayed cracking
PublikacjaPrzedstawiono wyniki badań podatności na opóźnine pękanie wodorowe stali o wysokiej wytrzymałości w oparciu o próbę stałego obciążenia. Badano stal do pracy w podwyższonych temperaturach 26H2MF oraz stal do ulepszania cieplnego 34HNM w środowisku przepracowanego oleju silnikowego. Badano również stal 14HNMBCu i jej złącza spawane w środowisku wody morskiej przy polaryzacji katodowej.
-
Evaluation of thermal cracking probability for asphalt concretes with high percentage of RAP
PublikacjaThe paper presents determination of the probability of thermal cracking of asphalt mixtures with different reclaimed asphalt pavement (RAP) content on the basis of laboratory tests and analytical evaluation using thermal stress development method. Probability was evaluated taking into consideration: the type and gradation of the mixture and the quality and content of RAP. Thermal stresses were determined using two models: elastic and...
-
Investigations of the passive layer cracking by means of dynamic electrochemical impedance spectroscopy.
PublikacjaDynamiczna elektrochemiczna spektroskopia impedancyjna została wykorzystana do badania pękania warstwy pasywnej na austenitycznej stali wysokostopowej.Zbadano efekt narzuconego potencjału oraz naprężeń rozciągających na pękanie korozyjne stali wysokostopowej 304L w środowisku 0.5M NaCl w temperaturze pokojowej. Praca przedstawia chwilowe widma impedancyjne uzyskane dla badanego układu przy różnych wartościach potencjałów. Uzyskane...
-
Environmental stress cracking in e-glass and aramid/glass epoxy composites
PublikacjaKompozyty epoksydowe wzmocnione włóknami szklanymi są dość odporne na wpływy środowiskowe w stanie nieobciążonym, jednak po przyłożeniu obciążeń łatwo pękają w środowisku wody i rozcieńczonych kwasów. Charakterystyki propagacji pęknięć środowiskowych w laminatach szklano/epoksydowych były przedmiotem szeregu prac, jednak brak jest danych na temat zachowania laminatów o wzmocnieniu hybrydowym aramidowo-szklanym stosowanych w budowie...
-
Investigations of the passive layer cracking by means of Dynamic Electrochemical Impedance Spectroscopy
Publikacja -
Detection of stress corrosion cracking dynamics by dynamic electrochemical impedance spectroscopy
Publikacja -
Effect of welding conditions on susceptibility to cold cracking of underwater welded joints
PublikacjaPrzedstawiono wybrane aspekty spawalności stali przy spawaniu pod wodą metodą lokalnej komory suchej. Zwrócono szczególną uwagę na skłonność do tworzenia peknięć zimnych w SWC. Przy pomocy planowania doświadczeń określono ilościowy wpływ parametrów spawania na naprężenia krytyczne z próby implant.
-
Stress corossion cracking susceptibility of dissimilar stainless steels welded joints
PublikacjaW artykule przedstawiono wyniki badań odporności na naprężeniowe pękanie korozyjne złączy różnoimiennych stali odpornych na korozję; austenitycznej 316L oraz typu duplex 2205. Badania próbek przeprowadzono techniką odkształcania z małą prędkością w agresywnym środowisku roztworu chlorku magnezowego. Wyniki badań korozyjnych uzupełniono analizą metalograficzną z obszarów przełomów.
-
Hydrogen-enhanced stress corrosion cracking in low alloy steels in seawater
PublikacjaBadano podatność stali niskostopowych w wodzie morskiej w warunkach polaryzacji katodowej. Stwierdzono spadek czasu do zniszczenia, energii zniszczenia i przewężenia ze wzrostem potencjału katodowego. Wykazano znaczącą korelację między stopniem degradacji wodorowej a stężeniem wodoru dyfuzyjnego.
-
The application of dynamic electrochemical impedance spectroscopy for stress corrosion cracking studies
PublikacjaElektrochemiczna Spektroskopia Impedancyjna (ESI) od wielu lat stanowi jedno z najważniejszych narzędzi wykorzystywanych do badania różnych procesów elektrochemicznych. Możliwość przeprowadzania badań w łącznej dziedzinie czasowo-częstotliwościowej ułatwia analizę pomiarów impedancyjnych w czasie. ESI pozwala również na analizę mechanizmu procesów elektrochemicznych w dziedzinie czasu z uwzględnieniem bardzo szybkich zjawisk, takich...
-
Detection of stress corrosion cracking dynamics by dynamic electrochemical impedance spectroscopy.
PublikacjaKlasyczne badania korozji naprężeniowej nie dają precyzyjnych informacji o dynamice takiego procesu korozyjnego. Nowa technika dynamicznej elektrochemicznej spektroskopii impedanyjnej, która została opracowana w Katedrze Elektrochemii, Korozji i Inżynierii Materiałowej stwarza takie możliwości. Fakt ten związany z zastosowaną metodologią analizy umożliwiającą selektywną analizą czasowo-częstotliwościową danych pomiarowych.Praca...
-
Hydrogen assisted cracking of high-strength weldable steel in sea-water.
PublikacjaOceniono niszczenie wodorowe stali o wysokiej wytrzymałości i jej złączy spawanych przy różnych rodzajach obciążenia w wodzie morskiej. Przeprowadzono próby rozciągania z małą prędkością odkształcenia i zmęczenia niskocyklowego w wodzie morskiej przy polaryzacji katodowej. Badano stal gatunku 17HMBVA o minimalnej granicy plasyczności 690 MPa oraz jej złącza spawane automatycznie łukiem krytym i ręcznie łukowo elektrodą otuloną.
-
Hydrogen assisted cracking of high-strength weldable steels in sea-water.
PublikacjaOceniono niszczenie wodorowe stalio wysokiej wytrzymałości i ich złączy spawanych przy różnych rodzajach obciążenia w wodzie morskiej. Prowadzono próby rozcią gania z małą prędkością odkształcenia i zmęczenia niskocyklowego w wodzie morskiej przy polaryzacji katodowej. Badano dwa gatunki stali o minimalnej granicy plastyczności 690 MPa, oraz jej złącza spawane automatycznie łukiem krytym i ręcznie łukowo elektrodą otuloną. Dla...
-
Mechanism of hydrogen enhanced-cracking of high-strength steel welded joints
PublikacjaPrzedstawiono badania podatności stali spawalnej o wysokiej wytrzymałości S690Q i jej złączy spawanych na niszczenie wodorowe w środowisku wody morskiej przy polaryzacji katodowej. Na podstawie wyników próby rozciągania z małą prędkością odkształcania i obserwacji przełomów próbek na SEM wskazano mechanizm pękania wspomaganego wodorem badanej stali i złączy spawanych.
-
Field Evaluation of High Modulus Asphalt Concrete Resistance to Low-Temperature Cracking
PublikacjaHigh-modulus asphalt concrete has numerous advantages in comparison to conventional asphalt concrete, including increased resistance to permanent deformations and increased pavement fatigue life. However, previous studies have shown that the construction of road pavements with High Modulus Asphalt Concrete (HMAC) may significantly increase the risk of low-temperature cracking. Those observations were the motivation for the research...
-
Cold Cracking Of Underwater Wet Welded S355G10+N High Strength Steel
PublikacjaWater as the welding environment determines some essential problems influencing steel weldability. Underwater welding of high strength steel joints causes increase susceptibility to cold cracking, which is an effect of much faster heat transfer from the weld area and presence of diffusible hydrogen causing increased metal fragility. The paper evaluates the susceptibility to cold cracking of the high strength S355G10+N steel used,...
-
Influence of bitumen type on cracking resistance of asphalt mixtures used in pavement overlays
PublikacjaCracking is one of the predominant distresses occurring in flexible pavements, especially in old pavements that were rehabilitated with an asphalt overlay. In such cases asphalt mixtures should be designed to ensure high resistance to reflective cracking because new asphalt layers are exposed to existing cracks of the old pavement. The nature of these cracks can be various (transverse, longitudinal as well as crazy cracking). One...
-
Hydrogen assisted cracking of 2205 duplex stainless steel in synthetic sea water
PublikacjaThe cracking behavior of 2205 duplex stainless steels (DSSs) in synthetic sea water under cathodic polarization condition was investigated. (SSRT) method was employed in aim to evaluate the susceptibility to hydrogen assisted cracking. The results showed that the reduction in the uniform elongation (UEL) and the reduction of area (RA) varied with the applied cathodic current density. Significant reductions in ductility were found,...
-
Influence of Selected Warm Mix Asphalt Additives on Cracking Susceptibility of Asphalt Mixtures
PublikacjaWarm mix asphalt (WMA) has been widely accepted as a future asphalt paving technology. Besides clear advantages, there are still some concerns regarding durability and long-term performance of pavements made with this type of asphalt mixtures. One of the most important issues is low temperature behaviour of WMA because certain additives used for temperature reduction can aect bitumen properties. This paper presents the evaluation...
-
Non-uniqueness of fracture parameter choice in simulations of concrete cracking at mesoscale level
PublikacjaIn the paper a non-uniqueness of fracture parameter choice in simulations of cracking process in plain concrete specimens at mesoscale level under monotonic static loading is analysed. The Finite Element Method is used, where cracks are defined in a discrete way using interface cohesive elements with nonlinear material law including softening. The concrete mesostructure (such as: cement matrix, air voids, aggregates, and Interfacial...
-
The Impact of Homogeneity of High Modulus Asphalt Concrete Layer on Low-Temperature Cracking
PublikacjaDuring winter season of 2012 numerous transverse cracks developed in high-modulus asphalt concrete (HMAC) base of newly constructed motorway. Pavement cracked both in transverse joint locations and in the area between them. Research which was conducted during investigation of the causes and mechanisms of cracking consisted of: field examination, laboratory testing of specimens cored out of the existing pavement, computational analyses...
-
Cracking of the Vault in a Church Building and Activities Undertaken in the View of the Further Mining Exploitation
Publikacja -
Effect of Cobalt Addition on the Activity of Nanocrystalline Iron Catalysts in the Cracking of Methane Reaction
Publikacja -
THE EFFECT OF WET UNDERWATER WELDING ON COLD CRACKING SUSCEPTIBILITY OF DUPLEX STAINLESS STEEL
PublikacjaABSTRACT The present work was conducted to assess the weldability of duplex stainless steel in underwater conditions. Metal manual arc welding (MMA) with the use of coated electrodes was used in the investigations. Tekken weldability tests were performed underwater at 0.5 m depth and in the air. Nondestructive tests, metallographic examinations of welds, ferrite content assessment in microstructure and hardness test were performed....
-
Long-term researches of stress corrosion cracking of Al-Zn-Mg alloys
PublikacjaPraca przedstawia wyniki odporności na korozję naprężeniową stopów Al-Zn-Mg uzyskane w warunkach stacjonarnych. Dodatkowo określono wpływ składu chemicznego oraz obróbki cieplnej na odporność korozyjną tych stopów. Badania prowadzono w 3% NaCl w warunkach stałego obciążenia σ = 0.8R0.2 przez 1500 godzin. Stwierdzono, iż zawartość Zn i Mg oraz szybkość chłodzenia to główne czynniki wpływające na podatność tych stopów na korozje...
-
Application of galvanodynamic impedance spectroscopy for studying passive film cracking under mechanical strain
PublikacjaThe paper reports the results of simultaneous mechanical and electrochemical investigations on austenitic (18/8) stainless steel in a 2 % solution of sulphuric acid. The measurements were performed using Galvanodynamic Electrochemical Impedance Spectroscopy (GDEIS). Electrochemical analysis of mechanical passive layer cracking and repassivation conditions during a tensile test was carried out. Application of this methodology allowed...
-
The influence of reinforcement on load carrying capacity and cracking of the reinforced concrete deep beam joint
PublikacjaThe paper presents the results of experimental research of the spatial reinforced concrete deep beam systems orthogonally reinforced and with additional inclined bars. Joint of the deep beams in this research was composed of the longitudinal deep beam with a cantilever suspended at the transversal deep beam. The cantilever deep beam was loaded throughout the depth and the transversal deep beam was loaded at the mid-span by longitudinal...
-
Stress corrosion cracking of the 26H2MF and 34HNM constructional allaysteels of different heat treatment in hydrocarbons
PublikacjaBadane są dwie stale stopowe 26HZMF i 34HNM o różnych właściwościach mechanicznych w różnych środowiskach.
-
Hydrogen-enhanced stress corrosion cracking and corrosion fatigue of HSLA steels in sea-water
PublikacjaPrzedstawiono ocenę podatności stali o wysokiej wytrzymałości na naprężeniowe pękanie korozyjne i zmęczenie korozyjne wspomagane przez wodór. Wykonano próby powolnego rozciągania i zmęczenia niskoczęstotliwościowego na stalach 17HMBVA i 14HNMBCu oraz ich złączach spawanych, w środowisku wody morskiej, przy polaryzacji katodowej. Zamieszczono wyniki badań elektrochemicznych oraz przełomów na skaningowym mikroskopie elektronowym.
-
Novel method of initiation stage of stress corrosion cracking monitoring with respect to marine constructions
PublikacjaKorozja konstrukcji morskich i jednostek pływających stanowi bardzo ważny problem w odniesieniu do aspektów bezpieczeństwa, gdyż w całym okresie eksploatacji narażone są na działanie bardzo agresywnego środowiska i innych czynników eksploatacyjnych. W rezultacie prowadzi to do niespodziewanych kolizji i wypadków. Praca przedstawia zastosowanie dynamicznej elektrochemicznej spektroskopii impedanycjnej (DEIS) do badania inicjacji...
-
Passive layer cracking studies performed on A95056 Aluminum Alloy by DEIS and acoustic emission
PublikacjaZbadano proces pękania warstwy pasywnej na stopie aluminium A95056 w warunkach zmiennych naprężeń rozciągających i polaryzacji anodowej z wykorzystaniem techniki DEIS oraz emisji akustycznej (AE), jako metody porównawczej. Określono elektrochemiczne i mechaniczne przyczyny badanego procesu. Wyznaczono progową (krytyczną) wartość naprężeń, przy których zarejestrowano proces pękania warstwy pasywnej na badanym stopie aluminium. Badanemu...
-
Sulfate‐reducing bacteria‐assisted hydrogen‐induced stress cracking of 2205 duplex stainless steels
PublikacjaThe paper presents the results of a laboratory investigation of the microbiologically assisted hydrogen‐induced stress cracking (HISC) of 2,205 duplex stainless steel (DSS). The testing of susceptibility toward HISC was performed with two different methods. Precharged in sulfate‐reducing bacteria (SRB), inoculated medium samples were subjected to slow strain‐rate testing in artificial seawater. In situ constant load tests were...
-
Dynamic electrochemical impedance spectroscopy measurements of passive layer cracking under static tensile stresses
Publikacja -
Dynamic elektrochemical impedance spectroscopy measurements of passive layer cracking under static tensile stresses.
PublikacjaDynamiczna elektrochemiczna spektroskopia impedancyjna umożliwia badanie podatności i odporności korozyjnej różnych materiałów konstrukcyjnych, a w szczególności określenie właściwości elektrochemicznych warstw pasywnych występujących na ich powierzchni. W wielu przypadkach pęknięcie warstwy pasywnej pod wpływem działania naprężeń rozciągających prowadzi do korozji naprężeniowej. Z tego względu badania pękania warstw pasywnych...
-
Dynamic electrochemical impedance spectroscopy measurements of passive layer cracking under static tensile stresses.
PublikacjaDynamiczna Elektrochemiczna Spektroskopia Impedancyjna umożliwia badanie podatności i odporności korozyjnej różnych materiałów konstrukcyjnych, a w szczególności określenie właściwości elektrochemicznych warstw pasywnych występujących na ich powierzchni. W wielu przypadkach pęknięcie warstwy pasywnej pod wpływem działania naprężeń rozciągających prowadzi do korozji naprężeniowej. Z tego względu badania pękania warstw pasywnych...
-
New possibilities of the passive layer cracking dynamics detection using a new Dynamic Electrochemical Impedance Spectroscopy.
PublikacjaNowa metoda Dynamicznej Elektrochemicznej Spektroskopii Impedancyjnej opracowana w Katedrze Elektrochemii, Korozji i Inżynierii Materiałowej Politechniki Gdańskiej daje możliwości określania charakterystyki impedancyjnej w dziedzinie czasu podczas procesu pękania ochronnej warstwy pasywnej. Fakt ten jest związany z procedurą analizującą wspomnianej techniki, która umożliwia selektywną analizę czasowo-częstotliwościową uzyskanych...
-
Investigation of low-temperature cracking in newly constructed high-modulus asphalt concrete base course of a motorway pavement
PublikacjaThe paper presents the issue of low-temperature transverse cracks which have developed in newly constructed base courses made of high-modulus asphalt concrete mix (HMAC). Numerous transverse cracks developed in the analysed HMAC base during the winter season before the pavement was actually completed, both at the transverse joint locations and in the areas between them. This had not happened so far on such a scale during road construction...
-
Factors affecting low-temperature cracking of asphalt pavements: analysis of field observations using the ordered logistic model
PublikacjaAccurate identification of factors that primarily affect the number of low-temperature cracks is crucial for selection of road materials and planning of pavement maintenance. Field investigations of lowtemperature cracks were performed in the years 2014 and 2020 on the same 68 road sections being in service in typical traffic conditions. The collected data were statistically analysed using the ordered logistic regression model....
-
Field investigation of low-temperature cracking and stiffness moduli on selected roads with conventional and high modulus asphalt concrete
PublikacjaHigh Modulus Asphalt Concrete (HMAC) was introduced in Poland as a one of the solutions to the problem of rutting, type of deterioration common in the 1990s. After first encouraging trials in 2002 HMAC was widely used for heavily loaded national roads and motorways. However some concerns were raised about low-temperature cracking of HMAC. This was the main reason of the studies presented in this article were started. The article...
-
Comparative electrochemical analysis of the passive layer cracking process on aluminum alloys performed by means of DC and AC techniques
PublikacjaZbadano proces pękania warstwy pasywnej na stopach aluminium AA1050, AA5052, AA5056, oraz AA7005 w warunkach zmiennych naprężeń rozciągających i polaryzacji anodowej z wykorzystaniem techniki stałoprądowej, DEIS oraz emisji akustycznej (AE), jako metody porównawczej. Przeprowadzone badania pokazały przewagę techniki DEIS oraz emisji akustycznej nad klasyczną techniką stałoprądową. Wyznaczono dokładny moment pęknięcia warstwy pasywnej...
-
Influence of retrogression and reaging on microstructure, mechanical properties and susceptibility to stress corrosion cracking of an Al-Zn-Mg alloy.
PublikacjaPrzedmiotem badań był stop AlZn5Mg1 poddany nawrotowi i starzeniu w różnej temperaturze i przez różny czas. Badano podatność na korozję naprężeniową przy stałej prędkości rozciągania 10-6 s-1. Obróbka cieplna, która polepsała własności, pogarszała odporność na korozję naprężeniową. Efekty te przypisano zmianiom wielkości i rozkładu wydzieleń.