Stabilization of the pyrochlore phase of Mn2Sb2O7 by double substitution
PublicationPolycrystalline samples of (Ce4+Mn2+3)(Ga3+Sb5+3)O14 were synthesized by a high-temperature solid-state reaction. In contrast with the parent Mn2Sb2O7 compound that adopts a rhombohedral or monoclinic structure at T > 600 °C, the pyrochlore structure of CeMn3GaSb3O14 is retained up to at least T = 1070°C. High-resolution synchrotron x-ray diffraction measurements show no sign of a superstructure or distortion from cubic symmetry...
-
Application of non-metal doped titania for inverted polymer solar cells
PublicationDomieszkowany jodem oraz domieszkowany jodem ditlenek tytanu uzyto jako warstwę buforową w ogniwie ITO/X-TiO2?P3HT-PCMB /MnO2/ Ag.Warswty X-TiO2 nalożono metodą spin-coatingu z zawiesiny nanocząstek w DMSO. Jednorodne struktury scharakteryzowane pod względem morfologii mikroskopowo metodą AFM. Charakterystyka prądowo-napięciowa urzdzeń wskazuje iż domieszkowany jodem TiO2 pozwala osiągnąć lepsze parametry PCE (1,67%) i prąd zwarcia...
-
Warunki krystalizacji cienkich warstw V2O5 i V2O3 wytwarzanych metodą zol-żel
PublicationPraca ta przedstawia wyniki badań struktury cienkich warstw tlenku wanadu otrzymanych metodą zol - żel. Cienkie warstwy osadzano metodą spin - coating na podłożach wykonanych ze szkła kwarcowego oraz krzemowych. Tak przygotowane próbki wygrzewano w zakresie temperatur od 200 °C do 1200 °C. Zakres temperatur dobrano w taki sposób, aby można było zarówno określić optymalną temperaturę krystalizacji nanoprętów V2O5 jak i otrzymać...
-
Synteza i badanie struktury nanoprętów V2O5 wytworzonych metodą zol-żel
PublicationPraca ta przedstawia wyniki badań struktury cienkich warstw tlenku wanadu otrzymanych metodą zol - żel. Cienkie warstwy osadzano metodą spin - coating na podłożach ze szkła kwarcowego oraz krzemowych a następnie wygrzewano w różnych temperaturach w zakresie od 400 °C do 600 °C w celu określenia optymalnej temperatury krystalizacji nanoprętów. Otrzymane próbki przebadano metodą dyfraktometrii rentgenowskiej, skaningowym mikroskopem...
-
The influence of thermal conditions on V2O5 nanostructures prepared by sol-gel method
PublicationThis work presents the result of structure investigations ofV 2O5 nanorods grown from thin films and powders prepared by sol-gel method. To examine the best temperature of nanorods crystallization, thin films deposited by spin-coating method on quartz glass or silicon substrates and bulk xerogel powders were annealed at various temperatures ranging from 100∘C to 600∘C. The structure of the samples was characterized by X-ray diffraction...
-
Strong-coupling superconductivity of SrIr2 and SrRh2 : Phonon engineering of metallic Ir and Rh
PublicationExperimental and theoretical studies on superconductivity in SrIr2 and SrRh2 Laves phases are presented. The measured resistivity, heat capacity, and magnetic susceptibility confirm the superconductivity of these compounds with Tc = 6.07 and 5.41 K, respectively. Electronic structure calculations show that the Fermi surface is mostly contributed by 5d (4d) electrons of Ir (Rh), with Sr atoms playing the role of electron donors....
-
High-Temperature Structural and Electrical Properties of BaLnCo2O6 Positrodes
PublicationThe application of double perovskite cobaltites BaLnCo2O6−δ (Ln = lanthanide element) in electrochemical devices for energy conversion requires control of their properties at operating conditions. This work presents a study of a series of BaLnCo2O6−δ (Ln = La, Pr, Nd) with a focus on the evolution of structural and electrical properties with temperature. Symmetry, oxygen non-stoichiometry, and cobalt valence state have been examined...
-
Evaluation of Three Peptide Immobilization Techniques on a QCM Surface Related to Acetaldehyde Responses in the Gas Phase
PublicationThe quartz-crystal microbalance is a sensitive and universal tool for measuring concentrations of various gases in the air. Biochemical functionalization of the QCM electrode allows a label-free detection of specific molecular interactions with high sensitivity and specificity. In addition, it enables a real-time determination of its kinetic rates and affinity constants. This makes QCM a versatile bioanalytical screening tool for...
-
JMATRIX - a package for relativistic J-matrix calculations in elastic scattering of electrons from model potentials
PublicationWe present a software package JMATRIX, consisting of two computer codes written in FORTRAN 95 and parallelized with OpenMP, implementing the so-called J-matrix method, applied to elastic scattering of electrons on the radial potential, vanishing faster than Coulomb one. In the J-matrix method, physical scattering problem is replaced by using well-defined model, which is solved analytically. Presented software implements both non-relativistic...
-
The LaPdIn 4 indide and elementary properties of the LaTIn 4 ( T = Ni, Pd, Pt) materials family
PublicationThe indium-rich intermetallic compound LaPdIn4 is reported, prepared by arc-melting and annealing at 600 C. Single crystal X-ray diffraction found the material to be orthorhombic, space group Cmcm (No. 63), with lattice parameters a ¼ 4.5462(3) Å, b ¼ 16.9208(10) Å, and c ¼ 7.3100(5) Å. This previously unreported indide is isostructural with LaNiIn4 and LaPtIn4. It is demonstrated that all three compounds in the LaTIn4 (T ¼ Ni,...
-
Study of nanomechanical properties of (1-y)BST-yMgO thin films
PublicationIn the present study thin films of MgO – modified Ba0.6Sr0.4TiO3 (BST60/40) solid solution were prepared by the sol-gel-type chemical solution deposition method on stainless steel substrates. A multilayer spin-coating approach was utilized for the Ba0.6Sr0.4TiO3-MgO thin film deposition with subsequent thermal annealing at T=650-750C. Dried BST60/40-MgO gel powders were studied with thermogravimetric and differential thermal analysis...
-
Influence of pyrolysis atmosphere on the lithium storage properties of carbon-rich polymer derived SiOC ceramic anodes
PublicationPolymer derived carbon-rich SiOC ceramics are prepared from polysiloxane precursors through a pyrolysis process at 1000 °C using pure argon and argon/hydrogen mixture as pyrolysis atmosphere. The precursor is synthesized from a linear (Si–H)-containing polysiloxane cross-linked with divinylbenzene using hydrosilylation reaction in the presence of a platinum catalyst. Pyrolysis in Ar/H2 mixtures, compared to the treatment under...
-
Superconductivity in a new intermetallic structure type based on endohedral Ta@Ir7Ge4 clusters
PublicationWe report the observation of superconductivity at a temperature near 3.5 K for the previously unreported compound TaIr2Ge2. In addition to being a superconductor, this material displays a new crystal structure type that contains endohedral clusters, as determined by single-crystal x-ray diffraction structure refinement; the structure is more complex than those of the commonly observed tetragonal 122 intermetallic phases. Despite...
-
Structure and magnetic properties of BeO-Fe2O3-Al2O3-TeO2 glass-ceramic composites
PublicationIn this work, glass-ceramics in the xBeO–20Fe2O3–(80-x)TeO2 system with x = 0–25 mol% were synthesized by the traditional melt quenching route and studied by inductively coupled plasma optical emission spectroscopy, X-ray diffraction, confocal microscopy, infrared and Raman spectroscopy. BeO addition was found to support the crystallization process of Fe2O3 during melting, and an increased BeO content was associated with an increased...
-
Two kinds of oxygen vacancies in lithium titaniate doped with copper as detected by EPR
PublicationLithium titanate (Li1+xTi2-xO4) doped with Cu2+ ions was synthesized by sol-gel processing method. The structure and morphology are characterized by X-ray Diffraction (XRD), X-ray Photoemission Spectroscopy (XPS), Scanning Electron Microscopy (SEM) and Electron Paramagnetic Resonance (EPR). Spin Hamiltonian parameters describing Zeeman and hyperfine interaction for 63Cu2+ ions were obtained from EPR spectra simulations. The spectra...
-
Fabrication and Crystal Structure of Sol-Gel Deposited BST Thin Films with Compositional Gradient
PublicationIn the present research technology of compositionally graded barium strontium titanate Ba1-xSrxTiO3 thin films deposited on stainless steel substrates by sol-gel spin coating followed with thermal annealing at T = 650°C is reported. Results of thermal behavior of the sol-gel derived powders with compositions used for fabrication of graded structure (i.e. with Sr mole fraction x = 0.5, 0.4 and 0.3) are described. X-ray diffraction...
-
Investigation of thin perovskite layers between cathode and doped ceria used as buffer layer in solid oxide fuel cells
PublicationIn this paper, thin perovskite layers between cathode material of solid oxide fuel cells and gadolinia-doped ceria buffer layer are investigated. Thin layers made of LaNi0.6Fe0.4O3-δ (LNF), La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF), or SrTi0.65Fe0.35O3-δ (STF) were symmetrically deposited by spin coating method from metallo-organic polymer precursors on a Ce0.8Gd0.2O2-δ (CGO) substrate. Porous and about 40-μm-thick LNF cathodes were deposited...
-
Crossover from charge density wave stabilized antiferromagnetism to superconductivity in Nd1−xLaxNiC2 compounds
PublicationThe path from the charge density wave antiferromagnet NdNiC2 to the noncentrosymmetric superconductor LaNiC2 is studied by gradual replacement of Nd by La ions. The evolution of physical properties is explored by structural, magnetic, transport, magnetoresistance, and specific heat measurements. With the substitution of La for Nd, the Peierls temperature is gradually suppressed, which falls within the BCS mean-field relation for...
-
Electric and magnetic properties of Lanthanum Barium Cobaltite
PublicationThe cubic Ba0.5La0.5CoO3‐δ was synthesized using solid state reaction. The structural properties were determined by the simultaneous refinement of Synchrotron Powder X‐ray Diffraction and Neutron Powder Diffraction data. Iodometric titration was used to examine the oxygen stoichiometry and average cobalt oxidation state. Low‐temperature magnetic studies show soft ferromagnetic character of fully oxidized material, with θP = 198(3)...
-
THE ROLE OF THIN FUNCTIONAL LAYERS IN SOLID OXIDE FUEL CELLS
PublicationWidespread commercialization of solid oxide fuel cells requires lowering its cost. It is generally accepted that to lower the cost of solid oxide fuel cells it is necessary to use metal alloys as interconnectors and, consequently, lower its operating temperature to slow down interconnectors degradation. As a result the area specific resistance of the cathodes should be lowered to sustain the performance of the cells. In order to...
-
Synthesis, characterization, and application of 2D/2D TiO2-GO-ZnFe2O4 obtained by the fluorine-free lyophilization method for solar light-driven photocatalytic degradation of ibuprofen
PublicationIn this study, we report the potential of 2D/2D TiO2- GO-ZnFe2O4 photocatalyst obtained using the fluorine-free lyophilization technique for the degradation of ibuprofen belonging to the group of active pharmaceutical ingredients (API). The improved ibuprofen degradation under simulated solar light was achieved in the presence of a composite of 2D TiO2 combined with GO and embedded ZnFe2O4, which additionally provides superparamagnetic...
-
Structure and hyperfine interactions in Bi1−xNdxFeO3 solid solutions prepared by solid-state sintering
PublicationThe series of polycrystalline ceramic powders, Bi1xNdxFeO3 (x = 0.11) was successfully synthesized by mixed oxide method followed by pressureless sintering. X-ray diffraction and Mössbauer spectroscopy were used as complementary methods to study structure and hyperfine interactions of the samples. It was found that with an increase of Nd content, within the range of x = 0.20.3 a structural phase transition from rhombohedral to...
-
Physical properties and electronic structure of La3Co and La3Ni intermetallic superconductors
PublicationLa3Co and La3Ni are reported superconductors with transition temperatures of 4.5 and 6 K, respectively. Here, we reinvestigate the physical properties of these two intermetallic compounds with magnetic susceptibility χ, specific heat Cp and electrical resistivity ρ measurements down to 1.9 K. Although bulk superconductivity is confirmed in La3Co, as observed previously, only a trace of it is found in La3Ni, indicating that the...
-
Superconductivity in CaBi2
PublicationSuperconductivity is observed with critical temperature Tc = 2.0 K in self-flux-grown single crystals of CaBi2. This material adopts the ZrSi2 structure type with lattice parameters a = 4.696(1) Å, b = 17.081(2) Å and c = 4.611(1) Å. The crystals of CaBi2 were studied by means of magnetic susceptibility, specific heat and electrical resistivity measurements. The heat capacity jump at Tc is DC/gTc = 1.41, confirming bulk superconductivity;...
-
Changes on the Surface of the SiO2/C Composite, Leading to the Formation of Conductive Carbon Structures with Complex Nature of DC Conductivity
PublicationSol–gel layers have been the subject of many studies in recent decades. However, very little information exists about layers in which carbon structures are developed in situ. Using the spin-coating method, we obtained thin iron-doped SiO2/C composite films. The results of Raman spectroscopy showed that our samples consisted of graphitic forms and polymers. The latter’s contribution decreases with rising temperature. FTIR and EDS...
-
Hierarchical MnO2 nanoflowers blooming on 3D nickel foam: A novel micro-macro catalyst for peroxymonosulfate activation
PublicationIn this work, birnessite-type δ-MnO2 nanoflowers were uniformly deposited on 3D nickel foam (NF) by one-step hydrothermal route for high-efficient activation of peroxymonosulfate (PMS) towards degradation of acid orange 7 (AO7). High specific surface area, large pore volume and 3D hierarchical structure promotes the mass and electron transfer for great catalytic activity. Low reaction energy barrier (Ea=27.5 kJ/mol) and outstanding...
-
Enhanced photocatalytic properties of lanthanide-TiO2 nanotubes: An experimental and theoretical study
PublicationA series of Er-, Yb-, Ho-, Tb-, Gd-, Pr-TiO2 nanotubes (RE-NTs) was prepared via an electrochemical method. The as-prepared photocatalysts were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV–vis absorption, scanning electron microscopy (SEM) and luminescent spectroscopy. The experiments demonstrated that toluene in the gas phase was successfully degraded under visible light (LEDs λmax = 465...
-
Study of the Layer-Type BST Thin Film with X-ray Diffraction and X-ray Photoelectron Spectroscopy
PublicationIn the present paper, results of X-ray photoelectron studies of electroceramic thin films of barium strontium titanate, Ba1xSrxTiO3 (BST), composition deposited on stainless-steel substrates are presented. The thin films were prepared by the sol-gel method. A spin-coating deposition of BST layers with different chemical compositions was utilized so the layer-type structure of (0-2) connectivity was formed. After the deposition,...
-
Hidden Tensor Structures
PublicationAny single system whose space of states is given by a separable Hilbert space is automatically equipped with infinitely many hidden tensor-like structures. This includes all quantum mechanical systems as well as classical field theories and classical signal analysis. Accordingly, systems as simple as a single one-dimensional harmonic oscillator, an infinite potential well, or a classical finite-amplitude signal of finite duration...
-
Superconductivity in Metal-Rich Chalcogenide Ta2Se
PublicationThe metal–metal bond in metal-rich chalcogenide is known to exhibit various structures and interesting physical properties. Ta2Se can be obtained by both arc-melting and solid-state pellet methods. Ta2Se crystallizes a layered tetragonal structure with space group P4/nmm (No. 129; Pearson symbol tP6). Each unit cell consists of four layers of body-centered close-packing Ta atoms sandwiched between two square nets of Se atoms, forming...
-
Synthesis and physical properties of the 10.6 K ferromagnet NdIr3
PublicationThe magnetic, transport, and thermodynamic properties of NdIr3 are reported. Its PuNi3-type crystal structure (space group R−3m), with lattice parameters a= 5.3262(1)Å and c=26.2218(3)Å, was confirmed by powder x-ray diffraction. Our measurements indicate that NdIr3 exhibits a previously unreported paramagnetic to ferromagnetic phase transition below TC=10.6 K(determined by using the Arrott plot). The magnetic susceptibility obeys...
-
Rubrene Thin Films with Viably Enhanced Charge Transport Fabricated by Cryo-Matrix-Assisted Laser Evaporation
PublicationAmong organic semiconductors, rubrene (RB; C42H28) is of rapidly growing interest for the development of organic and hybrid electronics due to exceptionally long spin diffusion length and carrier mobility up to 20 cm2V−1s−1 in single crystals. However, the fabrication of RB thin films resembling properties of the bulk remains challenging, mainly because of the RB molecule’s twisted conformation. This hinders the formation of orthorhombic...
-
Elucidating photoluminescent properties of Eu‐doped Ca–Al–Si–O(–N) glasses and the local structures of Eu ions
PublicationEuropium (Eu) ion–doped luminescent materials have attracted considerable attention for their numerous optical applications. Eu-doped Ca–Al–Si–O(–N) glasses were synthesized from a mixture of oxynitride glasses and Eu2O3 powder using a standard melt-quenching technique in a radiofrequency furnace. The source Eu trivalent ions primarily changed to Eu2+ during melting, and the ratio of Eu2+ ions increased with an increase in Eu content...
-
Fabrication of high-density nitrogen-vacancy (NV) center-enriched diamond particles through methyl trityl amine (C20H19N) seeding
PublicationDiamond particles (DPs) show promise for advanced applications in bioimaging and quantum sensing due to the presence of defect centers. This work reports a unique growth process for diamond particles composed of nitrogen-vacancy centers (NV-DPs) using a methyl trityl amine (C20H19N) diamondoid seed, which acts as a nitrogen source for NV creation. Growth was performed via microwave plasma-assisted chemical vapor deposition in a...
-
Magnetically sensitive fiber probe with nitrogen-vacancy center nanodiamonds integrated in a suspended core
PublicationEfficient collection of photoluminescence arising from spin dynamics of nitrogen vacancy (NV) centers in diamond is important for practical applications involving precise magnetic field or temperature mapping. These goals may be realized by the integration of nanodiamond particles with optical fibers and volumetric doping of the particles alongside the fiber core. That approach combines the advantages of robust axial fixation of...
-
Enhanced electrochemical performance of partially amorphous La0.6Sr0.4CoO3-δ oxygen electrode materials for low-temperature solid oxide cells operating at 400 °C
PublicationThis work evaluates partially amorphous La0.6Sr0.4CoO3-δ (LSC) as a potential oxygen electrode for lowtemperature solid oxide cells. LSC was deposited using the spin-coating technique onto Ce0.8Gd0.2O2-δ (CGO) substrates. The optimal oxygen electrode thickness was determined as 500 nm. The electrochemical impedance spectroscopy (EIS) study showed a significant improvement in oxygen reduction/oxidation reaction kinetics when annealing...
-
Optical and electrical properties of boron doped diamond thin conductive films deposited on fused silica glass substrates
PublicationThis paper presents boron-doped diamond (BDD) film as a conductive coating for optical and electronic purposes. Seeding and growth processes of thin diamond films on fused silica have been investigated. Growth processes of thin diamond films on fused silica were investigated at various boron doping level and methane admixture. Two step pre-treatment procedure of fused silica substrate was applied to achieve high seeding density....
-
Enhanced photocatalytic, electrochemical and photoelectrochemical properties of TiO2 nanotubes arrays modified with Cu, AgCu and Bi nanoparticles obtained via radiolytic reduction
PublicationTiO2 nanotubes arrays (NTs), obtained via electrochemical anodization of Ti foil, were modified with monometallic (Cu, Bi) and bimetallic (AgCu) nanoparticles. Different amounts of metals’ precursors were deposited on the surface of NTs by the spin-coating technique, and the reduction of metals was performed via gamma radiolysis. Surface modification of titania was studied by EDS and XPS analysis. The results show that AgCu nanoparticles...
-
Engineering TADF, Mechanochromism, and Second Harmonic Up- conversion Properties in Regioisomeric Substitution Space
PublicationThis research article explores the distinct TADF efficiency of three donor-acceptor based regio-isomers: DPAOCN (ortho- isomer), DPAMCN (meta-isomer), and DPAPCN (para-isomer). DPAPCN exhibits maximum TADF efficiency in both solution and solid-state with an impressive reverse inter-system crossing (RISC) rate of ~ 106 s-1; the underlying cause being the minimum singlet-triplet splitting energy or ∆EST and maximum SOC (spin-orbit...
-
Superconducting SrSnP with Strong Sn–P Antibonding Interaction: Is the Sn Atom Single or Mixed Valent?
PublicationThe large single crystals of SrSnP were prepared using Sn self-flux method. The superconductivity in the tetragonal SrSnP is observed with the critical temperature of ∼2.3 K. The results of a crystallographic analysis, superconducting characterization, and theoretical assessment of tetragonal SrSnP are presented. The SrSnP crystallizes in the CaGaN structure type with space group P4/nmm (S.G. 129, Pearson symbol tP6) according...
-
Organic-inorganic composites consisted of poly(3,4-ethylenedioxythiophene)and Prussian Blue analogues
PublicationThe organic-inorganic material consisted of poly(3,4-ethylenedioxythiophene) (pEDOT) and copper hexacyanoferrate (Cuhcf) was synthesized. The pEDOT film with Fe(CN)63−/4− as counter-ions potentiodynamically polarized in aqueous CuCl2 electrolyte brings about stable hybrid material (pEDOT/Cuhcf) performing single redox activity of FeII/III at a formal potential Ef = 0.61 V (vs. Ag/AgCl/0.1 M KCl) and less clearly shaped two redox...
-
Cadmium complex possessing simultaneously silanethiolato- and dithiocarbamato-ligands. A novel single-source precursor of cadmium sulfide
PublicationThermal decomposition of suitable coordination compounds may be used as efficient route for fabrication of semiconducting layers. A new potential CdS precursor—a cadmium complex with all-sulfur Cd-coordination sphere [Cd{l-SSi(OBut)3}(S2CNC4H8)]2 (1) —has been prepared and its properties are investigated. The complex was obtained in the reaction between dimeric bis(tri-tert-butoxysilanethiolato) cadmium(II) [Cd{SSi(OBut)3}2]2 and...
-
Poly-L-Lysine-functionalized fluorescent diamond particles: pH triggered fluorescence enhancement via surface charge modulation
PublicationRecently, the interest in applying fluorescent diamond particles (FDPs) containing nitrogen-vacancy (NV) centers for enhancing the mechanical and chemical properties of some materials, biological imaging, and sensing has been expanding rapidly. The unique properties of NV centers such as intensive, time-stable fluorescence, and an electron spin, which exhibits long coherence time and may be manipulated using external stimuli, such...
-
BODIPY‐Perylene Charge Transfer Compounds; Sensitizers for Triplet‐Triplet Annihilation Up‐conversion
PublicationBODIPY heterochromophores, asymmetrically substituted with perylene and/or iodine at the 2 and 6 positions were prepared and investigated as sensitizers for triplet-triplet annihilation up conversion (TTA-UC). Single-crystal X-ray crystallographic analyses show that the torsion angle between BODIPY and perylene units lie between 73.54 and 74.51, though they are not orthogonal. Both compounds show intense, charge transfer absorption...
-
Impedimetric sensing of α-amino acids driven by micro-patterned 1,8-Diazafluoren-9-one into titania- boron- doped maze-like nanocarbons
PublicationThe development of impedimetric, non-faradaic label-free sensors for the detection of α-amino acids constitutes a trailblazing technology for the fast and inexpensive quantification of such biomarkers. Since α-amino acids, such as glycine and sarcosine, are basic constituents in biological processes, a variation in their concentration may be an indicator of cardiovascular diseases and metabolic disorders or neurological conditions....
-
Fabrication methods of smart composite coatings - review
PublicationPostoperative bacterial infections are one of the main reasons for unsuccessful implantation of long-term implants. The development of bacterial infection requires antibiotic therapy, in extreme cases a reimplantation procedure is necessary. In order to provide materials for implants with antibacterial properties, they are subjected to modifications to create a coating that will release the drug substance, when the inflammation...
-
Magnetic field mapping along a NV-rich nanodiamond-doped fiber
PublicationIntegration of NV−-rich diamond with optical fibers enables guiding quantum information on the spin state of the NV− color center. Diamond-functionalized optical fiber sensors have been demonstrated with impressive sub-nanotesla magnetic field sensitivities over localized magnetic field sources, but their potential for distributed sensing remains unexplored. The volumetric incorporation of diamonds into the optical fiber core allows...
-
Crystal and electronic structures of Ni(II) silanethiolates containing flexible diamine ligands
PublicationFive nickel(II) complexes containing aliphatic diamines and tri-tert-butoxysilanethiolate ligand have been synthesized for the purpose of studying their structural, spectral (IR, UV–Vis, HF EPR) and thermal properties. Complexes (1)–(5) have been prepared in high yield by reactions of [Ni{SSi(OtBu)3}2(NH3)(H2O)] with 1.3-propanediamine (L1), 1,6-hexanediamine (L2), or 1,7-heptanediamine (L3). The X-ray structures were determined...
-
Characteristics of LaCo 0.4 Ni 0.6-x Cu x O 3-δ ceramics as a cathode material for intermediate-temperature solid oxide fuel cells
PublicationIn this study, the effects of Cu-ion substitution on the densification, microstructure, and physical properties of LaCo0.4Ni0.6-xCuxO3-δ ceramics were investigated. The results indicate that doping with Cu ions not only enhances the densification but also promotes the grain growth of LaCo0.4Ni0.6-xCuxO3-δ ceramics. The Cu substitution at x ≤ 0.2 can suppress the formation of La4Ni3O10, while the excess Cu triggers the formation...
-
Sugar matters: sugar moieties as reactivity-tuning factors in quercetin O-glycosides
PublicationQuercetin, one of the most abundant flavonoids in plant-based foods, commonly occurs in nature in various glycosylated forms. There is still a less explored aspect regarding the cause of its glycosides diversity, depending on the sugars moiety attached. This work focuses on four widespread quercetin glycosides—hyperoside, isoquercitrin, quercitrin and rutin—by testing property-tuning capacity of different sugar moieties and thus...