Tensile curve of E grade steel for shipbuilding
Open Research DataIn the shipbuilding industry, the risk of brittle fractures developing in constructions is limited by employing certified materials of specific impact strength, determined using the Charpy method (for a given design temperature) and by exercising control over the welding processes (technology qualification, supervision of production, tests of non-destructive...
-
Distinctive properties of Scots pine (Pinus sylvestris L.) originating from the Carpathian and Great Poland-Pomeranian of Nature and Forest Land
PublicationIn this paper values of properties of Scots pine, the fracture toughness and of shear yield stress in the shear zone are presented. Samples of Scotch pine (Pinus sylvestris L.) wood of two provenances from Poland were tested. These properties were determined from the values of cutting power obtained experimentally on the saw frame PRW-15M. The values of fracture toughness and shear yield stress based on the Atkins model for cutting...
-
Degradation of ferritic X10CrAlSi18 stainless steel caused by slurry
PublicationThe slurry erosion tests of ferritic X10CrAlSi18 steel were carried out using a slurry pot device. In order to investigate the erosion process, two series of tests were performed: first one with a constant impact velocity of 5 m/s, 7 m/s and 9 m/s and the second one, during which the impact velocity was changed after every exposure. During each test, an influence of test conditions on volume loss, surface hardness and roughness...
-
EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 60mm), a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 40mm), a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture SEM investigation (plate thicnkness 30mm), a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture SEM investigation (plate thicnkness 30mm), a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 30mm), a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 30mm), a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 40mm), a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 50mm), a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding - fracture documentation for CTOD test (plate thicnkness 50mm), a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
SAWING PROCESS AS A NEW ALTERNATIVE WAY OF DETERMINING SOME WOOD PROPERTIES
PublicationCutting forces (power) could be considered from a point of view of modern fracture mechanics. The developed cutting model, derived from fracture mechanics, includes work of separation (fracture toughness) in addition to plasticity and friction, and also dullness of the cutting edge described by the cutting edge radius. Moreover, forecasting of the shear plane angle for the cutting models, broaden possibilities of energetic effects...
-
Wulkanizaty kauczuku naturalnego otrzymane z użyciem plastyfikatorów pochodzenia roślinnego
PublicationCelem niniejszej pracy było zbadanie wpływu epoksydowanych olejów roślinnych na wybrane właściwości wul-kanizatów kauczuku naturalnego. Jako plastyfikatorów użyto epoksydowanego oleju sojowego oraz epoksydo-wanego oleju palmowego. Wpływ olejów naturalnych porównano także z wulkanizatami przygotowanymi bez użycia zmiękczaczy, jak i zawierającymi olej maszynowy, pochodzący z przerobu ropy naftowej. Zbadano wpływ rodzaju...
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - 3D fracture scan
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 40 mm) - CMOD - force record, a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 60 mm) - CMOD - force record, a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 50 mm) - CMOD - force record, a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 50mm) - CMOD - force record, a0/W = 0.6
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
EH36 steel for shipbuilding (plate thicnkness 30 mm) - CMOD - force record, a0/W = 0.5
Open Research DataThe basic method of ductility designation of structural steels is the Charpy impact test. The test consists of a single strike of the specimen using a Charpy pendulum. Its result is the value of work necessary to break a specimen at a test temperature. Despite its many advantages, such as its short implementation time and low costs, it has its disadvantages,...
-
Toughness augmentation by fibrillation and yielding in nanostructured blends with recycled polyurethane as a modifier
PublicationIn the present paper, we have carefully investigated the morphology and fracture mechanism of the recycled polyurethane (RPU) /epoxy blend system. The second phase (RPU) added to the epoxy resin has a positive effect on the overall mechanical properties. Interestingly, the recycled polymer has a remarkable effect on the fracture toughness of epoxy resin. The mechanism behind the fracture toughness improvement up on the addition...
-
Marcin Wekwejt dr inż.
PeopleMarcin Wekwejt holds a bachelor’s degree in Biomedical Engineering (2016; J. and J. Śniadecki Bydgoszcz University of Technology & L. Rydygier Collegium Medicum), a master’s degree in Mechanical-Medical Engineering (2018; Gdańsk University of Technology & Gdańsk Medical University), and a PhD in Materials Engineering (2021; Gdańsk University of Technology). He was awarded the title of Doctor of Engineering and Technical...
-
Influence of Heat Treatment Temperature on Fatigue Toughness in Medium-Carbon High-Strength Steels
PublicationCurrent research has demonstrated that the tempering temperature affects the martensitic transformation of medium-carbon high-strength steels. This temperature plays an important role in the final microstructure, percentage ratios of martensite to ferrite phases and, consequently, in the mechanical properties and the fatigue response. So far, the relationship between the martensitic tempering temperature and the cyclic deformation...
-
Identification of intermetallic phases in the structure of austenitic steel with use of Scanning Kelvin Probe Microscopy
Open Research DataDelta ferrite is formed in austenitic steels during the solidification of the alloy and its welds. It can also occur as a stable phase in any temperature range in high-alloy austenitic-ferritic steels. Depending on the amount, it can change into gamma and sigma phases and into ferrite with variable chromium content. The main role of delta ferrite in...
-
The effect of wax foundation addition to PCL filaments on mechanical properties.
Open Research DataThe dataset includes the effect of wax foundation addition on the basic mechanical properties of the filaments. PCL and wax foundation addition at 10 and 15% were used for extrusion. The mechanical properties of the resulting filaments were evaluated by a double compression test using an Instron model 5543 universal testing machine. Parameters such...
-
Cavitation Erosion Resistance Influence of Material Properties
PublicationThe cavitation erosion is the phenomena that causes degradation of fluid flow machinery components due to repetitive implosion of cavitation bubbles adjacent to the solid surface. Cavitation erosion is a complex phenomenon, which includes not only hydrodynamic factors of liquid, but also properties of erodible material e.g. microstructure, hardness or Young modulus. In order to reduce the negative impact of erosion on machine components,...
-
The influence of solution annealing temperature on the properties of Lean Duplex 2101 welded joints in tubes
PublicationThe article presents a technology of TIG longitudinal welding without filler material (142) of heat exchanger tubes made of Lean Duplex 2101. The results of studies on the effect of heat treatment (solution annealing) on tensile strength, plasticity, delta ferrite and the structure of smooth tubes are shown. It was found, that the change in solution annealing temperature across the tested range has an impact on mechanical properties...
-
Influence of bio-polyols with different molecular weight on properites of PUR-PIR foams
Open Research DataThis work attempts to validate the possibility of replacing petrochemical polyols with previously synthesized bio-polyols and their impact on the structure and properties of rigid polyurethane-polyisocyanurate (PUR-PIR). The influence of bio-polyols addition on foam properties was investigated by mechanical testing, Fourier transform infrared spectroscopy...
-
Effect of the Drying Method of Pine and Beech Wood on Fracture Toughness and Shear Yield Stress
PublicationThe modern wood converting processes consists of several stages and material drying belongs to the most influencing future performances of products. The procedure of drying wood is usually realized between subsequent sawing operations, affecting significantly cutting conditions and general properties of material. An alternative methodology for determination of mechanical properties (fracture toughness and shear yield stress) based...
-
Comparative Study of the Reinforcement Type Effect on the Thermomechanical Properties and Burning of Epoxy-Based Composites
PublicationAramid (AF), glass (GF), carbon (CF), basalt (BF), and flax (FF) fibers in the form of fabrics were used to produce the composites by hand-lay up method. The use of fabrics of similar grammage for composites’ manufacturing allowed for a comprehensive comparison of the properties of the final products. The most important task was to prepare a complex setup of mechanical and thermomechanical properties, supplemented by fire behavior...
-
Bio-Based Polyurethane Composites and Hybrid Composites Containing a New Type of Bio-Polyol and Addition of Natural and Synthetic Fibers
PublicationThis article describes how new bio-based polyol during the liquefaction process can be obtained. Selected polyol was tested in the production of polyurethane resins. Moreover, this research describes the process of manufacturing polyurethane materials and the impact of two different types of fibers—synthetic and natural (glass and sisal fibers)—on the properties of composites. The best properties were achieved at a reaction temperature...
-
SHEAR YIELD STRESSES AND FRACTURE TOUGHNESS OF SCOTS PINE (PINUS SYLVESTRIS L.) ACCORDING TO THE RAW MATERIAL PROVENANCE
PublicationIn this paper values of the fracture toughness and of shear yield stress in the shear zone of Scots pine are presented. Tests of cutting were carried on samples of Scotch pine (Pinus sylvestris L.) wood of five provenances from Poland. These experimentally cutting tests were carried on the sash gang saw PRW-15M and the values of cutting power were obtained. The values of fracture toughness and shear yield stress based on Atkins’s...
-
Dawid Ryś dr hab. inż.
PeopleCourses PRINCE2® Foundation Certificate in Project Management Tire-Pavement Interaction course Micromechanical Analysis of Asphalt Concrete
-
Influence of water soaking on the ultimate tensile strength of polyester-based coated woven fabrics
PublicationThis research aims to determine the influence of water-soaking on polyester-based coated woven fabrics for ultimate tensile strength and elongation at break under uniaxial tensile tests. The paper begins with a short survey of literature concerning the investigation of the determination of coated woven fabric properties. The authors carried out the uniaxial tensile tests with an application of a flat grip to establish the values...
-
Bead-on-plate welding on S235JR steel by underwater local dry chamber process
PublicationThe article presents the results of the effect of parameters of underwater local dry chamber welding on the properties of padding welds. The effect of heat input and the type of shielding gas on the structure and hardness of welds was established. the functions for estimating the maximum hardness of the heat affected zone have been also elaborated.
-
Valorization of bio-based polyols synthesized via biomass liquefaction
Open Research DataAs the properties of polyols have a huge impact on the properties of manufactured polyurethanes, this study aims to determine the influence of polyethylene glycols with different molecular masses on the course of the biomass liquefaction process and bio-polyol properties. The obtained polyols were characterized by rheological studies. To confirm the...
-
Determination of Failure Causes of a Steam Turbine Casing
PublicationThe paper presents results of research and failure analysis undertaken to determine failure causes of a steam turbine casing. After 130,000 hours of service the crack in a outer shell of the turbine casing was found. The inner shell of the casing was made of cast steel grade G21CrMoV5-7, and the outer shell of grade G20CrMo4-5. Following research were performed in order to determine causes of the casing failure: chemical analysis;...
-
Images of topography and mechanical properties (phase imaging) of cast iron samples from water installations
Open Research DataMeasurements in contact and semi-contact mode. NTEGRA Prima (NT-MDT) device. CSG 10.
-
The Impact of Homogeneity of High Modulus Asphalt Concrete Layer on Low-Temperature Cracking
PublicationDuring winter season of 2012 numerous transverse cracks developed in high-modulus asphalt concrete (HMAC) base of newly constructed motorway. Pavement cracked both in transverse joint locations and in the area between them. Research which was conducted during investigation of the causes and mechanisms of cracking consisted of: field examination, laboratory testing of specimens cored out of the existing pavement, computational analyses...
-
The Influence of the Aircraft Operating Fluids on the Mechanical Parameters of the Airport Surface Concrete
PublicationThe authors of the article assessed the impact of operating fluids used to service aircraft on changing mechanical parameters of cement concrete intended for airport pavement. The research concerned concrete designed with the use of CEM I 42.5N LH NA low-alkali cement, broken granite aggregate, fine washed aggregate, and admixtures. The analysis included the assessment of changes in dierences in endurance parameters over various...
-
Processing and structure–property relationships of natural rubber/wheat bran biocomposites
PublicationIn this work, wheat bran was used as cellulosic filler in biocomposites based on natural rubber. The impact of wheat bran content [ranging from 10 to 50 parts per hundred rubber (phr)] on processing, structure, dynamic mechanical properties, thermal properties, physico-mechanical properties and morphology of resulting biocomposites was investigated. For better characterization of interfacial interactions between natural rubber...
-
Mechanical testing of technical woven fabrics
PublicationThis article presents a review of technical fabrics testing methods used by the authors on the basis of their experience with research on properties of polytetrefluoroethylene-coated fabrics used for Forest Opera in Sopot (Poland). First, the different types of testing methods used for description of mechanical properties (uniaxial tensile tests, biaxial tensile tests and shear tests) of technical woven fabrics are described. The...
-
PROCESSING, MECHANICAL AND THERMAL PROPERTIES OF RECYCLED LOW-DENSITY POLYETHYLENE STREAMS
PublicationThe recycling of plastics is currently one of the most significant industrial challenges. Due to the enormous amounts of plastic wastes generated by various industry branches, it is essential to look for the potential methods of their utilization. Nevertheless, for the efficient application of recycled materials it is crucial to analyze their performance. Therefore, in presented paper we investigated the processing (melt flow index),...
-
Effects of Micro-Arc Oxidation Process Parameters on Characteristics of Calcium-Phosphate Containing Oxide Layers on the Selective Laser Melted Ti13Zr13Nb Alloy
PublicationTitania-based films on selective laser melted Ti13Zr13Nb have been formed by micro-arc oxidation (MAO) at different process parameters (voltage, current, processing time) in order to evaluate the impact of MAO process parameters in calcium and phosphate (Ca + P) containing electrolyte on surface characteristic, early-stage bioactivity, nanomechanical properties, and adhesion between the oxide coatings and substrate. The surface...
-
Influence of cooling rate and additives on low-temperature properties of asphalt mixtures in the TSRST
PublicationThe paper presents the results and analysis of low-temperature properties of asphalt mixtures according to Thermal Stress Restrained Specimen Test (TSRST) and Indirect Tensile Test methods. Different groups of bitumen were investigated: neat, SBS-modified and highly SBS-modified. Influence of cooling rates (1 C/h, 3 C/h, 5 C/h and 10 C/h) and additives (aramid fibres and crumb rubber) was identified as well. Moreover, for each...
-
Structure and performance properties of environmentally-friendly biocomposites based on poly(ɛ-caprolactone) modified with copper slag and shale drill cuttings wastes
PublicationThe potential application of two types of industrial wastes, drill cuttings (DC) and copper slag (CS), as silica-rich modifiers of poly(ɛ-caprolactone) (PCL) was investigated. Chemical structure and physical properties of DC and CS fillers were characterized using X-ray diffractometer, X-ray fluorescence spectroscopy, particle size and density measurements. PCL/DC and PCL/CS composites with a variable content of filler (5 to 50...
-
Characterization of volatile compounds, structural, thermal and physico-mechanical properties of cross-linked polyethylene foams degraded thermo-mechanically at variable times
PublicationWaste cross-linked polyethylene foam (wXLPE) was thermo-mechanically degraded at variable time using internal batch mixer. The progress of wXLPE degradation has been investigated by using a simultaneous thermogravimetric/differential scanning calorimetry analyzer coupled with Fourier transform infrared spectroscopy, swelling measurements, tensile tests and scanning electron microscopy. Volatile organic compounds generated during...
-
Mechanical properties for preliminary design of structures made from PVC coated fabric
PublicationIn this paper, laboratory tests necessary for the identification of non-linear elastic immediate properties of the PVC coated polyester fabric (like AF 9032) are described. The material parameters are specified on the basis of the uniaxial tensile tests in the warp and weft directions as well as on the base of the biaxial tensile tests. For the identification process techniques based on the least squares method are used. The authors...